Development of long-term antimicrobial poly(methyl methacrylate) by incorporating mesoporous silica nanocarriers

Valorizing Banana Peel Waste into Mesoporous Biogenic Nanosilica and Novel Nano-biofertilizer Formulation Thereof via Nano-biopriming Inspired Tripartite Interaction Studies

The present study attempts to valorize banana peel waste (BPW) into high-value precipitated nanosilica-based agri-input. XRD analysis revealed smaller-sized biogenic nanosilica (BNS) with an increase (without heating) or decrease (with heating) in the duration of acid pretreatment during the pre-calcination step. The highest BNS yield was recorded in post-calcinated BPW ash involving simultaneous acid and heat treatment (1 h) (SA-3). FTIR analysis displayed an intense peak at 1078.3 cm-1, indicating "Si-O-Si bond" asymmetric vibrations. FESEM-EDX micrographs revealed high-purity BNS of predominantly spheroid morphology. The BJH plot exhibited mesoporous nanosilica with a median pore diameter of ∼33.82 nm. The bipartite interaction of 0.001 g mL-1 BNS signifies growth-promoting effects on Bacillus subtilis (BS) and Raphanus sativus (RS). The nano-primed RS seeds showed higher germination indices over non-primed seeds at 0.001 g of BNS mL-1. Further, the nano-biopriming studies showed the synergistic response of BNS and BS interaction on RS seeds in terms of higher seedling growth, biomass content, and stress tolerance index. The findings open new avenues for developing nano-biofertilizer formulations that serve multifaceted functions such as waste management and biomass valorization into value-added products and fulfill sustainable development goals.

Physicochemical and biological properties of dental materials and formulations with silica nanoparticles: A narrative review

OBJECTIVE

Silica nanoparticles (SNPs) have been extensively studied and used in different dental applications to promote improved physicochemical properties, high substance loading efficiency, in addition to sustained delivery of substances for therapeutic or preventive purposes. Therefore, this study aimed to review the SNPs applications in nanomaterials and nanoformulations in dentistry, discussing their effect on physicochemical properties, biocompatibility and ability to nanocarry bioactive substances.

DATA RESOURCES

Literature searches were conducted on PubMed, Web of Science, and Scopus databases to identify studies examining the physicochemical and biological properties of dental materials and formulations containing SNPs. Data extraction was performed by one reviewer and verified by another STUDY SELECTION: A total of 50 were reviewed. In vitro studies reveal that SNPs improved the general properties of dental materials and formulations, such as microhardness, fracture toughness, flexural strength, elastic modulus and surface roughness, in addition to acting as efficient nanocarriers of substances, such as antimicrobial, osteogenic and remineralizing substances, and showed biocompatibility CONCLUSIONS: SNPs are biocompatible, improve properties of dental materials and serve as effective carriers for bioactive substances CLINICAL SIGNIFICANCE: Overall, SNPs are a promising drug delivery system that can improve dental materials biological and physicochemical and aesthetic properties, increasing their longevity and clinical performance. However, more studies are needed to elucidate SNPs short- and long-term effects in the oral cavity, mainly on in vivo and clinical studies, to prove their effectiveness and safety.

Formulation of arginine-loaded mesoporous silica nanoparticles (Arg@MSNs) modified orthodontic adhesive

OBJECTIVES

The objective of this study was to synthesize arginine loaded mesoporous silica nanoparticles (Arg@MSNs), develop a novel orthodontic adhesive using Arg@MSNs as modifiers, and investigate the adhesive performance, antibacterial activity, and biocompatibility.

METHODS

Arg@MSNs were synthesized by immobilizing arginine into MSNs and characterized using transmission electron microscope (TEM), dynamic light scattering (DLS), and Fourier Transform Infrared Spectrometer (FT-IR). Arg@MSNs were incorporated into Transbond XT adhesive with different mass fraction to form functional adhesives. The degree of conversion (DC), arginine release behavior, adhesive performance, antibacterial activity against Streptococcus mutans biofilm, and cytotoxicity were comprehensively evaluated.

RESULTS

TEM, DLS, and FT-IR characterizations confirmed the successful preparation of Arg@MSNs. The incorporation of Arg@MSNs did not significantly affect DC and exhibited clinically acceptable bonding strength. Compared to the commercial control, the Arg@MSNs modified adhesives greatly suppressed the metabolic activity and polysaccharide production while increased the biofilm pH values. The cell counting kit (CCK)-8 test indicated no cytotoxicity.

CONCLUSIONS

The novel orthodontic adhesive containing Arg@MSNs exhibited significantly enhanced antibacterial activities and inhibitory effects on acid production compared to the commercial adhesive without compromising their bonding strength or biocompatibility.

CLINICAL SIGNIFICANCE

The novel orthodontic adhesive containing Arg@MSNs exhibits potential clinical benefits in preventing demineralization of enamel surfaces around or beneath orthodontic brackets due to its enhanced antibacterial activities and acid-producing inhibitory effects.

Mapping the research landscape of nanoparticles and their use in denture base resins: a bibliometric analysis

BACKGROUND

Nanoparticles are increasingly used in dentistry for various applications, including enhancing the mechanical properties of denture base resins. This study aimed to comprehensively review and analyze the research landscape of nanoparticles and their effect on the flexural strength of denture base resins to identify key research areas and trends and to highlight the importance of collaboration between authors and institutions.

METHODS

A Bibliometric Analysis was conducted using the Keywords "Nanoparticle*" AND "Denture*" OR "CAD/CAM." The literature search from the WOS database was restricted to the publication years 2011 to 2022.

RESULTS

Key findings encompass an increase in research publications but a decline in citations. Saudi Arabia, China, and Iraq led this research, with specific institutions excelling. Notable journals with high impact factors were identified. Authorship patterns show variations in citation impact. Additionally, keyword analysis revealed that current research trends offer insights into influential authors and their networks.

CONCLUSIONS

The analysis of nanoparticles and denture base resins reveals a dynamic and evolving landscape that emphasizes the importance of collaboration, staying current with research trends, and conducting high-quality research in this ever-evolving domain.

Mechanophysical and Anti-Adhesive Properties of a Nanoclay-Containing PMMA Denture Resin

Poly(methyl methacrylate) (PMMA) is commonly used for dental dentures, but it has the drawback of promoting oral health risks due to oral bacterial adhesion. Recently, various nanoparticles have been incorporated into PMMA to tackle these issues. This study aims to investigate the mechanophysical and antimicrobial adhesive properties of a denture resin by incorporating of nanoclay into PMMA. Specimens were prepared by adding 0, 1, 2, and 4 wt % surface-modified nanoclay (Sigma) to self-polymerizing PMMA denture resin. These specimens were then evaluated using FTIR, TGA/DTG, and FE-SEM with EDS. Various mechanical and surface physical properties, including nanoindentation, were measured and compared with those of pure PMMA. Antiadhesion experiments were conducted by applying a Candida albicans (ATCC 11006) suspension to the surface of the specimens. The antiadhesion activity of C. albicans was confirmed through a yeast-wall component (mannan) and mRNA-seq analysis. The bulk mechanical properties of nanoclay-PMMA composites were decreased compared to those of pure PMMA, while the flexural strength and modulus met the ISO 20795-1 requirement. However, there were no significant differences in the nanoindentation hardness and elastic modulus. The surface energy revealed a significant decrease at 4 wt % nanoclay-PMMA. The antiadhesion effect of Candida albicans was evident along with nanoclay content in the nanocomposites and confirmed by the reduced attachment of mannan on nanoclay-PMMA composites. mRNA-seq analysis supported overall transcriptome changes in altering attachment and metabolism behaviors on the surface. The nanoclay-PMMA materials showed a lower surface energy as the content increased, leading to an antiadhesion effect against Candida albicans. These findings indicate that incorporating nanoclay into PMMA surfaces could be a valuable strategy for preventing the fungal biofilm formation of denture base materials.

Enhancing the inhibition of dental erosion and abrasion with quercetin-encapsulated hollow mesoporous silica nanocomposites

Introduction: Dental erosion and abrasion pose significant clinical challenges, often leading to exposed dentinal tubules and dentine demineralization. The aim of this study was to analyse the efficacy of quercetin-encapsulated hollow mesoporous silica nanocomposites (Q@HMSNs) on the prevention of dentine erosion and abrasion. Method: Q@HMSNs were synthesized, characterized, and evaluated for their biocompatibility. A total of 130 dentine specimens (2 mm × 2 mm × 2 mm) were prepared and randomly distributed into 5 treatment groups (n = 26): DW (deionized water, negative control), NaF (12.3 mg/mL sodium fluoride, positive control), Q (300 μg/mL quercetin), HMSN (5.0 mg/mL HMSNs), and Q@HMSN (5.0 mg/mL Q@HMSNs). All groups were submitted to in vitro erosive (4 cycles/d) and abrasive (2 cycles/d) challenges for 7 days. The specimens in the DW, NaF, and Q groups were immersed in the respective solutions for 2 min, while treatment was performed for 30 s in the HMSN and Q@HMSN groups. Subsequently, the specimens were subjected to additional daily erosion/abrasion cycles for another 7 days. The effects of the materials on dentinal tubule occlusion and demineralized organic matrix (DOM) preservation were examined by scanning electron microscopy (SEM). The penetration depth of rhodamine B fluorescein into the etched dentine was assessed using confocal laser scanning microscopy (CLSM). The erosive dentine loss (EDL) and release of type I collagen telopeptide (ICTP) were measured. The data were analysed by one-way analysis of variance (ANOVA) with post hoc Tukey's test (α = 0.05). Results: Q@HMSNs were successfully synthesized and showed minimal toxicity to human dental pulp stem cells (HDPSCs) and gingival fibroblasts (HGFs). Q@HMSNs effectively occluded the dentinal tubules, resulting in a thicker DOM in the Q@HMSN group. The CLSM images showed more superficial penetration in the HMSN and Q@HMSN groups than in the quercetin, NaF, and DW groups. The Q@HMSN group exhibited a significantly lower EDL and reduced ICTP levels compared to the other groups (p < 0.05). Conclusion: Q@HMSNs hold promise for inhibiting dentine erosion and abrasion by promoting tubule occlusion and DOM preservation.

Different Polymers for the Base of Removable Dentures? Part II: A Narrative Review of the Dynamics of Microbial Plaque Formation on Dentures

This review focuses on the current disparities and gaps in research on the characteristics of the oral ecosystem of denture wearers, making a unique contribution to the literature on this topic. We aimed to synthesize the literature on the state of current knowledge concerning the biological behavior of the different polymers used in prosthetics. Whichever polymer is used in the composition of the prosthetic base (poly methyl methacrylate acrylic (PMMA), polyamide (PA), or polyether ether ketone (PEEK)), the simple presence of a removable prosthesis in the oral cavity can disturb the balance of the oral microbiota. This phenomenon is aggravated by poor oral hygiene, resulting in an increased microbial load coupled with the reduced salivation that is associated with older patients. In 15-70% of patients, this imbalance leads to the appearance of inflammation under the prosthesis (denture stomatitis, DS). DS is dependent on the equilibrium-as well as on the reciprocal, fragile, and constantly dynamic conditions-between the host and the microbiome in the oral cavity. Several local and general parameters contribute to this balance. Locally, the formation of microbial plaque on dentures (DMP) depends on the phenomena of adhesion, aggregation, and accumulation of microorganisms. To limit DMP, apart from oral and lifestyle hygiene, the prosthesis must be polished and regularly immersed in a disinfectant bath. It can also be covered with an insulating coating. In the long term, relining and maintenance of the prosthesis must also be established to control microbial proliferation. On the other hand, several general conditions specific to the host (aging; heredity; allergies; diseases such as diabetes mellitus or cardiovascular, respiratory, or digestive diseases; and immunodeficiencies) can make the management of DS difficult. Thus, the second part of this review addresses the complexity of the management of DMP depending on the polymer used. The methodology followed in this review comprised the formulation of a search strategy, definition of the inclusion and exclusion criteria, and selection of studies for analysis. The PubMed database was searched independently for pertinent studies. A total of 213 titles were retrieved from the electronic databases, and after applying the exclusion criteria, we selected 84 articles on the possible microbial interactions between the prosthesis and the oral environment, with a particular emphasis on Candida albicans.

Highlights on Drug and Ion Release and Recharge Capacity of Antimicrobial Removable Prostheses

This article aimed to review the ion and drug release, recharge abilities, and antimicrobial properties of drug/ion-releasing removable prostheses, and to assess their capability in preventing and inhibiting denture stomatitis as well preventing caries and reversing carious lesions. Data was collected from published scientific papers listed in PubMed database from January 1975 to December 2021. English full-text articles, involving clinical or in vitro studies, focusing on removable prostheses and are concerned with drug/ion release and rechargeability as a way to prevent or inhibit denture stomatitis or dental caries were included. The relevant articles reported that ion- or drug-modified polymethylmethacrylate acts as a reservoir for these ions and drugs and is capable of releasing significant amounts with sustained release effect. Recharging of modified resin resulted in greater sustainability of ion and drug release, thus improving the long-term effects of protection against demineralization and reducing the adhesion of Streptococcus mutans and Candida albicans. Modifications of removable prostheses with rechargeable ions and drugs enhance remineralization, hinder demineralization, and reduce microbial adhesion in difficult-to-access areas. Selection of denture base for clinical use will consider its ability to act as an ion/drug reservoir that is capable of release and recharge.

Overview of incorporation of inorganic antimicrobial materials in denture base resin: A scoping review

STATEMENT OF PROBLEM

Dental hygiene for institutionalized patients and recurring Candida-associated denture stomatitis remain problematic because of a patient's limited dexterity or inability to eliminate Candida from denture surfaces. Although there has been extensive research into antimicrobial modification of denture base resins with inorganic materials, scoping reviews of the literature to identify knowledge gaps or efficacy of inorganic antimicrobial materials in denture base resins are lacking.

PURPOSE

The purpose of this scoping review was to provide a synopsis of the efficacy of the major classes of inorganic antimicrobial materials currently incorporated into denture base resins.

MATERIAL AND METHODS

The Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) extension for scoping reviews was applied. Four electronic databases, including Embase, PubMed, Web of Science, and Google Scholar, were accessed for articles in the English language, up to February 2019, without restrictions on the date of publication.

RESULTS

From the 53 articles selected, 25 distinguishable inorganic materials were found and divided into 3 subgroups. Forty-three articles evaluated nanomaterials, where mostly silver ion nanoparticles and/or titanium dioxide nanoparticles were incorporated into denture base resins. Fourteen articles examined antimicrobial drugs and medications, including azole group medications, amphotericin-B, Bactekiller, chlorhexidine, Novaron, and Zeomic. Two articles classified as others explored hydroxyapatite- and fiber-incorporated denture base resins.

CONCLUSIONS

Although nanotechnology and antimicrobial medications or drugs have been successfully used to reduce Candida-associated denture stomatitis, long-term solutions are still lacking, and their disadvantages continue to outweigh their advantages.

Polymeric Denture Base Materials: A Review

An ideal denture base must have good physical and mechanical properties, biocompatibility, and esthetic properties. Various polymeric materials have been used to construct denture bases. Polymethyl methacrylate (PMMA) is the most used biomaterial for dentures fabrication due to its favorable properties, which include ease of processing and pigmenting, sufficient mechanical properties, economy, and low toxicity. This article aimed to comprehensively review the current knowledge about denture base materials (DBMs) types, properties, modifications, applications, and construction methods. We searched for articles about denture base materials in PubMed, Scopus, and Embase. Journals covering topics including dental materials, prosthodontics, and restorative dentistry were also combed through. Denture base material variations, types, qualities, applications, and fabrication research published in English were considered. Although PMMA has several benefits and gained popularity as a denture base material, it has certain limitations and cannot be classified as an ideal biomaterial for fabricating dental prostheses. Accordingly, several studies have been performed to enhance the physical and mechanical properties of PMMA by chemical modifications and mechanical reinforcement using fibers, nanofillers, and hybrid materials. This review aimed to update the current knowledge about DBMs' types, properties, applications, and recent developments. There is a need for specific research to improve their biological properties due to patient and dental staff adverse reactions to possibly harmful substances produced during their manufacturing and use.

Adhesion of biofilm, surface characteristics, and mechanical properties of antimicrobial denture base resin

PURPOSE

This study incorporated the nanomaterial, nanostructured silver vanadate decorated with silver nanoparticles (AgVO₃), into heat-cured resin (HT) at concentrations of 2.5%, 5%, and 10% and compared the adhesion of multispecies biofilms, surface characteristics, and mechanical properties with conventional heat-cured (HT 0%) and printed resins.

MATERIALS AND METHODS

AgVO₃ was incorporated in mass into HT powder. A denture base resin was used to obtain printed samples. Adhesion of a multispecies biofilm of Candida albicans, Candida glabrata, and Streptococcus mutans was evaluated by colony-forming units per milliliter (CFU/mL) and metabolic activity. Wettability, roughness, and scanning electron microscopy (SEM) were used to assess the physical characteristics of the surface. The mechanical properties of flexural strength and elastic modulus were tested.

RESULTS

HT 10%-AgVO₃ showed efficacy against S. mutans; however, it favored C. albicans CFU/mL (P < .05). The printed resin showed a higher metabolically active biofilm than HT 0% (P < .05). There was no difference in wettability or roughness between groups (P > .05). Irregularities on the printed resin surface and pores in HT 5%-AgVO₃ were observed by SEM. HT 0% showed the highest flexural strength, and the resins incorporated with AgVO₃ had the highest elastic modulus (P < .05).

CONCLUSION

The incorporation of 10% AgVO₃ into heat-cured resin provided antimicrobial activity against S. mutans in a multispecies biofilm did not affect the roughness or wettability but reduced flexural strength and increased elastic modulus. Printed resin showed higher irregularity, an active biofilm, and lower flexural strength and elastic modulus than heat-cured resin.

Cerium oxide nanozymes confer a cytoprotective and bio-friendly surface micro-environment to methacrylate based oro-facial prostheses

Poly-(methyl methacrylate) (PMMA) is the preferred biomaterial for orofacial prostheses used for the rehabilitation of naso-palatal defects. However, conventional PMMA has limitations determined by the complexity of the local microbiota and the friability of oral mucosa adjacent to these defects. Our purpose was to develop a new type of PMMA, i-PMMA, with good biocompatibility and better biological effects such as higher resistance to microbial adhesion of multiple species and enhanced antioxidant effect. The addition of cerium oxide nanoparticles to PMMA using a mesoporous nano-silica carrier and polybetaine conditioning, resulted in an increased release of cerium ions and enzyme mimetic activity, without tangible loss of mechanical properties. Ex vivo experiments confirmed these observations. In stressed human gingival fibroblasts, i-PMMA reduced the levels of reactive oxygen species and increased the expression of homeostasis-related proteins (PPARg, ATG5, LCI/III). Furthermore, i-PMMA increased the levels of expression of superoxide dismutase and mitogen-activated protein kinases (ERK and Akt), and cellular migration. Lastly, we demonstrated the biosafety of i-PMMA using two in vivo models: skin sensitization assay and oral mucosa irritation test, respectively. Therefore, i-PMMA offers a cytoprotective interface that prevents microbial adhesion and attenuates oxidative stress, thus supporting physiological recovery of the oral mucosa.

Polymethyl methacrylate resin containing ε-poly-L-lysine and 2-methacryloyloxyethyl phosphorylcholine with antimicrobial effects

STATEMENT OF PROBLEM

Polymethyl methacrylate (PMMA) is commonly used in dentistry, including as a denture base material. However, the colonization of a PMMA surface by microbial microorganisms could increase the risk of oral diseases such as denture stomatitis and gingivitis. The development of PMMA with antibacterial properties should improve its clinical application, but whether adding ε-poly-L-lysine (ε-PL) and 2-methacryloyloxyethyl phosphorylcholine (MPC) provides antimicrobial effects is unclear.

PURPOSE

This in vitro study aimed to develop a novel antibacterial PMMA resin containing the natural nontoxic antibacterial agent ε-PL and the protein repellent agent MPC. The mechanical properties, protein repellency, and antimicrobial activities of the resin were then evaluated.

MATERIAL AND METHODS

Different mass fractions of ε-PL and MPC were mixed into PMMA as the experimental groups, with unaltered PMMA as the control group. The flexural strength (n=10) and surface roughness (n=6) of the resulting mixtures were measured to determine their mechanical properties. The antiprotein properties were measured by using the micro bicinchoninic acid method (n=6). The antimicrobial effect of the resin was assessed using live/dead staining (n=6) and methyltransferase (MTT) assays (n=10). According to the variance homogeneity and normal distribution results, 1-way analysis of variance followed by the Tukey honestly significant difference test or the Welch test and the Games-Howell test were used (α=.05 for all tests).

RESULTS

No significant differences were found in the flexural strength values and surface roughness of the specimens containing 1.5% MPC and 1.5% ε-PL compared with those of the control (P>.05). The addition of ε-PL to the PMMA resin alone significantly increased its bactericidal properties (P<.05). Adding both ε-PL and MPC further increased the antibacterial activity of the PMMA resin without increasing protein adhesion more than in the control group.

CONCLUSIONS

The incorporation of both ε-PL and MPC into PMMA improved its antibacterial capacity without affecting its mechanical properties and did not increase protein adhesion. Therefore, the novel PMMA fabricated in this study shows promise for dental applications.

PMMA-Based Nanocomposites for Odontology Applications: A State-of-the-Art

Polymethyl methacrylate (PMMA), a well-known polymer of the methacrylate family, is extensively used in biomedicine, particularly in odontological applications including artificial teeth, dentures and denture bases, obturators, provisional or permanent crowns, and so forth. The exceptional PMMA properties, including aesthetics, inexpensiveness, simple manipulation, low density, and adjustable mechanical properties, make it a perfect candidate in the field of dentistry. However, it presents some deficiencies, including weakness regarding hydrolytic degradation, poor fracture toughness, and a lack of antibacterial activity. To further enhance its properties and solve these drawbacks, different approaches can be performed, including the incorporation of nanofillers. In this regard, different types of metallic nanoparticles, metal oxide nanofillers, and carbon-based nanomaterials have been recently integrated into PMMA matrices with the aim to reduce water absorption and improve their performance, namely their thermal and flexural properties. In this review, recent studies regarding the development of PMMA-based nanocomposites for odontology applications are summarized and future perspectives are highlighted.

Silver-loaded mesoporous silica nanoparticles enhanced the mechanical and antimicrobial properties of 3D printed denture base resin

The aim of this study is to develop a novel 3D printed denture base resin material modified with mesoporous silica nanocarrier loaded with silver (Ag/MSN) to enhance mechanical and antimicrobial properties. Acrylate resin-based was incorporated with various proportion of Ag/MSN (0.0-2.0 wt%). Specimens with different geometry were printed and characterized accordingly for the effect of modification on properties such as: mechanical and physical properties, chemical composition and degree of conversion, as well as biological response in term of biocompatibility and antimicrobial against oral fibroblast and candida biofilm (C. albicans), respectively. The consecutive addition of Ag/MSN improved significantly surface hardness and crack propagation resistance, while flexural strength remained similar to control; however, a negligible decrease was observed with higher concentrations ≥1 wt%. No significant difference was noticed with water sorption, while water solubility had a remarkable trend of reduction associated with filler content. The surface roughness significantly increased when concentration of Ag/MSN was ≥1.0 wt%. A significant reduction in C. albicans biofilm mass, as the inhibition proficiency was correlated with the proportion of the filler. With respect to the amount of Ag/MSN, the modification was compatible toward fibroblast cells. The sequential addition of Ag/MSN enhanced significantly the mechanical and antimicrobial properties of the 3D printed resin-based material without affecting adversely compatibility. The acrylic resin denture base material has susceptibility of microbial adhesion which limits its application. Silver loaded MSN showed a significant performance to enhance antimicrobial activity against C. albicans which is the main cause of denture stomatitis. The proposed invention is a promise technique for clinical application to provide an advanced prosthesis fabrication and serve as long-term drug delivery.

Mechanical Characterization of Dental Prostheses Manufactured with PMMA-Graphene Composites

The use of a PMMA composite with graphene is being commercialized for application as dental prostheses. The different proportions of fibers provide a wide range of colors that favors dental esthetics in prostheses. However, there are no studies that have explained the influence that graphene has on the mechanical properties. In this contribution, we studied the PMMA and PMMA material with graphene fibers (PMMA-G) in the form of discs as supplied for machining. The presence of graphene fibers has been studied by Raman spectroscopy and the Shore hardness and Vickers micro hardness were determined. Mechanical compression tests were carried out to obtain the values of maximum strength and Young’s modulus (E) and by means of pin-on-disc wear tests, the specific wear rate and the friction coefficients were determined following the established international standards. Finally, the samples were characterized by field emission scanning electron microscopy (FESEM) to characterize the graphene’s morphology inside the PMMA. The results showed the presence of graphene in PMMA and was estimated in an amount of 0.1027% by weight in G-PMMA. The Shore hardness and Vickers microhardness values did not show statistically significant differences. Differences were observed in the compression maximum strength (129.43 MPa for PMMA and 140.23 for PMMA-G) and E values (2.01 for PMMA and 2.89 GPa for PMMA-G) as well as in the lower wear rate for the G-PMMA samples (1.93 × 10−7 for PMMA and 1.33 × 10−7 mm3/N·m) with a p < 0.005. The coefficients of friction for PMMA-G decreased from 0.4032 for PMMA to 0.4001 for PMMA-G. From the results obtained, a slight content in graphene produced a significant improvement in the mechanical properties that could be observed in the prosthesis material. Therefore, we can state that the main attraction of this material for dental prosthesis is its esthetics.

Application of antibacterial nanoparticles in orthodontic materials

During the orthodontic process, increased microbial colonization and dental plaque formation on the orthodontic appliances and auxiliaries are major complications, causing oral infectious diseases, such as dental caries and periodontal diseases. To reduce plaque accumulation, antimicrobial materials are increasingly being investigated and applied to orthodontic appliances and auxiliaries by various methods. Through the development of nanotechnology, nanoparticles (NPs) have been reported to exhibit excellent antibacterial properties and have been applied in orthodontic materials to decrease dental plaque accumulation. In this review, we present the current development, antibacterial mechanisms, biocompatibility, and application of antibacterial NPs in orthodontic materials.

The denture microbiome in health and disease: an exploration of a unique community

The United Nations suggests the global population of denture wearers (an artificial device that acts as a replacement for teeth) is likely to rise significantly by the year 2050. Dentures become colonized by microbial biofilms, the composition of which is influenced by complex factors such as patient’s age and health, and the nature of the denture material. Since colonization (and subsequent biofilm formation) by some micro‐organisms can significantly impact the health of the denture wearer, the study of denture microbiology has long been of interest to researchers. The specific local and systemic health risks of denture plaque are different from those of dental plaque, particularly with respect to the presence of the opportunist pathogen Candida albicans and various other nonoral opportunists. Here, we reflect on advancements in our understanding of the relationship between micro‐organisms, dentures, and the host, and highlight how our growing knowledge of the microbiome, biofilms, and novel antimicrobial technologies may better inform diagnosis, treatment, and prevention of denture‐associated infections, thereby enhancing the quality and longevity of denture wearers.

Molecular weight tuning optimizes poly(2-methoxyethyl acrylate) dispersion to enhance the aging resistance and anti-fouling behavior of denture base resin

Poly(methyl methacrylate) (PMMA)-based denture base resins easily develop oral bacterial and fungal biofilms, which may constitute a significant health risk. Conventional bacterial-resistant additives and coatings often cause undesirable changes in the resin. Reduced bacterial resistance over time in the harsh oral environment is a major challenge in resin development. Poly(2-methoxyethyl acrylate) (PMEA) has anti-fouling properties; however, due to the oily/rubbery state of this polymer, and its surface aggregation tendency in a resin mixture, its direct use as a resin additive is limited. This study aimed to optimize the use of PMEA in dental resins. Acrylic resins containing a series of PMEA polymers with various molecular weights (MWs) at different concentrations were prepared, and the mechanical properties, surface gloss, direct transmittance, and cytotoxicity were evaluated, along with the distribution of PMEA in the resin. Resins with low-MW PMEA (2000 g mol^-1) (PMEA-1) at low concentrations satisfied the clinical requirements for denture resins, and the PMEA was homogeneously distributed. The anti-fouling performance of the resin was evaluated for protein adsorption, bacterial and fungal attachment, and saliva-derived biofilm formation. The PMEA-1 resin most effectively inhibited biofilm formation (∼50% reduction in biofilm mass and thickness compared to those of the control). Post-aged resins maintained their mechanical properties and anti-fouling activity, and polished surfaces had the same anti-biofilm behavior. Based on wettability and tribological results, we propose that the PMEA additive creates a non-stick surface to inhibit biofilm formation. This study demonstrated that PMEA additives can provide a stable and biocompatible anti-fouling surface, without sacrificing the mechanical properties and aesthetics of denture resins.

Multifunctional GelMA platforms with nanomaterials for advanced tissue therapeutics

Polymeric hydrogels are fascinating platforms as 3D scaffolds for tissue repair and delivery systems of therapeutic molecules and cells. Among others, methacrylated gelatin (GelMA) has become a representative hydrogel formulation, finding various biomedical applications. Recent efforts on GelMA-based hydrogels have been devoted to combining them with bioactive and functional nanomaterials, aiming to provide enhanced physicochemical and biological properties to GelMA. The benefits of this approach are multiple: i) reinforcing mechanical properties, ii) modulating viscoelastic property to allow 3D printability of bio-inks, iii) rendering electrical/magnetic property to produce electro-/magneto-active hydrogels for the repair of specific tissues (e.g., muscle, nerve), iv) providing stimuli-responsiveness to actively deliver therapeutic molecules, and v) endowing therapeutic capacity in tissue repair process (e.g., antioxidant effects). The nanomaterial-combined GelMA systems have shown significantly enhanced and extraordinary behaviors in various tissues (bone, skin, cardiac, and nerve) that are rarely observable with GelMA. Here we systematically review these recent efforts in nanomaterials-combined GelMA hydrogels that are considered as next-generation multifunctional platforms for tissue therapeutics. The approaches used in GelMA can also apply to other existing polymeric hydrogel systems.

What Are the Cleaning and Disinfection Methods for Acrylic Orthodontic Removable Appliance? A Systematic Review

(1) Background: The use of removable orthodontic appliances, which is common in early ages, requires careful hygiene, as several different microorganisms are found on their surface during the orthodontic treatment. (2) Methods: Comprehensive electronic searches were conducted up to May 2021. Randomized controlled trials (RCTs) or controlled clinical trials (CCTs), prospective or retrospective, evaluating the efficacy of cleaning and disinfection methods for acrylic removable orthodontic appliances, redacted in the English language, were included. Three independent blinding review authors were involved in study selection, data extraction, and bias assessment. (3) Results: A total of 2491 records were screened and eight studies (six RCTs and two CCTs) fulfilled the inclusion criteria. Among the overall cleaning and disinfection methods described in the included studies, four categories could be defined: liquid antimicrobial agents, commercial tablet cleansers, natural plant extracts and incorporation of quaternary ammonium methacryloxy silicate, all of which demonstrated superior efficacy compared to the placebo/negative control. However, the different methods were not compared with each other. (4) Conclusions: Biofilm control on acrylic orthodontic removable appliances can be performed using the different cleaning and disinfection methods considered in the included studies. Further studies are needed to define the most effective technique. Registration: PROSPERO CRD 42021269297.

Inorganically modified particles FeAl-LDH@SiO2 as reinforcement in poly (methyl) methacrylate matrix composite

Silica particles were obtained from rice husk to which layered double hydroxide particles were deposited (weight ratio 1 : 1). Fe²⁺-Al³⁺ layered double hydroxides (FeAl-LDH) were synthesized by co-precipitation with ratios Fe : Al of 3 : 1 in the presence of SiO₂ particles from the rice husk. Characterization of the synthesized FeAl-LDH@SiO₂ particles was performed by X-ray diffraction, Fourier transforms infrared spectroscopy (FTIR) and scanning electron microscopy with EDS. Prepared FeAl-LDH@SiO₂ particles were used as reinforcing agents in 1, 3 and 5 wt% quantity in poly (methyl) methacrylate matrix. The aim of this study was to examine whether FeAl-LDH@SiO₂ particles affect the mechanical properties of polymer composite materials. The morphology of the composites was examined using a field emission scanning electron microscope. Microindentation, tensile and impact testing determined the mechanical properties of the obtained composites.

Incorporation of Copper-Doped Mesoporous Bioactive Glass Nanospheres in Experimental Dental Composites: Chemical and Mechanical Characterization

Experimental dental resin composites incorporating copper-doped mesoporous bioactive glass nanospheres (Cu-MBGN) were designed to impart antibacterial and remineralizing properties. The study evaluated the influence of Cu-MBGN on the mechanical properties and photopolymerization of resin composites. Cu-MBGN were synthesized using a microemulsion-assisted sol-gel method. Increasing amounts of Cu-MBGN (0, 1, 5, and 10 wt %) were added to the organic polymer matrix with inert glass micro- and nanofillers while maintaining a constant resin/filler ratio. Six tests were performed: X-ray diffraction, scanning electron microscopy, flexural strength (FS), flexural modulus (FM), Vickers microhardness (MH), and degree of conversion (DC). FS and MH of Cu-MBGN composites with silica fillers showed no deterioration with aging, with statistically similar results at 1 and 28 days. FM was not influenced by the addition of Cu-MBGN but was reduced for all tested materials after 28 days. The specimens with 1 and 5% Cu-MBGN had the highest FS, FM, MH, and DC values at 28 days, while controls with 45S5 bioactive glass had the lowest FM, FS, and MH. DC was high for all materials (83.7-93.0%). Cu-MBGN composites with silica have a potential for clinical implementation due to high DC and good mechanical properties with adequate resistance to aging.

Influence of the Surface Energy of Different Brands of Polymethyl Methacrylate on the Adherence of Candida albicans: An In Vitro Study

Objective:

The objective of this study was to evaluate the influence of the surface energy of different brands of polymethyl methacrylate (PMMA) on the adherence of Candida albicans ATCC 10231 in an in vitro study.

Materials and Methods:

The study had an in vitro, longitudinal, and comparative experimental design. The following groups were made: (1) Vitacryl versus controls (water, dimethyl sulfoxide, glycerol, diethylene glycol, and formamide); (2) Triplex versus the same controls; (3) Vitacryl versus Triplex (surface energy); and (4) Vitacryl versus Triplex (adhesion per cell/field). Adhesion was measured in the area of each field magnified 10 × 10, and with an increase in magnification to 40 × 10, very dense colonies of 0.152 mm² were observed.

Results:

The surface energy of Vitacryl and Triplex was 40.3 ± 0.3 and 39.5 ± 0.3N/m, respectively, showing statistically significant differences (P < 0.001). On the contrary, in relation to the adhesion per cell/field of C. albicans, Vitacryl presented 15.7 ± 1.1, whereas Triplex had 16.7 ± 2.3, with no significant differences (P = 0.058).

Conclusion:

In relation to the adhesion per cell/field of C. albicans, there was no evidence of significant differences between Vitacryl and Triplex.

Surface Characterization, Biocompatibility and Antifungal Efficacy of a Denture-Lining Material Containing Cnidium officinale Extracts

Herein, we investigated the surface characterization and biocompatibility of a denture-lining material containing Cnidium officinale extracts and its antifungal efficacy against Candida albicans. To achieve this, a denture-lining material containing various concentrations of C. officinale extract and a control group without C. officinale extract were prepared. The surface characterization and biocompatibility of the samples were investigated. In addition, the antifungal efficacy of the samples on C. albicans was investigated using spectrophotometric growth and a LIVE/DEAD assay. The results revealed that there was no significant difference between the biocompatibility of the experimental and control groups (p > 0.05). However, there was a significant difference between the antifungal efficiency of the denture material on C. albicans and that of the control group (p < 0.05), which was confirmed by the LIVE/DEAD assay. These results indicate the promising potential of the C. officinale extract-containing denture-lining material as an antifungal dental material.

Ceria-Incorporated Biopolymer for Preventing Fungal Adhesion

Although biopolymers are widely used in biomedical fields, the issue of poor antimicrobial properties remains unsolved, leading to a potential increase in infections. Here, ceria nanoparticles (CNPs) were incorporated into a representative biopolymer, poly(methyl methacrylate) (PMMA), for drug-free antimicrobial properties. After characterizing the CNPs and surface/mechanical properties of the CNP-PMMA nanocomposite, antiadhesive effects against Candida albicans, the most common fungal species responsible for fungal infections, were determined using metabolic activity assays, and the underlying microbial antiadhesive mechanism was revealed. Hydrothermally fabricated CNPs showed a size of ∼20 nm with a zeta potential of 12 ± 2.3 mV and showed catalytic properties as a ROS modulator. Successful incorporation of CNPs into PMMA up to 2 wt % was confirmed by EDS analysis. The surface roughness and mechanical properties such as flexural strength and modulus were relatively unchanged up to 2 wt %. In contrast, the surface energy increased, and the Vickers hardness decreased in the 2 wt % PMMA compared with the control. A drop of up to 90% of adherent Candida albicans was observed in CNP-incorporated PMMA, which was confirmed and quantified via fungus staining images. The antiadhesive mechanism was revealed from the direct antimicrobial effects of CNP via the upregulation of the intracellular ROS level. Taken together, the antimicrobial-adhesive properties of the CNP-PMMA nanocomposite suggest the potential usefulness of CNP as a promising drug-free antimicrobial ingredient for biopolymers, which could lead to the prevention of microbial-induced complications in clinical settings.

Nanotechnology in dentistry: Present and future perspectives on dental nanomaterials

OBJECTIVES

The number of dental nanomaterials has increased significantly over the past years. A variety of commercial dental nanomaterials are available and researched. Nevertheless, how these nanomaterials work, what makes them special and whether they are superior to traditional dental materials is not always clear to dentists and researchers. The objective of this review paper is, therefore, to give an overview of the principles of nanomaterials and basic research and applications of dental nanomaterials.

METHODS

The fundamentals of materials science of nanomaterials as well as their advantages and disadvantages are elaborated. The most important dental nanomaterials are discussed. This is mainly based on a survey of the literature and a review of the most frequently cited scientific papers in the international peer reviewed journal Dental Materials over the past five years. The developments of commercial dental nanomaterials as well as aspects of their clinical use are considered in this review.

RESULTS

Nanomaterials have unique structures and properties that distinguish them from other materials. The journal Dental Materials is the journal with the highest numbers of articles and citations on the subject of dental nanomaterials. The most frequently reported dental nanomaterials are nanocomposites, nanoparticles, antimicrobial nanomaterials and bio-mineralization systems. Hallmarks of dental nanomaterials include a set of unique properties and challenges in the preparation of these materials.

SIGNIFICANCE

By understanding the physical principles of dental nanomaterials, their strengths, limitations and their specific benefits will be better appreciated. Dental nanomaterials have potential for the future but currently do not always exhibit superior properties, for example in clinical situations.

Advances of Anti-Caries Nanomaterials

Caries is the most common and extensive oral chronic disease. Due to the lack of anti-caries properties, traditional caries filling materials can easily cause secondary caries and lead to treatment failure. Nanomaterials can interfere with the bacteria metabolism, inhibit the formation of biofilm, reduce demineralization, and promote remineralization, which is expected to be an effective strategy for caries management. The nanotechnology in anti-caries materials, especially nano-adhesive and nano-composite resin, has developed fast in recent years. In this review, the antibacterial nanomaterials, remineralization nanomaterials, and nano-drug delivery systems are reviewed. We are aimed to provide a theoretical basis for the future development of anti-caries nanomaterials.

Prosthodontic Applications of Polymethyl Methacrylate (PMMA): An Update

A wide range of polymers are commonly used for various applications in prosthodontics. Polymethyl methacrylate (PMMA) is commonly used for prosthetic dental applications, including the fabrication of artificial teeth, denture bases, dentures, obturators, orthodontic retainers, temporary or provisional crowns, and for the repair of dental prostheses. Additional dental applications of PMMA include occlusal splints, printed or milled casts, dies for treatment planning, and the embedding of tooth specimens for research purposes. The unique properties of PMMA, such as its low density, aesthetics, cost-effectiveness, ease of manipulation, and tailorable physical and mechanical properties, make it a suitable and popular biomaterial for these dental applications. To further improve the properties (thermal properties, water sorption, solubility, impact strength, flexural strength) of PMMA, several chemical modifications and mechanical reinforcement techniques using various types of fibers, nanoparticles, and nanotubes have been reported recently. The present article comprehensively reviews various aspects and properties of PMMA biomaterials, mainly for prosthodontic applications. In addition, recent updates and modifications to enhance the physical and mechanical properties of PMMA are also discussed.

Resin-Based Sealant with Bioactive Glass and Zwitterionic Material for Remineralisation and Multi-Species Biofilm Inhibition

Since pits and fissures are the areas most commonly affected by caries due to their structural irregularity, bioactive resin-based sealant (RBS) may contribute to the prevention of secondary caries. This study aims to investigate the mechanical, physical, ion-release, enamel remineralisation, and antibacterial capabilities of the novel RBS with bioactive glass (BAG) and 2-methacryloyloxyethyl phosphorylcholine (MPC). For the synthesis, 12.5 wt% BAG and 3 wt% MPC were incorporated into RBS. The contact angle, flexural strength, water sorption, solubility, and viscosity were investigated. The release of multiple ions relating to enamel remineralisation was investigated. Further, the attachments of bovine serum albumin, brain heart infusion broth, and Streptococcus mutans on RBS were studied. Finally, the thickness and biomass of a human saliva-derived microsm biofilm model were analysed before aging, with static immersion aging and with thermocycling aging. In comparison to commercial RBS, BAG+MPC increased the wettability, water sorption, solubility, viscosity, and release of multiple ions, while the flexural strength did not significantly differ. Furthermore, RBS with MPC and BAG+MPC significantly reduced protein and bacteria adhesion and suppressed multi-species biofilm attachment regardless of the existence of aging and its type. The novel RBS has great potential to facilitate enamel remineralisation and suppress biofilm adhesion, which could prevent secondary dental caries.

Silica Nanoparticles-A Versatile Tool for the Treatment of Bacterial Infections

The rapid emergence of drug resistance continues to outpace the development of new antibiotics in the treatment of infectious diseases. Conventional therapy is currently limited by drug access issues such as low intracellular drug accumulations, drug efflux by efflux pumps and/or enzymatic degradation. To improve access, targeted delivery using nanocarriers could provide the quantum leap in intracellular drug transport and retention. Silica nanoparticles (SiNPs) with crucial advantages such as large surface area, ease-of-functionalization, and biocompatibility, are one of the most commonly used nanoparticles in drug delivery applications. A porous variant, called the mesoporous silica nanoparticles (MSN), also confers additional amenities such as tunable pore size and volume, leading to high drug loading capacity. In the context of bacterial infections, SiNPs and its variants can act as a powerful tool for the targeted delivery of antimicrobials, potentially reducing the impact of high drug dosage and its side effects. In this review, we will provide an overview of SiNPs synthesis, its structural proficiency which is critical in loading and conjugation of antimicrobials and its role in different antimicrobial applications with emphasis on intracellular drug targeting in anti-tuberculosis therapy, nitric oxide delivery, and metal nanocomposites. The role of SiNPs in antibiofilm coatings will also be covered in the context of nosocomial infections and surgical implants.

Surface silanization and grafting reaction of nano-silver loaded zirconium phosphate and properties strengthen in 3D-printable dental base composites

In this work, surface modification of nano silver-loaded zirconium phosphate (6S-NP3) were obtained from simultaneous silanization of γ-methacryloxypropyltrimethoxysilane (MPS) and grafting reaction of methyl methacrylate (MMA), and then mixed with denture base resin (E-Denture) to prepare denture base composites using 3D printer printing. FT-IR spectra confirmed that surface silanization and grafting reaction had occurred and MPS and MMA were successfully anchored on the surface of 6S-NP3. XRD results demonstrated that surface modification had occurred on the surface of hexagonal lattice. The average diameter data indicated that the surface modification decreased the average diameter of nanoparticles. The water contact angle (WCA) was found increasing as the surface modification. SEM images illustrated that the dispersion and compatibility of nanoparticles in denture base composite materials had improved. The results of mechanical properties presented that composites with the addition of P-6S-NP3 nanoparticles achieved higher flexural strength, flexural modulus and impact strength. The data of antibacterial activities revealed that composites had exhibited good antibacterial activities against either S. aureus or E. coli and the latter showed better antibacterial efficacy than the former.

Current aspects and prospects of glass ionomer cements for clinical dentistry

Glass ionomer cement (GIC) is a tailor-made material that is used as a filling material in dentistry. GIC is cured by an acid-base reaction consisting of a glass filler and ionic polymers. When the glass filler and ionic polymers are mixed, ionic bonds of the material itself are formed. In addition, the extra polymer anion reacts with calcium in enamel or dentin to increase adhesion to the tooth tissue. GICs are widely used as adhesives for artificial crowns or orthodontic brackets, and are also used as tooth repair material, cavity liner, and filling materials. In this review, the current status of GIC research and development and its prospects for the future have been discussed in detail.

Preparation of Zn doped mesoporous silica nanoparticles (Zn-MSNs) for the improvement of mechanical and antibacterial properties of dental resin composites

OBJECTIVE

The purpose of this work was to explore the enhancement effect of zinc doped mesoporous silica nanoparticles (Zn-MSNs), which could form micromechanical interlocking with resin matrix and sustainably release Zn²⁺, on the mechanical and antibacterial properties of the dental resin composites.

METHODS

Zn-MSNs were prepared by a sol-gel method, and characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and N₂ adsorption/desorption. The mechanical properties of the dental composites reinforced by Zn-MSNs were measured by a universal mechanical testing machine. Antibacterial activities of dental composites were evaluated by both qualitative and quantitative analysis using Streptococcus mutans (S. mutans). The cytotoxicity of the Zn-MSNs filled dental composites was investigated by osteoblasts (OBs).

RESULTS

The synthesized Zn-MSNs possessed good monodispersity with an average particle size of about 138nm. The mechanical properties of the composites gradually increased with the increase of the content of Zn-MSNs. The flexural strength, flexural modulus, compressive strength and micro-hardness of the composites containing 15wt% Zn-MSNs were 31.21%, 50.47%, 53.83% and 26.79% higher than the samples with no Zn-MSNs, respectively. The antibacterial performance was significantly improved by the addition of Zn-MSNs and the antibacterial rate of the composite with 15wt% of Zn-MSNs reached 100%. Cytotoxicity tests revealed that all the composites were biocompatible during OBs incubation.

SIGNIFICANCE

The prepared Zn-MSNs can effectively improve the mechanical and antibacterial properties of the dental resin composites.

Novel Dental Poly (Methyl Methacrylate) Containing Phytoncide for Antifungal Effect and Inhibition of Oral Multispecies Biofilm

Despite the many advantages of poly (methyl methacrylate) (PMMA) as a dental polymer, its antifungal and antibacterial effects remain limited. Here, phytoncide was incorporated into PMMA to inhibit fungal and biofilm accumulation without impairing the basic and biological properties of PMMA. A variable amount of phytoncide (0 wt % to 5 wt %) was incorporated into PMMA, and the basic material properties of microhardness, flexural strength and gloss were evaluated. In addition, cell viability was confirmed by MTT assay. This MTT assay measures cell viability via metabolic activity, and the color intensity of the formazan correlates viable cells. The fungal adhesion and viability on the PMMA surfaces were evaluated using Candida albicans (a pathogenic yeast). Finally, the thickness of saliva-derived biofilm was estimated. The flexural strength of PMMA decreased with increasing phytoncide contents, whereas there were no significant differences in the microhardness and gloss (p > 0.05) and the cell viability (p > 0.05) between the control and the phytoncide-incorporated PMMA samples. The amounts of adherent Candida albicans colony-forming unit (CFU) counts, and saliva-derived biofilm thickness were significantly lower in the phytoncide-incorporated PMMA compared to the control (p < 0.05). Hence, it was concluded that the incorporation of appropriate amounts of phytoncide in PMMA demonstrated antifungal effects while maintaining the properties, which could be a possible use in dentistry application such as denture base resin.

Polymeric and inorganic nanoscopical antimicrobial fillers in dentistry

Failure of dental treatments is mainly due to the biofilm accumulated on the dental materials. Many investigations have been conducted on the advancements of antimicrobial dental materials. Polymeric and inorganic nanoscopical agents are capable of inhibiting microorganism proliferation. Applying them as fillers in dental materials can achieve enhanced microbicidal ability. The present review provides a broad overview on the state-of-the-art research in the field of antimicrobial fillers which have been adopted for incorporation into dental materials over the last 5 years. The antibacterial agents and applications are described, with the aim of providing information for future investigations. STATEMENT OF SIGNIFICANCE: Microbial infection is the primary cause of dental treatment failure. The present review provides an overview on the state-of-art in the field of antimicrobial nanoscopical or polymeric fillers that have been applied in dental materials. Trends in the biotechnological development of these antimicrobial fillers over the last 5 years are reviewed to provide a backdrop for further advancement in this field of research.

A New Antibacterial Agent-Releasing Polydimethylsiloxane Coating for Polymethyl Methacrylate Dental Restorations

Chlorhexidine (CHX) has been incorporated into the composition of polymethyl methacrylate (PMMA) dental restorations to enhance their antimicrobial performance. However, the controlled delivery of CHX remains a challenge. Although previous findings with pure silica or polymer coatings demonstrated the resistance to bacterial adhesion, they did not provide antibacterial activity beyond the coated surface. Polydimethylsiloxane (PDMS) and mesoporous silica nanoparticles (MSNs) are widely used in biomedical science as a transfer medium in drug delivery systems. Here, the MSNs are used to encapsulate CHX, and the combination is added to PDMS. A thin coating film is formed on the PMMA, using oxygen plasma and thermal treatment. The liquid chromatography analysis shows that the coating film has high encapsulation efficiency and loading capacity, with a slow and stable release rate of CHX. The cytotoxicity tests also show that the coating does not affect the proinflammatory cytokines, cellular mitotic activity, or apoptotic cell death. The ability of the coating to release CHX indicates that the coating may even be effective against bacteria that are not directly in contact with the surface. This antibacterial protective film is expected to be a novel method to inhibit bacterial activity distal to the coated surfaces of PMMA restorations.

Silver Nanoparticles Addition in Poly(Methyl Methacrylate) Dental Matrix: Topographic and Antimycotic Studies

The widespread use of nanoparticles (NPs) in medical devices has opened a new scenario in the treatment and prevention of many diseases and infections owing to unique physico-chemical properties of NPs. In this way, silver nanoparticles (AgNPs) are known to have a strong antimicrobial activity, even at low concentrations, due to their ability to selectively destroy cellular membranes. In particular, in the field of dental medicine, the use of AgNPs in different kinds of dental prosthesis matrixes could be a fundamental tool in immunodepressed patients that suffer of different oral infections. Candida albicans (C. albicans), an opportunistic pathogenic yeast with high colonization ability, is one of the causative agents of oral cavity infection. In our work, we added monodispersed citrate-capping AgNPs with a size of 20 nm at two concentrations (3 wt% and 3.5 wt%) in poly(methyl methacrylate) (PMMA), the common resin used to develop dental prostheses. After AgNPs characterization, we evaluated the topographical modification of PMMA and PMMA with the addition of AgNPs by means of atomic force microscopy (AFM), showing the reduction of surface roughness. The C. albicans colonization on PMMA surfaces was assessed by the Miles and Misra technique as well as by scanning electron microscopy (SEM) at 24 h and 48 h with encouraging results on the reduction of yeast viability after AgNPs exposure.

Novel Protein-Repellent and Antibacterial Resins and Cements to Inhibit Lesions and Protect Teeth

Orthodontic treatment is increasingly popular as people worldwide seek esthetics and better quality of life. In orthodontic treatment, complex appliances and retainers are placed in the patients’ mouths for at least one year, which often lead to biofilm plaque accumulation. This in turn increases the caries-inducing bacteria, decreases the pH of the retained plaque on an enamel surface, and causes white spot lesions (WSLs) in enamel. This article reviews the cutting-edge research on a new class of bioactive and therapeutic dental resins, cements, and adhesives that can inhibit biofilms and protect tooth structures. The novel approaches include the use of protein-repellent and anticaries polymeric dental cements containing 2-methacryloyloxyethyl phosphorylcholine (MPC) and dimethylaminododecyl methacrylate (DMAHDM); multifunctional resins that can inhibit enamel demineralization; protein-repellent and self-etching adhesives to greatly reduce oral biofilm growth; and novel polymethyl methacrylate resins to suppress oral biofilms and acid production. These new materials could reduce biofilm attachment, raise local biofilm pH, and facilitate the remineralization to protect the teeth. This novel class of dental resin with dual benefits of antibacterial and protein-repellent capabilities has the potential for a wide range of dental and biomedical applications to inhibit bacterial infection and protect the tissues.

Carbon nanotube incorporation in PMMA to prevent microbial adhesion

Although PMMA-based biomaterials are widely used in clinics, a major hurdle, namely, their poor antimicrobial (i.e., adhesion) properties, remains and can accelerate infections. In this study, carboxylated multiwalled carbon nanotubes (CNTs) were incorporated into poly(methyl methacrylate) (PMMA) to achieve drug-free antimicrobial adhesion properties. After characterizing the mechanical/surface properties, the anti-adhesive effects against 3 different oral microbial species (Staphylococcus aureus, Streptococcus mutans, and Candida albicans) were determined for roughened and highly polished surfaces using metabolic activity assays and staining for recognizing adherent cells. Carboxylated multiwalled CNTs were fabricated and incorporated into PMMA. Total fracture work was enhanced for composites containing 1 and 2% CNTs, while other mechanical properties were gradually compromised with the increase in the amount of CNTs incorporated. However, the surface roughness and water contact angle increased with increasing CNT incorporation. Significant anti-adhesive effects (35~95%) against 3 different oral microbial species without cytotoxicity to oral keratinocytes were observed for the 1% CNT group compared to the PMMA control group, which was confirmed by microorganism staining. The anti-adhesive mechanism was revealed as a disconnection of sequential microbe chains. The drug-free antimicrobial adhesion properties observed in the CNT-PMMA composite suggest the potential utility of CNT composites as future antimicrobial biomaterials for preventing microbial-induced complications in clinical settings (i.e., Candidiasis).

Mesoporous Silica Materials as Drug Delivery: "The Nightmare" of Bacterial Infection

Mesoporous silica materials (MSM) have a great surface area and a high pore volume, meaning that they consequently have a large loading capacity, and have been demonstrated to be unique candidates for the treatment of different pathologies, including bacterial infection. In this text, we review the multiple ways of action in which MSM can be used to fight bacterial infection, including early detection, drug release, targeting bacteria or biofilm, antifouling surfaces, and adjuvant capacity. This review focus mainly on those that act as a drug delivery system, and therefore that have an essential characteristic, which is their great loading capacity. Since MSM have advantages in all stages of combatting bacterial infection; its prevention, detection and finally in its treatment, we can venture to talk about them as the "nightmare of bacteria".

Novel resin-based dental material with anti-biofilm activity and improved mechanical property by incorporating hydrophilic cationic copolymer functionalized nanodiamond

There is an increasing clinical need to design dental restorative materials that combine excellent mechanical property and anti-biofilm activity. In the current study, photocurable polycation functionalized nanodiamond (QND) was synthesized and proposed as novel filler for dental resins. By reason of increased repulsive force between nanoparticles and enhanced compatibility with resin matrix, QND dispersed uniformly in reinforced resins, which would help to transfer stress and deformation from the matrix to fillers more efficiently, resulting in a significant improvement in mechanical properties. Notably, the Vickers's hardness, flexural strength and flexural modulus of resins containing 1.0 wt% QND were 44.5, 36.1 and 41.3% higher than that of control, respectively. The antibacterial activity against Streptococcus mutans (S. mutans) showed that QND-incorporated resins produced anti-adhesive property due to their hydrophilic surfaces and could suppress bacterial growth as a result of the contact-killing effect of embedded nanocomposites. As the synergistic effect of anti-adhesive and bactericidal performance, resins loading 1.0~1.5 wt% QNDs displayed excellent anti-biofilm activity. Meanwhile, the results of macrophage cytotoxicity showed that the proliferation of RAW 264.7 cells remained 84.3%, even at a concentration of 1.0 wt% QNDs after 7-day incubation. Therefore, the QND-containing dental resin with the combination of high mechanical property, bacteria-repellent capability and antibacterial performance holds great potential as a restorative material based on this scheme.

Biostable, antidegradative and antimicrobial restorative systems based on host-biomaterials and microbial interactions

OBJECTIVES

Despite decades of development and their status as the restorative material of choice for dentists, resin composite restoratives and adhesives exhibit a number of shortcomings that limit their long-term survival in the oral cavity. Herein we review past and current work to understand these challenges and approaches to improve dental materials and extend restoration service life.

METHODS

Peer-reviewed work from a number of researchers as well as our own are summarized and analyzed. We also include yet-unpublished work of our own. Challenges to dental materials, methods to assess new materials, and recent material improvements and research directions are presented.

RESULTS

Mechanical stress, host- and bacterial-biodegradation, and secondary caries formation all contribute to restoration failure. In particular, several host- and bacterial-derived enzymes degrade the resin and collagen components of the hybrid layer, expanding the marginal gap and increasing access to bacteria and saliva. Furthermore, the virulence of cariogenic bacteria is up-regulated by resin biodegradation by-products, creating a positive feedback loop that increases biodegradation. These factors work synergistically to degrade the restoration margin, leading to secondary caries and restoration failure. Significant progress has been made to produce hydrolytically stable resins to resist biodegradation, as well as antimicrobial materials to reduce bacterial load around the restoration. Ideally, these two approaches should be combined in a holistic approach to restoration preservation.

SIGNIFICANCE

The oral cavity is a complex environment that poses an array of challenges to long-term material success; materials testing conditions should be comprehensive and closely mimic pathogenic oral conditions.

Protein-repellent and antibacterial effects of a novel polymethyl methacrylate resin

OBJECTIVES

Heat-cured resins are commonly used in orthodontics; however, there is a high incidence of caries, periodontal diseases and denture-induced stomatitis. The objectives of this study were to: (1) develop a new bioactive polymethyl methacrylate (PMMA) resin containing 2-methacryloyloxyethyl phosphorylcholine (MPC) and quaternary ammonium dimethylaminohexadecyl methacrylate (DMAHDM), and (2) investigate the effects on mechanical properties, protein-repellency and antibacterial properties.

METHODS

MPC and DMAHDM were mixed into a commercial acrylic resin (Nature Cryl™ MC). Mechanical properties were measured in three-point flexure. Surface roughness was assessed using atomic force microscopy (AFM). Protein adsorption onto the PMMA resin was measured using a micro bicinchoninic acid (BCA) method. A human saliva microcosm model was used to investigate the live/dead staining and metabolic activity of the biofilms.

RESULTS

Incorporation of 3% MPC and 1.5% DMAHDM into PMMA resin achieved protein repellent and antibacterial capabilities, without compromising the mechanical properties. PMMA resin with 3% MPC + 1.5% DMAHDM had protein adsorption that was 1/6 that of a commercial control (p < 0.05). The PMMA resin with 3% MPC + 1.5% DMAHDM had much greater reduction in biofilm growth than using MPC or DMAHDM alone (p < 0.05).

CONCLUSIONS

A bioactive PMMA resin with a combination of strong protein-repellent and antibacterial capabilities was developed for the first time. The new resin greatly reduced the biofilm growth and metabolic activity, without compromising its mechanical properties.

SIGNIFICANCE

Novel PMMA resin is promising for applications in orthodontic retainers and orthodontic appliances to reduce biofilm activity and protein adsorption around the resin.

Responsive antimicrobial dental adhesive based on drug-silica co-assembled particles

Most dental resin composite restorations are replacements for failing restorations. Degradation of the restoration-tooth margins by cariogenic bacteria results in recurrent caries, a leading cause for restoration failure. Incorporating antimicrobial agents in dental adhesives could reduce interfacial bacterial count and reduce recurrent caries rates, inhibit interfacial degradation, and prolong restoration service life, while minimizing systemic exposure. Direct addition of antimicrobial compounds into restorative materials have limited release periods and could affect the integrity of the material. Attempts to incorporate antimicrobial within mesoporous silica nanoparticles showed theoretical promise due to their physical robustness and large available internal volume, yet yielded short-term burst release and limited therapeutic payload. We have developed novel broad-spectrum antimicrobial drug-silica particles co-assembled for long-term release and high payload incorporated into dental adhesives. The release of the drug, octenidine dihydrochloride, is modulated by the oral degradative environment and mathematically modeled to predict effective service life. Steady-state release kills cariogenic bacteria, preventing biofilm formation over the adhesive surface, with no toxicity. This novel material could extend dental restoration service life and may be applied to other long-term medical device-tissue interfaces for responsive drug release upon bacterial infection.

STATEMENT OF SIGNIFICANCE

This study describes a novel dental adhesive that includes a broad-spectrum antimicrobial drug-silica co-assembled particles for long-term antimicrobial effect. The release of the drug, octenidine dihydrochloride, is modulated by the oral degradative environment and mathematically modeled to predict effective release throughout the service life of the restoration. Steady-state drug-release kills caries-forming bacteria, preventing biofilm formation over the adhesive surface, without toxicity. This novel material could extend dental restoration service life and may be applied to other long-term medical device-tissue interfaces for responsive drug release upon bacterial infection. Since recurrent cavities (caries) caused by bacteria are the major reason for dental filling failure, this development represents a significant contribution to the biomaterials field in methodology and material performance.

Incorporation of the microencapsulated antimicrobial agent phytoncide into denture base resin

BACKGROUND

This study aimed to fabricate a denture base resin (DBR) containing phytoncide microcapsules (PTMCs) and determine the mechanical properties of the resin and antifungal activity.

METHODS

Fifty-four heat-cured rectangular DBR specimens (64 × 10 × 3.3 ± 0.2 mm) containing nine concentrations of PTMC between 0 and 5% (wt/wt) were fabricated and subjected to a three-point bending test. A phytoncide release bioassay was developed using DBR containing 0% and 2.5% PTMCs (wt/wt) in a 24 well-plate assay with incubation of Porphyromonas gingivalis at 37 °C for 74 h. The antifungal activity of PTMCs against Candida albicans, in a pH 5.5 acidic environment was determined in a plate assay.

RESULTS

Flexural strength decreased with increasing PTMC concentration from 97.58 ± 4.79 MPa for the DBR alone to 53.66 ± 2.46 MPa for DBR containing 5.0% PTMC. No release of phytoncide from the PTMCs in the DBR was detected at pH 7.4. The PTMCs had a minimal inhibitory concentration of 2.6% (wt/vol) against C. albicans at pH 5.5.

CONCLUSIONS

PTMCs can be added to DBR 2.5% (wt/wt) without adversely affecting flexural strength. PTMCs released the antimicrobial agent at pH 5.5 at concentrations sufficient to inhibit the growth of the C. albicans.