Ceramic Matrix Composites Obtained by the Reactive Sintering of Boron Carbide with Intermetallic Compounds from the Ti-Si System

In this study, we investigated the effect of adding two different intermetallics, Ti₅Si₃ and TiSi₂, for the preparation of TiB₂-SiC-B₄C composites. As part of the research, stoichiometric composites consisting only of two phases TiB₂ and SiC were obtained. The TiB₂-SiC-B₄C composites were prepared via pressureless sintering. The presence of the phases in the sintered composites was confirmed using X-ray diffraction and scanning electron microscopy. The SEM-EDS examination revealed that the TiB₂ and SiC phases were formed during the composite process synthesis and were distributed homogeneously in the B₄C matrix. The obtained results allowed us to usually exceed 2000 °C and the use of specialized equipment for firing, that is, vacuum or protective atmosphere furnaces as well as control and measurement equipment. Such an approach generates high costs that are decisive for the economics of the technological processes. In the case of our compositions, it is possible to lower the temperature to 1650 °C. The TiB₂-SiC-B₄C composites were classified as UHTCs.

Microstructure and Properties of TiB2 Composites Produced by Spark Plasma Sintering with the Addition of Ti5Si3

Titanium diboride (TiB₂) is a hard, refractory material, attractive for a number of applications, including wear-resistant machine parts and tools, but it is difficult to densify. The spark plasma sintering (SPS) method allows producing TiB₂-based composites of high density with different sintering aids, among them titanium silicides. In this paper, Ti₅Si₃ is used as a sintering aid for the sintering of TiB₂/10 wt % Ti₅Si₃ and TiB₂/20 wt % Ti₅Si₃ composites at 1600 °C and 1700 °C for 10 min. The phase composition of the initial powders and produced composites was analyzed by the X-ray diffraction method using CuK_α radiation. The microstructure was examined using scanning electron microscopy, accompanied by energy-dispersive spectroscopy (EDS). The hardness was determined using a diamond indenter of Vickers geometry loaded at 9.81 N. Friction–wear properties were tested in the dry sliding test in a ball-on-disc configuration, using WC as a counterpart material. The major phases present in the TiB₂/Ti₅Si₃ composites were TiB₂ and Ti₅Si_3. Traces of TiC were also identified. The hardness of the TiB₂/Ti₅Si₃ composites was in the range of 1860–2056 HV1 and decreased with Ti₅Si₃ content, as well as the specific wear rate W_v. The coefficient of friction for the composites was in the range of 0.5–0.54, almost the same as for TiB₂ sinters. The main mechanism of wear was abrasive.

Microstructural Characterization of Melt Extracted High-Nb-Containing TiAl-Based Fiber

The microstructure of melt extracted Ti-44Al-8Nb-0.2W-0.2B-1.5Si fiber were investigated. When the rotation speed increased from 2000 to 2600 r/min, the appearance of the wire was uniform with no Rayleigh-wave default. The structure was mainly composed of fine α₂ (α) phase dendritic crystal and a second phase between dendrite arms and grain boundaries. The precipitated second phases were confirmed to be Ti₅Si₃ from the eutectic reaction L→Ti₅Si₃ + α and TiB. As the lower content of Si and higher cooling rate, a divorced eutectic microstructure was obtained. Segregation of Ti, Nb, B, Si, and Al occurred during rapid solidification.