Characterization and cytotoxicity assessment of cadmium sulfide quantum dots synthesized with Fusarium oxysporum f. sp. lycopersici

The potential of CdS quantum dots for biomedical and bioimaging applications depends on their cytotoxicity, which can be modulated by coating molecules. Using sulfur as a precursor can be used along with cadmium nitrate to synthesize CdS quantum dots with the fungus Fusarium oxysporum f. sp. lycopersici. The latter replaces pure chemical sulfur as a precursor for CdS quantum dot synthesis, thus transforming waste into a value-added product, increasing sustainability, reducing the environmental impact of the process through the implementation of green synthesis techniques, and contributing to the circular economy. Therefore, we compared the cytotoxicity on HT-29 cells of biogenic, and chemical CdSQDs, synthesized by a chemical method using pure sulfur. Biogenic and chemical CdSQDs had diameters of 4.08 ± 0.07 nm and 3.2 ± 0.20 nm, Cd/S molar ratio of 43.1 and 1.1, Z-potential of - 14.77 ± 0.64 mV and - 5.52 ± 1.11 mV, and hydrodynamic diameters of 193.94 ± 3.71 nm and 152.23 ± 2.31 nm, respectively. The cell viability improved 1.61 times for biogenic CdSQDs over chemical CdSQDs, while cytotoxicity, measured as IC50, diminished 1.88-times. The lower cytotoxicity of biogenic CdSQDs was attributed to their organic coating consisting of lipids, amino acids, proteins, and nitrate groups that interacted with CdS through -OH and -SH groups. Therefore, the biogenic synthesis of CdSQDs has repurposed a pathogenic fungus, taking advantage of the biomolecules it secretes, to transform hazardous sulfur waste and metal ions into stable CdSQDs with advantageous structural and cytotoxic properties for their potential application in biomedicine and bioimaging.

Recovery of sulfur from sulfur-rich filter cakes in a rotary kiln: Process optimization

In this work, sulfur recovery from sulfur-rich wastes deriving from sulfur filtration was investigated through laboratory experiments and full-scale tests in an industrial combustion rotary kiln, where elemental sulfur is converted to SO₂ in a sulfuric acid production plant. Phase equilibria experiments carried out in the temperature range 1100-1400 °C and industrial scale tests demonstrated that temperature is the most important operating parameter in determining the recovery efficiency and the plant operability. The full-scale tests performed on the rotary kiln showed that, at operating temperatures around 1200 °C, a continuous sulfur recovery from the filter cakes was obtained with an average efficiency of 87% and a consequent reduction of about 70% of the solid waste material to be disposed as inert in landfills or used in cement/glass industries. The efficiency of sulfur recovery increases with the increasing operating temperature but, above 1300 °C, the melting of the residual Ca-Fe-Al-silicate phase and the eventual recrystallization at the kiln refractory walls occurred, causing a forced plant shutdown. The chemical-physical interaction between the sulfur-rich filter cake and different refractory materials was further investigated in the temperature range 1100-1300 °C. At the recommended operation temperatures of 1100-1200 °C, the interaction between the refractory material and the combustion ashes is negligible for all tested materials. Nonetheless, the use of Fe- and Cr-free refractory materials for the internal lining of the kiln must be preferred to minimize the deposition/adhesion of Ca-Fe-Al-silicates derived from combustion over long-term operation.