Morphological characteristics of cartilage-bone transitional structures in the human knee joint and CAD design of an osteochondral scaffold

Effect of collagen-based scaffolds with hydroxyapatite on the repair of cartilage defects in the rabbit knee joint

BACKGROUND

The repair of articular cartilage defects is always a significant clinical challenge in joint treatment. Therefore, the aim of this study was to investigate that the ColII-HA-CS-HAP scaffolds with BMSCs could repair cartilage defects of knee.

METHODS

Bone marrow mesenchymal stem cells (BMSCs) were extracted from rabbits, identified using immunofluorescence staining, and successfully induced into chondrocytes. Type II collagen (ColII) was isolated from bovine cartilage and constructed into scaffolds with hyaluronic acid, chondroitin sulfate, and hydroxyapatite. Then BMSCs were seeded on the ColII-HA-CS-HAP scaffold to detect biocompatibility.

RESULTS

The results of DAPI fluorescence staining showed that the number of BMSCs on the ColII-HA-CS-HAP scaffolds increased rapidly after culturing for 12 d. The rabbit knee cartilage defect model with a diameter of approximately 3 mm and a thickness of approximately 4 mm was selected to evaluate the regenerative potential of the scaffolds using histological and immunohistochemical analyses. At 6 months, the regenerated cartilage in the ColII-HA-CS-HAP scaffolds with BMSCs was more similar to that of native cartilage than the ColII-HA-CS-HAP scaffold group.

CONCLUSIONS

Our study proved that the ColII-HA-CS-HAP scaffolds with differentiated BMSCs can produce an excellent healing response and repair cartilage defects successfully in a rabbit model.

3D printing tissue-engineered scaffolds for auricular reconstruction

Congenital microtia is the most common cause of auricular defects, with a prevalence of approximately 5.18 per 10,000 individuals. Autologous rib cartilage grafting is the leading treatment modality at this stage of auricular reconstruction currently. However, harvesting rib cartilage may lead to donor site injuries, such as pneumothorax, postoperative pain, chest wall scarring, and deformity. Therefore, in the pursuit of better graft materials, biomaterial scaffolds with great histocompatibility, precise control of morphology, non-invasiveness properties are gradually becoming a new research hotspot in auricular reconstruction. This review collectively presents the exploit and application of 3D printing biomaterial scaffold in auricular reconstruction. Although the tissue-engineered ear still faces challenges before it can be widely applied to patients in clinical settings, and its long-term effects have yet to be evaluated, we aim to provide guidance for future research directions in 3D printing biomaterial scaffold for auricular reconstruction. This will ultimately benefit the translational and clinical application of cartilage tissue engineering and biomaterials in the treatment of auricular defects.

Knee Measurement System with Osteoarthritis Levels Using Artificial Cartilage and Skeletons

Knee osteoarthritis (OA), also known as degenerative arthritis, is a disease characterized by irreversible changes in the cartilage and bones comprising the joints, resulting in pain, impaired function, and deformity. Furthermore, independent of natural aging, the rate of change in joint cartilage has increased in recent years, which is mainly attributed to environmental factors. The rising incidence of knee-related disorders emphasizes the importance of analyzing the morphology and kinematics of knee structure. This study introduces a knee measurement system designed to replicate the motions of knee using 3D-printing technology, providing insights into knee mechanics with OA level. The research explores the stages of OA using the Kellgren-Lawrence (KL) grade scale, highlighting the variations in the force applied to the knee bone according to movement. The developed knee-simulation system, utilizing the four-bar-link theory, presents a novel approach to studying OA levels 0 to 4. As OA progresses, the cartilage deteriorates, affecting the movement of OA. The OA-based knee measurement system that incorporates soft tissues and skeletons can assist in developing a personalized diagnostic approach for knee disease. This will also help to enhance surgical effectiveness by facilitating the creation of personalized prosthetic joints for individual patients and offering a customized surgical simulation.

Microarchitecture Alternations of Osteochondral Junction in Patients with Osteonecrosis of the Femoral Head

The study was aimed to investigate microarchitecture of osteochondral junction in patients with osteonecrosis of the femoral head (ONFH). We hypothesis that there were microarchitecture alternations in osteochondral junction and regional differences between the necrotic region (NR) and adjacent non-necrotic region(ANR) in patients with ONFH. Femoral heads with ONFH or femoral neck fracture were included in ONFH group (n = 11) and control group (n = 11). Cylindrical specimens were drilled on the NR/ANR of femoral heads in ONFH group and matched positions in control group (CO.NR/ CO.ANR). Histology, micro-CT, and scanning electron microscope were used to investigate microarchitecture of osteochondral junction. Layered analysis of subchondral bone plate was underwent. Mankin scores on NR were higher than that on ANR or CO.NR, respectively (P < 0.001, P < 0.001). Calcified cartilage zone on the NR and ANR was thinner than that on the CO.NR and CO.ANR, respectively (P = 0.002, P = 0.002). Tidemark roughness on the NR was larger than that on the ANR (P = 0.002). Subchondral bone plate of NR and ANR was thicker than that on the CON.NR and CON.ANR, respectively (P = 0.002, P = 0.009). Bone volume fraction of subchondral bone plate on the NR was significantly decreasing compared to ANR and CON.NR, respectively (P = 0.015, P = 0.002). Subchondral bone plate on the NR had larger area percentages and more numbers of micropores than ANR and CON.NR (P = 0.002/0.002, P = 0.002/0.002). Layered analysis showed that bone mass loss and hypomineralization were mainly on the cartilage side of subchondral bone plate in ONFH. There were microarchitecture alternations of osteochondral junction in ONFH, including thinned calcified cartilage zone, thickened subchondral bone plate, decreased bone mass, altered micropores, and hypomineralization of subchondral bone plate. Regional differences in microarchitecture of osteochondral junction were found between necrotic regions and adjacent non-necrotic regions. Subchondral bone plate in ONFH had uneven distribution of bone volume fraction and bone mineral density, which might aggravate cartilage degeneration by affecting the transmission of mechanical stresses.

3D Printing of Bone Substitutes Based on Vat Photopolymerization Processes: A Systematic Review

Treatment options for critically sized bone defects are currently limited to metal osteosynthesis, autologous bone grafting, or calcium-based implants to bridge the gap. Additive manufacturing techniques pose a possible alternative. The light-basedthree-dimensional printing process of vat photopolymerization (VP) is of particular interest since it enables the printing of complex scaffold architectures at high resolution. This review compares multiple vat photopolymerization processes as well as the employed resin components' interactions with musculoskeletal cells and tissue. The results show an outstanding printing capability, exceeding the potential of other printing methods. However, despite the availability of various biocompatible materials, neither the mechanical strength of bone nor the scale necessary for clinical application has been achieved so far when relying on single material constructs. One possible solution is the development of adaptive hybrid constructs produced with multimaterial VP.

Intra-osseous plasma rich in growth factors enhances cartilage and subchondral bone regeneration in rabbits with acute full thickness chondral defects: Histological assessment

Background

Intra-articular (IA) combined with intra-osseous (IO) infiltration of plasma rich in growth factors (PRGF) have been proposed as an alternative approach to treat patients with severe osteoarthritis (OA) and subchondral bone damage. The aim of the study is to evaluate the efficacy of IO injections of PRGF to treat acute full depth chondral lesion in a rabbit model by using two histological validated scales (OARSI and ICRS II).

Methodology

A total of 40 rabbits were included in the study. A full depth chondral defect was created in the medial femoral condyle and then animals were divided into 2 groups depending on the IO treatment injected on surgery day: control group (IA injection of PRGF and IO injection of saline) and treatment group (IA combined with IO injection of PRGF). Animals were euthanized 56 and 84 days after surgery and the condyles were processed for posterior histological evaluation.

Results

Better scores were obtained in treatment group in both scoring systems at 56- and 84-days follow-up than in control group. Additionally, longer-term histological benefits have been obtained in the treatment group.

Conclusions

The results suggests that IO infiltration of PRGF enhances cartilage and subchondral bone healing more than the IA-only PRGF infiltration and provides longer-lasting beneficial effects.

Acrylamide-based hydrogels with distinct osteogenic and chondrogenic differentiation potential

Regeneration solutions for the osteochondral interface depth are limited, where multi-material implants have the potential to delaminate affecting the regeneration process and impacting the final integrity of tissue interface. Here we explore regionally mixed hydrogel networks, presenting distinct chemical features to determine their compatibility in supporting osteogenic or chondrogenic cell behaviour and differentiation. Poly(N-isopropylacrylamide) (pNIPAM) and poly(N-tert-butylacrylamide) (pNTBAM) hydrogels were assessed in terms of their chemical differences, mechanical strength, internal architecture, porosity and capacity to support cell viability, migration, and differentiation. pNTBAM polymerized with a Young’s modulus of up to 371 ± 31 kPa compared to the more flexible pNIPAM, 16.5 ± 0.6 kPa. Viability testing revealed biocompatibility of both hydrogels with significantly increased cell numbers observed in pNTBAM (500 ± 95 viable cells/mm²) than in pNIPAM (60 ± 3 viable cells/mm²) (P ≤ 0.05). Mineralization determined through alkaline phosphatase (ALP) activity, calcium ion and annexin A2 markers of mineralization) and osteogenic behaviour (collagen I expression) were supported in both hydrogels, but to a greater extent in pNTBAM. pNTBAM supported significantly elevated levels of chondrogenic markers as evidenced by collagen II and glycosaminoglycan expression in comparison to little or no evidence in pNIPAM (P ≤ 0.05). In conclusion, structurally similar, chemically distinct, acrylamide hydrogels display variable capacities in supporting osteochondral cell behaviours. These systems demonstrate spatial control of cell interaction through simple changes in monomer chemistry. Fine control over chemical presentation during the fabrication of biomaterial implants could lead to greater efficacy and targeted regeneration of semi-complex tissues.

High-performance bilayer composites for the replacement of osteochondral defects

Two novel bilayer constructs for the repair of osteochondral defects were developed from nanofibers and ceramic particles embedded into PVA matrices, exhibiting multiple promising properties similar to those of corresponding natural tissues.

Biomimetic Approaches for the Design and Fabrication of Bone-to-Soft Tissue Interfaces

Bone-to-soft tissue interfaces are responsible for transferring loads between tissues with significantly dissimilar material properties. The examples of connective soft tissues are ligaments, tendons, and cartilages. Such natural tissue interfaces have unique microstructural properties and characteristics which avoid the abrupt transitions between two tissues and prevent formation of stress concentration at their connections. Here, we review some of the important characteristics of these natural interfaces. The native bone-to-soft tissue interfaces consist of several hierarchical levels which are formed in a highly specialized anisotropic fashion and are composed of different types of heterogeneously distributed cells. The characteristics of a natural interface can rely on two main design principles, namely by changing the local microarchitectural features (e.g., complex cell arrangements, and introducing interlocking mechanisms at the interfaces through various geometrical designs) and changing the local chemical compositions (e.g., a smooth and gradual transition in the level of mineralization). Implementing such design principles appears to be a promising approach that can be used in the design, reconstruction, and regeneration of engineered biomimetic tissue interfaces. Furthermore, prominent fabrication techniques such as additive manufacturing (AM) including 3D printing and electrospinning can be used to ease these implementation processes. Biomimetic interfaces have several biological applications, for example, to create synthetic scaffolds for osteochondral tissue repair.

Cellular alterations and crosstalk in the osteochondral joint in osteoarthritis and promising therapeutic strategies

Osteoarthritis (OA) is a joint disorder involving cartilage degeneration and subchondral bone sclerosis. The bone-cartilage interface is implicated in OA pathogenesis due to its susceptibility to mechanical and biological factors. The crosstalk between cartilage and the underlying subchondral bone is elevated in OA due to multiple factors, such as increased vascularization, porosity, microcracks and fissures. Changes in the osteochondral joint are traceable to alterations in chondrocytes and bone cells (osteoblasts, osteocytes and osteoclasts). The phenotypes of these cells can change with the progression of OA. Aberrant intercellular communications among bone cell-bone cell and bone cell-chondrocyte are of great importance and might be the factors promoting OA development. An appreciation of cellular phenotypic changes in OA and the mechanisms by which these cells communicate would be expected to lead to the development of targeted drugs with fewer side effects.

Comparison of chondrogenesis-related biological behaviors between human urine-derived stem cells and human bone marrow mesenchymal stem cells from the same individual

BACKGROUND

Stem cells are the main choice for seed cells in tissue engineering, but using most traditional stem cells requires invasive and complicated procedures. Human urine-derived stem cells (hUSCs) are an alternative stem cell source with the advantages of being isolated noninvasively and repetitively from the same individual. The aim of this study was to compare chondrogenesis-related biological behaviors between hUSCs and human bone marrow mesenchymal stem cells (hBMSCs) from the same individual.

METHODS

hUSCs and hBMSCs were isolated from six patients who underwent iliac bone grafting. Cell morphology, proliferation, colony-forming, migration, and multidifferentiation analyses were performed in vitro. Then, acellular cartilage extracellular matrix (ACM) scaffolds were fabricated for in vivo implantation. The comparisons of cell viability, morphology, proliferation, and chondrogenesis between hUSCs and hBMSCs cultured on scaffolds were performed before implantation. The scaffolds loaded with hUSCs or hBMSCs were implanted into a rabbit knee model to repair cartilage defects. Magnetic resonance imaging (MRI) and micro-computed tomography (μCT) Analyses, inflammation and toxicity assays, gross observation, and histological evaluation were performed to evaluate the cartilage repair effects.

RESULTS

In in vitro experiments, hUSCs had better capacity for proliferation, colony-forming, and migration compared to hBMSCs in the same passage, while hBMSCs had greater osteogenic, adipogenic, and chondrogenic abilities compared to hUSCs in the same passage. Both hUSCs and hBMSCs at passage 3 had the strongest potential for proliferation, colony-forming, and multilineage differentiation compared to cells in other passages. The ACM scaffolds loaded with hUSCs or hBMSCs both significantly promoted the repair of cartilage defects in the rabbit knee model at 12 weeks' postimplantation, and the new tissue was mainly hyaline cartilage. However, there was no significant difference in cartilage repair effects between hUSCs and hBMSCs.

CONCLUSIONS

In in vitro experiments, hUSCs presented better capacity for proliferation, while hBMSCs had greater chondrogenic ability. However, hUSCs and hBMSCs had similar cartilage repair effects in vivo. Results indicated that hUSCs can be a stem cell alternative for cartilage regeneration and provide a powerful platform for cartilage tissue engineering and clinical transformation.

Subchondral Bone Remodeling: A Therapeutic Target for Osteoarthritis

There is emerging awareness that subchondral bone remodeling plays an important role in the development of osteoarthritis (OA). This review presents recent investigations on the cellular and molecular mechanism of subchondral bone remodeling, and summarizes the current interventions and potential therapeutic targets related to OA subchondral bone remodeling. The first part of this review covers key cells and molecular mediators involved in subchondral bone remodeling (osteoclasts, osteoblasts, osteocytes, bone extracellular matrix, vascularization, nerve innervation, and related signaling pathways). The second part of this review describes candidate treatments for OA subchondral bone remodeling, including the use of bone-acting reagents and the application of regenerative therapies. Currently available clinical OA therapies and known responses in subchondral bone remodeling are summarized as a basis for the investigation of potential therapeutic mediators.

Biphasic Double-Network Hydrogel With Compartmentalized Loading of Bioactive Glass for Osteochondral Defect Repair

Periarticular injury usually causes the defects of superficial cartilage and the underlying subchondral bone. Although some efficacious outcomes have been achieved by the existing therapeutic methods both in clinics and research, like symptomatic treatment, microfracture surgery, and tissue engineering technology, they still present specific disadvantages and complications. To improve this situation, we designed a biphasic (bi-) scaffold aiming to repair the structure of cartilage and subchondral bone synchronously. The scaffold consisted of a superior double-network (DN) hydrogel layer and a lower bioactive glass (BG) reinforced hydrogel layer, and the DN hydrogel included glycol chitosan (GC) and dibenzaldhyde functionalized poly(ethylene oxide) network, and sodium alginate (Alg) and calcium chloride (CaCl₂) network. To investigate its effectiveness, we applied this biphasic scaffold to repair osteochondral full-thickness defects in rabbit models. We set up six observation groups in total, including Untreated group, Microfracture group, BG only group, DN gel group, bi-DN gel group, and bi-DN/TGF-β gel group. With a follow-up period of 24 weeks, we evaluated the treatment effects by gross observation, micro-CT scan and histological staining. Besides, we further fulfilled the quantitative analysis of the data from ICRS score, O’Driscoll score and micro-CT parameters. The results revealed that neat GC/Alg DN hydrogel scaffold was only conductive to promoting cartilage regeneration and neat BG scaffold merely showed the excellent ability to reconstruct subchondral bone. While the biphasic scaffold performed better in repairing osteochondral defect synchronously, exhibiting more well-integrated cartilage-like tissue with positive staining of toluidine blue and col II immunohistochemistry, and more dense trabecular bone connecting closely with the surrounding host bone. Therefore, this method possessed the clinical application potential in treating articular injury, osteochondral degeneration, osteochondral necrosis, and sclerosis.

Combining multi-scale 3D printing technologies to engineer reinforced hydrogel-ceramic interfaces

Multi-material 3D printing technologies that resolve features at different lengths down to the microscale open new avenues for regenerative medicine, particularly in the engineering of tissue interfaces. Herein, extrusion printing of a bone-biomimetic ceramic ink and melt electrowriting (MEW) of spatially organized polymeric microfibres are integrated for the biofabrication of an osteochondral plug, with a mechanically reinforced bone-to-cartilage interface. A printable physiological temperature-setting bioceramic, based on α-tricalcium phosphate, nanohydroxyapatite and a custom-synthesized biodegradable and crosslinkable poloxamer, was developed as bone support. The mild setting reaction of the bone ink enabled us to print directly within melt electrowritten polycaprolactone meshes, preserving their micro-architecture. Ceramic-integrated MEW meshes protruded into the cartilage region of the composite plug, and were embedded with mechanically soft gelatin-based hydrogels, laden with articular cartilage chondroprogenitor cells. Such interlocking design enhanced the hydrogel-to-ceramic adhesion strength >6.5-fold, compared with non-interlocking fibre architectures, enabling structural stability during handling and surgical implantation in osteochondral defects ex vivo. Furthermore, the MEW meshes endowed the chondral compartment with compressive properties approaching those of native cartilage (20-fold reinforcement versus pristine hydrogel). The osteal and chondral compartment supported osteogenesis and cartilage matrix deposition in vitro, and the neo-synthesized cartilage matrix further contributed to the mechanical reinforcement at the ceramic-hydrogel interface. This multi-material, multi-scale 3D printing approach provides a promising strategy for engineering advanced composite constructs for the regeneration of musculoskeletal and connective tissue interfaces.

Recent Advances in Tissue Engineering Strategies for the Treatment of Joint Damage

PURPOSE OF REVIEW

While the clinical potential of tissue engineering for treating joint damage has yet to be realized, research and commercialization efforts in the field are geared towards overcoming major obstacles to clinical translation, as well as towards achieving engineered grafts that recapitulate the unique structures, function, and physiology of the joint. In this review, we describe recent advances in technologies aimed at obtaining biomaterials, stem cells, and bioreactors that will enable the development of effective tissue-engineered treatments for repairing joint damage.

RECENT FINDINGS

3D printing of scaffolds is aimed at improving the mechanical structure and microenvironment necessary for bone regeneration within a damaged joint. Advances in our understanding of stem cell biology and cell manufacturing processes are informing translational strategies for the therapeutic use of allogeneic and autologous cells. Finally, bioreactors used in combination with cells and biomaterials are promising strategies for generating large tissue grafts for repairing damaged tissues in pre-clinical models. Together, these advances along with ongoing research directions are making tissue engineering increasingly viable for the treatment of joint damage.

From intricate to integrated: Biofabrication of articulating joints

Articulating joints owe their function to the specialized architecture and the complex interplay between multiple tissues including cartilage, bone and synovium. Especially the cartilage component has limited self-healing capacity and damage often leads to the onset of osteoarthritis, eventually resulting in failure of the joint as an organ. Although in its infancy, biofabrication has emerged as a promising technology to reproduce the intricate organization of the joint, thus enabling the introduction of novel surgical treatments, regenerative therapies, and new sets of tools to enhance our understanding of joint physiology and pathology. Herein, we address the current challenges to recapitulate the complexity of articulating joints and how biofabrication could overcome them. The combination of multiple materials, biological cues and cells in a layer-by-layer fashion, can assist in reproducing both the zonal organization of cartilage and the gradual transition from resilient cartilage toward the subchondral bone in biofabricated osteochondral grafts. In this way, optimal integration of engineered constructs with the natural surrounding tissues can be obtained. Mechanical characteristics, including the smoothness and low friction that are hallmarks of the articular surface, can be tuned with multi-head or hybrid printers by controlling the spatial patterning of printed structures. Moreover, biofabrication can use digital medical images as blueprints for printing patient-specific implants. Finally, the current rapid advances in biofabrication hold significant potential for developing joint-on-a-chip models for personalized medicine and drug testing or even for the creation of implants that may be used to treat larger parts of the articulating joint. © 2017 The Authors. Journal of Orthopaedic Research Published by Wiley Periodicals, Inc. on behalf of the Orthopaedic Research Society. J Orthop Res 35:2089-2097, 2017.

Histological, Physical Studies after Xenograft of Porcine Ear Cartilage

BACKGROUND

Because of the relatively similar size of organs to human and the physiological and structural similarities, the use of porcine as xenograft donors is progressing very actively. In this study, we analyzed the characteristics of porcine ear cartilage and evaluated its suitability as graft material in reconstructive and cosmetic surgery.

METHODS

The auricular cartilage was harvested from two pigs, and subjected to histological examination by immunohistochemical staining. To determine the collagen content, samples were treated with collagenase and weight changes were measured. After sterilization by irradiation, the samples were grafted into rats and stained with Hematoxylin and Eosin and Masson Trichrome to observe inflammation and xenograft rejection.

RESULTS

In IHC staining, extracellular matrices were mainly stained with type II collagen (20.69%), keratin sulfate (10.20%), chondroitin sulfate (2.62%), and hyaluronic acid (0.84%). After collagenase treatment, the weight decreased by 68.3%, indicating that about 70% of the porcine ear cartilage was composed of collagen. Upon xenograft of the sterilized cartilages in rats, inflammatory cells were observed for up to 2 months. However, they gradually decreased, and inflammation and reject-response were rarely observed at 5 months.

CONCLUSION

The porcine ear cartilage was covered with perichondrium and cellular constituents were found to be composed of chondrocytes and chondroblasts. In addition, the extracellular matrices were mainly composed of collagen. Upon xenograft of irradiated cartilage into rats, there was no specific inflammatory reaction around the transplanted cartilage. These findings suggest that porcine ear cartilage could be a useful alternative implant material for human cosmetic surgery.