Enhance the Er3+ Upconversion Luminescence by Constructing NaGdF4:Er3+@NaGdF4:Er3+ Active-Core/Active-Shell Nanocrystals

NaGdF4:12%Er3+@NaGdF4:x%Er3+ (x = 0, 6, 8, 10, and 12) active-core/active-shell nanoparticles (NPs) were peculiarly synthesized via a delayed nucleation pathway with procedures. The phase, shape, and size of the resulting core-shell NPs are confirmed by transmission electron microscopy and X-ray diffraction. Coated with a NaGdF4:10%Er3+ active shell around the NaGdF4:12%Er3+ core NPs, a maximum luminescent enhancement of about 336 times higher than the NaGdF4:12%Er3+ core-only NPs was observed under the 1540 nm excitation. The intensity ratio of green to red was adjusted through the construction of the core-shell structure and the change of Er3+ concentration in the shell. By analyzing the lifetimes of emission bands and exploring the energy transition mechanism, the giant luminescence enhancement is mainly attributed to the significant increase in the near-infrared absorption at 1540 nm and efficient energy migration from the shell to core.

Controllable synthesis and luminescent properties of rare earth doped Gd2(MoO4)3 nanoplates

For the first time, we have successfully synthesized rare-earth doped Gd₂(MoO₄)₃: RE³⁺ (RE=Eu, Tb) nanoplates by solvothermal method. The morphology of Gd₂(MoO₄)₃ can be manipulated by changing the reaction times and reaction temperatures. The composition and surface morphology have been investigated by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM), respectively. Under the excitation of UV, Photoluminescence (PL) has been used to explore the excellent luminescence properties of the synthesized nanophosphors. The Gd₂(MoO₄)₃: Eu³⁺ phosphors shows a hypersensitive red emission (612nm) when excitation wavelength within the scope of 200-350nm corresponding to a ⁵D₀-⁷F₂ transition. Similarly, the Gd₂(MoO₄)₃: Tb³⁺ phosphors certificate a highly strong green emission at 544nm at an excitation wavelength of 298nm corresponding to a ⁵D₄-⁷F₅ transition. Furthermore, the characteristic spectrum peak of the Gd₂(MoO₄)₃: Eu³⁺/Tb³⁺ nanophosphor exhibits the corresponding spectra position (green emission at 544nm and red emission at 612nm). Hence, the obtained Gd₂(MoO₄)₃: RE³⁺ nanoplates may establish highly potentiality in light field applications.