Induction of Osteogenic Differentiation of Mesenchymal Stem Cells by Bioceramic Root Repair Material

Push-out Bond Strength of Two Bioceramic Sealers after Using Various Final Irrigation Solutions: An In Vitro Study

AIM

This study assessed how different final irrigation solutions impact the push-out bond strength (PBS) of EndoSequence Bioceramic (BC) and cerafill BC sealers.

METHODS

Eighty single-root lower premolars were selected and decoronated. The root canals were then cleaned and shaped chemo-mechanically using ProTaper files up to F5, with 5.25% sodium hypochlorite applied between each file for rinsing. Subsequently, the teeth were categorized into four primary groups of 20 each, distinguished by their final irrigation solution. Group A utilized 17% glycolic acid (GA), group B used a 5% apple vinegar solution, group C employed 17% ethylenediamine tetraacetic acid (EDTA), and group D used saline. Each group was further divided into two subgroups of 10 teeth each, based on the type of BC sealer applied-Cerafill BC sealer for subgroup a, and EndoSequence BC sealer for subgroup b. Two dentin disks were then obtained from the middle third of each root (n = 20) and subjected to the PBS test. Upon completion of this test, the dentin disks were scrutinized under a stereomicroscope to determine the mode of failure for each disk.

RESULTS

The use of EndoSequence BC sealer in obturation led to the apple vinegar final irrigation group exhibiting significantly higher PBS than the GA and saline solution groups. Furthermore, when implemented with cerafill BC sealer, the EDTA final irrigation solution group displayed the greatest PBS, showing a significant difference compared with the GA and saline solution groups.

CONCLUSION

Apple vinegar solution could be a potential alternative to EDTA as a chelating agent during root canal treatment, though further research is required.

CLINICAL SIGNIFICANCE

The EDTA and apple vinegar are effective at removing smear layers, which improves sealer penetration and prevents obturation materials dislodgment. How to cite this article: Alnoury AS, Abdalwassie MK, Alawbthani MW, et al. Push-out Bond Strength of Two Bioceramic Sealers after Using Various Final Irrigation Solutions: An In Vitro Study. J Contemp Dent Pract 2024;25(12):1092-1098.

Root-filling materials for endodontic surgery: biological and clinical aspects

The placement of root filling materials aims to prevent the occurrence of post-treatment apical periodontitis following completion of endodontic treatment. Materials should possess properties that will not permit bacterial invasion and infection, namely excellent sealing ability and/or antibacterial properties. In root-end filling procedures or repair of root perforations, the root filling materials are placed in a particularly challenging clinical environment, as they interface with a relatively large area with the periradicular tissues. The biological properties of these materials are therefore of significant importance. The current review discusses the most widely used materials for endodontic surgery (i.e., root-end filling and perforation repair), with particular focus on their biological characteristics, namely antibacterial properties and interactions with host tissue cells, together with clinical studies. Properties of amalgam, glass ionomer cements (GICs), resin systems, zinc oxide eugenol-based cements and hydraulic calcium silicate cements (HCSCs), together with representative and well-researched commercial materials in the context of their use in endodontic surgery are presented. While the use of HCSCs seems to offer several biological advantages, together with addressing issues with the initial formulation in the most recent versions, materials with different chemical compositions, such as zinc oxide eugenol-based cements, are still in use and appear to provide similar clinical success rates to HCSCs. Thus, the significance of the currently available materials on clinical outcomes remains unclear.

Evaluating osteogenic potential of a 3D-printed bioceramic-based scaffold for critical-sized defect treatment: an in vivo and in vitro investigation

The integration of precision medicine principles into bone tissue engineering has ignited a wave of research focused on customizing intricate scaffolds through advanced 3D printing techniques. Bioceramics, known for their exceptional biocompatibility and osteoconductivity, have emerged as a promising material in this field. This article aims to evaluate the regenerative capabilities of a composite scaffold composed of 3D-printed gelatin combined with hydroxyapatite/tricalcium phosphate bioceramics (G/HA/TCP), incorporating human dental pulp-derived stem cells (hDPSCs). Using 3D powder printing, we created cross-shaped biphasic calcium phosphate scaffolds with a gelatin layer. The bone-regenerating potential of these scaffolds, along with hDPSCs, was assessed through in vitro analyses and in vivo studies with 60 rats and critical-sized calvarial defects. The assessment included analyzing cellular proliferation, differentiation, and alkaline phosphatase activity (ALP), and concluded with a detailed histological evaluation of bone regeneration. Our study revealed a highly favorable scenario, displaying not only desirable cellular attachment and proliferation on the scaffolds but also a notable enhancement in the ALP activity of hDPSCs, underscoring their pivotal role in bone regeneration. However, the histological examination of calvarial defects at the 12-wk mark yielded a rather modest level of bone regeneration across all experimental groups. The test and cell group exhibited significant bone formation compared to all other groups except the control and cell group. This underscores the complexity of the regenerative process and paves the way for further in-depth investigations aimed at improving the potential of the composite scaffolds.

Bioceramic versus traditional biomaterials for endodontic sealers according to the ideal properties

Odontology, as a scientific discipline, continuously collaborates with biomaterials engineering to enhance treatment characteristics and patients' satisfaction. Endodontics, a specialized field of dentistry, focuses on the study, diagnosis, prevention, and treatment of dental disorders affecting the dental pulp, root, and surrounding tissues. A critical aspect of endodontic treatment involves the careful selection of an appropriate endodontic sealer for clinical use, as it significantly influences treatment outcomes. Traditional sealers, such as zinc oxide-eugenol, fatty acid, salicylate, epoxy resin, silicone, and methacrylate resin systems, have been extensively used for decades. However, advancements in endodontics have given rise to bioceramic-based sealers, offering improved properties and addressing new challenges in endodontic therapy. In this review, a classification of these materials and their ideal properties are presented to provide evidence-based guidance to clinicians. Physicochemical properties, including sealing ability, stability over time and space, as well as biological properties such as biocompatibility and antibacterial characteristics, along with cost-effectiveness, are essential factors influencing clinicians' decisions based on individual patient evaluations.

Evaluation of the genotoxicity, cytotoxicity, and bioactivity of calcium silicate-based cements

BACKGROUND

As calcium silicate-based cements (CSCs) have found success in various vital pulp therapy applications, several new CSC products have emerged. This study aimed to assess the genotoxicity, cytotoxicity, and bioactivity of four CSCs by comparing the newly introduced materials Bio MTA+ and MTA Cem with previously studied materials, Biodentine and NeoMTA.

METHODS

Genotoxicity was evaluated using the micronucleus (MN) assay in human peripheral blood lymphocyte cells, measuring MN frequency and nuclear division index (NDI). Cytotoxicity was assessed in human dental pulp stem cells through the Water-Soluble Tetrazolium Salt-1 (WST-1) colorimetric assay. Bioactivity was determined by ELISA, measuring the levels of angiogenic and odontogenic markers (BMP-2, FGF-2, VEGF, and ALP). Statistical analyses included ANOVA, Dunnet and Sidak tests, and Wald chi-square test. (p < .05).

RESULTS

The MN frequency in the groups was significantly lower than that in the positive control group (tetraconazole) (p < .05). NDI values decreased with increasing concentration (p < .05). Bio MTA+ and NeoMTA showed decreased cell viability at all concentrations in 7-day cultures (p < .01). All materials increased BMP-2, FGF-2, and VEGF levels, with Biodentine and NeoMTA showing the highest levels of BMP-2 and FGF-2 on day 7. Biodentine displayed the highest VEGF levels on day 7. Biodentine and NeoMTA groups exhibited significantly higher ALP activity than the Bio MTA+ and MTA Cem groups by day 7.

CONCLUSION

Bio MTA+ and MTA Cem demonstrated no genotoxic or cytotoxic effects. Moreover, this study revealed bioactive potentials of Bio MTA+ and MTA Cem by enhancing the expression of angiogenic and osteogenic growth factors.

Characterisation of the Bioactivity and the Solubility of a New Root Canal Sealer

OBJECTIVES

This study aimed to analyse the effect of using phosphate buffer solution (PBS) on the solubility, pH changes, surface structure, and elemental composition of a new bioceramic Cerafill sealer compared with Endosequence sealer and AH26 resin-based sealer.

METHODS

A fresh mixture of each sealer moistened with either deionised water or PBS was subjected to a setting time test. Set discs (n = 10) were submerged in either deionised water or PBS to evaluate pH changes and solubility at 1, 7, 14, 21, and 28 days. Surface characterisation of the sealers was done before and after solubility tests using scanning electron microscopy (SEM), energy-dispersive X-ray (EDX), and Fourier transform infrared (FTIR) spectroscopy analyses.

RESULTS

An analysis of variance revealed a significant delay in setting of BC-Endosequence (P < .001) with no significant difference when each sealer was moistened with deionised water or PBS (P > .05). Both bioceramic sealers exhibited highly alkaline pH (range, 9.47-10.72). When the sealer was submerged in deionised water, Endosequence exhibited significantly greater solubility, whilst Cerafill and AH26 gained weight. When the sealers were submerged in PBS, both bioceramic sealers gained more weight, with significantly greater values for Endosequence (P < .001). Hydroxyapatite formation was revealed by SEM/EDX and FTIR.

CONCLUSIONS

PBS promoted the formation of hydroxyapatite crystals that protect the bioceramic sealers from dissolving.

Cytotoxicity and bioactive potential of new root repair materials for use with BMP-2 transfected human osteoblast cells

Modified formulations of calcium silicate repair materials with additives have been developed to enhance handling, consistency, biocompatibility and bioactivity. Considering the relevance of osteoblastic cell response to mineralized tissue repair, human osteoblastic cells (Saos-2 cells overexpressing BMP-2) were exposed to mineral trioxide aggregate (MTA) (with calcium tungstate - CaWO4), MTA HP Repair, Bio-C Repair and Bio-C Pulpo. Cell viability was assessed by 3-(4,5-dimethylthiazol)-2,5-diphenyltetrazolium bromide (MTT) and neutral red (NR), and cell death, by flow cytometry. Gene expression of bone morphogenetic protein 2 (BMP-2), runt-related transcription factor 2 (RUNX-2), and alkaline phosphatase (ALP) osteogenic markers were evaluated by real-time polymerase chain reaction (RT-qPCR). ALP activity and alizarin red staining (ARS) were used to detect mineralization nodule deposition. Bioactive cements presented no cytotoxic effect, and did not induce apoptosis at the higher dilution (1:12). MTA, Bio-C Repair and Bio-C Pulpo exhibited higher ALP activity than the control group (P < 0.05) after 7 days. MTA, MTA HP and Bio-C Pulpo affected the formation of mineralized nodules (p < 0.05). Exposure to all cement extracts for 1 day increased BMP-2 gene expression. RUNX-2 mRNA was greater in MTA, MTA HP and Bio-C Repair. MTA, MTA HP and Bio-C Pulpo increased the ALP mRNA expression, compared with BMP-2 unexposed cells (P < 0.05). Calcium silicate cements showed osteogenic potential and biocompatibility in Saos-2 cells transfected BMP-2, and increased the mRNA expression of BMP-2, RUNX-2, and ALP osteogenic markers in the BMP-2 transfected system, thereby promoting a cellular response to undertake the mineralized tissue repair.

Effects of calcium silicate-based cements on odonto/osteogenic differentiation potential in mesenchymal stem cells

The objective of this study was to evaluate the biological effects and odonto/osteogenic differentiation potential of Biodentine, NeoMTA Plus and TheraCal LC in tooth germ-derived stem cells (TGSCs). TGSCs were exposed to the material extracts. Biocompatibility was tested with MTS cell proliferation assay. Odonto/osteogenic differentiation was assessed with alkaline phosphatase (ALP) activity and mRNA gene expressions (RUNX2, DSPP and DMP-1). Scanning electronic microscopy/energy-dispersive X-ray (SEM/EDX) analysis and pH analysis were also performed for the materials. Data were evaluated using the one-way ANOVA and Tukey's tests. TGSCs remained viable after 7 days of incubation with all tested materials. Biodentine and NeoMTA Plus showed high ALP activity and increased expression of RUNX2, DSPP and DMP-1 compared to that of TheraCal LC. All materials can induce odonto/osteogenic differentiation of MSCs in various levels. Biocompatibility and odonto/osteogenic differentiation potential of Biodentine and NeoMTA Plus are similar and superior to that of TheraCal LC.

Response of periodontal ligament stem cells to lipopolysaccharide and calcium silicate-based materials

This study was conducted to assess the in vitro response of human periodontal ligament stem cells (hPDLSCs) to bacterial lipopolysaccharide (LPS) activation and application of three calcium silicate-based materials (CSBM): Bio-C Sealer, MTA Fillapex and Cimmo HP. Characterization of the CSBM was performed by FTIR (n = 3). Extracts of Bio-C Sealer, MTA Fillapex and Cimmo HP were prepared and diluted (1:1, 1:4 and 1:16). Culture of hPDLSCs was established and treated or not with LPS from Escherichia coli (1 µg/mL) for 7 days. MTT assay was used to assess cell viability at 24, 48 and 72 h (n = 9). Alkaline phosphatase (ALP) activity was indirectly assayed at day 7 (n = 5). TNF-α and Il -1 0 cytokines were quantified by ELISA at 24h-cell supernatants (n = 6). Data were analyzed by ANOVA and Tukey's test (α = 0.05). The cell viability of the LPS-activated hPDLSCs were higher than untreated control (p < 0.05). The application of CSBM affected the cell viability of untreated and LPS-activated cells (p < 0.05). ALP activity was higher for Bio-C Sealer and Cimmo HP in untreated and LPS-activated cells, respectively (p < 0.05). Application of CSBM normalized the TNF-α secretion in the LPS-activated cells (p < 0.05). Only MTA Fillapex in untreated hPDLSCs presented higher values of Il -1 0 (p < 0.05). Taken collectively, the results suggests that the simulation of the inflammatory process by LPS affect the in vitro response the hPDLSCs to the application of the CSBM.

Effect of biodentine coated with emdogain on proliferation and differentiation of human stem cells from the apical papilla

BACKGROUND

This study assessed the effect of Biodentine coated with Emdogain (Biodentine/Emdogain) on proliferation and differentiation of human stem cells from the apical papilla (SCAPs). METHODS AND RESULTS: In this in vitro, experimental study, SCAPs were isolated from two immature impacted third molars and cultured. After ensuring the stemness of the cells by assessing the cell surface markers, they were exposed to Biodentine, Emdogain, and Biodentine/Emdogain for 24 and 72 h. The control cells did not receive any intervention. Cell viability was evaluated by the methyl thiazolyl tetrazolium assay. Expression of odontogenic differentiation genes was analyzed by the quantitative reverse transcription polymerase chain reaction. Alkaline phosphatase (ALP) activity was quantified by the respective kit. Data were analyzed by one-way ANOVA, t-test, and Mann-Whitney test (α = 0.05). Cell viability did not change after 24 h of exposure to biomaterials. At 72 h, the viability of the cells exposed to Biodentine and Biodentine/Emdogain decreased compared with the control group. The expression of dentin sialophosphoprotein, dentin matrix protein 1, and bone sialoprotein genes, and ALP activity significantly increased in all three experimental groups, compared with the control group at both 24 and 72 h; this increase was significantly greater in Biodentine/Emdogain group. The number of mineralized nodules significantly increased in all groups after 72 h with a greater rate in Biodentine/Emdogain group.

CONCLUSIONS

All biomaterials increased the differentiation of SCAPs, expression of odontogenic genes, and ALP activity, but Biodentine/Emdogain was significantly more effective for this purpose.

Impact of Water Solubility on Chemical Composition and Surface Structure of Two Generations of Bioceramic Root Canal Sealers

Aimed to evaluate the effect of water solubility on chemical properties and surface structure of bioceramic-based (BC-HiFlow and BC-EndoSeqence) compared with resin-based (Adseal) root canal sealers. Fresh mix was inserted into polyethylene mold (n = 10) and subjected to Vicat needle to evaluate the setting time. The set discs were analyzed by Fourier transform infrared (FTIR) spectroscopy then immersed in deionized water for 1, 7, 14 and 28 days. The solubility%, pH changes, released calcium (Ca2+), phosphate (PO43−) and silicon (Si4+) ions were evaluated after each immersion period. The discs were analyzed by scanning electron microscopy/Energy dispersed X-ray (SEM/EDX) before and after solubility test. Although FTIR detected similar composition of both bioceramic-sealers, BC-EndoSequence determined the prolonged setting times. At the end of solubility test, both bioceramic-sealers exhibited significant greater solubility (>3%), alkaline pH (>11) at p < 0.001. Adseal displayed the significant greatest Ca2+ and PO43− released, while BC-HiFlow displayed the significant greatest Si4+ release (p < 0.001). SEM revealed voids and pores on the surface of all tested sealers with the greatest value on Adseal surface. In conclusion, although both bioceramic-sealers had high solubility, BC-Hiflow complied the ISO standard regarding setting time and least surface micropores better than that of BC-EndoSequence.

Antimicrobial and Antibiofilm Properties of Bioceramic Materials in Endodontics

Microbes are prevalent in the root canals of necrotic teeth, and they are the cause of primary and post-treatment apical periodontitis. Bacteria can dwell within the infected root canal system as surface-adherent biofilm structures, which exhibit high resistance to antimicrobial agents. Bioceramic materials, with their biocompatible nature and excellent physico-chemical properties, have been widely used in dental applications, including endodontics. This review focuses on the application of bioceramic technology in endodontic disinfection and the antibiofilm effects of endodontic bioceramic materials. Different bioceramic materials have shown different levels of antibiofilm effects. New supplements have emerged to potentially enhance the antibiofilm properties of bioceramics aiming to achieve the goal of microbial elimination in the root canal system.

Physicochemical Properties of Two Generations of MTA-Based Root Canal Sealers

This study evaluated the physicochemical properties and the effect of solubility on the surface morphology and composition of the root canal sealers MTA-Bioseal, MTA-Fillapex, and Adseal. Discs (n = 10) of freshly mixed sealer were prepared and then analyzed by Fourier transform infrared (FTIR) spectroscopy and scanning electron microscopy/energy-dispersive X-ray spectroscopy (SEM/EDX). The discs were immersed for 1, 7, 14, and 28 days in deionized water. The solubility %; pH change of the solution; and released calcium, phosphate, and silicon were measured for each period. The flowability and film thickness were also evaluated. Changes in the surface morphology and composition after 28 days of immersion were evaluated by SEM/EDX. The data were statistically analyzed by one-way ANOVA at p < 0.05. The FTIR and EDX results revealed similar compositions of MTA-Bioseal and MTA-Fillapex, but with different concentrations. The two MTA-based sealers had higher solution alkalinity (pH > 10) than Adseal (pH ≈ 8.5). MTA-Fillapex exhibited the highest solubility % and the largest calcium and silicon ion release. MTA-Bioseal had the highest phosphate ion release. After 28 days, the sealer surfaces showed large micropores, with larger pores in MTA-Fillapex. Adseal had an intermediate flowability but exhibited the greatest film thickness. Finally, the highest solubility and largest amount of silicon release was exhibited by MTA-Fillapex, which might predispose it to the development of large micropores, compromising the apical seal of obturation.

In vitro biocompatibility and bioactivity of calcium silicate‑based bioceramics in endodontics (Review)

Calcium silicate-based bioceramics have been applied in endodontics as advantageous materials for years. In addition to excellent physical and chemical properties, the biocompatibility and bioactivity of calcium silicate-based bioceramics also serve an important role in endodontics according to previous research reports. Firstly, bioceramics affect cellular behavior of cells such as stem cells, osteoblasts, osteoclasts, fibroblasts and immune cells. On the other hand, cell reaction to bioceramics determines the effect of wound healing and tissue repair following bioceramics implantation. The aim of the present review was to provide an overview of calcium silicate-based bioceramics currently applied in endodontics, including mineral trioxide aggregate, Bioaggregate, Biodentine and iRoot, focusing on their in vitro biocompatibility and bioactivity. Understanding their underlying mechanism may help to ensure these materials are applied appropriately in endodontics.

Electrical therapies act on the Ca2+ /CaM signaling pathway to enhance bone regeneration with bioactive glass [S53P4] and allogeneic grafts

This study aimed to investigate the application of low-intensity electrostimulation (ES) and electromagnetic stimulation (EM) associated with bioactive glass (BG) or allogeneic grafts (BB) in bone regeneration. A cell viability test on osteoblasts (UMR-106) was performed in the presence of BB and BG grafts associated with ES (10 μA/5 min) and EM (500 Hz/2 min). Critical defects (25 mm² ) in calvaria were generated in male Wistar rats, and bone regeneration was evaluated on the 30th, 60th, and 120th days after surgery. Cell proliferation increased with the application of ES in both grafts and after EM with BG. Bone remodeling was more effective using the allogeneic graft in both therapies, with increased angiogenesis, osteoblast proliferation, and OPN expression in the BB + EM group. A higher number of osteoblasts and osteoclasts, and an increase in bone sialoprotein, Runx-2, and Opn gene expression were found in the BB + ES group. The BG graft associated with EM therapy had an increased proliferation of osteoblasts and increased expression of Runx-2 and Opn. Groups that had BG and ES therapy had increased numbers of osteoblasts, osteoclasts, and increased OPN expression. The expression of voltage-gated calcium channels increased in groups with ES, while calmodulin expression increased in therapies without grafting. ES and EM therapies favored the repair of bone defects upon grafting by improving angiogenesis, osteogenic gene expression, and tissue reorganization. Despite activating different pathways, both therapies increased the intracellular concentrations of calmodulin, leading to cell proliferation and bone regeneration.

From a plant secretion to the promising bone grafts: Cryogels of silicon-integrated quince seed mucilage by microwave-assisted sol-gel reaction

Design and fabrication of biologically active cryogels using novel biopolymer(s) are still of great importance at regenerating bone defects such as traumatic bone injuries, maxillofacial surgery, osteomyelitis, and osteoporosis. Nowadays, plant mucilage, an herbal biomaterial, has been drawn attention by scientists due to their marvelous potential to fabricate 3-dimensional (3D) physical constructs for the field of regenerative medicine. Herein, a 3D cryogel from silicon-integrated quince seed mucilage (QSM) is constructed using microwave-assisted sol-gel reaction, characterized in-depth by attenuated total reflectance Fourier transform-infrared spectroscopy (ATR-FTIR), solid-state silicon cross-polarization magic-angle nuclear magnetic resonance (²⁹Si-CP-MAS NMR), X-ray diffraction (XRD), thermogravimetric analysis (TGA), differential scanning calorimeter (DSC), micro-mechanical testing, porosity, and swelling tests, contact angle measurements, Brunauer-Emmet-Teller and Barret-Joyner-Halenda (BET-BJH) analysis, enzymatic biodegradation test, and field emission-scanning electron microscopy-energy dispersive X-ray spectroscopy (FE-SEM-EDX) mapping. The osteobiologic capacity of the cryogels is determined using human adipose-derived mesenchymal stem cells (hAMSCs) under in vitro conditions. Osteogenic differentiation of hAMSCs on both QSM and silica-modified QSM (Si-QSM) cryogels is analyzed by histochemistry, immunohistochemistry, and quantitative-real time (q-RT) PCR techniques. The results obtained from in vitro experiments demonstrate that the upregulation of osteogenesis-related genes in Si-QSM cryogels presents a stronger and earlier development over QSM cryogels throughout the culture period, which in turn reveals the great potential of this novel Si-incorporated QSM cryogels for bone tissue engineering applications.

Biocompatibility and Bioactivity of Set Direct Pulp Capping Materials on Human Dental Pulp Stem Cells

In this study, we assessed the biocompatibility and bioactivity of various pulp capping materials—ProRoot MTA (Dentsply Tulsa Dental Specialties), Biodentine (Septodont), TheraCal LC (Bisco), and Dycal (Dentsply Caulk)—on human dental pulp stem cells (hDPSCs). Experimental disks (diameter, 7 mm; height, 4 mm) were stored in a humified incubator at 37 °C for 48 h. Then, the pulp capping materials were tested for cytotoxic effects by methyl-thiazoldiphenyl-tetrazolium and scratch wound healing assays, and for mineralization potential by Alizarin red S (ARS) staining assay and alkaline phosphatase enzyme (ALP) activity. Cell viability and cell migration did not significantly differ between ProRoot MTA, Biodentine, and control (p > 0.05). TheraCal LC exhibited slower cell migration on days 2–4 compared to control (p < 0.05), and Dycal showed no cell migration. ALP activity was highest with Biodentine on days 10 and 14, and was lowered with TheraCal LC and Dycal (p < 0.05). In the ARS assay, hDPSCs grown in ProRoot MTA and TheraCal LC eluates showed significantly increased mineralized nodule formation on day 21 compared to Biodentine, Dycal, and control (p < 0.05). These findings indicate that ProRoot MTA, Biodentine, and TheraCal LC exhibit better biocompatibility and bioactivity than Dycal.