Catechol-thiol-based dental adhesive inspired by underwater mussel adhesion

Micro-shear bond strength of a novel resin-modified glass ionomer luting cement (eRMGIC) functionalized with organophosphorus monomer to different dental substrates

Objectives

This study aims to assess and compare the micro-shear bond strength (μSBS) of a novel resin-modified glass-ionomer luting cement functionalized with a methacrylate co-monomer containing a phosphoric acid group, 30 wt% 2-(methacryloxy) ethyl phosphate (2-MEP), with different substrates (dentin, enamel, zirconia, and base metal alloy). This assessment is conducted in comparison with conventional resin-modified glass ionomer cement and self-adhesive resin cement.

Materials and methods

In this in vitro study, ninety-six specimens were prepared and categorized into four groups: enamel (A), dentin (B), zirconia (C), and base metal alloys (D). Enamel (E) and dentin (D) specimens were obtained from 30 human maxillary first premolars extracted during orthodontic treatment. For zirconia and metal alloys, 48 disks were manufactured using IPS e.max ZirCAD through dry milling and Co-Cr powder alloy by selective laser milling. Each group was further subdivided into three subgroups (n = 8) according to the luting cement used: (1) Fuji PLUS resin-modified glass ionomer luting cement (FP) as a control cement, (2) modified control cement (eRMGIC), and (3) RelyX U 200 (RU 200) self-adhesive resin cement. The two-way analysis of variance and Tukey's HSD were used to assess the data obtained from measuring the μSBS of the samples.

Results

The results of this study showed that the mean μSBS values of eRMGIC were statistically higher compared to FP in all tested groups (p < 0.001). The mean μSBS results of eRMGIC were non-significantly different from those recorded by RU 200 for all substrates except for the dentin substrate, where the RU200 cement produced significantly higher strength (p < 0.001). The failure modes were limited to a combination of mixed and adhesive failures without pure cohesive failure.

Significance

The functionalization of FP with an organophosphorus co-monomer (2-MEP) directly affects the adhesion performance of the functionalized cement, which may be utilized to develop a new type of acid-base cement. It exhibited a performance comparable to that of resin-based cement and should serve well under different clinical conditions.

Underwater Adhesives from Redox-Responsive Polyplexes of Thiolated Polyamide Polyelectrolytes

We report the fabrication of optically clear underwater adhesives using polyplexes of oppositely charged partially-thiolated polyamide polyelectrolytes (TPEs). The thiol content of the constituent PEs was varied to assess its influence on the adhesive properties of the resulting glues. These catechol-free, redox-responsive TPE-adhesives were formulated in aquo and exhibited high optical transparency and strong adhesion even on submerged or moist surfaces of diverse polar substrates such as glass, aluminium, wood, and bone pieces. The adhesives could be cured under water through oxidative disulphide crosslinking of the constituent TPEs. The polyamide backbone provided multi-site H-bonding interactions with the substrates while the disulphide crosslinking provided the cohesive strength to the glue. Strong adhesion of mammalian bones (load bearing capacity upto 7 kg/cm2 ) was achieved using the adhesive containing 30 mol % thiol residues. Higher pH and use of oxidants such as povidone-iodine solution enhanced the curing rate of the adhesives, and so did the use of Tris buffer instead of Phosphate buffer. The porous architecture of the adhesive and its progressive degradation in aqueous medium over the course of three weeks bode well for diverse biomedical applications where temporary adhesion of tissues is required.

Design and synthesis of unnatural coordination glycopolymer particles (CGPs): unleashing the potential of catechol-saccharide derivatives

Our study unveils an innovative methodology that merges catechols with mono- and disaccharides, yielding a diverse array of compounds. This strategic fusion achieves robust yields and introduces ligands with a dual nature: encompassing both the chelating attributes of catechols and the recognition capabilities of carbohydrates. This synergistic design led us to couple one of the novel ligands with an Fe(iii) salt, resulting in the creation of Coordination Glycopolymer Particles (CGPs). These CGPs demonstrate remarkable qualities, boasting outstanding dispersion in both aqueous media and Phosphate Buffered Saline (PBS) solution (pH ∼7.4) at higher concentrations (0.26 mg μL-1). Displaying an average Z-size of approximately 55 nm and favourable polydispersity indices (<0.25), these particles exhibit exceptional stability, maintaining their integrity over prolonged periods and temperature variations. Notably, they retain their superior dispersion and stability even when subjected to freezing or heating to 40 °C, making them exceptionally viable for driving biological assays. In contrast to established methods for synthesizing grafted glycopolymers, where typically a glycopolymer is doped with catechol derivatives to create synergy between chelating properties and those inherent to the saccharide, our approach provides a more efficient and versatile pathway for generating CGPs. This involves combining catechols and carbohydrates within a single molecule, enabling the fine-tuning of organic structure from a monomer design step and subsequently transferring these properties to the polymer.

Mussel-Inspired Caries Management Strategy: Constructing a Tribioactive Tooth Surface with Remineralization, Antibiofilm, and Anti-inflammation Activity

Dental caries is a common chronic oral disease in humans resulting from tooth demineralization caused by acid production of bacterial plaque, which leads to the destruction of enamel and dentin and oral inflammation. However, it is still a challenge that the function of natural active ingredients in currently available oral care products is not comprehensive, especially the lack of remineralization. Here, inspired by the strong biological adhesion ability of mussels and ancient oral disease plant therapy, a multifunctional strategy is proposed to construct a bioactive tooth surface to treat dental caries. It has been demonstrated that the Turkish gall extract (TGE) can inhibit adhesion of cariogenic bacteria Streptococcus mutans and Actinomyces viscosus and destroy biofilms on the tooth surface. Meanwhile, TGE can reduce the expression of inflammatory factors. Notably, the TGE coating can induce the growth of hydroxyapatite (HAP) crystals in vivo and in vitro, recovering the enamel mechanical properties under normal oral conditions. MD simulations interpreted the adsorption mechanism by which the hydroxyl groups in TGE bind to phosphate group (PO₄^3-) on the tooth surface, attracting calcium ions (Ca²⁺) as nucleation sites for remineralization. This work underlines the importance of TGE coating in remineralization, antibiofilm, and anti-inflammation activity as a promising strategy for dental caries.

Solvent effects on catechol's binding affinity: investigating the role of the intra-molecular hydrogen bond through a multi-level computational approach

The subtle interplay between the inter-molecular interactions established by catechol with the surrounding solvent and the intra-molecular hydrogen bond (HB) characterizing its conformational dynamics is investigated through a multi-level computational approach. First, quantum mechanical (QM) calculations are employed to accurately characterize both large portions of the catechol's potential energy surface and the interaction energy with neighboring solvent molecules. The acquired information is thereafter exploited to develop a QM derived force-field (QMD-FF), in turn employed in molecular dynamics (MD) simulations based on classical mechanics. The reliability of the QMD-FF is further validated through a comparison with the outcomes of ab initio molecular dynamics, also purposely carried out in this work. In agreement with recent experimental findings, the MD results reveal remarkable differences in the conformational behavior of isolated and solvated catechol, as well as among the investigated solvents, namely water, acetonitrile or cyclohexane. The rather strong intramolecular HB, settled between the vicinal phenolic groups and maintained in the gas phase, loses stability when catechol is solvated in polar solvents, and is definitively lost in protic solvents such as water. In fact, the internal energy increase associated with the rotation of one hydroxyl group and the breaking of the internal HB is well compensated by the intermolecular HB network available when both phenolic hydrogens point toward the surrounding solvent. In such a case, catechol is stabilized in a chelating conformation, which in turn could be very effective in water removal and surface anchoring. Besides unraveling the role of the different contributors that govern catechol's conformational dynamics, the QMD-FF developed in this work could be in future employed to model larger catechol containing molecules, due to its accuracy to reliably model both internal flexibility and solvent effects, while exploiting MD computational benefits to include more complex players as for instance surfaces, ions or biomolecules.

Extracellular matrix-based sticky sealants for scar-free corneal tissue reconstruction

Regenerative medicine requires both tissue restoration and ease of compliance for clinical application. Considering this, sticky tissue sealants have been shown to have great potentials over surgical suturing and wound treatment. However, tissue sealants currently used pose challenges such as uncontrollable adhesion formation, mechanical mismatch, and lack of tissue restoration. A new sticky sealant based on gelatinized cornea-derived extracellular matrix (GelCodE) with a visible light-activating system is firstly being introduced in this study. De novo tissue regeneration relies on the matrisome in charge of tissue-organization and development within GelCodE while visible light-based photopolymerization with ruthenium/sodium persulfate rapidly induces covalent bonds with the adjacent tissues. The ease of not only in vivo application, biocompatibility, and biointegration, but also exceptional de novo tissue formation is demonstrated in this study. Interestingly, newly regenerated tissues were shown to have normal tissue-like matrices with little scar formation. Hence, this work presents a promising strategy to meet clinical demands for scar-free tissue recovery with superior ease of clinical application.

Bridging wounds: tissue adhesives' essential mechanisms, synthesis and characterization, bioinspired adhesives and future perspectives

Bioadhesives act as a bridge in wound closure by forming an effective interface to protect against liquid and gas leakage and aid the stoppage of bleeding. To their credit, tissue adhesives have made an indelible impact on almost all wound-related surgeries. Their unique properties include minimal damage to tissues, low chance of infection, ease of use and short wound-closure time. In contrast, classic closures, like suturing and stapling, exhibit potential additional complications with long operation times and undesirable inflammatory responses. Although tremendous progress has been made in the development of tissue adhesives, they are not yet ideal. Therefore, highlighting and summarizing existing adhesive designs and synthesis, and comparing the different products will contribute to future development. This review first provides a summary of current commercial traditional tissue adhesives. Then, based on adhesion interaction mechanisms, the tissue adhesives are categorized into three main types: adhesive patches that bind molecularly with tissue, tissue-stitching adhesives based on pre-polymer or precursor solutions, and bioinspired or biomimetic tissue adhesives. Their specific adhesion mechanisms, properties and related applications are discussed. The adhesion mechanisms of commercial traditional adhesives as well as their limitations and shortcomings are also reviewed. Finally, we also discuss the future perspectives of tissue adhesives.

Addressing the Shortcomings of Polyphenol-Derived Adhesives: Achievement of Long Shelf Life for Effective Hemostasis

For rapid and effective hemostasis of uncontrollable bleeding, versatile hemostatic agents have been emerging. Among them, polyphenol-derived adhesives have attracted those hemostatic materials due to instantaneous formation of sticky barriers by robust interactions between the material and the serum proteins from wound. However, a critical challenge in such phenolic materials lies in long-term storage due to spontaneous oxidation under humid environments, leading to changes in hemostatic capability and adhesive strength. Here, we report a transparent hemostatic film consisting of gallol-conjugated chitosan (CHI-G) for minimizing the phenolic oxidation even for 3 months and maintaining strong tissue adhesiveness and its hemostatic ability. The film undergoes a phase transition from solid to injectable hydrogels at physiological pH for efficiently stopping internal and external hemorrhage. Interestingly, the hemostatic capability of the CHI-G hydrogels after 3 month storage depends on (i) the folded microstructure of the polymer with optimal gallol modification and (ii) an initial phase of either a solution state or a solid film. When the hydrogels are originated from the dehydrated film, their successful hemostasis is observed in a liver bleeding model. Our finding would provide an insight for design rationale of hemostatic formulations with long shelf-life.

Complexes of Alkaline and Ammonium Cations with Dopamine and Eumelanin Precursors: Dissecting the Role of Noncovalent Cation-π and Cation-Lone Pair (σ-Type) Interactions

Cation-π interactions and their possible competition with other noncovalent interactions (NCI) might play a key role in both dopamine- and eumelanin-based bioinspired materials. In this contribution, to unravel the delicate interplay between cation-π interactions and other possible competing forces, the configurational space of noncovalent complexes formed by dopamine or eumelanin precursors (o-benzoquinone, DHI and a semiquinone dimer) and three different cations (Na⁺, K⁺, and NH₄⁺) is sampled by means of accurate ab initio calculations. To this end, we resort to the mp2^mod method, recently validated by us for benzene-, phenol-, and catechol-cation complexes, whose computational convenience allows for an extensive exploration of the cation-molecule interaction energy surface, by sampling a total of more than 10⁴ arrangements. The mp2^mod interaction energy landscapes reveal that, besides the expected cation-π driven arrangements, for all considered molecule-cation pairs the most stable complexes are found when the cation lies within the plane containing the six-membered ring, thus maximizing the σ-type interaction with the oxygen's lone pairs. Due to the loss of aromaticity, the σ-type/cation-π strength ratio is remarkably large in o-benzoquinone, where cation-π complexes seem unlikely to be formed. The above features are shared among all considered cations but are significantly larger when considering the smaller Na⁺. Besides delivering a deeper insight onto the NCI network established by the considered precursors in the presence of ions, the present results can serve as a reference database to validate or refine lower level methods, as, for instance, the force fields employed in classical simulations.

A mussel glue-inspired monomer-etchant cocktail for improving dentine bonding

OBJECTIVES

The humid oral environment adversely affects the interaction between a functionalised primer and dentine collagen after acid-etching. Robust adhesion of marine mussels to their wet substrates instigates the quest for a strategy that improves the longevity of resin-dentine bonds. In the present study, an etching strategy based on the incorporation of biomimetic dopamine methacrylamide (DMA) as a functionalised primer into phosphoric acid etchant was developed. The mechanism and effect of this DMA-containing acid-etching strategy on bond durability were examined.

METHODS

Etchants with different concentrations of DMA (1, 3 or 5 mM) were formulated and tested for their demineralisation efficacy. The interaction between DMA and dentine collagen, the effect of DMA on collagen stability and the collagenase inhibition capacity of the DMA-containing etchants were evaluated. The effectiveness of this new etching strategy on resin-dentine bond durability was investigated.

RESULTS

All etchants were capable of demineralising dentine and exposing the collagen matrix. The latter strongly integrated with DMA via covalent bond, hydrogen bond and Van der Waals' forces. These interactions significantly improve collagen stability and inhibited collagenase activity. Application of the etchant containing 5 mM DMA achieved the most durable bonding interface.

CONCLUSION

Dopamine methacrylamide interacts with dentine collagen in a humid environment and improves collagen stability. The monomer effectively inactivates collagenase activity. Acid-etching with 5 mM DMA-containing phosphoric acid has the potential to prolong the longevity of bonded dental restorations without compromising clinical operation time.

CLINICAL SIGNIFICANCE

The use of 5 mM dopamine methacrylamide-containing phosphoric acid for etching dentine does not require an additional clinical step and has potential to improve the adhesive performance of bonded dental restorations.

A Universal and Reversible Wet Adhesive via Straightforward Aqueous Self-Assembly of Polyethylenimine and Polyoxometalate

The excellent adhesion of mussels under wet conditions has inspired the development of numerous catechol-based wet adhesives. Nevertheless, the performance of catechol-based wet adhesive suffers from the sensitivity toward temperature, pH, or oxidation stimuli. Therefore, it is of great significance to develop non-catechol-based wet adhesives to fully recapitulate nature's dynamic function. Herein, a novel type of non-catechol-based wet adhesive is reported, which is readily formed by self-assembly of commercially available branched polyethylenimine and phosphotungstic acid in aqueous solution through the combination of electrostatic interaction and hydrogen bonding. This wet adhesive shows reversible, tunable, and strong adhesion on diverse substrates and further exhibits high efficacy in promoting biological wound healing. During the healing of the wound, the as-prepared wet adhesive also possesses inherent antimicrobial properties, thus avoiding inflammations and infections due to microorganism accumulation.

Effect of Substituents in Mussel-inspired Surface Primers on their Oxidation and Priming Efficiency

Marine mussels contain an abundant catechol moiety, 3,4-dihydroxyphenylalanine (DOPA), in their interfacial foot proteins. DOPA contributes to both surface adhesion and bridging between the surface and overhead proteins (surface priming) by taking advantage of the unique redox properties of catechol. Inspired by the mussel surface priming mechanism, herein we synthesized a series of DOPA-mimetic analogs - a bifunctional group molecule, consisting of a catechol group and an acrylic group at the opposite ends. The surface primers with differently substituted (-COOH, -CH3 ) alkyl chains in the middle spacer were synthesized. Time-dependent oxidation and redox potentials of the surface primers were studied in an oxidizing environment to gain a better understanding of the mussel's redox chemistry. The thickness and degree of priming of the surface primers on silicon-based substrates were analyzed by ellipsometry and UV/Vis absorption spectroscopy. The post-reactivity of the acrylic groups of the primed layer was first visualized through a reaction with an acrylic group-reactive dye.

The application of novel mussel-inspired compounds in dentistry

OBJECTIVE

To give a current review of the mechanism of mussel adhesion, the application of mussel-inspired compounds in dentistry and the challenges associated with clinical application.

METHODS

Inspired by the wet adhesion property of 3,4-dihydroxyphenol-l-alanine (Dopa) in mussel plaques, various chemical compounds have been synthesized to mimic the mussel as an adhesion model for medical applications. Similar to mussels in the marine environment, dental materials in the oral environment have to endure long-term water hydrolysis, mechanical stress and other chemical challenges. These challenges have influenced an increasing number of studies that are exploring the translation of mussel-inspired adhesion to clinical applications. Therefore, this review discusses the mussel adhesion chemistry and its related application in dentistry.

RESULTS

Mussel-inspired compounds have achieved relatively acceptable performances in various dental fields, including surface coating, metal ions chelation, dentin bonding and mucosal adhesion. However, two practical problems remain to be comprehensively addressed, namely the protection of catechol groups from oxidation, and the feasibility for clinical application.

SIGNIFICANCE

The mussel's wet adhesion ability has attracted much research interest in the dental field because of its properties of moisture-resistant adhesion and surface coating. Despite the emergence of several mussel-inspired compounds in recent years, a comprehensive and timely review of their applications in dentistry is lacking. Therefore, the current review hopes to provide valuable information around the application of mussel-inspired compounds in dentistry with their pros and cons discussed.

Nanomechanics of π-cation-π interaction with implications for bio-inspired wet adhesion

Cation-π interactions play a vital role in modulating various biological processes, e.g., potassium-selective channel, protein folding and adhesion of marine organism. Previous studies mainly focus on binary cation-π interaction, whereas due to the complexity of biological systems and surrounding environments, a single cation is often in close proximity with more than one π-conjugated unit, which could exhibit essentially different binding behavior. Herein, the first experimental evidence of ternary π-cation-π interaction is reported through direct nanomechanical force measurement in a model π-conjugated poly(catechol) (PC) system coexisting with K⁺. Ternary π-cation-π interactions can bridge π-conjugated moieties, resulting in robust adhesion and promoting PC assembly and deposition. Particularly, these ternary complexes are discovered to transit to binary binding pairs by increasing K⁺ concentration, undermining adhesion and assembly due to lack of bridging. The π-cation-π binding strength follows the trend of NMe₄⁺ > K⁺ > Na⁺ > Li⁺. Employing the π-cation-π interaction, a deposition strategy to fabricate π-conjugated moiety based adhesive coatings on different substrates is realized. Our findings provide useful insights in engineering wet adhesives and coatings with reversible adhesion properties, and more broadly, with implications on rationalizing biological assembly.