Effect of Substrates on the Physicochemical Properties of Li7La3Zr2O12 Films Obtained by Electrophoretic Deposition

Thin film technology of lithium-ion solid electrolytes should be developed for the creation of all-solid-state power sources. Solid electrolytes of the Li7La3Zr2O12 (LLZ) family are one of the promising membranes for all-solid-state batteries. LLZ films were obtained by electrophoretic deposition on Ti, Ni and steel substrates. The influence of different metal substrates on microstructure, phase composition and conductivity of the LLZ films after their heat treatment was studied. It was shown that the annealing of dried LLZ films in an Ar atmosphere leads to the transition from tetragonal modification to a low-temperature cubic structure. It was established that an impurity phase (Li2CO3) was not observed for LLZ films deposited on Ti foil after heat treatment, in contrast to films deposited on Ni and steel substrates. The highest lithium-ion conductivity values were achieved for the LLZ films annealed at 300 °C, 1.1 × 10-8 S cm-1 (at 100 °C) and 1.0 × 10-6 S cm-1 (at 200 °C).

Electrophoretic Deposition and Characterization of Thin-Film Membranes Li7La3Zr2O12

In the presented study, films from tetragonal Li₇La₃Zr₂O₁₂ were obtained by electrophoretic deposition (EPD) for the first time. To obtain a continuous and homogeneous coating on Ni and Ti substrates, iodine was added to the Li₇La₃Zr₂O₁₂ suspension. The EPD regime was developed to carry out the stable process of deposition. The influence of annealing temperature on phase composition, microstructure, and conductivity of membranes obtained was studied. It was established that the phase transition from tetragonal to low-temperature cubic modification of solid electrolyte was observed after its heat treatment at 400 °C. This phase transition was also confirmed by high-temperature X-ray diffraction analysis of Li₇La₃Zr₂O₁₂ powder. Increasing the annealing temperature leads to the formation of additional phases in the form of fibers and their growth from 32 (dried film) to 104 μm (annealed at 500 °C). The formation of this phase occurred due to the chemical reaction of Li₇La₃Zr₂O₁₂ films obtained by electrophoretic deposition with air components during heat treatment. The total conductivity of Li₇La₃Zr₂O₁₂ films obtained has values of ~10^-10 and ~10^-7 S cm^-1 at 100 and 200 °C, respectively. The method of EPD can be used to obtain solid electrolyte membranes based on Li₇La₃Zr₂O₁₂ for all-solid-state batteries.