Assessment of the Micro-Tensile Strength of the Composites for the Various Antioxidants: An In Vitro Study

Introduction

The application of the antioxidants after the teeth are bleached has been advocated to fasten the restorative process post-bleaching. The motive of this study was to examine and assess the micro-tensile binding strength of bleached enamel to the resin using a variety of antioxidant solutions. Finding the reason for the tooth fracture was the secondary outcome measured.

Materials and Methods

An in vitro study was planned with 100 human extracted teeth, with 20 in each group with one as controls and 4 others tested for the antioxidants sodium ascorbate, epigallocatechin gallate, chitosan, and proanthocyanidin application. The bond strength of bleached enamel to the resin was well as the failure type was assessed after the values were noted and compared using the ANOVA and Tukey's methods keeping P < 0.05 as significant.

Results

Epigallocatechin gallate specimens displayed the maximum micro-tensile bond strength under the investigational circumstances, whereas controls displayed the lowest micro-tensile bond strength. There was statistical alteration in micro-tensile bond strengths between all the groups except between epigallocatechin gallate vs chitosan and sodium ascorbate vs proanthocyanidin. High statistical significance was seen between the control and the antioxidant groups as well as between sodium ascorbate and epigallocatechin gallate and chitosan.

Conclusion

The antioxidant chemicals significantly augmented the bond strength of bleached enamel to the resin that had been bleached. Also, when compared to the other experimental groups, epigallocatechin gallate and chitosan treatment displayed the greatest mean bond strength values.

[Influence of the dentin smear layer trait on the bond strength of the self-adhesive resin cements]

OBJECTIVE

This work aimed to evaluate the influence of smear layer on the bonding effectiveness and durability of the self-adhesive resin cements to dentin.

METHODS

A total of 48 fresh caries-free third molars with exposed dentin surface were divided into two groups. The dentin surfaces were treated using a standard grit diamond bur (group A) or further polished using a fine grit diamond bur (group B) and then bonded with either of the two self-adhesive resin cements, namely, Clearfil SA Cement (CSA, Kuraray) and Multilink Speed (MS, Ivoclar Vivadent). After 24 h or 2-year water storage, a microtensile bond strength test was performed.

RESULTS

In group A, the dentin surface was rough, the smear layer was thick, and the dentin tubule orifice detritus showed low embolism value. In group B, the dentin surface roughness decreased, the embolism proportion increased, and the smear layer became thin. The initial bonding strengths of CSA and MS in group A were significantly lower than those in group B (P<0.05). The bonding strengths of CSA and MS significantly decreased after two years of water storage (P<0.05). For CSA, the bond strength of group B was significantly lower than that of group A (P<0.05). For MS, the differences in the bonding strength between groups A and B were insignificant (P>0.05).

CONCLUSIONS

The properties of the smear layer and the types of self-adhesive resin cement used affected the bond strength and durability.

Effect of Dentin Wetness on the Bond Strength of Universal Adhesives

The effects of dentin wetness on the bond strength and adhesive interface morphology of universal adhesives have been investigated using micro-tensile bond strength (μTBS) testing and confocal laser scanning microscopy (CLSM). Seventy-two human third molars were wet ground to expose flat dentin surfaces. They were divided into three groups according to the air-drying time of the dentin surfaces: 0 (without air drying), 5, and 10 s. The dentin surfaces were then treated with three universal adhesives: G-Premio Bond, Single Bond Universal, and All-Bond Universal in self-etch or etch-and-rinse mode. After composite build up, a μTBS test was performed. One additional tooth was prepared for each group by staining the adhesives with 0.01 wt % of Rhodamine B fluorescent dye for CLSM analysis. The data were analyzed statistically using ANOVA and Tukey's post hoc tests (α = 0.05). Two-way ANOVA showed significant differences among the adhesive systems and dentin moisture conditions. An interaction effect was also observed (p < 0.05). One-way ANOVA showed that All-Bond Universal was the only material influenced by the wetness of the dentin surfaces. Wetness of the dentin surface is a factor influencing the micro-tensile bond strength of universal adhesives.