ZnCl2 Incorporated into Experimental Adhesives: Selected Physicochemical Properties and Resin-Dentin Bonding Stability

Influence of Specimen Dimension, Water Immersion Protocol, and Surface Roughness on Water Sorption and Solubility of Resin-Based Restorative Materials

The evaluation of water sorption and solubility is pivotal for the development of new resin-based restorative materials with the potential for clinical application. The purpose of the present study was to evaluate the influence of the specimen dimension, water immersion protocol, and surface roughness on the water sorption and solubility of three resin-based restorative materials. Disk-shaped specimens of 15 mm × 1 mm, 10 mm × 1 mm, and 6 mm × 1 mm were produced with a composite resin (Z100), a resin cement (RelyX ARC), and an adhesive system (Single Bond 2-SB2). The specimens were immersed in distilled water according to four protocols: ISO (all the specimens for each group were vertically immersed in 50 mL); IV-10 (the specimens were individually and vertically immersed in 10 mL); IH-10 (the specimens were individually and horizontally immersed in 10 mL); and IH-2 (the specimens were individually and horizontally immersed in 2 mL). The surface roughness (Sa and Sp) was evaluated using an atomic force microscope, and the degree of conversion was determined using FT-IR spectrometry. The specimen dimension and water immersion protocol had no effect on water sorption and solubility. For the three resin-based restorative materials, Sp was higher than Sa. The degree of conversion was not influenced by the specimen dimension. The variations in the specimen dimension and water immersion protocol compared to those determined by ISO 4049 did not prevent the comparison between the values of water sorption and solubility obtained for a given resin-based restorative material.

Incorporation of MMP inhibitors into dental adhesive systems and bond strength of coronal composite restorations: A systematic review and meta-analysis of in vitro studies

Purpose

To systematically review in vitro studies that incorporated MMP inhibitors into adhesive systems in terms of the effect on immediate and aged bond strength of dental composite to dentine.

Materials and methods

Independently, two reviewers conducted an electronic search in three databases (MEDLINE, EMBASE, and Google Scholar) following the Preferred Reporting Items for Systematic Review and Meta-Analyses Protocols (PRISMA-P), up to 6 March 2022.

Results

The search resulted in 894 papers, 33 of which were eligible to be included in the review; of those, 13 fulfilled the meta-analysis eligibility criteria. Nineteen inhibitors were used among the studies, and those included in the meta-analysis were 2%, 0.2% chlorhexidine (CHX), 5 µM GM1489, and 0.5%, 1% benzalkonium chloride (BAC). In the meta-analysis, while above inhibitors showed no adverse effect on bond strength, 0.2% CHX and 5 µM GM1489 caused a significant increase in immediate and 12-months bond strength. All other inhibitors resulted in a significant increase in bond strength at six months of ageing.

Conclusions

Incorporation of MMP inhibitors into the adhesive system has no unfavourable effect on immediate bond strength but a favourable effect on longer-term bond strength. Additionally, inhibitors other than CHX could have similar or better effects on bond strength.

Zn-containing Adhesives Facilitate Collagen Protection and Remineralization at the Resin-Dentin Interface: A Narrative Review

This is a narrative review of the literature assessing the potential effectiveness of doping dentin polymeric adhesives with zinc compounds in order to improve bonding efficacy, remineralization and protection against degradation. A literature search was conducted using electronic databases, such as PubMed, MEDLINE, DIMDI and Web of Science. Through our search, we found literature demonstrating that Zn-doped dentin adhesives promote protection and remineralization of the resin-dentin interfaces. The increased bioactivity has also facilitated dentinal tubules' occlusion by crystals' precipitation contributing to improved sealing efficacy of restorations. Loading dentin adhesives with zinc gives rise to an increase of both crystallinity of mineral and crosslinking of collagen. The main role of zinc, in dentin adhesives, is to inhibit collagen proteolysis. We concluded that zinc exerts a protective effect through binding at the collagen-sensitive cleavage sites of matrix-metalloproteinases (MMPs), contributing to dentin matrix stabilization. Zinc may not only act as a MMPs inhibitor, but also influence signaling pathways and stimulate metabolic effects in dentin mineralization and remineralization processes. Zn-doped adhesives increase the longevity of dentin bonding through MMPs inhibition. Zn poses a remineralization strategy in demineralized dentin.

Evaluation of resveratrol-doped adhesive with advanced dentin bond durability

OBJECTIVES

This paper aimed to evaluate the influence of resveratrol-doped adhesive on the durability and antibiofilm capability of dentin bonding.

METHODS

Experimental adhesives were prepared by incorporating resveratrol into a universal adhesive at concentrations of 0 (control), 0.1, 1, and 10 mg/mL. The microtensile bond strength, fracture modes, and adhesive-dentin interface nanoleakage were assessed after 24 h of water storage, 10,000 times of thermocycling or 1-month of collagenase ageing. Relevant antibiofilm capability on Streptococcus mutans (S. mutans), in situ zymography, degree of conversion, and cytotoxicity of resveratrol-doped adhesives were also determined.

RESULTS

Irrespective of thermocycled or collagenase ageing, the resveratrol-doped adhesive (1 mg/mL) maintained the bond strength and reduced the nanoleakage expression. Meanwhile, the inhibitory ability on endogenous protease activity and S. mutans biofilm formation with acceptable biocompatibility were obtained.

CONCLUSIONS

This study suggested that the resveratrol-doped adhesive achieved effective improvement on dentin bond durability and secondary caries management.

CLINICAL SIGNIFICANCE

The application of the resveratrol-doped adhesive indicates promising benefits to increase the lifetime of composite restorations.

Synergistic Effect of Bioactive Inorganic Fillers in Enhancing Properties of Dentin Adhesives-A Review

Dentin adhesives (DAs) play a critical role in the clinical success of dental resin composite (DRC) restorations. A strong bond between the adhesive and dentin improves the longevity of the restoration, but it is strongly dependent on the various properties of DAs. The current review was aimed at summarizing the information present in the literature regarding the improvement of the properties of DAs noticed after the addition of bioactive inorganic fillers. From our search, we were able to find evidence of multiple bioactive inorganic fillers (bioactive glass, hydroxyapatite, amorphous calcium phosphate, graphene oxide, calcium chloride, zinc chloride, silica, and niobium pentoxide) in the literature that have been used to improve the different properties of DAs. These improvements can be seen in the form of improved hardness, higher modulus of elasticity, enhanced bond, flexural, and ultimate tensile strength, improved fracture toughness, reduced nanoleakage, remineralization of the adhesive-dentin interface, improved resin tag formation, greater radiopacity, antibacterial effect, and improved DC (observed for some fillers). Most of the studies dealing with the subject area are in vitro. Future in situ and in vivo studies are recommended to positively attest to the results of laboratory findings.

Influence of ER-CR-YSGG Laser and Photodynamic Therapy on the Dentin Bond Integrity of Nano-Hydroxyapatite Containing Resin Dentin Adhesive: SEM-EDX, Micro-Raman, Micro-Tensile, and FTIR Evaluation

The study aimed to analyze the effect of the addition of nano-hydroxyapatite (nano-HA) particles on the mechanical properties of experimental adhesive (EA). Furthermore, dentin interaction of EA (without nano-HA) and EA with nano-HA (hereon referred to as HA-10%) were also investigated and equated. Methods consisting of scanning electron microscopy (SEM)-energy-dispersive X-ray spectroscopy (EDX), micro-Raman spectroscopy, micro-tensile bond strength (µTBS) test, and Fourier transform infrared (FTIR) spectroscopy were employed to study nano-HA particles shape, dentin bond strength, degree of conversion (DC), and adhesive-dentin interaction. Ninety teeth (N = 90) were collected, and pre-bonding, conditioning of dentin was performed utilizing phosphoric acid (H₃PO₄) etching, photodynamic therapy (PDT), and ER-CR-YSGG (ECY) laser. The teeth were set to form bonded specimens using two adhesives. Nano-HA particles were spherical-shaped, and EDX confirmed the presence of oxygen, calcium, and phosphorus. Micro-Raman spectroscopy revealed distinct phosphate and carbonate peaks for nano-HA. The µTBS test demonstrated highest values for HA-10% group on the H₃PO₄ conditioned dentin. The greatest DC was observed for the EA group. The addition of nano-HA-10 wt.% particles in dentin adhesive resulted in improved bond strength. The incorporation also demonstrated acceptable DC (although lower than EA group), suitable dentin interaction, and resin tag formation.

Antimicrobial potential of resin matrices loaded with coffee compounds

This study evaluated the biological behavior of the coffee compounds Trigonelline (T), chlorogenic acid (C), and nicotinic acid (N), correlating with their release from a resin matrix. Minimum inhibitory concentration (MIC) was evaluated against Streptococcus mutans UA159, and cytotoxicity was assessed by methyl tetrazolium salt on OD-21 cells. Resin matrices (bisphenol A-glycidyl-dimethacrylate/triethylene glycol-dimethacrylate 70/30 wt%, camphorquinone/ethyl 4-dimethyl aminobenzoate 0.5/1 wt%) were doped with coffee compounds in different concentrations (10/20/30/40/50 wt%), performing 15 groups (T10-T50, C10-C50, N10-N50), and a control group with no coffee compound. Degree of conversion (DC%) was analyzed by Fourier transform infrared spectroscopy. Antimicrobial properties were evaluated by bioluminescence (Luciferase assay). The release from loaded matrices was analyzed over time (24 hr, 6, 14, 21 and 28 days), using high-performance liquid chromatography (HPLC). Data were submitted to ANOVA/Tukey's test (α = 0.05). MIC for T and C was 6 mg/ml, and 4 mg/ml for N. None of them were cytotoxic. Only T50 and C50 showed lower DC% than control (α < 0.05). Some groups (T30/T40/T50/C40/C50/N50) were strongly antimicrobial, reducing bacterial activity approximately five times compared to control (α < 0.05). For T30, T40, T50, C40, and C50, the HPLC showed a release above or closer to MIC values mainly in 24 hr, but for N50, up to 28 days. In conclusion, the coffee compounds presented antimicrobial activity, depending on their concentration when added in resin matrices, being found a correlation with their release.