Direct radiation-induced effects on dental hard tissue

Background

Radiation caries is a complication of radiotherapy characterized by enamel erosion and dentin exposure. The mechanisms of characteristic radiation caries formation are not well-understood. The aim of this study was to evaluate the direct radiation-induced effects on dental hard tissue and investigate their role in the formation of radiation caries.

Methods

Sixty non-carious third molars were divided into three groups (n = 20), which would be exposed to 0 Gy, 30 Gy, and 60 Gy radiation, respectively. After radiation, microhardness and elastic modulus were measured at four depths by means of a Vickers microhardness tester and atomic force microscopy (AFM). The microstructure was observed by scanning electron microscopy (SEM). X-ray diffraction and Raman microspectroscopy were used to determine crystal properties and protein/mineral (2931/960 cm^− 1) ratios.

Results

A statistically significant decrease in microhardness and elastic modulus values 50 μm from the dentino-enamel junction (DEJ) in enamel was revealed in the 30-Gy and 60-Gy groups. With the increasing dose, destruction of interprismatic substance and fissures at the DEJ-adjacent region were found. A greater reduction of crystallinity was revealed in enamel compared with dentin. Raman spectroscopic analysis showed a slight increase of the protein/mineral ratio for enamel following accumulated radiation, while the protein/mineral ratio for dentin was decreased.

Conclusions

Radiation could directly alter the mechanical properties, micro-morphology, crystal properties, and chemical composition of dental hard tissue. The early destruction of DEJ-adjacent enamel, combined with decreased crystallinity of enamel under radiation exposure, may be related to the formation of characteristic radiation caries.

Mesoscale porosity at the dentin-enamel junction could affect the biomechanical properties of teeth

In this paper, the 3D-morphology of the porosity in dentin is investigated within the first 350μm from the dentin-enamel junction (DEJ) by fluorescence confocal laser scanning microscopy (CLSM). We found that the porous microstructure exhibits a much more complex geometry than classically described, which may impact our fundamental understanding of the mechanical behavior of teeth and could have practical consequences for dental surgery. Our 3D observations reveal numerous fine branches stemming from the tubules which may play a role in cellular communication or mechanosensing during the early stages of dentinogenesis. The effect of this highly branched microstructure on the local mechanical properties is investigated by means of numerical simulations. Under simplified assumptions on the surrounding tissue characteristics, we find that the presence of fine branches negatively affects the mechanical properties by creating local stress concentrations. However, this effect is reduced by the presence of peritubular dentin surrounding the tubules. The porosity was also quantified using the CSLM data and compared to this derived from SEM imaging. A bimodal distribution of channel diameters was found near the DEJ with a mean value of 1.5-2μm for the tubules and 0.3-0.5μm for the fine branches which contribute to 30% of the total porosity (∼1.2%). A gradient in the branching density was observed from the DEJ towards the pulp, independently of the anatomical location. Our work constitutes an incentive towards more elaborate multiscale studies of dentin microstructure to better assess the effect of aging and for the design of biomaterials used in dentistry, e.g. to ensure more efficient bonding to dentin. Finally, our analysis of the tubular network structure provides valuable data to improve current numerical models.

Ultrastructural features of dentinoenamel junction revealed by focused gallium ion beam milling

To take full advantage of focused ion beam (FIB) in preparation of ultrathin sections of biological tissues, we have used a cryo-milling process. In this study, extracted human teeth were scanned by optical coherence tomography to inspect the samples for intactness and to determine the area of interest. Then, the selected area of interest was cross-sectioned for examination under a confocal laser scanning microscope to determine the target location of the dentinoenamel junction (DEJ) that was later milled by cryo-FIB at preset parameters, followed by transmission electron microscope examination of the final sliced specimens for ultrastructural characterization. The proposed technique was able to outline the DEJ and to identify the different tooth layers in a single section, without artefacts or tissue damage. The DEJ was outlined as fine longitudinal projections intermingling between the solid electron-dense enamel and intricate electron-lucent hollow dentin. In conclusion, this study has shown the great potential of cryo-FIB in handling different biological tissues having different physical properties, with great precision and accuracy and minimum artefacts.