Involvement of distant octacalcium phosphate scaffolds in enhancing early differentiation of osteocytes during bone regeneration

Histochemical analysis of osteoclast and osteoblast distributions on hydroxyapatite/collagen bone-like nanocomposite embedded in rat tibiae

OBJECTIVES

Hydroxyapatite (HAp)/collagen (Col) cylinders with laminated collagen layers were implanted into the tibial diaphysis of rats and examined histochemically to clarify how the orientation of HAp and Col bone-like nanocomposite fibers in HAp/Col blocks affects bone resorption and formation.

METHODS

HAp/Col fibers were synthesized and compressed into cylindrical blocks to mimic bone nanostructures. These were implanted into the cortical bone cavities of 10-week-old male Wistar rats with fiber bundles parallel to the tibial surface. The implants were histologically analyzed at 3, 5, 7, 14, and 28 days after implantation.

RESULTS

TRAP-positive osteoclasts appeared after 3-5 days in the lateral region of the graft, where the fiber ends were exposed, but not in the bottom region, where the HAp/Col fibers were parallel to the surface. Osteoclasts were observed in both regions by day 14. PHOSPHO1-positive osteoblasts were first detected on day 5, appearing slightly away from the cylinder laterally but directly on the bottom surface. A few osteoblasts contacted the block laterally, whereas many were observed on the new bone tissue at the bottom, between days 7 and 14. Bone formation was induced earlier in the bottom region, whereas lateral resorption was dominant. This suggested the uncoupling of bone resorption and formation in the early postimplantation stages. However, bone remodeling shifted to coupling between osteoclasts and osteoblasts throughout the cylinder by day 28.

CONCLUSION

The orientation of HAp/Col fibers in HAp/Col graft materials substantially affected the preferential induction of bone resorption or formation during the early stages of bone regeneration.

Enhanced osteogenic capacity of octacalcium phosphate involving adsorption of stromal-derived factor-1 in a standardized defect of a rat femur

This study investigated whether octacalcium phosphate (OCP) enhances bone regeneration through its synergistic effect with stromal-derived factor-1 (SDF-1). Recombinant SDF-1 (0.5-5.0 μg) was combined with OCP granules through lyophilization. OCP/SDF-1 granules were implanted into a rat femoral standardized defect for 2 and 4 weeks and subjected to histomorphometry, C-X-C motif chemokine receptor 4 (CXCR4) and osteocalcin immunohistomorphometry, and tartrate-resistant acid phosphatase (TRAP) staining. Calcium-deficient hydroxyapatite (CDHA) was used as a control for in vitro analyses. Mesenchymal stem cell (MSC) migration was estimated using a Transwell system with OCP/SDF-1. SDF-1 release from OCP/SDF-1 into the supernatant was determined without cells. SDF-1 adsorption in 4-(2-hydroxyethyl)-1-piperazineethanesulfonic acid buffer onto OCP, the chemical structure of OCP immersed in the medium using Fourier transform infrared spectroscopy, and the degree of supersaturation of the medium were determined. Bone regeneration and OCP degradation were enhanced the most by 1.0 μg of OCP/SDF-1 at 2 weeks after implantation by CT analysis and increasing CXCR4-positive, osteocalcin-positive, and TRAP-positive cells accumulation around the OCP. MSC migration increased until 48 h in the following order: SDF-1 only, CDHA/SDF-1, and OCP/SDF-1, with the greatest effect with 1.0 μg of SDF-1 than from OCP. CDHA promoted a greater release than OCP at 48 h. The physicochemical analyses indicated that SDF-1 interacted with OCP through Freundlich-type adsorption and that the adsorption controlled SDF-1 release from OCP during the hydrolysis into CDHA. Therefore, leveraging its molecular affinity for the OCP surface, OCP/SDF-1 facilitates MSC migration and enhances bone formation by ensuring the controlled, sustained release of SDF-1 from OCP.

Advances in Bioceramics for Bone Regeneration: A Narrative Review

Large osseous defects resulting from trauma, tumor resection, or fracture render the inherent ability of the body to repair inadequate and necessitate the use of bone grafts to facilitate the recovery of both form and function of the bony defect sites. In the United States alone, a large number of bone graft procedures are performed yearly, making it an essential area of investigation and research. Synthetic grafts represent a potential alterative to autografts due to their patient-specific customizability, but currently lack widespread acceptance in the clinical space. Early in their development, non-autologous bone grafts composed of metals such as stainless steel and titanium alloys were favorable due to their biocompatibility, resistance to corrosion, mechanical strength, and durability. However, since their inception, bioceramics have also evolved as viable alternatives. This review aims to present an overview of the fundamental prerequisites for tissue engineering devices using bioceramics as well as to provide a comprehensive account of their historical usage and significant advancements over time. This review includes a summary of commonly used manufacturing techniques and an evaluation of their use as drug carriers and bioactive coatings-for therapeutic ion/drug release, and potential avenues to further enhance hard tissue regeneration.

β-glycerophosphate, not low magnitude fluid shear stress, increases osteocytogenesis in the osteoblast-to-osteocyte cell line IDG-SW3

AIM

As osteoblasts deposit a mineralized collagen network, a subpopulation of these cells differentiates into osteocytes. Biochemical and mechanical stimuli, particularly fluid shear stress (FSS), are thought to regulate this, but their relative influence remains unclear. Here, we assess both biochemical and mechanical stimuli on long-term bone formation and osteocytogenesis using the osteoblast-osteocyte cell line IDG-SW3.

METHODS

Due to the relative novelty and uncommon culture conditions of IDG-SW3 versus other osteoblast-lineage cell lines, effects of temperature and media formulation on matrix deposition and osteocytogenesis were initially characterized. Subsequently, the relative influence of biochemical (β-glycerophosphate (βGP) and ascorbic acid 2-phosphate (AA2P)) and mechanical stimulation on osteocytogenesis was compared, with intermittent application of low magnitude FSS generated by see-saw rocker.

RESULTS

βGP and AA2P supplementation were required for mineralization and osteocytogenesis, with 33°C cultures retaining a more osteoblastic phenotype and 37°C cultures undergoing significantly higher osteocytogenesis. βGP concentration positively correlated with calcium deposition, whilst AA2P stimulated alkaline phosphatase (ALP) activity and collagen deposition. We demonstrate that increasing βGP concentration also significantly enhances osteocytogenesis as quantified by the expression of green fluorescent protein linked to Dmp1. Intermittent FSS (~0.06 Pa) rocker had no effect on osteocytogenesis and matrix deposition.

CONCLUSIONS

This work demonstrates the suitability and ease with which IDG-SW3 can be utilized in osteocytogenesis studies. IDG-SW3 mineralization was only mediated through biochemical stimuli with no detectable effect of low magnitude FSS. Osteocytogenesis of IDG-SW3 primarily occurred in mineralized areas, further demonstrating the role mineralization of the bone extracellular matrix has in osteocyte differentiation.

Effects of Different Surface Functionalizations of Silica Nanoparticles on Mesenchymal Stem Cells

Physicochemical properties of nanoparticles, such as particle size, surface charge, and particle shape, have a significant impact on cell activities. However, the effects of surface functionalization of nanoparticles with small chemical groups on stem cell behavior and function remain understudied. Herein, we incorporated different chemical functional groups (amino, DETA, hydroxyl, phosphate, and sulfonate with charges of +9.5, + 21.7, -14.1, -25.6, and -37.7, respectively) to the surface of inorganic silica nanoparticles. To trace their effects on mesenchymal stem cells (MSCs) of rat bone marrow, these functionalized silica nanoparticles were used to encapsulate Rhodamine B fluorophore dye. We found that surface functionalization with positively charged and short-chain chemical groups facilitates cell internalization and retention of nanoparticles in MSCs. The endocytic pathway differed among functionalized nanoparticles when tested with ion-channel inhibitors. Negatively charged nanoparticles mainly use lysosomal exocytosis to exit cells, while positively charged nanoparticles can undergo endosomal escape to avoid scavenging. The cytotoxic profiles of these functionalized silica nanoparticles are still within acceptable limits and tolerable. They exerted subtle effects on the actin cytoskeleton and migration ability. Last, phosphate-functionalized nanoparticles upregulate osteogenesis-related genes and induce osteoblast-like morphology, implying that it can direct MSCs lineage specification for bone tissue engineering. Our study provides insights into the rational design of biomaterials for effective drug delivery and regenerative medicine.

Doxorubicin loaded octacalcium phosphate particles as controlled release drug delivery systems: Physico-chemical characterization, in vitro drug release and evaluation of cell death pathway

Mastering new and efficient ways to obtain successful drug delivery systems (DDS) with controlled release became a paramount quest in the scientific community. Increase of malignant bone tumors and the necessity to optimize an approach of localized drug delivery require research to be even more intensified. Octacalcium phosphate (OCP), with a number of advantages over current counterparts is extensively used in bone engineering. The aim of the present research was to synthesize bioactive and biocompatible doxorubicin (DOX) containing OCP particles. DOX-OCP was successfully obtained in situ in an exhaustive range of added drug (1-20 wt%, theoretical loading). Based on XRD, above 10 wt% of DOX, OCP formation was inhibited and the obtained product was low crystalline α-TCP. In-vitro drug release was performed in pH 7.4 and 6.0. In both pH environments DOX had a continuous release over six weeks. However, the initial drug burst for pH 7.4, in the first 24 h, ranged from 15.9 ± 1.3 % to 33.5 ± 12 % and for pH 6.0 23.7 ± 1.5 % to 36.2 ± 12 %.The DOX-OCP exhibited an inhibitory effect on viability of osteosarcoma cell lines MG63, U2OS and HOS. In contrast, MC3T3-E1 cells (IC50 > 0.062 µM) displayed increased viability and proliferation from 3rd to 7th day. Testing of the DDS on ferroptotic markers (CHAC1, ACSL4 and PTGS2) showed that OCP-DOX does not induce ferroptotic cell death. Moreover, the evaluation of protein levels of cleaved PARP, by western blotting analysis, corroborated that apoptosis is the main pathway of programmed cell death in osteosarcoma cells induced by DOX-OCP.

Engineered cyclodextrin-based supramolecular hydrogels for biomedical applications

Cyclodextrin (CD)-based supramolecular hydrogels are polymer network systems with the ability to rapidly form reversible three-dimensional porous structures through multiple cross-linking methods, offering potential applications in drug delivery. Although CD-based supramolecular hydrogels have been increasingly used in a wide range of applications in recent years, a comprehensive description of their structure, mechanical property modulation, drug loading, delivery, and applications in biomedical fields from a cross-linking perspective is lacking. To provide a comprehensive overview of CD-based supramolecular hydrogels, this review systematically describes their design, regulation of mechanical properties, modes of drug loading and release, and their roles in various biomedical fields, particularly oncology, wound dressing, bone repair, and myocardial tissue engineering. Additionally, this review provides a rational discussion on the current challenges and prospects of CD-based supramolecular hydrogels, which can provide ideas for the rapid development of CD-based hydrogels and foster their translation from the laboratory to clinical medicine.

Comparative study of hydroxyapatite synthesized using Schiff base and wet chemical precipitation methods

Hydroxyapatite (HAp) exists as an inorganic and crystalline composition present in bones and dental enamel, and hence can be utilized as a direct element or as part of the composition of biomaterials and implants for dental and orthopaedic applications. Listed below are a few synthesis techniques for HAp that are listed in the literature: solid-state and mechano-chemical methods (dry methods), wet chemical precipitation and sol-gel methods (wet methods), and combustion and pyrolysis methods (high-temperature processes). Nevertheless, there are new and more productive techniques that result in HAp with a regulated morphology, such as the Schiff base method, which, on reaction with calcium and phosphate precursors, forms chelating complexes to produce HAp nuclei. This research paper presents the comparison in characteristics between HAp synthesized using Schiff base (HAp-SB), wet chemical precipitation (HAp-WC) methods, and commercial HAp (HAp-CM) in their powdered and pelleted form. The average size of HAp-WC particles in the spherical form was found to be 603 nm ± 176, HAp-SB were found to have rod-like morphology, which is very similar to human bone-like HAp, with an average length and width of 1522 nm ± 759 and 400 nm ± 112, respectively, and HAp-CM were found to have spherical morphology with dimensions of 52 nm ± 25. Biological studies show that cell viability of HAp-SB pellet (202.01% ± 8.16) seemed to have higher cell proliferation properties than HAp-WC pellet (145.7% ± 5.11) and HAp-CM pellet (71.53% ± 3.61) due to its higher aspect ratio, and hence higher surface area for the cells to adhere. In a detailed study, it is observed that both techniques had their advantages, and there were no significant disadvantages observed.

Phosphorylated pullulan promotes calcification during bone regeneration in the bone defects of rat tibiae

The current study aimed to evaluate bone tissue regeneration using a combination of β-tricalcium phosphate (βTCP) and phosphorylated pullulan (PPL, a phosphate-rich polysaccharide polymer consisting of maltotriose units). Round defects of 2 mm diameter were created in the arterial center of rat tibiae, which were further treated with vehicle (control group), βTCP (βTCP group), or βTCP + PPL (βTCP + PPL group) grafts. The control specimens without bone grafts exhibited rapid bone formation after 1 week; however, the regenerated bone was not resorbed until 4 weeks. In contrast, βTCP-grafted specimens exhibited fewer but thicker trabeculae, whereas the βTCP + PPL group displayed many fine trabeculae at 4 weeks. In the βTCP + PPL group, new bone was associated with the βTCP granules and PPL. Similarly, PHOSPHO1-positive osteoblasts were localized on the βTCP granules as well as the PPL. On the other hand, TRAP-reactive osteoclasts predominantly localized on newly-formed bone and βTCP granules rather than on the PPL. No significant differences were observed in the expression of Alp, Integrin αv, Osteopontin, Osteocalcin, and Dmp-1 in PPL-treated MC3T3-E1 osteoblastic cells, suggesting that PPL did not facilitate osteoblastic differentiation. However, von Kossa staining identified abundant needle-like calcified structures extending inside the PPL. Furthermore, transmission electron microscopy (TEM) revealed many globular structures identical to calcified nodules. In addition, calcified collagen fibrils were observed in the superficial layer of the PPL. Thus, PPL may serve as a scaffold for osteoblastic bone formation and promotes calcification on its surface. In conclusion, we speculated that βTCP and PPL might promote bone regeneration and could be integrated into promising osteoconductive materials.

The material design of octacalcium phosphate bone substitute: increased dissolution and osteogenecity

Octacalcium phosphate (OCP) has been advocated as a precursor of bone apatite crystals. Recent studies have shown that synthetic OCP exhibits highly osteoconductive properties as a bone substitute material that stems from its ability to activate bone tissue-related cells, such as osteoblasts, osteocytes, and osteoclasts. Accumulated experimental evidence supports the proposition that the OCP-apatite phase conversion under physiological conditions increases the stimulatory capacity of OCP. The conversion of OCP progresses by hydrolysis toward Ca-deficient hydroxyapatite with Ca²⁺ ion incorporation and inorganic phosphate ion release with concomitant increases in the solid Ca/P molar ratio, specific surface area, and serum protein adsorption affinity. The ionic dissolution rate during the hydrolysis reaction was controlled by introducing a high-density edge dislocation within the OCP lattice by preparing it through co-precipitation with gelatin. The enhanced dissolution intensifies the material biodegradation rate and degree of osteogenecity of OCP. Controlling the biodegradation rate relative to the dissolution acceleration may be vital for controlling the osteogenecity of OCP materials. This study investigates the effects of the ionic dissolution of OCP, focusing on the structural defects in OCP, as the enhanced metastability of the OCP phase modulates biodegradability followed by new bone formation. STATEMENT OF SIGNIFICANCE: Octacalcium phosphate (OCP) is recognized as a highly osteoconductive material that is biodegradable by osteoclastic resorption, followed by new bone formation by osteoblasts. However, if the degradation rate of OCP is increased by maintaining the original osteoconductivity or acquiring a bioactivity better than its current properties, then early replacement with new bone can be expected. Although cell introduction or growth factor addition by scaffold materials is the standard method for tissue engineering, material activity can be augmented by introducing dislocations into the lattice of the OCP. This review article summarizes the effects of introducing structural defects on activating OCP, which was obtained by co-precipitation with gelatin, as a bone substitute material and the mechanism of improved bone replacement performance.

Building Osteogenic Microenvironments with a Double-Network Composite Hydrogel for Bone Repair

The critical factor determining the in vivo effect of bone repair materials is the microenvironment, which greatly depends on their abilities to promote vascularization and bone formation. However, implant materials are far from ideal candidates for guiding bone regeneration due to their deficient angiogenic and osteogenic microenvironments. Herein, a double-network composite hydrogel combining vascular endothelial growth factor (VEGF)-mimetic peptide with hydroxyapatite (HA) precursor was developed to build an osteogenic microenvironment for bone repair. The hydrogel was prepared by mixing acrylated β-cyclodextrins and octacalcium phosphate (OCP), an HA precursor, with gelatin solution, followed by ultraviolet photo-crosslinking. To improve the angiogenic potential of the hydrogel, QK, a VEGF-mimicking peptide, was loaded in acrylated β-cyclodextrins. The QK-loaded hydrogel promoted tube formation of human umbilical vein endothelial cells and upregulated the expression of angiogenesis-related genes, such as Flt1 , Kdr , and VEGF , in bone marrow mesenchymal stem cells. Moreover, QK could recruit bone marrow mesenchymal stem cells. Furthermore, OCP in the composite hydrogel could be transformed into HA and release calcium ions facilitating bone regeneration. The double-network composite hydrogel integrated QK and OCP showed obvious osteoinductive activity. The results of animal experiments showed that the composite hydrogel enhanced bone regeneration in skull defects of rats, due to perfect synergistic effects of QK and OCP on vascularized bone regeneration. In summary, improving the angiogenic and osteogenic microenvironments by our double-network composite hydrogel shows promising prospects for bone repair.

Synthesis of Octacalcium Phosphate Containing Glutarate Ions with a High Incorporation Fraction

Octacalcium phosphate (OCP) has received considerable attention in the field of ceramic biomaterials as an advanced functional material. It exhibits a layered structure composed of apatitic and hydrated layers and can incorporate various dicarboxylate ions into the hydrated layer. Saturated dicarboxylic acids (HOOC(CH2)nCOOH) with an odd number of methylene groups (-CH2-) exhibit lower incorporation fractions than those with an even number of methylene groups, possibly owing to a compositional dependence on the synthetic method. In this study, calcium carbonate, phosphoric acid, and various amounts of glutaric acid were used to produce glutarate-ion-incorporated OCP by a wet chemical method, which is different from the conventional synthetic strategy. While utilising 1-20 mmol of glutaric acid during synthesis did not produce the desired product, using 25 mmol of glutaric acid resulted in the formation of single-phase glutarate-ion-incorporated OCP with a Ca/P molar ratio of 1.57 and a 90% incorporation fraction of glutarate ions. This glutarate-ion-incorporation fraction is significantly higher than that reported in the previous studies (35%). Thus, the synthetic procedure proposed herein was able to produce single-phase OCP containing glutarate ions with a high incorporation fraction. Our findings can contribute to development of novel functional ceramic biomaterials in the future.

Gallium containing calcium phosphates: potential antibacterial agents or fictitious truth

Amidst an ever-increasing demand for the enhancement of the lifestyle and the modulation of modern diseases, the functionalization of biomaterials is of utmost importance. One of the leading materials for the aforementioned purpose have been calcium phosphates (CaPs). They have been widely used in bone regeneration displaying favourable regenerative potential and biological properties. Many studies have placed their entire focus on facilitating the osteogenic differentiation of stem cells and bone progenitor cells, while the aspect of antibacterial properties has been surmounted. Nevertheless, increasing antibiotic resistance of bacteria requires the development of new materials and the usage of alternative approaches such as ion doping. Gallium (Ga) has been the potential star on the rise among the ions. However, the obstacle that accompanies gallium is the scarcity of research performed and the variety of amalgamations. The question that imposes itself is how a growing field of therapeutics can be further entwined with advances in material science, and how will the incorporation of gallium bring a new outlook. The present study offers a comprehensive overview of state-of-the-art gallium containing calcium phosphates (GaCaPs), their synthesis methods, antibacterial properties, and biocompatibility. Considering their vast potential as antibacterial agents, the need for a methodical perspective is highly necessary to determine if it is a direction on the brink of recognition or a fruitless endeavour. STATEMENT OF SIGNIFICANCE: : Although several studies have been published on various metal ions-containing calcium phosphates, to this date there is no systematic overview pointing out the properties and benefits of gallium containing calcium phosphates. Here we offer a critical overview, including synthesis, structure and biological properties of gallium containing calcium phosphates.

Microwave Treatment of Calcium Phosphate/Titanium Dioxide Composite to Improve Protein Adsorption

Calcium phosphate has attracted enormous attention as a bone regenerative material in biomedical fields. In this study, we investigated the effect of microwave treatment on calcium phosphate deposited TiO₂ nanoflower to improve protein adsorption. Hierarchical rutile TiO₂ nanoflowers (TiNF) fabricated by a hydrothermal method were soaked in modified simulated body fluid for 3 days to induce calcium phosphate (CAP) formation, followed by exposure to microwave radiation (MW). Coating the dental implants with CAP/TiNF provides a means of improving the biological properties, as the structure, morphology, and thickness of the composites can be controlled. The composites were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), field emission transmission electron microscopy (TEM), and Fourier-transform infrared spectroscopy (FTIR), respectively. The composites were identified to be composed of aggregated nano-sized particles with sphere-like shapes, and the calcium phosphate demonstrated low crystallinity. The ability of bovine serum albumin (BSA) to adsorb on MW-treated CAP/TiNF composites was studied as a function of BSA concentration. The Sips isotherm was used to analyze the BSA adsorption on MW-treated CAP/TiNF composites. The MW-treated samples showed high protein adsorption capacity, thereby indicating their potential in various biomedical applications.

Differentiation of committed osteoblast progenitors by octacalcium phosphate compared to calcium-deficient hydroxyapatite in Lepr-cre/Tomato mouse tibia

This study aimed to investigate the accumulation and differentiation of mesenchymal stem cells (MSCs) around octacalcium phosphate (OCP) compared with those around calcium-deficient hydroxyapatite (CDHA), a material obtained through hydrolysis of the original OCP. Leptin receptor (Lepr)-expressing bone marrow-derived MSCs around the OCP and CDHA were pursued utilizing genetically modified Lepr-cre/Tomato mice. OCP and CDHA granules were implanted into the tibia defect of the mice for 10 weeks and subjected to histomorphometric and immunohistochemical analyses. The structural properties of OCP and CDHA after inoculation into mouse subcutaneous tissue (until 4 weeks) or culture mediums (14 days) were analyzed using physicochemical techniques. In vitro osteoblastic differentiation of primary MSCs was examined with the materials for 14 days. While Lepr-cre/Tomato positive cells (red) accumulated around both OCP and CDHA, Lepr and osteocalcin double-positive osteoblastic cells (yellow) were significantly more abundant around OCP than around CDHA in the early implantation period. OCP enhanced the osteoblastic differentiation of MSCs more than CDHA in vitro. Physicochemical and structual analyses provided evidence that OCP tended to convert to the apatitic phase in the tested physiological environments. The higher osteoconductivity of OCP originated from a capacity-enhancing osteoblastic differentiation of committed osteoblast progenitors in bone marrow accompanied by OCP hydrolysis. STATEMENT OF SIGNIFICANCE: MSCs play a key role in bone regeneration through osteoblastic differentiation. Calcium phosphates have been widely applied as bone substitute materials, and OCP has a better ability to promote osteoblast differentiation of MSCs than that of HA in vitro. However, it is not clear how MSCs accumulate in the bone marrow and differentiate into osteoblasts during bone regeneration in vivo. In this study, we focused on the leptin receptor, a marker of bone marrow-derived MSCs. Using genetically modified mice labeled with the red fluorescent protein Tomato, we observed the accumulation of MSCs around calcium phosphates implanted in tibia bone defects and their differentiation into osteoblasts.

Octacalcium phosphate: Innovative vehicle for the local biologically active substance delivery in bone regeneration

Disadvantages of conventional drug delivery systems (DDS), such as systemic circulation, interaction with physiochemical factors, reduced bioavailability, and insufficient drug concentration at bone defect site, have underlined the importance of developing efficacious local drug delivery systems. Octacalcium phosphate (OCP) is presumed to be the precursor of biologically formed apatite, owing to its similarity to hydroxyapatite (HAp) and readiness to convert to it. Specific crystal structure of OCP is constructed of compiled apatite layers and water layers, which make possible the incorporation of various ions in its structure, making it feasible to alter the overall effect OCP has in the system. Next to that intrinsic property, characteristics as high solubility, biodegradability and osteoconductivity have made it indispensable to tailor OCP as a carrier material. In this review, we present the main characteristics and progress done on utilizing OCP as an innovative vehicle and provide suggestions for possible research pathways and advantages for local drug delivery in bone tissue engineering. STATEMENT OF SIGNIFICANCE: Octacalcium phosphate (OCP), being a precursor to biologically formed apatite, has many assets when compared to other calcium phosphates. Owing to its highly pertinent structure, it is being used as a vehicle for biologically active substances or ions for bone regeneration. However, orchestrating drug delivery systems with OCP, in order to achieve the best possible outcome, is still a pioneering concept, and the all-encompassing data is still scarce. Although several articles have been published on this matter, to this date there is no systematic overview pointing out the benefits that OCP can bring in the field of drug delivery. Here we offer a comprehensive overview, starting from the OCP synthesis to its structure, morphology, and the biological significance OCP has.

Macrophage Polarization Related to Crystal Phases of Calcium Phosphate Biomaterials

Calcium phosphate (CaP) materials influence macrophage polarization during bone healing. However, the effect of the crystal phase of CaP materials on the immune response of bone remains unclear. In this study, the effect of the crystal phases of CaP materials on the regulation of macrophage polarization was investigated. Human THP-1 cells and mouse RAW 264 cells were cultured with octacalcium phosphate (OCP) and its hydrolyzed form Ca-deficient hydroxyapatite to assess the expression of pro-inflammatory M1 and anti-inflammatory M2 macrophage-related genes. OCP inhibited the excessive inflammatory response and switched macrophages to the anti-inflammatory M2 phenotype, which promoted the expression of the interleukin 10 (IL10) gene. In contrast, HL stimulated an excessive inflammatory response by promoting the expression of pro-inflammatory M1 macrophage-related genes. To observe changes in the microenvironment induced by OCP and HL, inorganic phosphate (Pi) and calcium ion (Ca²⁺) concentrations and pH value in the medium were measured. The expression of the pro-inflammatory M1 macrophage-related genes (tumor necrosis factor alpha (TNFα) and interlukin 1beta (IL1β)) was closely related to the increase in ion concentration caused by the increase in the CaP dose. Together, these results suggest that the microenvironment caused by the crystal phase of CaP materials may be involved in the immune-regulation capacity of CaP materials.

Bone Tissue Response to Different Grown Crystal Batches of Octacalcium Phosphate in Rat Long Bone Intramedullary Canal Area

The microstructure of biomaterials influences the cellular and biological responses in the bone. Octacalcium phosphate (OCP) exhibits higher biodegradability and osteoconductivity than hydroxyapatite (HA) during the conversion process from OCP to HA. However, the effect of the microstructure of OCP crystals on long tubular bones has not been clarified. In this study, two types of OCPs with different microstructures, fine-OCP (F-OCP) and coarse-OCP (C-OCP), were implanted in rat tibia for 4 weeks. F-OCP promoted cortical bone regeneration compared with C-OCP. The osteoclasts appearance was significantly higher in the C-OCP group than in the control group (defect only) at 1-week post-implantation. To investigate whether the solubility equilibrium depends on the different particle sizes of OCPs, Nano-OCP, which consisted of nanometer-sized OCPs, was prepared. The degree of supersaturation (DS) tended to decrease modestly in the order of C-OCP, F-OCP, and Nano-OCP with respect to HA and OCP in Tris-HCl buffer. F-OCP showed a higher phosphate ion concentration and lower calcium ion concentration after immersion in the buffer than C-OCP. The crystal structures of both OCPs tended to be converted to HA by rat abdominal implantation. These results suggest that differences in the microstructure of OCPs may affect osteoclastogenesis and result in osteoconductivity of this material in long tubular bone by altering dissolution behavior.