Influence of a MnO2-WC interlayer on the stability and electrocatalytic activity of titanium-based PbO2 anodes

Influence of Bi3+ Doping on Electrochemical Properties of Ti/Sb-SnO2/PbO2 Electrode for Zinc Electrowinning

Bi3+ doped Ti/Sb-SnO2/PbO2 electrode materials were fabricated by electrodeposition to improve their electrochemical performance in zinc electrowinning. The surface morphology, chemical composition, and hydrophilicity of the as-prepared electrodes were characterized using scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and contact angle. An electrochemical measurement and an accelerated lifetime experiment were also conducted to investigate the electrocatalytic performance and stability of the electrodes. The results show that the Bi3+ modification electrode has an important effect on the coating morphology, the crystal structure, the surface hydrophilicity, the electrocatalytic activity, and the stability. The electrode prepared from the solution containing 2 mmol·L-1 Bi(NO3)3 (marked as the Ti/Sb-SnO2/2Bi-PbO2 electrode) exhibits the best hydrophilicity performance (θ = 21.6°) and the longest service life (1196 h). During the electrochemical characterization analysis, the Ti/Sb-SnO2/2Bi-PbO2 electrode showed the highest oxygen evolution activity, which can be attributed to it having the highest electroactive surface (qT* = 21.20 C·cm-2) and the best charge-transfer efficiency. The DFT calculation demonstrated that the doping of Bi3+ leads to a decrease in the OER reaction barrier and an increase in the DOS of the electrode, which further enhances the catalytic activity and the conductivity of the electrode. Moreover, the simulated zinc electrowinning experiment demonstrated that the Ti/Sb-SnO2/2Bi-PbO2 electrode consumes less energy than other electrodes. Therefore, it is expected that the Bi3+ modified electrode will become a very promising electrode material for zinc electrowinning in the future.

B4C/Ce co-modified Ti/PbO2 dimensionally stable anode: Facile one-step electrodeposition preparation and highly efficient electrocatalytic degradation of tetracycline

The application of PbO2 for electrochemical oxidation technology is limited by its low electrocatalytic activity and short service life. Herein, based on the facile one-step electrodeposition, we prepared a boron carbide (B4C) and cerium (Ce) co-modified Ti/PbO2 (Ti/PbO2-B4C-Ce) electrode to overcome these shortcomings. Compared with Ti/PbO2 electrode, the denser surface is displayed by Ti/PbO2-B4C-Ce electrode. Meanwhile, electrochemical characterization indicates that the introduction of B4C and Ce significantly enhance the electrochemical performance of PbO2 electrode. In degradation experiments, under optimized conditions (current density 20 mA cm-2, pH 9, 0.15 M Na2SO4 and 30 °C), the fully degradation of tetracycline (TC) can be completed within 30 min. Furthermore, the trapping experiment demonstrates that ∙OH and SO4·- radicals have a synergistic effect in the degradation process of TC. Based on results of liquid chromatography-mass spectrometer, the generated ·OH preferentially attacks amides, phenols and conjugated double bond groups in TC. Importantly, Ti/PbO2-B4C-Ce electrode maintains a constant degradation efficiency even after 10 recycling tests, and its service life is 2.4 times of traditional Ti/PbO2 electrode. Hence, Ti/PbO2-B4C-Ce electrode is a promising electrode for degradation of organic wastewater containing amides, phenols, and conjugated double bond groups.

Modification of Ti/Sb-SnO2/PbO2 Electrode by Active Granules and Its Application in Wastewater Containing Copper Ions

Active granule (WC/Co3O4) doping Ti/Sb-SnO2/PbO2 electrodes were successfully synthesized by composite electrodeposition. The as-prepared electrodes were systematically characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), electrochemical performance, zeta potential, and accelerated lifetime. It was found that the doping of active granules (WC/Co3O4) can reduce the average grain size and increase the number of active sites on the electrode surface. Moreover, it can improve the proportion of surface oxygen vacancies and non-stoichiometric PbO2, resulting in an outstanding conductivity, which can improve the electron transfer and catalytic activity of the electrode. Electrochemical measurements imply that Ti/Sb-SnO2/Co3O4-PbO2 and Ti/Sb-SnO2/WC-Co3O4-PbO2 electrodes have superior oxygen evolution reactions (OERs) relative to those of Ti/Sb-SnO2/PbO2 and Ti/Sb-SnO2/WC-PbO2 electrodes. A Ti/Sb-SnO2/Co3O4-PbO2 electrode is considered as the optimal modified electrode due to its long lifetime (684 h) and the remarkable stability of plating solutions. The treatment of copper wastewater suggests that composite electrodes exhibit low cell voltage and excellent extraction efficiency. Furthermore, pilot simulation tests verified that a composite electrode consumes less energy than other electrodes. Therefore, it is inferred that composite electrodes may be promising for the treatment of wastewater containing high concentrations of copper ions.

Energy-efficient electrochemical degradation of ciprofloxacin by a Ti-foam/PbO2-GN composite electrode: Electrode characteristics, parameter optimization, and reaction mechanism

Reducing energy comsuption is crucial to commercialize electrochemical oxidation technologies. In this study, a novel PbO₂ composite electrode (Ti-foam/PbO₂-GN) was successfully fabricated based on a porous titanium (Ti) foam substrate and a β-PbO₂ active layer embedded with multiple graphene (GN) interlayers, and applied as an anode for energy-efficient pulse electrochemical oxidation of ciprofloxacin (CIP). In contrast to PbO₂ and Ti-foam/PbO₂ electrodes, the Ti-foam/PbO₂-GN electrode surface exhibited a more compact structure, smaller crystal grain size, and greater electrochemical active surface area. CIP removal of 89.7% was obtained with a low energy consumption (EE/O) of 6.17 kWh m^-3 under pulse electrolysis conditions with a current density of 25.00 mA cm^-2, pulse frequency of 5000 Hz, and pulse duty cycle of 50.0%. Up to 70.7% of the energy was saved in the pulse current mode compared to the direct current mode. Narrowing the electrode spacing to 2 cm facilitated the mass transfer process and enhanced oxidation efficiency. According to the intermediates identified, the pulse electrolysis of CIP primarily involved hydroxylation of the quinolone ring, breaking of the piperazine ring, defluorination, and decarboxylation processes, and a possible degradation mechanism of CIP was proposed. The continuous oxidation performance of CIP and the relatively low leaching of Pb²⁺ suggested that the Ti-foam/PbO₂-GN electrode exhibited excellent stability, repeatability, and safety. The degradation results of CIP in real water also exhibits the great potential of environmental application. As a result, pulse electrochemical oxidation using a Ti-foam/PbO₂-GN electrode has proven to be an energy-efficient and promising alternative for antibiotic wastewater treatment.

Elaboration of Highly Modified Stainless Steel/Lead Dioxide Anodes for Enhanced Electrochemical Degradation of Ampicillin in Water

Lead dioxide-based electrodes have shown a great performance in the electrochemical treatment of organic wastewater. In the present study, modified PbO2 anodes supported on stainless steel (SS) with a titanium oxide interlayer such as SS/TiO2/PbO2 and SS/TiO2/PbO2-10% Boron (B) were prepared by the sol–gel spin-coating technique. The morphological and structural properties of the prepared electrodes were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and X-ray photoelectron spectroscopy (XPS). It was found that the SS/TiO2/PbO2-10% B anode led to a rougher active surface, larger specific surface area, and therefore stronger ability to generate powerful oxidizing agents. The electrochemical impedance spectroscopy (EIS) measurements showed that the modified PbO2 anodes displayed a lower charge transfer resistance Rct. The influence of the introduction of a TiO2 intermediate layer and the boron doping of a PbO2 active surface layer on the electrochemical degradation of ampicillin (AMP) antibiotic have been investigated by chemical oxygen demand measurements and HPLC analysis. Although HPLC analysis showed that the degradation process of AMP with SS/PbO2 was slightly faster than the modified PbO2 anodes, the results revealed that SS/TiO2/PbO2-10%B was the most efficient and economical anode toward the pollutant degradation due to its physico-chemical properties. At the end of the electrolysis, the chemical oxygen demand (COD), the average current efficiency (ACE) and the energy consumption (EC) reached, respectively, 69.23%, 60.30% and 0.056 kWh (g COD)−1, making SS/TiO2/PbO2-10%B a promising anode for the degradation of ampicillin antibiotic in aqueous solutions.

When MXene (Ti3C2Tx) meet Ti/PbO2: An improved electrocatalytic activity and stability

Stable electrode materials with high catalytic activity are urgently required for electrochemical degradation of refractory organic pollutants in wastewater treatment. Herein, high conductive MXene (Ti₃C₂T_x) was firstly fabricated by electrophoretic deposition (EPD) as an interlayer for preparing a novel PbO₂ electrode. The well-conducted Ti₃C₂T_x interlayer significantly improved the electrochemical performance of the EPD-2.0/PbO₂ (EPD time was 2.0 min) electrode with the charge transfer resistance decreased by 9.51 times, the inner active sites increased by 5.21 times and the ∙OH radicals generation ability enhanced by 4.07 times than the control EPD-0/PbO₂ anode. Consequently, the EPD-2.0/PbO₂ electrode achieved nearly 100% basic fuchsin (BF) and 86.78% COD removal efficiency after 3.0 h electrolysis. Therefore, this new PbO₂ electrode presented a promising potential for electrochemical degradation of BF and the new Ti₃C₂T_x middle layer could also be used to fabricate other efficient and stable anodes, such as SnO₂, MnO₂, TiO₂, etc.

Two-step facile synthesis of Co3O4@C reinforced PbO2 coated electrode to promote efficient oxygen evolution reaction for zinc electrowinning

The conventional Pb-Ag alloy possesses a high oxygen evolution reaction overpotential, poor stability, and short service life in acidic solutions, making it an unsuitable sort of anode material for the zinc electrowinning process. Therefore, a layered carbon-covered cobalt tetroxide (Co3O4@C)-reinforced PbO2-coated electrode is fabricated via a facile two-step pyrolysis-oxidation and subsequent electrodeposition process. As a result, the reinforced PbO2-coated electrode exhibits a low OER overpotential of 517 mV at 500 A m-2 and a Tafel slope of 0.152 V per decade in a zinc electrowinning simulation solution (0.3 M ZnSO4 and 1.53 M H2SO4). The reduced overpotential of 431 mV at 500 A m-2 compared to traditional Pb-0.76%Ag alloy leads to improved energy savings, which is attributable to the presence of Co3O4@C to refine the grain size and thus increase the effective contact area. Moreover, the reinforced PbO2-coated electrode has a prolonged service life of 93 h at 20 000 A m-2 in 1.53 M H2SO4. Therefore, an accessible and efficient strategy for preparing a coated electrode to improve OER performance for zinc electrowinning is presented in this research.

Research trends in the development of anodes for electrochemical oxidation of wastewater

The review focuses on the recent development in anode materials and their synthesis approach, focusing on their compatibility for treating actual industrial wastewater, improving selectivity, electrocatalytic activity, stability at higher concentration, and thereby reducing the mineralization cost for organic pollutant degradation. The advancement in sol–gel technique, including the Pechini method, is discussed in the first section. A separate discussion related to the selection of the electrodeposition method and its deciding parameters is also included. Furthermore, the effect of using advanced heating approaches, including microwave and laser deposition synthesis, is also discussed. Next, a separate discussion is provided on using different types of anode materials and their effect on active •OH radical generation, activity, and electrode stability in direct and indirect oxidation and future aspects. The effect of using different synthesis approaches, additives, and doping is discussed separately for each anode. Graphene, carbon nanotubes (CNTs), and metal doping enhance the number of active sites, electrochemical activity, and mineralization current efficiency (MCE) of the anode. While, microwave or laser heating approaches were proved to be an effective, cheaper, and fast alternative to conventional heating. The electrodeposition and nonaqueous solvent synthesis were convenient and environment-friendly techniques for conductive metallic and polymeric film deposition.

Application of lead oxide electrodes in wastewater treatment: A review

Electrochemical oxidation (EO) based on hydroxyl radicals (·OH) generated on lead dioxide has become a typical advanced oxidation process (AOP). Titanium-based lead dioxide electrodes (PbO₂/Ti) play an increasingly important role in EO. To further improve the efficiency, the structure and properties of the lead dioxide active surface layer can be modified by doping transition metals, rare earth metals, nonmetals, etc. Here, we compare the common preparation methods of lead dioxide. The EO performance of lead dioxide in wastewater containing dyes, pesticides, drugs, landfill leachate, coal, petrochemicals, etc., is discussed along with their suitable operating conditions. Finally, the factors influencing the contaminant removal kinetics on lead dioxide are systematically analysed.

Influence of Cu–Zn co-doping on the degradation performance of a Ti/SnO2–Sb anode

A Ti/SnO2–Sb–Cu–Zn electrode was prepared for the electrocatalytic oxidation of Acid Red 18 (AR18).

Fabrication and characterization of porous titanium-based PbO2 electrode through the pulse electrodeposition method: Deposition condition optimization by orthogonal experiment

Porous titanium-based PbO₂ electrodes were successfully fabricated by pulse electrodeposition method. The primary pulse electrodeposition parameters, including pulse frequency (f), duty ratio (γ), average current density (J_a) and electrodeposition time (t) were considered in this study. An orthogonal experiment was designed based on those four factors and in three levels. SEM images and XRD results suggest that the surface morphology and structure of PbO₂ electrodes could be easily changed by varying pulse electrodeposition parameters. Orthogonal analysis reveals that the increase of f and J_a could decrease the average grain size of PbO₂ electrodes, which is conducive to create more active sites and promote the generation of hydroxide radicals. The electrochemical degradation of Azophloxine was carried out to evaluate the electrochemical oxidation performance of pulse electrodeposited electrodes. The results indicate that the influences of four factors can be ranked as follow: J_a >γ≈ t > f. The higher f, larger J_a and longer t could facilitate the optimization of the integrated electrochemical degradation performance of prepared PbO₂ electrode. The accelerated life time is dominated by J_a and t, coincident with the average weight increase of β-PbO₂ layer. The optimal parameters of pulse electrodeposition turn out to be: f = 50 Hz, γ = 30%, J_a = 25 mA cm^-2, t = 60 min. Together, the consequences of the experiments give assistance to uncover and roughly conclude the mechanism of pulse electrodeposition.