Novel enhancement of interfacial interaction and properties in biodegradable polymer composites using green chemically treated spent coffee ground microfiller

This study investigates the potential of utilizing green chemically treated spent coffee grounds (SCGs) as micro biofiller reinforcement in Poly-3-hydroxybutyrate-co-3-hydroxyvalerate (PHBV) biopolymer composites. The aim is to assess the impact of varying SCG concentrations (1 %, 3 %, 5 %, and 7 %) on the functional, thermal, mechanical properties and biodegradability of the resulting composites with a PHBV matrix. The samples were produced through melt compounding using a twin-screw extruder and compression molding. The findings indicate successful dispersion and distribution of SCGs microfiller into PHBV. Chemical treatment of SCG microfiller enhanced the interfacial bonding between the SCG and PHBV, evidenced by higher water contact angles of the biopolymer composites. Field Emission Scanning Electron Microscopy (FE-SEM) confirmed the successful interaction of treated SCG microfiller, contributing to enhanced mechanical characteristics. A two-way ANOVA was conducted for statistical analysis. Mass losses observed after burying the materials in natural soil indicated that the composites degraded faster than the pure PHBV polymer suggesting that both composites are biodegradable, particularly at high levels of spent coffee grounds (SCG). Despite the possibility of agglomeration at higher concentrations, SCG incorporation resulted in improved functional properties, positioning the green biopolymer composite as a promising material for sustainable packaging and diverse applications.

Isolation and characterization of novel bioplasticizers from rose (Rosa damascena Mill.) petals and its suitability investigation for poly (butylene adipate-co-terephthalate) biofilm applications

The current growing environmental awareness has forced the use of biodegradable plasticizers, which are sustainable and abundant in plant resources. Rose petal plasticizers (RPP) act as an actual substitute for chemical plasticizers in this situation as they are biocompatible and biodegradable. Chemical procedures like amination, alkalization, and surface catalysis are used to extract the natural emollients from rose petals. XRD, FT-IR, and UV studies were used to understand the characteristics of the rose petal plasticizer. Based on the XRD data, the RPP's crystallinity size (CS) and crystallinity index (CI) values were determined to be 9.36 nm and 23.87%, respectively. The surface morphology of the isolated plasticizer is investigated using SEM, EDAX analysis and AFM. RPP surface pores with rough surfaces are visible in SEM images, which make them appropriate for plasticizing novel bioplastics with superior mechanical qualities. The plasticizer's heat degradation behaviour is investigated using thermogravimetric and differential thermogram analysis curves. Following the characterization of the synthesised molecules, the plasticization effect was examined using a biodegradable polymer matrix called poly (butylene adipate-co-terephthalate) (PBAT). The reinforcement interface was also examined using scanning electron microscopy analysis. RPP-reinforced films demonstrated greater flexibility and superior surface compatibility at a 5% loading compared to PBAT-only films. Based on a number of reported features, RPP could be a great plasticizer to address future environmental problems.

Facile exfoliation and physicochemical characterization of Thespesia populnea plant leaves based bioplasticizer macromolecules reinforced with polylactic acid biofilms for packaging applications

Plasticizers are active ingredients added to the polymer to increase its workability. Since synthetic plasticizer is not ecofriendly and toxic in nature, it is a real cause for concern. On this basis, our study focuses on plasticizer extraction from plant-based resources. In this research work, Thespesia populnea leaves are utilized for the isolation of biological macromolecules with a plasticizing effect for biofilm applications. This extraction process is done through solvent extraction, amination, slow pyrolysis, and surface catalysis process. The physico-chemical and microstructural characterization of novel plasticizer particles were studied for the first time. The lower crystallinity index and crystalline size obtained from X-ray diffraction is 50.08 % and 20.45 nm respectively. Energy dispersive spectroscopy, particle sizer analysis, atomic force microscopy, and scanning electron microscopy are used to assess surface morphology of this plasticizer. The thermogram and differential thermal analysis curves give the information about degradation behavior of plasticizers and their thermal stability. The glass transition temperature of the extracted plasticizer is 60.56 °C. The plasticizing effect of the plasticizer is studied through film fabrication of polylactic acid which was blended with the extracted plasticizer. The mechanical property of biofilm was improved with the addition of plasticizer. The elongation break percentage (for 5 % plasticizer 46.12 %) was increased compared to others with moderate tensile strength. However, the tensile and elongation modulus decreases with the increase of plasticizer content. The crystallinity of the PLA film was improved after the plasticization. The thermal stability also increased with 3 % addition of the plasticizer. The isolated plasticizer was soluble in water and its molecular weight ≈380.

Isolation and characterization of microcrystalline cellulose from an agro-waste tamarind (Tamarindus indica) seeds and its suitability investigation for biofilm formulation

The exploration of potential bio-fillers for bio-film application is a promising approach to ensure biodegradable, eco-friendly, good-quality materials with high-performance applications. This is a comprehensive study executed to establish the utility of an agro-waste Tamarindus indica seeds for microcrystalline cellulose production and to assess its feasibility for biofilm fabrication. The extraction was carried out through consecutive chemical-mediated alkalization, acid hydrolysis and bleaching. The isolated microcrystalline cellulose from Tamarindus indica seeds (TSMCC) was characterized through chemical, thermal and morphological characterization to validate the cellulose contribution, thermal resistance, and compatibility of the material. The physical parameters as density and yield percentage were assessed to evaluate its light-weight utility and economic productivity. These examinations revealed that TSMCC has good specific properties such as high cellulose content (90.57 %), average density (1.561 g/cm3), feasible average roughness (12.161 nm), desired particle size (60.40 ± 21.10 μm), good crystallinity (CI-77.6 %) and thermal stability (up to 230 °C); which are worthwhile to consider TSMCC for bio-film formulation. Subsequently, bio-films were formulated by reinforcing TSMCC in polylactic acid (PLA) matrix and the mechanical properties of the bio-films were then studied to establish the efficacy of TSMCC. It is revealed that the properties of pure PLA film increased after being incorporated with TSMCC, where 5 %TSMCC addition showed greater impact on crystalline index (26.16 % to 39.62 %), thermal stability (333oc to 389 °C), tensile strength (36.11 ± 2.90 MPa to 40.22 ± 3.22 MPa) and modulus (2.62 ± 0.55GPa to 4.15 ± 0.53GPa). In light of all promising features, 5 % TSMCC is recommended as a potential filler reinforcement for the groundwork of good quality bio-films for active packaging applications in future.

Platelet-Rich Plasma in Aesthetics

Platelet-rich plasma (PRP) is being used as a treatment modality for skin rejuvenation since the last decade. There has been a lot of ambiguity regarding the ideal protocol to be followed and the specific indications where its use should be promoted. The use of PRP as monotherapy for skin rejuvenation, acne scars, periorbital rejuvenation, lipofilling and in combination with fractional CO₂ and other resurfacing modalities is increasing rapidly. In this article, we have reviewed the current scientific evidence available and the IADVL national task force for PRP has come up with standard recommendations for use of PRP in esthetics along with the grade of evidence and strength of recommendation for each indication. The aim of this review is to provide a standard protocol for use of PRP in esthetics, for clinicians and academicians, leading to excellent results with this promising treatment modality.