Polymerization with the argon laser: curing time and shear bond strength

Application of Laser Irradiation for Restorative Treatments

Nowadays, lasers are widely used in many fields of medicine. Also, they can be applied at many branches of dental practice such as diagnosis, preventive procedures, restorative treatments, and endodontic therapies. Procedures like caries removal, re-mineralization, and vital pulp therapy are the most noticeable effects of laser irradiation which has gained much attention among clinicians. With controlled and appropriate wavelength, they can help stimulating dentinogenesis, controlling pulpal hemorrhage, sterilization, healing of collagenic proteins, formation of a fibrous matrix, and inducing hard tissue barrier. Nevertheless, there are many controversies in literatures regarding their effects on the quality of bonded restorations. It hampered a wide application of lasers in some aspects of restorative dentistry and requirements to identify the best way to use this technology. The aim of this mini review is to explain special characteristics of laser therapy and to introduce the possible applications of laser devices for dental purposes.

Shear bond strength of a self-adhering flowable composite when used for lingual retainer bonding

OBJECTIVE

The goal of this work was to assess the shear bond strength (SBS) and fracture mode of a self-adhering flowable composite when used after thermocycling for lingual retainer bonding.

MATERIALS AND METHODS

A total of 80 human mandibular incisor teeth were categorized into four equal groups: group 1: Vertise™ Flow (VF) without acid etching; group 2: VF with acid etching; group 3: VF with a self-etching bonding agent accompanied by an additional acid etching; group 4: Transbond LR control. Either VF or Transbond LR was applied to the lingual surface of the teeth by packing the material into cylindrical plastic matrices to simulate the lingual retainer bonding area. After all teeth were thermocycled (5000 cycles, 5 and 55 °C), fracture modes were examined under × 20 magnification. The SBS data were assessed via analysis of variance (ANOVA) and Tukey's tests. Fracture modes were analyzed by the χ(2) test at a significance level of 0.05.

RESULTS

Statistically significant differences in SBS values between groups (p < 0.001) were observed. Group 4 exhibited the highest (14.63 ± 1.36 MPa) and group 1 the lowest SBS (2.67 ± 1.35 MPa) values. Statistically significant differences were noted in fracture modes between groups 1, 3, and 4 (p < 0.001). In all the self-adhering flowable composite groups, the adhesive type (tooth-composite interface) fracture occurred more frequently than cohesive and mixed-type fractures.

CONCLUSION

When applied to bond lingual retainers to unetched enamel or with self-etching bonding agent accompanied by an additional acid etching, Vertise™ Flow resulted in a significant decrease in bond strength.

Effect of a DPSS laser on the shear bond strength of ceramic brackets with different base designs

This study evaluated the shear bond strength (SBS) and adhesive remnant index (ARI) of ceramic brackets with different base designs using a 473-nm diode-pumped solid-state (DPSS) laser to test its usefulness as a light source. A total of 180 caries-free human premolars were divided into four groups according to the base designs: microcrystalline, crystalline particle (CP), dovetail, and mesh. For each base design, teeth were divided into three different subgroups for light curing using three different light-curing units (LCUs) (quartz-tungsten-halogen unit, light-emitting diode unit, and a DPSS laser of 473 nm). Applied light intensities for the DPSS laser and the other LCUs were approximately 630 and 900 mW/cm(2), respectively. Stainless steel brackets with a mesh design served as controls. The failure modes of debonded brackets were scored using ARI. As a result, brackets bonded using the DPSS laser had the highest SBS values (16.5-27.3 MPa) among the LCUs regardless of base design. Regarding base designs, the CP groups showed the highest SBS values (22.9-27.3 MPa) regardless of LCU. Furthermore, stainless steel brackets with a mesh design had the lowest SBS values regardless of LCU. In many cases, brackets bonded using the DPSS laser had higher ARI scores and had more adhesive on their bases than on tooth surfaces. The study shows that the 473-nm DPSS laser has considerable potential for bonding ceramic brackets at lower light intensities than the other light-curing units examined.