Noncarious cervical lesions: Morphology and progression, prevalence, etiology, pathophysiology, and clinical guidelines for restoration

PURPOSE

To synthesize the literature regarding noncarious cervical lesions (NCCLs) and propose clinical guidelines when lesion restoration is indicated.

MATERIAL AND METHODS

A PubMed search was performed related to NCCL morphology, progression, prevalence, etiology, pathophysiology, and restoration.

RESULTS

NCCLs form as either rounded (saucerlike) depressions with smooth, featureless surfaces that progress mainly in height or as V-shaped indentations that increase in both height and depth. Prevalence ranges from less than 10% to over 90% and increases with age. Common locations are the facial surfaces of maxillary premolars. They have a multifactorial etiology due to personal habits such as excessive horizontal toothbrushing and consumption of acidic foods and drinks. Occlusal factors have been identified as contributing to the prevalence of NCCLs in some studies, whereas other studies indicate there is no relationship. The concept of abfraction has been proposed whereby mechanical stress from occlusal loading plays a role in the development and progression of NCCLs with publications supporting the concept and others indicating it lacks the required clinical documentation. Regardless of the development mechanism, demineralization occurs and they are one of the most common demineralization diseases in the body. Treatment should be managed conservatively through preventive intervention with restorative treatment delayed until it becomes necessary due to factors such as lesion progression, impact on patient's quality of life, sensitivity, poor esthetics, and food collection may necessitate restoration. Composite resins are commonly used to restore NCCLs although other materials such as glass ionomer and resin-modified glass ionomer are also used. Sclerotic dentin does not etch like normal dentin and therefore it has been recommended to texture the dentin surface with a fine rotary diamond instrument to improve restoration retention. Some clinicians use mechanical retention to increase retention. Beveling of enamel is used to increase the bonding area and retention as well as enhance the esthetic result by gradually creating a color change between the restoration and tooth. Both multistep and single-step adhesives have been used. Dentin etching should be increased to 30 seconds due to the sclerotic dentin with the adhesive agent applied using a light scrubbing motion for 20 seconds but without excessive force that induces substantial bending of a disposable applicator. Both flowable and sculptable composite resins have been successfully used with some clinicians applying and polymerizing a layer of flowable composite resin and then adding an external layer of sculptable composite resin to provide enhanced resistance to wear. When caries is present, silver diamine fluoride has been used to arrest the caries rather than restore the lesion.

CONCLUSIONS

Noncarious cervical lesions (NCCLs) form as smooth saucerlike depressions or as V-shaped notches. Prevalence values as high as 90% and as low as 10% have been reported due to habits such as excessive toothbrushing and an acidic diet. Occlusal factors have been proposed as contributing to their presence but it remains controversial. Publications have both supported and challenged the concept of abfraction. They are one of the most common demineralization diseases in the body. Conservative treatment through prevention is recommended with restorative treatment delayed as long as possible. When treatment is needed, composite resins are commonly used with proposed restorative guidelines including texturing the sclerotic dentin, beveling the enamel, potential use of mechanical retention, 30 seconds of acid etching, and use of either multistep or single-step adhesives in conjunction with a light scrubbing motion for 20 seconds without excessive force placed on disposable applicators.

Adhesive Class VI Resin Composite Restorations of Worn Mandibular Incisal Edges: A Two-year Case Report

Many authors have advocated retentive tooth preparations for resin composite restorations intended to halt progression of incisal edge attrition with worn concave dentin, probably due to frustration with adhesive restorations being lost from these defects. Unfortunately, this technique further removes the dentin these restorations are intended to preserve. The purpose of this article is to demonstrate a purely adhesive, less invasive technique for restoration of worn concave incisal edges, which includes air particle abrasion and increased etching time for the sclerotic dentin and unprepared enamel. Favorable two-year results for mandibular anterior teeth opposed by natural teeth are reported.

Effect of different surface treatments of human occlusal sclerotic dentin on micro-tensile bond strength to resin composite core material

The objectives of this study were to evaluate the micro-tensile bond strength (μTBS) of composite bonded to human occlusal sclerotic dentin following different surface treatments to determine the sclerotic dentin morphology. Human molars without (normal dentin; group 1) or with occlusal wear (sclerotic dentin; groups 2-5) were divided and subjected to different surface treatments, including the normal protocol for the Contax self-etch bonding system (group 1 and 2); doubled etch-prime time (group 3); pre-conditioning with 37% phosphoric acid before normal protocol (group 4); or pre-conditioning with 37% phosphoric acid before doubling the self-etching time (group 5). All teeth were restored with composite (Luxacore Z dual), sectioned into stick specimens and stored for 24 h in water before specimens were subjected to the μTBS test (n = 50 per group). The μTBS of normal dentin was not statistically significantly different from that of the sclerotic dentin groups, except for the doubled etch-prime time group which showed lower μTBS. Sclerotic dentin pre-treated with phosphoric acid resulted in less sclerotic casts and wider dentinal tubules, while doubled etch-prime time did not alter the morphology, as shown by scanning electron microscopy. In conclusion, the use of 37% phosphoric acid before applying self-etch bonding resulted in more tubule openings and a significantly higher μTBS when compared with the doubled etch-prime time group.

Microshear Bond Strength of Different Adhesive Systems to Dentin

Objectives:

The aim of this study was to compare the microshear bond strength (μSBS) of various adhesive systems to dentin.

Materials and Methods:

In this in vitro experimental study, 60 sound human third molars were divided into four groups. Dentin discs were prepared of middle-third dentin measuring 4 mm in diameter and 2 mm in thickness. Dentin surfaces were bonded with one of the four types of adhesives: (A) Single Bond (3M ESPE), Scotchbond Universal (3M ESPE) in etch and rinse (B) and self-etch (C) modes and (D) Clearfil SE Bond (Kuraray Noritake Dental). After the application of adhesive systems according to the manufacturers’ instructions, composite cylinders (Vit-l-escence) were bonded to dentin surfaces. The μSBS test was performed using a universal testing machine at a crosshead speed of 1 mm/min. Data were analyzed with one-way ANOVA and Tukey’s test (α=0.05).

Results:

The μSBS was the highest in self-etch Scotchbond Universal (15.8±6.08 MPa) followed by Clearfil SE Bond (15.24±4.6 MPa), etch and rinse Scotchbond Universal (11.68±4.07MPa) and Single Bond (11.24±3.74 MPa). A significant difference was only found between Single Bond and etch and rinse Scotchbond Universal groups (P=0.04).

Conclusion:

Based on the results of this study, application of Scotchbond Universal in self-etch mode provides a reliable bond to dentin.

A comparative study of the microtensile bond strength and microstructural differences between sclerotic and Normal dentine after surface pretreatment

Background

The resin bond strength of sclerotic dentine is significantly lower than that of the normal dentine, which paused a challenge for bonding procedures clinically. The aim of this study was to compare the effects of different surface pretreatments on the micro-tensile bond strength and microstructure between sclerotic dentine and normal dentine.

Methods

Eighty teeth that were collected, forty premolars with typical wedge-shaped defects visually graded as class III were assigned as the sclerotic dentine group (SD), the other forty normal premolars with artificial wedge-shaped defects were assigned as the normal dentine group (ND). Each group was randomly subdivided into eight subgroups according to the solution used: 35% phosphoric acid, 15% EDTA, 5% or 10% NaClO. Then the dentine surface was examined using a scanning electron microscope (SEM). The lesions were restored using self-etching adhesive and the subsequent resin composite. The teeth were sectioned into sticks for the micro-tensile bond strength analysis, and the data were analysed using the SPSS17.0 software package (α = 0.05).

Results

First, for the ND groups, after pretreatment using 35% phosphoric acid, and 35% phosphoric acid + 5% or 10% sodium hypochlorite, the bonding strengths of the normal dentine were higher than that of the other groups (P < 0.05). Second, for the SD groups, after pretreatment using 35% phosphoric acid, 15% EDTA, and 35% phosphoric acid + 5% or 10% sodium hypochlorite, the bonding strengths of the sclerotic dentine were higher than that of the other groups (P < 0.05). Third, the bond strengths of the sclerotic dentine were lower than that of the normal dentine without any pretreatment (P < 0.05). After pretreatment using 35% phosphoric acid + 5% or 10% sodium hypochlorite, the bonding strengths of the sclerotic dentine were higher than that of the normal dentine (P < 0.05). SEM observation showed that the appearances of dentine surface were changed after pretreatment using the above solutions, with the reduced smear layer, opened small groove and increased dentinal tubules.

Conclusion

Pretreatment of dentine using 35% phosphoric acid+ 5% or + 10% sodium hypochlorite changed the microstructure of the sclerotic dentine surface and subsequently increased the micro-tensile bond strength.

Analysis of the bond interface between self-adhesive resin cement to eroded dentin in vitro

The purpose of this study was to evaluate the bonding interface between a self-adhesive resin cement to in vitro eroded dentin. Seventy-two third molars were used and divided into two groups: sound dentin and in vitro eroded dentin. The in vitro erosion was performed following a demineralization protocol, in which the specimens were immersed in a demineralizing solution for 2 minutes per cycle and remineralizing solution for 10 minutes per cycle for 9 days. Both groups were submitted to four dentin surface treatments: control group (without any treatment), 2% chlorhexidine, 20% polyacrylic acid, and 0.1 M EDTA (n = 9). Blocks of resin-based composite were bonded with RelyX U200 self-adhesive resin cement applied on the pretreated dentin surfaces. The teeth were sectioned into beams (1mm²) and submitted to microtensile bond strength testing to evaluate the bond strength of self-adhesive resin cement to dentin after 24 hours and 8 months of immersion in artificial saliva. Three specimens of each group were longitudinally cut and evaluated using confocal laser scanning microscopy to analyze the dentin/cement interface. Eroded dentin showed higher bond strength values when compared to sound dentin for the 2% chlorhexidine group (p = 0.03), 24 hours after adhesion. When considering eroded dentin, the 0.1M EDTA group showed higher bond strength values with a statistically significant difference only for the control group (p = 0.002). After 8 months of storage, the present results showed that there was no statistically significant difference between the two substrates for all experimental groups (p>0.05). Analysis of the microscopy confocal showed different types of treatments performed on dentin generally increased tags formation when compared to the control group. The eroded dentin showed a significant increase in density and depth of resinous tags when compared to sound dentin. The storage of samples for 8 months seems to have not caused significant degradation of the adhesive interface.

Bond Capability of Universal Adhesive Systems to Dentin in Self-etch Mode after Short-term Storage and Cyclic Loading

Objective:

The aim was to evaluate, in vitro, the tensile bond strength to dentin of Scotchbond Universal (SU), All-Bond Universal (AU) and One Coat 7 Universal (OC7) adhesives applied in self-etch mode, after 24 h of storage and after 500,000 loading cycles, using Clearfil SE Bond (SE) as a control.

Materials and Methods:

The adhesives were applied on the dentin of bovine teeth, followed by the application of a composite resin. Thirty specimens were obtained for each adhesive. Half of the specimens were submitted to cyclic loading for 500,000 cycles. All specimens were submitted to a tensile bond strength test in a universal testing machine at a crosshead speed of 0.5 mm/minute.

Results:

According to two-way ANOVA and Tukey’s test (α=5%), the interaction between the adhesive and cyclic loading factors was significant (p=0.001). The means followed by the same letter represent no significant difference in the bond strength (MPa) after 24 h: OC7=7.86^A (±2.90), SU=6.78^AB (±2.03), AU=5.61^BC (±2.32), and SE=3.53^C (±1.89). After cyclic loading, SE, SU and AU maintained bond strength comparable to 24 h period. There was a significant decrease only for OC7.

Conclusion:

SU, AU and OC7 had bond strength to dentin comparable to that of SE. Only OC7 had decreased bond strength to dentin after cyclic loading.

Effect of Different Protocols in Preconditioning With EDTA in Sclerotic Dentin and Enamel Before Universal Adhesives Applied in Self-etch Mode

Objectives:

The aim of this study was to investigate the effect of different protocols of 17% ethylene diamine tetra-acetic acid (EDTA) conditioning on the etching pattern and immediate bond strength of universal adhesives to enamel and sclerotic dentin.

Methods and Materials:

Forty bovine teeth with sclerotic dentin and 20 human third molars were randomly divided into eight groups resulting from the combination of the main factors surface treatment (none, two-minute EDTA conditioning manual application, 30-second EDTA manual application, 30-second EDTA sonic application) and adhesives systems (Scotchbond Universal Adhesive [SBU] and Prime & Bond Elect [PBE]). Resin-dentin and enamel-dentin bond specimens were prepared and tested under the microtensile bond strength (μTBS) and microshear bond strength (μSBS) tests, respectively. The etching pattern produced on the unground enamel and the sclerotic dentin surfaces under the different protocols and adhesive systems was evaluated under scanning electron microscopy.

Results:

For enamel, only the main factor adhesive was significant (p&lt;0.0001), with SBU showing the highest μSBS. In sclerotic dentin, the lowest mean was observed for the group without EDTA application and the highest mean in the group with EDTA application with the sonic device for 30 seconds. Regardless of the EDTA protocol, the highest means of μTBS were observed for SBU (p&lt;0.05).

Conclusions:

EDTA conditioning improves the bonding performance of universal adhesives in the self-etch mode on sclerotic dentin, mainly when applied for 30 seconds with the aid of a sonic device. EDTA pretreatment also improves the retentive etching pattern of enamel, but it does not result in higher enamel bond strength.

Effect of Er,Cr:YSGG Laser at Different Output Powers on the Micromorphology and the Bond Property of Non-Carious Sclerotic Dentin to Resin Composites

BACKGROUND

The objective of this study was to investigate the influence of Er,Cr:YSGG laser irradiated at different powers on the micromorphology and the bonding property of non-carious sclerotic dentin to resin composites.

METHODS

Two hundred bovine incisors characterized by non-carious sclerotic dentin were selected, and the seventy-two teeth of which for surface morphological analysis were divided into nine groups according to various treatments (A: the control group, B: only treated with the adhesive Adper Easy One, C: diamond bur polishing followed by Adper Easy One, D-I: Er,Cr:YSGG laser irradiating at 1W, 2W, 3W, 4W, 5W, 6W output power, respectively, followed by Adper Easy One). The surface roughness values were measured by the non-contact three-dimensional morphology scanner, then the surface micromorphologies of surfaces in all groups were assessed by scanning electron microscopy (SEM); meanwhile, Image Pro-Plus 6.0 software was used to measure the relative percentage of open tubules on SEM images. The rest, one hundred twenty-eight teeth for bond strength test, were divided into eight groups according to the different treatments (A: only treated with the adhesive Adper Easy One, B: diamond bur polishing followed by the above adhesive, C-H: Er,Cr:YSGG laser irradiating at 1 W, 2 W, 3 W, 4 W, 5 W, 6 W output power, respectively, followed by the above adhesive), and each group was subsequently divided into two subgroups according to whether aging is performed (immediately tested and after thermocycling). Micro-shear bond strength test was used to evaluate the bond strength.

RESULTS

The 4W laser group showed the highest roughness value (30.84±1.93μm), which was statistically higher than the control group and the diamond bur groups (p<0.05). The mean percentages ((27.8±1.8)%, (28.0±2.2)%, (30.0±1.9)%) of open tubules area in the 4W, 5W, 6W group were higher than other groups (p<0.05). The 4W laser group showed the highest micro-shear bond strength not only in immediately tested (17.60±2.55 PMa) but after thermocycling (14.35±2.08MPa).

CONCLUSION

The Er,Cr:YSGG laser at 4W power can effectively improve the bonding property between non-carious sclerotic dentin and resin composites by increasing the roughness and mean percentage area of open tubules.

Effect of the application time of phosphoric acid and self-etch adhesive systems to sclerotic dentin

Objectives:

To evaluate the effect of application time on the resin-dentin bond strength (µTBS) and etching pattern of adhesive systems applied on sclerotic dentine.

Material and Methods:

A total of forty-two bovine incisors had their roots removed. The 1-step self-etch GO (SDI), the 2-step self-etch Adper SE Bond (3MESPE) and the 35% phosphoric acid (3MESPE) from the 2-step etch-and-rinse Adper Single Bond 2 (3MESPE) were applied on the bovine incisal surfaces according to the manufacturer's instructions or duplicating the recommended conditioning time. After adhesive application, thirty teeth were restored with composite resin, stored for 24 h in distilled water at 37º C, and sectioned into resin-dentin bonded sticks (0.8 mm²⁾ and tested according to the µTBS at 0.5 mm/min. The etching pattern of the remaining twelve teeth (n=4 for each material) was examined under scanning electron microscopy. Each tooth was divided into a buccal-to-lingual direction into three thirds, and each third randomly assigned to the groups: control (no treatment), according to the manufacturers' instructions and duplicating the recommended application time. The µTBS and the relative percentage of the tubule area opening were evaluated by two-way repeated measures ANOVA and Tukey's tests (α=0.05).

Results:

The duplication of the conditioning time favored only the GO adhesive (p<0.05). Both application methods significantly increased the tubule area opening (p<0.05) compared to the controls.

Conclusions:

The efficacy of duplicating the conditioning time was only effective for the 1-step self-etch adhesive system tested.

Effect of bur roughness on bond to sclerotic dentin with self-etch adhesive systems

PURPOSE

To evaluate the effect of bur roughness on bond strength values and conditioner pattern of two-step self-etch adhesives applied on sclerotic dentin.

METHODS

The roots of 48 bovine incisors were removed and the crowns were divided into four groups: the control group (CO) teeth were left untreated or the teeth were slightly roughened with coarse-, medium-, or fine-grit diamond burs. Next, the teeth were subdivided and Clearfil SE Bond (CSE) and Adper SE Bond (ASE) were applied according to the manufacturers' instructions. Composite resin (Opallis) buildups were incrementally constructed on the bonded surfaces. After storage for 24 hours in distilled water at 37°C, the teeth were sectioned into sticks (area of 0.8 mm(2)). The sticks were stressed until failure by tensile forces (0.5 mm/min). Additionally, eight bovine teeth were treated as previously described, and after adhesive application, the surface was rinsed off and examined by scanning electron microscopy to measure the relative number of open tubules (OT). Data (MPa) were analyzed by two-way analysis of variance and Tukey test (p=0.05).

RESULTS

CO showed the highest bond strength values (p<0.05). As regards OT, the lowest mean was observed for CO (p<0.05) and the highest was found after application of CSE or ASE (p<0.05).

Effect of air abrasion and thermocycling on resin adaptation and shear bond strength to dentin for an etch-and-rinse and self-etch resin adhesive

This study examined the effect of air abrasion and thermocycling on the adaptation and shear bond strength, of composite resin bonded to dentin using etch-and-rinse and self-etch resin adhesives. Confocal microscopy showed both adhesives closely adapted to dentin and a significantly (p<0.001) greater number of resin tags were observed for the etch-and-rinse adhesive. Air abrasion significantly increased resin tag length (p<0.05) for the etch-and-rinse adhesive and significantly increased the number (p<0.001), length (p<0.001) and thickness (p<0.01) of tags for the self-etch adhesive. However, air abrasion resulted in defect formation within the hybrid layer and thermocycling caused separation of the hybrid layer from adjacent dentin containing resin tags. A significant (p<0.05) reduction in shear bond strength was observed for the etch-and-rinse adhesive following thermocycling. Both adhesive systems adapted well to dentin in vitro and shear bond strengths were similar. The area of tag penetration into dentin was significantly (p<0.0001) enhanced following air abrasion.

Effect of thermal and mechanical loading on marginal adaptation and microtensile bond strength of a self-etching adhesive with caries-affected dentin

Aim:

This study evaluated the effect of thermal and mechanical loading on marginal adaptation and microtensile bond strength in total-etch versus self-etch adhesive systems in caries-affected dentin.

Materials and Methods:

Forty class II cavities were prepared on extracted proximally carious human mandibular first molars and were divided into two groups: Group I — self-etch adhesive system restorations and Group II — total-etch adhesive system restorations. Group I and II were further divided into sub-groups A (Without thermal and mechanical loading) and B (With thermal and mechanical loading of 5000 cycles, 5 ± 2°C to 55 ± 2°C, dwell time 30 seconds, and 150,000 cycles at 60N). The gingival margin of the proximal box was evaluated at 200X magnification for marginal adaptation in a low vacuum scanning electron microscope. The restorations were sectioned, perpendicular to the bonded surface, into 0.8 mm thick slabs. All the specimens were subjected to microtensile bond strength testing. The marginal adaptation was analyzed using descriptive studies, and the bond strength data was analyzed using the one-way analysis of variance (ANOVA) test.

Results and Conclusions:

The total-etch system performed better under thermomechanical loading.

Microtensile bond strength of one- and two-step self-etching adhesives on sclerotic dentin: the effects of thermocycling

This study evaluated the effects of thermocycling on the microtensile bond strength (microTBS) of one- and two-step self-etch adhesives (SEAs) to sclerotic dentin. Two adhesives, Clearfil S3 Bond (S3), a one-step self-etch adhesive (1-SEA), and Clearfil SE Bond (SE), a two-step self-etch adhesive (2-SEA), were applied on cervical lesions in human premolars with sclerotic or normal dentin. After adhesive application, the lesions were restored and built up using a resin composite (Clearfil AP-X). After 24 hours in water storage, the restored teeth were sectioned into 0.7 x 0.7 mm composite-dentin beams. The beams were then aged with 0, 5,000 or 10,000 thermocycles. The use of two adhesives, two substrate types and three thermocycling regimens yielded 12 experimental groups of 14-19 beams each. The beams were subsequently subjected to microTBS testing at a crosshead speed of 1 mm/minute and statistical analyses were computed with three-way ANOVA and Tukey's post hoc test at p < 0.05. Three-way ANOVA showed statistically significant effects on bonding effectiveness by lesion type, adhesive system, thermocycling or combinations of the adhesive system and thermocycling (p < 0.05). With sclerotic dentin, although S3 and SE provided comparable microTBS after 24 hours of water storage, S3 showed significantly lower microTBS than SE after thermocycling (p < 0.05). Regardless of lesion type, the microTBS for S3 decreased significantly after 5,000 or 10,000 thermocycles, while the microTBS for SE showed a significant decrease only after 10,000 thermocycles. Regardless of the extent of thermocycling, the microTBS values for either SE or S3 bonded to sclerotic dentin were significantly lower than to normal dentin (p < 0.05). The results suggested that thermocycling had a significant negative effect on the bond strength of the two SEAs tested. In contrast to 2-SEA, 1-SEA might not be a good choice for sclerotic dentin when seeking durability of the resin-dentin bond.