Dense Dithiolene Units on Metal-Organic Frameworks for Mercury Removal and Superprotonic Conduction

Harnessing Coordination Microenvironment of Metal-bis(dithiolene) Sites for Modulating Electrocatalytic CO2 Reduction by Metal-Organic Framework

Nature's metalloenzymes inspire biomimetic catalysts for the CO2 reduction reaction (CO2RR), particularly using metal-bis(dithiolene) ([MS4]) cores in frameworks. While prior research focused on tuning the chelating atoms of Ni-centered sites or [NiS4] in metal-organic frameworks (MOFs), how different metal centers affect the electronic structure and catalytic activity is often overlooked. Notably, reported [NiS4] molecular analogues exhibits a Faradaic efficiency (FE) of less than 70% for the major carbon product and shows operational stability for only about 4 hours (say falling FE and current density beyond). In this study, MOFs are used to host [MS4] units with varying central metals (M = Ni, Cu, Co, Fe) to assess how the metal center affects electrocatalytic CO2RR. Among the studied MS4-In MOFs, NiS4-In demonstrates the best performance, achieving a FECO of 88.54% and operational stability greater than 6 hours-significantly outlasting the ≈200 seconds of the [NiS4] molecule. This work underscores the importance of frameworks in stabilizing [MS4] units and highlights [MS4] as essential for CO2 binding and reduction, with [NiS4] exhibiting optimal catalytic performance due to its favorable electronic properties. This findings clarify how substituting the metal center within the framework enhances electronic structure and coordination, leading to improved electrocatalytic performance.

Nonmetal Organic Frameworks Exhibit High Proton Conductivity

Porous materials, such as metal-organic frameworks (MOFs) and porous organic salts, are promising materials for proton conduction. Recently, we developed a new subclass of porous materials, isoreticular nonmetal organic frameworks (N-MOFs), which can be designed using crystal structure prediction (CSP). Here, two porous, isostructural, and water-stable halide N-MOFs were prepared and found to show good proton conductivity of up to 1.1 × 10-1 S cm-1 at 70 °C and 90% relative humidity. Changing the halides in these N-MOF materials affects the resulting proton conductivity, as observed in previous studies involving MOFs and lead halides. Although this is the first study of proton conductivity in N-MOFs, the bromide salt, TTBT.Br, shows a higher conductivity than most polycrystalline MOFs and porous organic salts, approaching that of Nafion.

Thiolated non-conjugated nano polymer network for advanced mercury removal from water

Developing advanced adsorbents for selectively deducing mercury (Hg) in water to one billionth level is of great significance for public health and ecological security, but achieving the balance among efficiency, cost and environmental friendliness of adsorbents still faces enormous challenges. Herein, we present a high thiol content non-conjugated nano polymer network (PVB-SH) through simple microemulsion polymerization for efficient Hg ion (Hg(II)) removal. The PVB-SH is prepared by conventional commercial reagents and does not consume toxic organic solutions. This nano network reveals uniformly distributed nano sizes, leading to good accessibility of adsorption sites. The long and flexible polymer chains in the network allow two thiol sites to coordinate with one Hg(II), displaying significantly stronger binding than 1:1 coordination. Therefore, PVB-SH shows high affinity toward Hg(II) (Kd = 3.04 × 107 mL/g) and can selectively reduce Hg(II) in water to extremely low level of 0.14 μg/L, well below the safe limit of 2 μg/L. PVB-SH possesses excellent renewability (removal efficiency = 99.58 % after 10 regenerations), good resistance to various environmental factors (pH, ions and organic matter) and long-term stability in acid, alkali, and salt solutions. Impressively, PVB-SH is further made into a membrane by simple phase-inversion and can effectively purify 1592.4 L/m2 Hg(II) polluted drinking water before the breakthrough point of 2 μg/L. These results demonstrate the good practical potential of PVB-SH for decontamination of Hg from aqueous media.

A single-crystal 3D Zn-tetrathiolate connected metal-organic framework

Due to thiolate's fast and robust coordination, crystallographically resolved thiolate-ligated metal-organic frameworks (MOFs) are hard to obtain. Following the previous success of the masked synthetic strategy to achieve single-crystal Pb-thiolate connected MOFs, thioester-protected hexathiotriphenylene (HVaTT) was employed in this work to assemble with a Zn(II) centre to yield the first example of a first-row transition-metal based crystallographically resolved metal-tetrathiolate connected MOF, HTT-Zn. HTT-Zn features a 3D anionic framework connected by tetrahedral [ZnS4] nodes with 3-fold interpenetration and windmill-like topology. Thanks to the anionic nature, HTT-Zn demonstrates a fast colorimetric response (from yellow to black) to the positively charged toxic pollutant, paraquat, and potentially serves as a naked-eye sensor for paraquat. Isolation of HTT-Zn proves masked synthesis as a general approach and adds a new dimension to explore metal-thiolate-based MOFs.

Synthesis of Thiol Functionalized MOF-808 and its Efficiency for Mercury Removal

A thiol-functionalized MOF-808 was produced and used to remove mercury by post-synthetic modification using 6-mercaponicotinic acid (6mna). Parent MOF-808 was impregnated for varied periods in the 6mna solution to create modified MOF-808 materials, known as MOF-808-6mna-x, where x refers to the impregnation time. Diffraction and several spectroscopic techniques were employed to quantify and confirm the coordination of 6mna into MOF-808 framework. The amount of grafted 6man and the ability for adsorption of mercury (Hg) was shown to be linearly associated; the functionalized MOF-808-6mna-36 demonstrated improved Hg(II) removal, with an adsorption capacity of 250 mg/g.

Cysteamine-Anchored MOF through Post-Synthetic Modification Strategy for the Effective Removal of Mercury from Water

The introduction of cysteamine functionality, referred to as Q-ZIF-67-SH, was successfully achieved through postsynthetic modification while maintaining the structural and thermal stability of the quasi metal-organic framework Q-ZIF-67. By subjecting ZIF-67 to controlled partial deligandation at 310 °C under an air atmosphere, a substantial number of unsaturated cobalt sites were generated within the quasi ZIF-67 (Q-ZIF-67) structure. These unsaturated cobalt sites facilitated effective coordination with cysteamine, resulting in the development of the thiol-functionalized framework Q-ZIF-67-SH. The potential of these metal-organic frameworks (MOFs) for the adsorptive removal of hazardous Hg(II) was investigated. Various factors, such as the type of sorbent, pH, adsorbent dosage, initial concentration of Hg(II), and presence of coexisting ions, were thoroughly examined and comprehensively explained. Thiol-anchored MOF significantly enhanced the efficiency of Hg(II) removal, achieving an impressive removal rate of up to 99.2%. Furthermore, it demonstrated a maximum adsorption capacity of 994 mg g-1 and a distribution coefficient of 2.5 × 106 mL g-1. A good correspondence with pseudo-second-order kinetics and the Langmuir model was observed through the fitting of adsorption kinetics and the isotherm model. The thermodynamic data strongly indicate that the adsorptive removal of Hg(II) is characterized by endothermicity and spontaneity. This signifies that the process is energetically favorable and has potential for efficient Hg(II) removal. Therefore, the Q-ZIF-67-SH sorbent emerges as a promising and advantageous option for the removal of Hg(II) from water.

Thiol and thioether-based metal-organic frameworks: synthesis, structure, and multifaceted applications

Metal-organic frameworks (MOFs) are unique hybrid porous materials formed by combining metal ions or clusters with organic ligands. Thiol and thioether-based MOFs belong to a specific category of MOFs where one or many thiols or thioether groups are present in organic linkers. Depending on the linkers, thiol-thioether MOFs can be divided into three categories: (i) MOFs where both thiol or thioether groups are part of the carboxylic acid ligands, (ii) MOFs where only thiol or thioether groups are present in the organic linker, and (iii) MOFs where both thiol or thioether groups are part of azolate-containing linkers. MOFs containing thiol-thioether-based acid ligands are synthesized through two primary approaches; one is by utilizing thiol and thioether-based carboxylic acid ligands where the bonding pattern of ligands with metal ions plays a vital role in MOF formation (HSAB principle). MOFs synthesized by this approach can be structurally differentiated into two categories: structures without common structural motifs and structures with common structural motifs (related to UiO-66, UiO-67, UiO-68, MIL-53, NU-1100, etc.). The second approach to synthesize thiol and thioether-based MOFs is indirect methods, where thiol or thioether functionality is introduced in MOFs by techniques like post-synthetic modifications (PSM), post-synthetic exchange (PSE) and by forming composite materials. Generally, MOFs containing only thiol-thioether-based ligands are synthesized by interfacial assisted synthesis, forming two-dimensional sheet frameworks, and show significantly high conductivity. A limited study has been done on MOFs containing thiol-thioether-based azolate ligands where both nitrogen- and sulfur-containing functionality are present in the MOF frameworks. These materials exhibit intriguing properties stemming from the interplay between metal centres, organic ligands, and sulfur functionality. As a result, they offer great potential for multifaceted applications, ranging from catalysis, sensing, and conductivity, to adsorption. This perspective is organised through an introduction, schematic representations, and tabular data of the reported thiol and thioether MOFs and concluded with future directions.

A Multifunctional Co-Based Metal-Organic Framework as a Platform for Proton Conduction and Ni trophenols Reduction

The design and development of proton conduction materials for clean energy-related applications is obviously important and highly desired but challenging. An ultrastable cobalt-based metal-organic framework Co-MOF, formulated as [Co2(btzip)2(μ2-OH2)] (namely, LCUH-103, H2btzip = 4, 6-bis(triazol-1-yl)-isophthalic acid) had been successfully synthesized via the hydrothermal method. LCUH-103 exhibits a three-dimensional framework and a one-dimensional microporous channel structure with scu topology based on the binuclear metallic cluster {Co2}. LCUH-103 indicated excellent chemical and thermal stability; peculiarly, it can retain its entire framework in acid and alkali solutions with different pH values for 24 h. The excellent stability is a prerequisite for studying its proton conductivity, and its proton conductivity σ can reach up to 1.25 × 10-3 S·cm-1 at 80 °C and 100% relative humidity (RH). In order to enhance its proton conductivity, the proton-conducting material Im@LCUH-103 had been prepared by encapsulating imidazole molecules into the channels of LCUH-103. Im@LCUH-103 indicated an excellent proton conductivity of 3.18 × 10-2 S·cm-1 at 80 °C and 100% RH, which is 1 order of magnitude higher than that of original LCUH-103. The proton conduction mechanism was systematically studied by various detection means and theoretical calculations. Meanwhile, LCUH-103 is also an excellent carrier for palladium nanoparticles (Pd NPs) via a wetness impregnation strategy, and the nitrophenols (4/3/2-NP) reduction in aqueous solution by Pd@LCUH-103 indicated an outstanding conversion efficiency, high rate constant (k), and exceptional cycling stability. Specifically, the k value of 4-NP reduction by Pd@LCUH-103 is superior to many other reported catalysts, and its k value is as high as 1.34 min-1 and the cycling stability can reach up to 6 cycles. Notably, its turnover frequency (TOF) value is nearly 196.88 times more than that of Pd/C (wt 5%) in the reaction, indicating its excellent stability and catalytic activity.

Minimalist Design for Solar Energy Conversion: Revamping the π-Grid of an Organic Framework into Open-Shell Superabsorbers

We apply a versatile reaction to a versatile solid: the former involves the electron-deficient alkene tetracyanoethylene (TCNE) as the guest reactant; the latter consists of stacked 2D honeycomb covalent networks based on the electron-rich β-ketoenamine hinges that also activate the conjugated, connecting alkyne units. The TCNE/alkyne reaction is a [2 + 2] cycloaddition-retroelectrocyclization (CA-RE) that forms strong push-pull units directly into the backbone of the framework-i.e., using only the minimalist "bare-bones" scaffold, without the need for additional side groups of alkynes or other functions. The ability of the stacked alkyne units (i.e., as part of the honeycomb mass) to undergo such extensive rearrangement highlights the structural flexibility of these covalent organic framework (COF) hosts. The COF solids remain porous, crystalline, and air-/water-stable after the CA-RE modification, while the resulting push-pull units feature distinct open-shell/free-radical character, are strongly light-absorbing, and shift the absorption ends from 590 nm to around 1900 nm (band gaps from 2.17-2.23 to 0.87-0.95 eV), so as to better capture sunlight (especially the infrared region which takes up 52% of the solar energy). As a result, the modified COF materials achieve the highest photothermal conversion performances, holding promise in thermoelectric power generation and solar steam generation (e.g., with solar-vapor conversion efficiencies >96%).

Utilizing Metal-Thiocatecholate Functionalized UiO-66 Framework for Photocatalytic Hydrogen Evolution Reaction

Exploiting clean energy is essential for sustainable development and sunlight-driven photocatalytic water splitting represents one of the most promising approaches toward this goal. Metal-organic frameworks (MOFs) are competent photocatalysts owing to their tailorable functionality, well-defined structure, and high porosity. Yet, the introduction of the unambiguous metal-centered active site into MOFs is still challenging since framework motifs capable of anchoring metal ions firmly are lacking. Herein, the assembly using 1,4-dicarboxylbenzene-2,3-dithiol (H₂ dcbdt) and Zr-Oxo clusters to give a thiol-functionalized UiO-66 type framework, UiO-66-dcbdt, is reported. The thiocatechols on the struts are allowed to capture transition metal (TM) ions to generate UiO-66-dcbdt-M (M  = Fe, Ni, Cu) with unambiguous metal-thiocatecholate moieties for photocatalytic hydrogen evolution reaction (HER). UiO-66-dcbdt-Cu is found the best catalyst exhibiting an HER rate of 4.18 mmol g^-1  h^-1  upon irradiation with photosensitizing Ru-polypyridyl complex. To skip the use of the external sensitizer, UiO-66-dcbdt-Cu is heterojunctioned with titanium dioxide (TiO₂ ) and achieves an HER rate of 12.63 mmol g^-1  h^-1  (32.3 times that of primitive TiO₂ ). This work represents the first example of MOF assembly employing H₂ dcbdt as the mere linker followed by chelation with TM ions and undoubtedly fuels the rational design of MOF photocatalysts bearing well-defined active sites.

Systematic Thiol Decoration in a Redox-Active UiO-66-(SH)2 Metal-Organic Framework: A Case Study under Oxidative and Reductive Conditions

The practical applicability of thiolated metal-organic frameworks (MOFs) remains challenging due to their low crystallinity and transient stability. Herein, we present a one-pot solvothermal synthesis process using varying ratios of 2,5-dimercaptoterephthalic acid (DMBD) and 1,4-benzene dicarboxylic acid (100/0, 75/25, 50/50, 25/75, and 0/100) to prepare stable mixed-linker UiO-66-(SH)₂ MOFs (ML-U66SX). For each variant, the effects of different linker ratios on the crystallinity, defectiveness, porosity, and particle size have been discussed in detail. In addition, the impact of modulator concentration on these features has also been described. The stability of ML-U66SX MOFs was investigated under reductive and oxidative chemical conditions. The mixed-linker MOFs were used as sacrificial catalyst supports to highlight the interplay of template stability on the rate of the gold-catalyzed 4-nitrophenol hydrogenation reaction. The release of catalytically active gold nanoclusters originating from the framework collapse decreased with the controlled DMBD proportion, resulting in a 59% drop in the normalized rate constants (9.11-3.73 s^-1 mg^-1). In addition, post-synthetic oxidation (PSO) was used to further probe the stability of the mixed-linker thiol MOFs under harsh oxidative conditions. Following oxidation, the UiO-66-(SH)₂ MOF underwent immediate structural breakdown, unlike other mixed-linker variants. Along with crystallinity, the microporous surface area of the post-synthetically oxidized UiO-66-(SH)₂ MOF could be increased from 0 to 739 m² g^-1. Thus, the present study delineates a mixed-linker strategy to stabilize the UiO-66-(SH)₂ MOF under harsh chemical conditions through meticulous thiol decoration.

Organic radicals stabilization above 300 °C in Eu-based coordination polymers for solar steam generation

Organic radicals feature unpaired electrons, and these compounds may have applications in biomedical technology and as materials for solar energy conversion. However, unpaired electrons tend to pair up (to form chemical bonds), making radicals unstable and hampering their applications. Here we report an organic radical system that is stable even at 350 °C, surpassing the upper temperature limit (200 °C) observed for other organic radicals. The system reported herein features a sulfur-rich organic linker that facilitates the formation of the radical centers; on the solid-state level, the molecules are crystallized with Eu(III) ions to form a 3D framework featuring stacks of linker molecules. The stacking is, however, somewhat loose and allows the molecules to wiggle and transform into sulfur-stabilized radicals at higher temperatures. In addition, the resulting solid framework remains crystalline, and it is stable to water and air. Moreover, it is black and features strong broad absorption in the visible and near IR region, thereby enhancing both photothermal conversion and solar-driven water evaporation.

Organic radicals have potential applications in a variety of fields, including energy conversion. Here, the authors report Eu-based coordination polymers that enable the stabilization of organic radicals up to 350 °C; these systems can be used to enhance solar steam generation.

Post-synthesis functionalization of ZIF-90 with sulfonate groups for high proton conduction

Introducing sulfonic acid groups into MOF materials is one of the effective approaches to enhance proton conduction. Here, we attempted to prepare a new post-modified ZIF-90-based material by addition reaction of the aldehyde group with bisulfite to obtain partially functionalized ZIF-90-SO₃Na_(2.3). ZIF-90-SO₃Na_(2.3) exhibits a high proton conductivity of 2.26 × 10^-2 S cm^-1 at 98% RH and 100 °C.

Remarkable proton conducting behavior driven by synergistic effects in acid-base conjugated MOFs impregnated with sulphuric acid molecules

The Coulomb force between protons and negative charges usually leads to low proton diffusion and poor proton conductivity. Herein, acid-base conjugated MOFs of UiO-66-SO₃^--NH₃⁺ were constructed by linking sulfonic acid and amine groups to an organic skeleton. According to the XPS and elemental analysis, the ratio of 2-aminoterephthalic acid/2-sulfoterephthalic acid was ∼1.9 in UiO-66-SO₃^--NH₃⁺. After introducing sulphuric acid molecules, the MOF-based electrolyte exhibited a remarkable proton conductivity of 5.40 × 10^-1 S cm^-1 and low activation energy of 0.15 eV at 100% RH and 90 °C. This remarkable proton conducting behavior was generated by the synergistic system in the MOF, which contained certain synergistic effects such as between -SO₃^-⋯H⁺⋯SO₄^2- and NH₃⁺⋯SO₄^2-, therefore possessing a Grotthuss mechanism, which facilitates facile proton transport.

A Porous Sulfonated 2D Zirconium Metal-Organic Framework as a Robust Platform for Proton Conduction

By using the strategy of pre-assembly chlorosulfonation applied to a linker precursor, the first sulfonated zirconium metal-organic framework (JUK-14) with two-dimensional (2D) structure, was synthesized. Single-crystal X-ray diffraction reveals that the material is built of Zr₆ O₄ (OH)₄ (COO)₈ oxoclusters, doubly 4-connected by angular dicarboxylates, and stacked in layers spaced 1.5 nm apart by the presence of sulfonic groups. JUK-14 exhibits excellent hydrothermal stability, permanent porosity confirmed by gas adsorption studies, and shows high (>10^-4  S/cm) and low (<10^-8  S/cm) proton conductivity under humidified and anhydrous conditions, respectively. Post-synthesis inclusion of imidazole improves the overall conductivity increasing it to 1.7×10^-3  S/cm at 60 °C and 90 % relative humidity, and by 3 orders of magnitude at 160 °C. The combination of 2D porous nature with robustness of zirconium MOFs offers new opportunities for exploration of the material towards energy and environmental applications.

Superprotonic conduction of intrinsically zwitterionic microporous polymers based on easy-to-make squaraine, croconaine and rhodizaine dyes

Porous organic polymers (POPs) have been prepared via a novel metal free polycondensation between a tritopic indole-based monomer and squaric, croconic and rhodizonic acids. Each of the three POPs exhibited high BET surface areas (331-667 m² g^-1) and zwitterionic structures. Impedance measurements revealed that the intrinsic POPs were relatively weak proton conductors, with a positive correlation between the density of oxo-groups and the proton conduction. Doping the materials with LiCl vastly improved the proton conductivity up to a value of 0.54 S cm^-1 at 90 °C and 90% relative humidity.