Catalyst-free synthesis of copper oxide composites as solar radiative filters

Global popularization of CuNiO2 and their rGO nanocomposite loveabled to the photocatalytic properties of methylene blue

New advancements of photocatalytic activity with higher efficiency, low price are most important, which is challenging in industrialized and many fields. We have introduced CuNiO₂ and CuNiO₂/rGO nanocomposite was generally prepared by the hydrothermal treatment and tested to the photocatalytic studies. Photocatalytic measurements of CuNiO₂ with different weight percentages CuNiO₂/rGO (25/75), (50/50), and (75/25) are achieved to the efficiency under visible light, in this case, CuNiO₂/rGO (50/50) composite have the highest performance is scrutinized. This was obeyed for a synergistic effect between CuNiO₂ nanoparticles and rGO composites. Furthermore, the CuNiO₂, CuNiO₂/rGO (25/75), (50/50), and (75/25) nanocomposite were tested by several analyses like XRD, FT-IR, DRS UV Visible spectroscopy, Raman spectroscopy, and FESEM & HRTEM investigations. In this regard all measurements are very clear and satisfied; therefore we are encouraged for future developing environmental applications.

Rapid Fabrication of Renewable Carbon Fibres by Plasma Arc Discharge and Their Humidity Sensing Properties

Submicron-sized carbon fibres have been attracting research interest due to their outstanding mechanical and electrical properties. However, the non-renewable resources and their complex fabrication processes limit the scalability and pose difficulties for the utilisation of these materials. Here, we investigate the use of plasma arc technology to convert renewable electrospun lignin fibres into a new kind of carbon fibre with a globular and porous microstructure. The influence of arc currents (up to 60 A) on the structural and morphological properties of as-prepared carbon fibres is discussed. Owing to the catalyst-free synthesis, high purity micro-structured carbon fibres with nanocrystalline graphitic domains are produced. Furthermore, the humidity sensing characteristics of the treated fibres at room temperature (23 °C) are demonstrated. Sensors produced from these carbon fibres exhibit good humidity response and repeatability in the range of 30% to 80% relative humidity (RH) and an excellent sensitivity (0.81/%RH) in the high RH regime (60–80%). These results demonstrate that the plasma arc technology has great potential for the development of sustainable, lignin-based carbon fibres for a broad range of application in electronics, sensors and energy storage.

Calcination Strategy for Scalable Synthesis of Pithecellobium-Type Hierarchical Dual-Phase Nanostructured Cu x O to Columnar Self-Assembled CuO and Its Electrochemical Performances

The search for low-cost environmentally benign promising electrode materials for high-performance electrochemical application is an urgent need for an applaudable solution for the energy crisis. For this, the present attempt has been made to develop a scalable synthetic strategy for the preparation of pure and dual-phase copper oxide self-hybrid/self-assembled materials from a copper oxalate precursor using the calcination route. The obtained samples were characterized by means of various physicochemical analytical techniques. Notably, we found that the BET surface area and pore volume of copper oxides measured by N2 adsorption-desorption decrease with the elevation of calcination temperature. From the XRD analysis, we observed the formation of a Cu2O cubic phase at low temperatures and a CuO monoclinic phase at high temperatures (i.e., 450 and 550 °C). FTIR and RAMAN spectroscopy were employed for bonding and vibrational structure analysis. The self-assembled dual-phase copper oxide particle as a pithecellobium-type hierarchical structure was observed through SEM of the sample prepared at 350 °C. The surface morphological structure for the samples obtained at 450 and 550 °C was a bundle-like structure developed though columnar self-assembling of the particles. All the above techniques confirmed the successful formation of Cu2O/CuO nanoparticles. Afterward, the electrochemical properties of the as-synthesized copper oxides reinforced by introducing carbon black (10% wt) were explored via cyclic voltammetry, electrochemical impedance spectroscopy, and galvanometric charge-discharge analysis. The Cu2O system exhibits the maximum specific capacitance performance value of 1355 F/g, whereas in the CuO system (at 450 and 550 °C), it possesses values of 903 and 724 F/g at a scan rate of 2 mV/s. This study reveals that the electrochemical properties of Cu2O are better than those of the CuO nanoparticles, which could be ascribed to the high surface area and morphology. The present assessment of the electrochemical properties of the developed material could pave the way to a low-cost electrode material for developing other high-performance hybrid electrodes for supercapacitor or battery applications.