El-Sayed AF, Aboulthana WM, Sherief MA, El-Bassyouni GT, Mousa SM. Synthesis, structural, molecular docking, and in vitro biological activities of Cu-doped ZnO nanomaterials. Sci Rep 2024; 14:9027. [PMID: 38641640 PMCID: PMC11031592 DOI: 10.1038/s41598-024-59088-2] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/23/2024] [Accepted: 04/08/2024] [Indexed: 04/21/2024] Open
Abstract
Copper-doped ZnO nanoparticles with the formula Zn1-x(Cu)O, where x = 0.0, 0.03, 0.05, and 0.07 were produced using the co-precipitation process. Physical, chemical, and structural properties were properly examined. Powdered X-ray diffraction (P-XRD) patterns revealed the formation of hexagonal wurtzite crystal structure in all samples, through atomic substitutional incorporation in the Cu-doped ZnO lattice. The presence of Cu ions and their dissolution in the host ZnO crystal structure was supported by FT-IR spectra. HR-TEM images were used to assess the average size, morphology, and shape regularity of the synthesized samples. The form and homogeneity of the ZnO changed when Cu ions were substituted, as evidenced by FE-SEM/EDX analysis. The presence of copper signals in the Cu-doped samples indicates that the doping was successful. The decrease in zeta potential with an increased copper doping percentage designates that the nanoparticles (NPs) are more stable, which could be attributed to an increase in the ionic strength of the aqueous solution. The synthesized NPs were evaluated for their substantial in vitro antioxidant properties. In addition, the antimicrobial efficacy of the materials was tested against pathogenic microorganisms. Regarding the anti-diabetic activity, the 7Cu ZnO sample showed the highest inhibitory effect on the α-amylase enzyme. No variations were observed in the activities of the acetylcholinesterase enzyme (AChE) and proteinase enzymes with ZnO and samples doped with different concentrations of Cu. Therefore, further studies are recommended to reveal the in-vitro anti-diabetic activity of the studied doped samples. Finally, molecular docking provided valuable insights into the potential binding interactions of Cu-doped ZnO with α-amylase, FabH of E. coli, and Penicillin-binding proteins of S. aureus. These outcomes suggest that the prepared materials may have an inhibitory effect on enzymes and hold promise in the battle against microbial infections and diabetes.
Collapse
Affiliation(s)
- Ahmed F El-Sayed
- Microbial Genetics Department, Biotechnology Research Institute, National Research Centre, 33 El Bohouth St. (Former El Tahrir St.), P.O. 12622, Dokki, Cairo, Egypt
- Egypt Center for Research and Regenerative Medicine (ECRRM), Cairo, Egypt
| | - Wael M Aboulthana
- Biochemistry Department, Biotechnology Research Institute, National Research Centre, 33 El Bohouth St. (Former El Tahrir St.), P.O. 12622, Dokki, Cairo, Egypt.
| | - Marwa A Sherief
- Inorganic Chemistry Department, Advanced Materials Technology and Mineral Resources Research Institute, National Research Centre, 33 El Bohouth St. (Former El Tahrir St.), P.O. 12622, Dokki, Cairo, Egypt
| | - Gehan T El-Bassyouni
- Refractories, Ceramics and Building Materials Department, Advanced Materials Technology and Mineral Resources Research Institute, National Research Centre, 33 El Bohouth St. (Former El Tahrir St.), P.O. 12622, Dokki, Cairo, Egypt
| | - Sahar M Mousa
- Inorganic Chemistry Department, Advanced Materials Technology and Mineral Resources Research Institute, National Research Centre, 33 El Bohouth St. (Former El Tahrir St.), P.O. 12622, Dokki, Cairo, Egypt
| |
Collapse
|
2
|
Jose M, Bezerra Alexandre E, Neumaier L, Rauter L, Vijjapu MT, Muehleisen W, Malik MH, Zikulnig J, Kosel J. Future Thread: Printing Electronics on Fibers. ACS APPLIED MATERIALS & INTERFACES 2024; 16:7996-8005. [PMID: 38310570 DOI: 10.1021/acsami.3c15422] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 02/06/2024]
Abstract
This article introduces a methodology to increase the integration density of functional electronic features on fibers/threads/wires through additive deposition of functional materials via printed electronics. It opens the possibility to create a multifunctional intelligent system on a single fiber/thread/wire while combining the advantages of existing approaches, i.e., the scalability of coating techniques and the microfeatures of semiconductor-based fabrication. By directly printing on threads (of diameters ranging from 90 to 1000 μm), micropatterned electronic devices and multifunctional electronic systems could be formed. Contact and noncontact printing methods were utilized to create various shapes from serpentines and meanders to planar coils and interdigitated electrodes, as well as complex multilayer structures for thermal and light actuators, humidity, and temperature sensors. We demonstrate the practicality of the method by integrating a multifunctional thread into a FFP mask for breath monitoring. Printing technologies provide virtually unrestricted choices for the types of threads, materials, and devices used. They are scalable via roll-to-roll processes and offer a resource-efficient way to democratize electronics across textile products.
Collapse
Affiliation(s)
- Manoj Jose
- Silicon Austria Labs GmbH, Europastraße 12, Villach 9524, Austria
| | - Emily Bezerra Alexandre
- Silicon Austria Labs GmbH, Europastraße 12, Villach 9524, Austria
- Bio/CMOS Interfaces Lab, École Polytechnique Fédérale de Lausanne, EPFL, Neuchâtel CH-2000, Switzerland
| | - Lukas Neumaier
- Silicon Austria Labs GmbH, Europastraße 12, Villach 9524, Austria
| | - Lukas Rauter
- Silicon Austria Labs GmbH, Europastraße 12, Villach 9524, Austria
| | | | | | | | - Johanna Zikulnig
- Silicon Austria Labs GmbH, Europastraße 12, Villach 9524, Austria
- Bio/CMOS Interfaces Lab, École Polytechnique Fédérale de Lausanne, EPFL, Neuchâtel CH-2000, Switzerland
| | - Jürgen Kosel
- Silicon Austria Labs GmbH, Europastraße 12, Villach 9524, Austria
| |
Collapse
|
3
|
Kim J, Lee J, Lee JM, Facchetti A, Marks TJ, Park SK. Recent Advances in Low-Dimensional Nanomaterials for Photodetectors. SMALL METHODS 2024; 8:e2300246. [PMID: 37203281 DOI: 10.1002/smtd.202300246] [Citation(s) in RCA: 5] [Impact Index Per Article: 5.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 02/25/2023] [Revised: 04/21/2023] [Indexed: 05/20/2023]
Abstract
New emerging low-dimensional such as 0D, 1D, and 2D nanomaterials have attracted tremendous research interests in various fields of state-of-the-art electronics, optoelectronics, and photonic applications due to their unique structural features and associated electronic, mechanical, and optical properties as well as high-throughput fabrication for large-area and low-cost production and integration. Particularly, photodetectors which transform light to electrical signals are one of the key components in modern optical communication and developed imaging technologies for whole application spectrum in the daily lives, including X-rays and ultraviolet biomedical imaging, visible light camera, and infrared night vision and spectroscopy. Today, diverse photodetector technologies are growing in terms of functionality and performance beyond the conventional silicon semiconductor, and low-dimensional nanomaterials have been demonstrated as promising potential platforms. In this review, the current states of progress on the development of these nanomaterials and their applications in the field of photodetectors are summarized. From the elemental combination for material design and lattice structure to the essential investigations of hybrid device architectures, various devices and recent developments including wearable photodetectors and neuromorphic applications are fully introduced. Finally, the future perspectives and challenges of the low-dimensional nanomaterials based photodetectors are also discussed.
Collapse
Affiliation(s)
- Jaehyun Kim
- Department of Chemistry and Materials Research Center, Northwestern University, Evanston, IL, 60208, USA
| | - Junho Lee
- Displays and Devices Research Lab. School of Electrical and Electronics Engineering, Chung-Ang University, Seoul, 06974, South Korea
| | - Jong-Min Lee
- Displays and Devices Research Lab. School of Electrical and Electronics Engineering, Chung-Ang University, Seoul, 06974, South Korea
| | - Antonio Facchetti
- Department of Chemistry and Materials Research Center, Northwestern University, Evanston, IL, 60208, USA
| | - Tobin J Marks
- Department of Chemistry and Materials Research Center, Northwestern University, Evanston, IL, 60208, USA
| | - Sung Kyu Park
- Displays and Devices Research Lab. School of Electrical and Electronics Engineering, Chung-Ang University, Seoul, 06974, South Korea
| |
Collapse
|
4
|
Mengistu A, Naimuddin M, Abebe B. Optically amended biosynthesized crystalline copper-doped ZnO for enhanced antibacterial activity. RSC Adv 2023; 13:24835-24845. [PMID: 37608973 PMCID: PMC10440632 DOI: 10.1039/d3ra04488b] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/05/2023] [Accepted: 08/09/2023] [Indexed: 08/24/2023] Open
Abstract
The emergence and re-emergence of antibiotic-resistant bacteria is a potential threat to treating infectious diseases. This study employed a nanometer-scale green synthesis using an extract of Solanum incanum leaves to obtain nanoparticles (NPs) and nanocomposites (NCs) possessing antibacterial properties. The FESEM-EDS elemental mapping analysis proved the novelty of the green synthesis approach in synthesizing a copper-doped ZnO NCs with good dopant distribution. The crystallinity and ZnO bandgap were adjusted by extrinsic copper doping in the ZnO lattice. The optical property adjustments from 3.04 to 2.97 eV for indirect Kubelka-Munk functions were confirmed from DRS-UV-vis analysis. The dopant inclusion in the host lattice was also confirmed by the angle shift on the XRD pattern analysis relative to single ZnO. In addition to doping, the XRD pattern analysis also showed the development of CuO crystals. The lattice fringe values from HRTEM analysis confirmed the existence of both CuO and ZnO crystals with local heterojunctions. Doping and heterojunctions have crucial values in charge transfer and visible light harvesting behaviour, as proved by the PL analysis. The synergistic effects of the doped NCs showed greater antibacterial activity against both Gram-positive and Gram-negative bacteria as a result of more ROS generation through the bacteria-cell-catalyst interaction and release of metal ions. The antioxidant potential of the doped NCs was found to be higher than that of single NPs, using the 2,2-diphenyl-1-picrylhydrazyl free radical scavenging assay and is expected to impart protective effects to the host cells by scavenging destructive free radicals. Thus, the overall analysis leads to the conclusion that the potentiality of synthesized materials has a future outlook for biological applications, especially in the development of antimicrobials to combat antibiotic-resistant bacteria and microbes.
Collapse
Affiliation(s)
- Adam Mengistu
- Department of Applied Biology, School of Applied Natural Science, Adama Science and Technology University P.O. Box:1888 Adama Ethiopia
| | - Mohammed Naimuddin
- Department of Applied Biology, School of Applied Natural Science, Adama Science and Technology University P.O. Box:1888 Adama Ethiopia
| | - Buzuayehu Abebe
- Department of Applied Chemistry, School of Applied Natural Science, Adama Science and Technology University P.O. Box:1888 Adama Ethiopia
| |
Collapse
|
5
|
Costas A, Preda N, Zgura I, Kuncser A, Apostol N, Curutiu C, Enculescu I. Silver nanoparticles decorated ZnO-CuO core-shell nanowire arrays with low water adhesion and high antibacterial activity. Sci Rep 2023; 13:10698. [PMID: 37400545 PMCID: PMC10318101 DOI: 10.1038/s41598-023-37953-w] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/18/2023] [Accepted: 06/30/2023] [Indexed: 07/05/2023] Open
Abstract
Nanostructured surfaces based on silver nanoparticles decorated ZnO-CuO core-shell nanowire arrays, which can assure protection against various environmental factors such as water and bacteria were developed by combining dry preparation techniques namely thermal oxidation in air, radio frequency (RF) magnetron sputtering and thermal vacuum evaporation. Thus, high-aspect-ratio ZnO nanowire arrays were grown directly on zinc foils by thermal oxidation in air. Further ZnO nanowires were coated with a CuO layer by RF magnetron sputtering, the obtained ZnO-CuO core-shell nanowires being decorated with Ag nanoparticles by thermal vacuum evaporation. The prepared samples were comprehensively assessed from morphological, compositional, structural, optical, surface chemistry, wetting and antibacterial activity point of view. The wettability studies show that native Zn foil and ZnO nanowire arrays grown on it are featured by a high water droplet adhesion while ZnO-CuO core-shell nanowire arrays (before and after decoration with Ag nanoparticles) reveal a low water droplet adhesion. The antibacterial tests carried on Escherichia coli (a Gram-negative bacterium) and Staphylococcus aureus (a Gram-positive bacterium) emphasize that the nanostructured surfaces based on nanowire arrays present excellent antibacterial activity against both type of bacteria. This study proves that functional surfaces obtained by relatively simple and highly reproducible preparation techniques that can be easily scaled to large area are very attractive in the field of water repellent coatings with enhanced antibacterial function.
Collapse
Affiliation(s)
- Andreea Costas
- National Institute of Materials Physics, Atomistilor 405A, 077125, Magurele, Romania
| | - Nicoleta Preda
- National Institute of Materials Physics, Atomistilor 405A, 077125, Magurele, Romania.
| | - Irina Zgura
- National Institute of Materials Physics, Atomistilor 405A, 077125, Magurele, Romania
| | - Andrei Kuncser
- National Institute of Materials Physics, Atomistilor 405A, 077125, Magurele, Romania
| | - Nicoleta Apostol
- National Institute of Materials Physics, Atomistilor 405A, 077125, Magurele, Romania
| | - Carmen Curutiu
- Microbiology Immunology Department, Faculty of Biology, University of Bucharest, Aleea Portocalelor 1-3, 060101, Bucharest, Romania
| | - Ionut Enculescu
- National Institute of Materials Physics, Atomistilor 405A, 077125, Magurele, Romania
| |
Collapse
|
6
|
Abebe B, Tsegaye D, Sori C, Renuka Prasad RC, Murthy HCA. Cu/CuO-Doped ZnO Nanocomposites via Solution Combustion Synthesis for Catalytic 4-Nitrophenol Reduction. ACS OMEGA 2023; 8:9597-9606. [PMID: 36936329 PMCID: PMC10018707 DOI: 10.1021/acsomega.3c00141] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Grants] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 01/09/2023] [Accepted: 02/22/2023] [Indexed: 06/18/2023]
Abstract
The synthesis of optoelectrically enhanced nanomaterials should be continuously improved by employing time- and energy-saving techniques. The porous zinc oxide (ZnO) and copper-doped ZnO nanocomposites (NCs) were synthesized by the time- and energy-efficient solution combustion synthesis (SCS) approach. In this SCS approach, once the precursor-surfactant complex ignition point is reached, the reaction starts and ends within a short time without the need for any external energy. The TGA-DTA analysis confirmed that 500 °C was the point at which stable metal oxide was obtained. The doping and heterojunction strategy improved the optoelectric properties of the NCs more than the individual constituents, which then enhanced the materials' charge transfer and optical absorption capabilities. The porosity, nanoscale crystallite size (15-50 nm), and formation of Cu/CuO-ZnO NCs materials were confirmed from the XRD, SEM, and TEM/HRTEM analyses. The obtained d-spacing values of 0.275 and 0.234 nm confirm the formation of ZnO and CuO crystals, respectively. The decrease in photoluminescence intensity for the doped NCs corroborates a reduction in electron-hole recombination. On the Mott-Schottky analysis, the positive slope for ZnO confirms the n-type character, while the negative and positive slopes of the NCs confirm the p- and n-type characters, respectively. A diffusion-controlled type of charge transfer process on the electrode surface was confirmed from the cyclic voltammetric analysis. Thus, the overall analysis shows the applicability of the less expensive and more efficient SCS for several applications, such as catalysis and sensors. To confirm this, an organic catalytic reduction reaction of 4-nitrophenol to 4-aminophenol was tested. Within three and a half minutes, the catalytic reduction result showed the great potential of NCs over ZnO NPs. Thus, the energy- and time-saving SCS approach has a great future outlook as an industrial pollutant catalytic reduction application.
Collapse
Affiliation(s)
- Buzuayehu Abebe
- Department
of Applied Chemistry, School of Applied Natural Science, Adama Science and Technology University, P.O. Box 1888, Adama 1888, Ethiopia
| | - Dereje Tsegaye
- Department
of Applied Chemistry, School of Applied Natural Science, Adama Science and Technology University, P.O. Box 1888, Adama 1888, Ethiopia
| | - Chaluma Sori
- Department
of Applied Chemistry, School of Applied Natural Science, Adama Science and Technology University, P.O. Box 1888, Adama 1888, Ethiopia
| | | | - H. C. Ananda Murthy
- Department
of Applied Chemistry, School of Applied Natural Science, Adama Science and Technology University, P.O. Box 1888, Adama 1888, Ethiopia
- Department
of Prosthodontics, Saveetha Dental College & Hospital, Saveetha
Institute of Medical and Technical Science (SIMATS), Saveetha University, Chennai 600077, Tamil Nadu, India
| |
Collapse
|
7
|
Kosri E, Ibrahim F, Thiha A, Madou M. Micro and Nano Interdigitated Electrode Array (IDEA)-Based MEMS/NEMS as Electrochemical Transducers: A Review. NANOMATERIALS (BASEL, SWITZERLAND) 2022; 12:nano12234171. [PMID: 36500794 PMCID: PMC9741053 DOI: 10.3390/nano12234171] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 10/19/2022] [Accepted: 11/15/2022] [Indexed: 05/28/2023]
Abstract
Micro and nano interdigitated electrode array (µ/n-IDEA) configurations are prominent working electrodes in the fabrication of electrochemical sensors/biosensors, as their design benefits sensor achievement. This paper reviews µ/n-IDEA as working electrodes in four-electrode electrochemical sensors in terms of two-dimensional (2D) planar IDEA and three-dimensional (3D) IDEA configurations using carbon or metal as the starting materials. In this regard, the enhancement of IDEAs-based biosensors focuses on controlling the width and gap measurements between the adjacent fingers and increases the IDEA's height. Several distinctive methods used to expand the surface area of 3D IDEAs, such as a unique 3D IDEA design, integration of mesh, microchannel, vertically aligned carbon nanotubes (VACNT), and nanoparticles, are demonstrated and discussed. More notably, the conventional four-electrode system, consisting of reference and counter electrodes will be compared to the highly novel two-electrode system that adopts IDEA's shape. Compared to the 2D planar IDEA, the expansion of the surface area in 3D IDEAs demonstrated significant changes in the performance of electrochemical sensors. Furthermore, the challenges faced by current IDEAs-based electrochemical biosensors and their potential solutions for future directions are presented herein.
Collapse
Affiliation(s)
- Elyana Kosri
- Department of Biomedical Engineering, Faculty of Engineering, Universiti Malaya, Kuala Lumpur 50603, Malaysia
- Centre for Innovation in Medical Engineering (CIME), Faculty of Engineering, Universiti Malaya, Kuala Lumpur 50603, Malaysia
| | - Fatimah Ibrahim
- Department of Biomedical Engineering, Faculty of Engineering, Universiti Malaya, Kuala Lumpur 50603, Malaysia
- Centre for Innovation in Medical Engineering (CIME), Faculty of Engineering, Universiti Malaya, Kuala Lumpur 50603, Malaysia
- Centre of Printable Electronics, Universiti Malaya, Kuala Lumpur 50603, Malaysia
| | - Aung Thiha
- Department of Biomedical Engineering, Faculty of Engineering, Universiti Malaya, Kuala Lumpur 50603, Malaysia
- Centre for Innovation in Medical Engineering (CIME), Faculty of Engineering, Universiti Malaya, Kuala Lumpur 50603, Malaysia
| | - Marc Madou
- Centre for Innovation in Medical Engineering (CIME), Faculty of Engineering, Universiti Malaya, Kuala Lumpur 50603, Malaysia
- Department of Mechanical and Aerospace Engineering, University of California Irvine, Irvine, CA 92697, USA
- School of Engineering and Sciences, Tecnologico de Monterrey, Monterrey 64849, NL, Mexico
- Academia Mexicana de Ciencias, Ciudad de México 14400, CDMX, Mexico
| |
Collapse
|