Understanding the Surface Regeneration and Reactivity of Garnet Solid-State Electrolytes

Accelerating the Development of LLZO in Solid-State Batteries Toward Commercialization: A Comprehensive Review

Solid-state batteries (SSBs) are under development as high-priority technologies for safe and energy-dense next-generation electrochemical energy storage systems operating over a wide temperature range. Solid-state electrolytes (SSEs) exhibit high thermal stability and, in some cases, the ability to prevent dendrite growth through a physical barrier, and compatibility with the "holy grail" metallic lithium. These unique advantages of SSEs have spurred significant research interests during the last decade. Garnet-type SSEs, that is, Li7La3Zr2O12 (LLZO), are intensively investigated due to their high Li-ion conductivity and exceptional chemical and electrochemical stability against lithium metal anodes. However, poor interfacial contact with cathode materials, undesirable lithium plating along grain boundaries, and moisture-induced chemical degradation greatly hinder the practical implementation of LLZO-based SSEs for SSBs. In this review, the recent advances in synthesis methods, modification strategies, corresponding mechanisms, and applications of garnet-based SSEs in SSBs are critically summarized. Furthermore, a comprehensive evaluation of the challenges and development trends of LLZO-based electrolytes in practical applications is presented to accelerate their development for high-performance SSBs.

Dynamical evolution of CO2 and H2O on garnet electrolyte elucidated by ambient pressure X-ray spectroscopies

Garnet-type Li6.5La3Zr1.5Ta0.5O12 (LLZO) is considered a promising solid electrolyte, but the surface degradation in air hinders its application for all-solid-state battery. Recent studies have mainly focused on the final products of the LLZO surface reactions due to lacking of powerful in situ characterization methods. Here, we use ambient pressure X-ray spectroscopies to in situ investigate the dynamical evolution of LLZO surface in different gas environments. The newly developed ambient pressure mapping of resonant Auger spectroscopy clearly distinguishes the lithium containing species, including LiOH, Li2O, Li2CO3 and lattice oxygen. The reaction of CO2 with LLZO to form Li2CO3 is found to be a thermodynamically favored self-limiting reaction. On the contrary, the reaction of H2O with LLZO lags behind that of CO2, but intensifies at high pressure. More interestingly, the results provide direct spectroscopic evidence for the existence of Li+/H+ exchange and reveal the importance of the initial layer formed on clean electrolyte surface in determining their air stability. This work demonstrates that the newly developed in situ technologies pave a new way to investigate the oxygen evolution and surface degradation mechanism in energy materials.

Regulating Grind-Induced Lattice Distortion for Nickel-Rich Cathodes by Annealing

The commercialization of high-performance nickel-rich cathodes always awaits a cost-effective, environmentally friendly, and large-scale preparation method. Despite a grinding process normally adopted in the synthesis of the nickel-rich cathodes, lattice distortion, rough surface, and sharp edge transformation inevitably occurr in the resultant samples. In this work, an additional annealing process is proposed that aims at regulating lattice distortion as well as achieving round and smoother morphologies without any structural or elemental modifications. Such a structural enhancement is favored for improved lithium diffusion and electrochemical stability during cycling. Consequently, the annealed cathodes demonstrate a considerable enhancement in capacity retention, escalating from 68.7% to 91.9% after 100 cycles at 1 C. Additionally, the specific capacity is significantly increased from 64 to 142 mAh g-1 at 5 C when compared to the unannealed cathodes. This work offers a straightforward and effective approach for reinforcing the electrochemical properties of nickel-rich cathodes.

Clarifying the Dopant Local Structure and Effect on Ionic Conductivity in Garnet Solid-State Electrolytes for Lithium-Ion Batteries

The high Li-ion conductivity and wide electrochemical stability of Li-rich garnets (Li7La3Zr2O12) make them one of the leading solid electrolyte candidates for solid-state batteries. Dopants such as Al and Ga are typically used to enable stabilization of the high Li+ ion-conductive cubic phase at room temperature. Although numerous studies exist that have characterized the electrochemical properties, structure, and lithium diffusion in Al- and Ga-LLZO, the local structure and site occupancy of dopants in these compounds are not well understood. Two broad 27Al or 69,71Ga resonances are often observed with chemical shifts consistent with tetrahedrally coordinated Al/Ga in the magic angle spinning nuclear magnetic resonance (MAS NMR) spectra of both Al- and Ga-LLZO, which have been assigned to either Al and/or Ga occupying 24d and 96h/48g sites in the LLZO lattice or the different Al/Ga configurations that arise from different arrangements of Li around these dopants. In this work, we unambiguously show that the side products γ-LiAlO2 and LiGaO2 lead to the high frequency resonances observed by NMR spectroscopy and that both Al and Ga only occupy the 24d site in the LLZO lattice. Furthermore, it was observed that the excess Li often used during synthesis leads to the formation of these side products by consuming the Al/Ga dopants. In addition, the consumption of Al/Ga dopants leads to the tetragonal phase formation commonly observed in the literature, even after careful mixing of precursors. The side-products can exist even after sintering, thereby controlling the Al/Ga content in the LLZO lattice and substantially influencing the lithium-ion conductivity in LLZO, as measured here by electrochemical impedance spectroscopy.