Innovative macroporous granules of nanostructured-hydroxyapatite agglomerates: bioactivity and osteoblast-like cell behaviour

Natural bone-mimicking nanopore-incorporated hydroxyapatite scaffolds for enhanced bone tissue regeneration

Background

A considerable number of studies has been carried out to develop alloplastic bone graft materials such as hydroxyapatite (HAP) that mimic the hierarchical structure of natural bones with multiple levels of pores: macro-, micro-, and nanopores. Although nanopores are known to play many essential roles in natural bones, only a few studies have focused on HAPs containing them; none of those studies investigated the functions of nanopores in biological systems.

Method

We developed a simple yet powerful method to introduce nanopores into alloplastic HAP bone graft materials in large quantities by simply pressing HAP nanoparticles and sintering them at a low temperature.

Results

The size of nanopores in HAP scaffolds can be controlled between 16.5 and 30.2 nm by changing the sintering temperature. When nanopores with a size of ~ 30.2 nm, similar to that of nanopores in natural bones, are introduced into HAP scaffolds, the mechanical strength and cell proliferation and differentiation rates are significantly increased. The developed HAP scaffolds containing nanopores (SNPs) are biocompatible, with negligible erythema and inflammatory reactions. In addition, they enhance the bone regeneration when are implanted into a rabbit model. Furthermore, the bone regeneration efficiency of the HAP-based SNP is better than that of a commercially available bone graft material.

Conclusion

Nanopores of HAP scaffolds are very important for improving the bone regeneration efficiency and may be one of the key factors to consider in designing highly efficient next-generation alloplastic bone graft materials.

Supplementary Information

The online version contains supplementary material available at 10.1186/s40824-022-00253-x.

Translational Research for Orthopedic Bone Graft Development

Designing biomaterials for bone-substitute applications is still a challenge regarding the natural complex structure of hard tissues. Aiming at bone regeneration applications, scaffolds based on natural collagen and synthetic nanohydroxyapatite were developed, and they showed adequate mechanical and biological properties. The objective of this work was to perform and evaluate a scaled-up production process of this porous biocomposite scaffold, which promotes bone regeneration and works as a barrier for both fibrosis and the proliferation of scar tissue. The material was produced using a prototype bioreactor at an industrial scale, instead of laboratory production at the bench, in order to produce an appropriate medical device for the orthopedic market. Prototypes were produced in porous membranes that were e-beam irradiated (the sterilization process) and then analysed by scanning electron microscopy (SEM), confocal laser scanning microscopy (CLSM), dynamic mechanical analysis (DMA), cytotoxicity tests with mice fibroblasts (L929), human osteoblast-like cells (MG63) and human MSC osteogenic differentiation (HBMSC) with alkaline phosphatase (ALP) activity and qPCR for osteogenic gene expression. The prototypes were also implanted into critical-size bone defects (rabbits' tibia) for 5 and 15 weeks, and after that were analysed by microCT and histology. The tests performed for the physical characterization of the materials showed the ability of the scaffolds to absorb and retain water-based solvents, as well as adequate mechanical resistance and viscoelastic properties. The cryogels had a heteroporous morphology with microporosity and macroporosity, which are essential conditions for the interaction between the cells and materials, and which consequently promote bone regeneration. Regarding the biological studies, all of the studied cryogels were non-cytotoxic by direct or indirect contact with cells. In fact, the scaffolds promoted the proliferation of the human MSCs, as well as the expression of the osteoblastic phenotype (osteogenic differentiation). The in vivo results showed bone tissue ingrowth and the materials' degradation, filling the critical bone defect after 15 weeks. Before and after irradiation, the studied scaffolds showed similar properties when compared to the results published in the literature. In conclusion, the material production process upscaling was optimized and the obtained prototypes showed reproducible properties relative to the bench development, and should be able to be commercialized. Therefore, it was a successful effort to harness knowledge from the basic sciences to produce a new biomedical device and enhance human health and wellbeing.

In Vitro Biocompatibility Assessment of Nano-Hydroxyapatite

Hydroxyapatite (HA) is an important component of the bone mineral phase. It has been used in several applications, such as bone regenerative medicine, tooth implants, drug delivery and oral care cosmetics. In the present study, three different batches of a commercial nanohydroxyapatite (nHA) material were physicochemically-characterized and biologically-evaluated by means of cytotoxicity and genotoxicity using appropriate cell lines based on well-established guidelines (ISO10993-5 and OECD 487). The nHAs were characterized for their size and morphology by dynamic light scattering (DLS) and transmission electron microscopy (TEM) and were found to have a rod-like shape with an average length of approximately 20 to 40 nm. The nanoparticles were cytocompatible according to ISO 10993-5, and the in vitro micronucleus assay showed no genotoxicity to cells. Internalization by MC3T3-E1 cells was observed by TEM images, with nHA identified only in the cytoplasm and extracellular space. This result also validates the genotoxicity since nHA was not observed in the nucleus. The internalization of nHA by the cells did not seem to affect normal cell behavior, since the results showed good biocompatibility of these nHA nanoparticles. Therefore, this work is a relevant contribution for the safety assessment of this nHA material.

State-of-the-Art of Eggshell Waste in Materials Science: Recent Advances in Catalysis, Pharmaceutical Applications, and Mechanochemistry

Eggshell waste is among the most abundant waste materials coming from food processing technologies. Despite the unique properties that both its components (eggshell, ES, and eggshell membrane, ESM) possess, it is very often discarded without further use. This review article aims to summarize the recent reports utilizing eggshell waste for very diverse purposes, stressing the need to use a mechanochemical approach to broaden its applications. The most studied field with regards to the potential use of eggshell waste is catalysis. Upon proper treatment, it can be used for turning waste oils into biodiesel and moreover, the catalytic effect of eggshell-based material in organic synthesis is also very beneficial. In inorganic chemistry, the eggshell membrane is very often used as a templating agent for nanoparticles production. Such composites are suitable for application in photocatalysis. These bionanocomposites are also capable of heavy metal ions reduction and can be also used for the ozonation process. The eggshell and its membrane are applicable in electrochemistry as well. Due to the high protein content and the presence of functional groups on the surface, ESM can be easily converted to a high-performance electrode material. Finally, both ES and ESM are suitable for medical applications, as the former can be used as an inexpensive Ca2+ source for the development of medications, particles for drug delivery, organic matrix/mineral nanocomposites as potential tissue scaffolds, food supplements and the latter for the treatment of joint diseases, in reparative medicine and vascular graft producing. For the majority of the above-mentioned applications, the pretreatment of the eggshell waste is necessary. Among other options, the mechanochemical pretreatment has found an inevitable place. Since the publication of the last review paper devoted to the mechanochemical treatment of eggshell waste, a few new works have appeared, which are reviewed here to underline the sustainable character of the proposed methodology. The mechanochemical treatment of eggshell is capable of producing the nanoscale material which can be further used for bioceramics synthesis, dehalogenation processes, wastewater treatment, preparation of hydrophobic filters, lithium-ion batteries, dental materials, and in the building industry as cement.

Combining local antibiotic delivery with heparinized nanohydroxyapatite/collagen bone substitute: A novel strategy for osteomyelitis treatment

Osteomyelitis is a major challenge in bone surgery and conventional treatment is frequently ineffective to control the infection, with an alternative approach being required. In the present work, a heparinized nanohydroxyapatite/collagen biocomposite was produced in granular form, and loaded with vancomycin, to work as a local drug delivery system for osteomyelitis and as a bone substitute. This strategy involves the local delivery of high concentrations of vancomycin, to eradicate the infection. Additionally, these granules work as a scaffold with regenerative properties, to induce bone regeneration after antibiotic release. The heparinized nanohydroxyapatite/collagen granular bone substitute was produced using two different sintering temperatures to study their effect on granules properties and on vancomycin release profile. Morphological, topographic, chemical and mechanical characterization were carried out for granules sintered at both temperatures and some relevant differences were found. The mechanical strength was increased by several orders of magnitude with increasing sintering temperature, being able to maintain their porous macrostructure and withstand important processes for their commercialization such as packaging, shipping and surgical manipulation. The nanohydroxyapatite/collagen granules were able to release high concentrations of vancomycin, always above MIC, for 19 days. The released antibiotic was able to eradicate both planktonic and sessile methicillin-resistant Staphylococcus aureus. The cytotoxicity was assessed according to ISO 10993-5:2009 and the granules sintered at higher temperature showed no cytotoxic effect. Considering these results nanohydroxyapatite/collagen biocomposite loaded with vancomycin is a promising solution for osteomyelitis treatment.

Development and characterisation of bilayered periosteum-inspired composite membranes based on sodium alginate-hydroxyapatite nanoparticles

BACKGROUND AND AIM

Membranes for guided bone regeneration should have a mechanical structure and a chemical composition suitable for mimicking biological structures. In this work, we pursue the development of periosteum-inspired bilayered membranes obtained by crosslinking alginate with different amounts of nanohydroxyapatite.

EXPERIMENTS

Alginate-nanohydroxyapatite interaction was studied by rheology and infrared spectroscopy measurements. The membranes were characterized regarding their tensile strength, degradation and surface morphology. Finally, cell cultures were performed on each side of the membranes.

FINDINGS

The ionic bonding between alginate polysaccharide networks and nanohydroxyapatite was proven, and had a clear effect in the strength and microstructure of the hydrogels. Distinct surface characteristics were achieved on each side of the membranes, resulting in a highly porous fibrous side and a mineral-rich side with higher roughness and lower porosity. Moreover, the effect of amount of nanohydroxyapatite was reflected in a decrease of the membranes' plasticity and an increment of degradation rate. Finally, it was proved that osteoblast-like cells proliferated and differentiated on the mineral-rich side, specially when a higher amount of nanohydroxyapatite was used, whereas fibroblasts-like cells were able to proliferate on the fibrous side. These periosteum-inspired membranes are promising biomaterials for guided tissue regeneration applications.

Biomimetic Composite Scaffold With Phosphoserine Signaling for Bone Tissue Engineering Application

In guided bone tissue engineering, successful ingrowth of MSCs depends primarily on the nature of the scaffold. It is well-known that only seconds after implantation, biomaterials are coated by a layer of adsorbed proteins/peptides which modulates the subsequent cell/scaffold interactions, especially at early times after implantation. In this work, nanohydroxyapatite and collagen based composite materials (Coll/nanoHA) were modified with phosphorylated amino acid (O-phospho-L-serine-OPS) to mimic bone tissue, and induce cell differentiation. The choice for this phosphorylated amino acid is due to the fact that osteopontin is a serine-rich glycol-phosphoprotein and has been associated to the early stages of bone formation, and regeneration. Several concentrations of OPS were added to the Coll/nanoHA scaffold and physico-chemical, mechanical, and in vitro cell behavior were evaluated. Afterwards, the composite scaffold with stronger mechanical and best cellular behavior was tested in vivo, with or without previous in vitro culture of human MSC's (bone tissue engineering). The OPS signaling of the biocomposite scaffolds showed similar cellular adhesion and proliferation, but higher ALP enzyme activity (HBMSC). In vivo bone ectopic formation studies allowed for a thorough evaluation of the materials for MSC's osteogenic differentiation. The OPS-scaffolds results showed that the material could modulated mesenchymal cells behavior in favor of osteogenic differentiation into late osteoblasts that gave raised to their ECM with human bone proteins (osteopontin) and calcium deposits. Finally, OPS-modified scaffolds enhanced cell survival, engraftment, migration, and spatial distribution within the 3D matrix that could be used as a cell-loaded scaffold for tissue engineering applications and accelerate bone regeneration processes.

Nano-hydroxyapatite in oral care cosmetics: characterization and cytotoxicity assessment

Nano-hydroxyapatite has been used as an oral care ingredient, being incorporated in several products for the treatment of dental hypersensitivity and enamel remineralisation. Despite its promising results, regulatory and safety concerns have been discussed and questioned by the European Scientific Committee on Consumer Safety (SCCS) regarding the usage of hydroxyapatite nanoparticles in oral care products. In this work, a commercially available nano-hydroxyapatite was characterized and its cytocompatibility towards human gingival fibroblasts was evaluated, as well as its irritation potential using the in vitro HET-CAM assay. All the conditions chosen in this study tried to simulate the tooth brushing procedure and the hydroxyapatite nanoparticles levels normally incorporated in oral care products. The commercial hydroxyapatite nanoparticles used in this study exhibited a rod-like morphology and the expected chemical and phase composition. The set of in vitro cytotoxicity parameters accessed showed that these nanoparticles are highly cytocompatible towards human gingival fibroblasts. Additionally, these nanoparticles did not possess any irritation potential on HET-CAM assay. This study clarifies the issues raised by SCCS and it concludes that this specific nano-hydroxyapatite is cytocompatible, as these nanoparticles did not alter the normal behaviour of the cells. Therefore, they are safe to be used in oral care products.

Eggshell Based Nano-Engineered Hydroxyapatite and Poly(lactic) Acid Electrospun Fibers as Potential Tissue Scaffold

Nanocomposite electrospun fibers were fabricated from poly(lactic) acid (PLA) and needle-like hydroxyapatite nanoparticles made from eggshells. The X-ray diffraction spectrum and the scanning electron micrograph showed that the hydroxyapatite particles are highly crystalline and are needle-liked in shape with diameters between 10 and 20 nm and lengths ranging from 100 to 200 nm. The microstructural, thermal, and mechanical properties of the electrospun fibers were characterized using scanning electron microscope (SEM), thermogravimetric analysis (TGA), dynamic scanning calorimetry (DSC), and tensile testing techniques. The SEM study showed that both pristine and PLA/EnHA fibers surfaces exhibited numerous pores and rough edges suitable for cell attachment. The presence of the rod-liked EnHA particles was found to increase thermal and mechanical properties of PLA fibers relative to pristine PLA fibers. The confocal optical images showed that osteoblast cells were found to attach on dense pristine PLA and PLA/HA-10 wt% fibers after 48 hours of incubation. The stained confocal optical images indicated the secretion of cytoplasmic extension linking adjoining nuclei after 96 hours of incubation. These findings showed that eggshell based nanohydroxyapatite and poly(lactic acid) fibers could be potential scaffold for tissue regeneration.

Size effect of nano-hydroxyapatite on proliferation of odontoblast-like MDPC-23 cells

Nano-hydroxyapatite (nano-HAP) is supposed to be a promising candidate for apatite substitute in hard tissue engineering. We aimed to investigate the effect of nano-HAP particles on the proliferation of odontoblast-like MDPC-23 cells compared with conventional hydroxyapatite (c-HAP). HAP in diameter of ~20 nm (np20), ~70 nm (np70) and ~200 nm (c-HAP) were synthesized and characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), transmission electron microscopy (TEM) and field emission scanning electron microscopy (FESEM). Inverted microscope and MTT assay were used to detect the morphology and proliferation rate of MDPC-23 cells; TEM was used to reveal the internalization of HAP. We found that nano-HAP (np20 and np70), especially np20 expressed obvious growth-promoting effect on MDPC-23 cells compared with c-HAP, which caused the most vacuole in MDPC-23 cells. These results suggest that nano-HAP may be an optimal choice of apatite substitute for MDPC-23 cells on the aspect of cell proliferation.

Micropatterned Silica Films with Nanohydroxyapatite for Y-TZP Implants

This investigation aimed at developing micropatterned silica thin films (MSTFs) containing nanohydroxyapatite (nano-HA) microaggregates that were not completely covered by silica so that they could directly interact with the surrounding cells. The objectives were 1) to evaluate the effect of the presence of 2 films (MSTF with or without nano-HA addition) on the characteristic strength (σ₀) and Weibull modulus ( m) of a yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) and 2) to evaluate the effect of these 2 films, as applied onto the Y-TZP surface, on the morphology, orientation, and proliferation of MG63 cells. Sol-gel process and soft lithography were used to apply the MSTF onto the Y-TZP specimens. Three experimental groups were produced: Y-TZP, Y-TZP + MSTF, and Y-TZP + MSTF + sprayed nano-HA. All surfaces were characterized by scanning electron microscopy and energy-dispersive X-ray spectroscopy and tested for 4-point flexural strength ( n = 30) in water at 37 °C. Weibull analysis was used to determine m and σ₀ (maximum likelihood method). In vitro biological behavior was performed with human osteoblast-like cells (MG63). Y-TZP was successfully coated with MSFT and MSFT + nano-HA. Scanning electron microscopy micrographs indicated that the microaggregates of nano-HA were not entirely covered by the silica. There was no statistically significant difference among the experimental groups for σ₀ and m. In the groups containing the films, the cells were elongated and aligned along the lines. The MSFT + nano-HA group showed significantly higher cell metabolic activity than that obtained for the Y-TZP group at day 7. This investigation was successful in producing an MSTF containing nano-HA microaggregates that remained exposed to the environment. The developed films did not jeopardize the structural reliability of a commercial Y-TZP, as confirmed by the Weibull statistics. The MG63 cells seeded over the films became elongated and aligned along the films' micropatterned lines. Y-TZP specimens coated with MSTF and nano-HA showed a higher cell metabolic activity and proliferation after 7 d of culture when compared with uncoated Y-TZP.

Multifunctional PLLA-ceramic fiber membranes for bone regeneration applications

A novel method to process electrospun poly(l-lactic acid) (PLLA) membranes incorporating glass reinforced hydroxyapatite granules (gHA) interspacially between the polymeric fibers is reported, thus increasing the surface area for cellular interactions. gHA granules (≤150μm) electrospun together with the polymer solution, lead to an average fiber diameter of 550±150nm for pristine PLLA and 440±170nm for the composite samples. An increase of the overall porosity was observed, from 79±3% for the PLLA up to 88±5% for the hybrid samples, keeping material's wettability and mechanical properties. Bone-bonding ability showed that both samples induced HA crystal nucleation, but with a distinct pattern of mineral deposition. gHA microcomposite allows a better F-actin cytoskeleton organization during the initial adhesion and spreading, favoring cell-fibers and cell-to-cell interactions and enhanced alkaline phosphatase activity, making them potential candidates for bone healing strategies.

Antibacterial activity and biocompatibility of three-dimensional nanostructured porous granules of hydroxyapatite and zinc oxide nanoparticles--an in vitro and in vivo study

Ceramic scaffolds are widely studied in the bone tissue engineering field due to their potential in regenerative medicine. However, adhesion of microorganisms on biomaterials with subsequent formation of antibiotic-resistant biofilms is a critical factor in implant-related infections. Therefore, new strategies are needed to address this problem. In the present study, three-dimensional and interconnected porous granules of nanostructured hydroxyapatite (nanoHA) incorporated with different amounts of zinc oxide (ZnO) nanoparticles were produced using a simple polymer sponge replication method. As in vitro experiments, granules were exposed to Staphylococcus aureus and Staphylococcus epidermidis and, after 24 h, the planktonic and sessile populations were assessed. Cytocompatibility towards osteoblast-like cells (MG63 cell line) was also evaluated for a period of 1 and 3 days, through resazurin assay and imaging flow cytometry analysis. As in vivo experiments, nanoHA porous granules with and without ZnO nanoparticles were implanted into the subcutaneous tissue in rats and their inflammatory response after 3, 7 and 30 days was examined, as well as their antibacterial activity after 1 and 3 days of S. aureus inoculation. The developed composites proved to be especially effective at reducing bacterial activity in vitro and in vivo for a weight percentage of 2% ZnO, with a low cell growth inhibition in vitro and no differences in the connective tissue growth and inflammatory response in vivo. Altogether, these results suggest that nanoHA-ZnO porous granules have a great potential to be used in orthopaedic and dental applications as a template for bone regeneration and, simultaneously, to restrain biomaterial-associated infections.

Heparinized nanohydroxyapatite/collagen granules for controlled release of vancomycin

The purpose of this study was to develop a bone substitute material capable of preventing or treating osteomyelitis through a sustainable release of vancomycin and simultaneously inducing bone regeneration. Porous heparinized nanohydroxyapatite (nanoHA)/collagen granules were characterized using scanning electron microscopy, micro-computed tomography and attenuated total reflectance Fourier transform infrared spectroscopy. After vancomycin adsorption onto the granules, its releasing profile was studied by UV molecular absorption spectroscopy. The heparinized granules presented a more sustainable release over time, in comparison with nonheparinized nanoHA and nanoHA/collagen granules. Vancomycin was released for 360 h and proved to be bioactive until 216 h. Staphylococcus aureus adhesion was higher on granules containing collagen, guiding the bacteria to the material with antibiotic, improving their eradication. Moreover, cytotoxicity of the released vancomycin was assessed using osteoblast cultures, and after 14 days of culture in the presence of vancomycin, cells were able to remain viable, increasing their metabolic activity and colonizing the granules, as observed by scanning electron microscopy and confocal laser scanning microscopy. These findings suggest that heparinized nanoHA/collagen granules are a promising material to improve the treatment of osteomyelitis, as they are capable of releasing vancomycin, eliminating the bacteria, and presented morphological and chemical characteristics to induce bone regeneration.

Dual-setting brushite-silica gel cements

The current study describes a dual-mechanism-setting cement that combines a brushite-forming cement paste with a second inorganic silica-based precursor. Materials were obtained by pre-hydrolyzing tetraethyl orthosilicate (TEOS) under acidic conditions following the addition of a calcium phosphate cement (CPC) powder mixed of β-tricalcium phosphate and monocalcium phosphate. Cement setting occurred by a dissolution-precipitation process, while changes in pH during setting simultaneously initiated the condensation reaction of the hydrolyzed TEOS. This resulted in an interpenetrating phase composite material in which the macropores of the CPC were infiltrated by the microporous silica gel, leading to a higher density and a compressive strength ∼5-10 times higher than the CPC reference. This also altered the release of vancomycin as a model drug, whereby in contrast to the quantitative release from the CPC reference, 25% of the immobilized drug remained in the composite matrix. By varying the TEOS content in the composite, the cement phase composition could be controlled to form either brushite, anhydrous monetite or a biphasic mixture of both. The composites with the highest silicate content showed a cell proliferation similar to a hydroxyapatite reference with a significantly higher activity per cell. Surprisingly, the biological response did not seem to be attributed to the released silicate ions, but to the release of phosphate and the adsorption of magnesium ions from the cell culture medium.

Freeze-Casted Nanostructured Apatite Scaffold Obtained from Low Temperature Biomineralization of Reactive Calcium Phosphates

Macroporous nanostructured calcium phosphate scaffold was produced at low temperature using freeze casting technique. Aqueous suspension of tetracalcium phosphate and dicalcium phosphate anhydrous was freeze-casted into cylindrical samples using an automated freeze casting device and subsequently freeze-dried. The sample was stored at 37 °C and 100% relative humidity for 24h, and then kept in simulated body fluid (SBF) for 7 days. The phase composition and microstructure of scaffold was characterized by X-ray diffraction and scanning electronic microscopy, respectively. Cell proliferation and attachment was also studied using Rat calvarium osteoblasts. The results showed a porous structure with total porosity of 75% and pore diameter ranging 50-150 μm and compressive strength of 5 ± 1 Mpa. The scaffolds had been composed of needle-like nanocrystals at the range of 40-100 nm. The XRD and FTIR data confirmed complete conversion of tetracalcium phosphate and dicalcium phosphate reactants into carbonate-substituted apatite phase due to the immersion process without any other impure phases. The results of cell studies revealed well attachment of osteoblasts on the pores and walls of the scaffolds as well as a time dependent proliferation and increased alkaline phosphatase activity. The produced scaffold has the requirements of an osteoinductive material but more in vitro and in vivo studies are required to prove this suggestion.

Influence of nanohydroxyapatite surface properties on Staphylococcus epidermidis biofilm formation

Nanohydroxyapatite (nanoHA), due to its chemical properties, has appeared as an exceptionally promising bioceramic to be used as bone regeneration material. Staphylococcus epidermidis have emerged as major nosocomial pathogens associated with infections of implanted medical devices. In this work, the purpose was to study the influence of the nanoHA surface characteristics on S. epidermidis RP62A biofilm formation. Therefore, two different initial inoculum concentrations (Ci) were used in order to check if these would affect the biofilm formed on the nanoHA surfaces. Biofilm formation was followed by the enumeration of cultivable cells and by scanning electron microscopy. Surface topography, contact angle, total surface area and porosimetry of the biomaterials were studied and correlated with the biofilm data. The surface of nanoHA sintered at 830℃ (nanoHA830) showed to be more resistant to S. epidermidis attachment and accumulation than that of nanoHA sintered at 1000℃ (nanoHA1000). The biofilm formed on nanoHA830 presented differences in terms of structure, surface coverage and EPS production when compared to the one formed on nanoHA1000 surface. It was observed that topography and surface area of nanoHA surfaces had influence on the bacterial attachment and accumulation. Ci influenced bacteria attachment and accumulation on nanoHA surfaces over time. The choice of the initial inoculum concentration was relevant proving to have an effect on the extent of adherence thus being a critical point for human health if these materials are used in implantable devices. This study showed that the initial inoculum concentration and surface material properties determine the rate of microbial attachment to substrata and consequently are related to biofilm-associated infections in biomaterials.

Preparation and characterization of collagen-nanohydroxyapatite biocomposite scaffolds by cryogelation method for bone tissue engineering applications

Recent efforts of bone repair focus on development of porous scaffolds for cell adhesion and proliferation. Collagen-nanohydroxyapatite (HA) scaffolds (70:30; 50:50; and 30:70 mass percentage) were produced by cryogelation technique using 1-ethyl-3-(3-dimethyl aminopropyl) carbodiimide hydrochloride/N-hydroxysuccinimide as crosslinking agents. A pure collagen scaffold was used as control. Morphology analysis revealed that all cryogels had highly porous structure with interconnective porosity and the nanoHA aggregates were randomly dispersed throughout the scaffold structure. Chemical analysis showed the presence of all major peaks related to collagen and HA in the biocomposites and indicated possible interaction between nanoHA aggregates and collagen molecules. Porosity analysis revealed an enhancement in the surface area as the nanoHA percentage increased in the collagen structure. The biocomposites showed improved mechanical properties as the nanoHA content increased in the scaffold. As expected, the swelling capacity decreased with the increase of nanoHA content. In vitro studies with osteoblasts cells showed that they were able to attach and spread in all cryogels surfaces. The presence of collagen-nanoHA biocomposites resulted in higher overall cellular proliferation compared to pure collagen scaffold. A statistically significant difference between collagen and collagen-nanoHA cryogels was observed after 21 day of cell culture. These innovative collagen-nanoHA cryogels could have potentially appealing application as scaffolds for bone regeneration.

Reciprocal induction of human dermal microvascular endothelial cells and human mesenchymal stem cells: time-dependent profile in a co-culture system

OBJECTIVES

Angiogenesis is closely associated with osteogenesis where reciprocal interactions between endothelial and osteoblast cells play an important role in bone regeneration. For these reasons, the aim of this work was to develop a co-culture system to study in detail any time-dependent interactions between human mesenchymal stem cells (HMSC) and human dermal microvascular endothelial cells (HDMEC), co-cultured in a 2D system, for 35 days.

MATERIALS AND METHODS

HMSC and HDMEC were co-cultured at a ratio of 1:4, respectively. Single-cell cultures were used as controls. Cell viability/proliferation was assessed using MTT, DNA quantification and calcein-AM assays. Cell morphology was monitored using confocal microscopy, and real time PCR was performed. Alkaline phosphatase activity and histochemical staining were evaluated. Matrix mineralization assays were also performed.

RESULTS

Cells were able to grow in characteristic patterns maintaining their viability and phenotype expression throughout culture time, compared to HMSC and HDMEC monocultures. HMSC differentiation seemed to be enhanced in the co-culture conditions, since it was observed an over expression of osteogenesis-related genes, and of ALP activity. Furthermore, presence of calcium phosphate deposits was also confirmed.

CONCLUSIONS

This work reports in detail the interactions between HMSC and HDMEC in a long-term co-culture 2D system. Endothelial and mesenchymal stem cells cultured in the present co-culture conditions ensured proliferation and phenotype differentiation of cell types, osteogenesis stimulation and over-expression of angiogenesis-related genes, in the same culture system. It is believed that the present work can lead to significant developments for bone tissue regeneration and cell biology studies.

Effect of crystallization heat treatment on the microstructure of niobium-doped fluorapatite glass-ceramics

Our goal was to study the effect of heat treatment temperature and heating rate on the microstructure and crystalline phases and assess the domain of existence of submicrometer fluorapatite crystals in niobium-doped fluorapatite glass-ceramics for biomedical applications. Glass-ceramic specimens were prepared by casting and heat treatment between 700 and 1200°C using a fast or a slow heating rate. The microstructure was characterized by atomic force microscopy and scanning electron microscopy. Crystalline phases were analyzed by x-ray diffraction. AFM of the as-cast glass revealed that amorphous phase separation occurred in this system. XRD confirmed the presence of fluorapatite in all specimens, together with forsterite and enstatite at higher temperatures. Both heating rate and heat treatment temperature strongly influenced microstructure and crystallinity. A dual microstructure with submicrometer fluorapatite crystals and polygonal forsterite crystals was obtained when slow heating rates and crystallization temperatures between 950 and 1100°C were used. Needle-shaped fluorapatite crystals appeared after heat treatment above 1100°C. Fast heating rates led to an increase in crystal size. Heat treatment temperatures should remain below 1100°C, together with slow heating rates, to prevent crystal dissolution, and preserve a dual microstructure of finely dispersed submicrometer crystals without growth of needle-shaped crystals.