Aqueous-phase Selective Hydrogenation of Furfural to Furfuryl Alcohol over Ordered-mesoporous Carbon Supported Pt Catalysts Prepared by One-step Modified Soft-template Self-assembly Method

Ordered mesoporous carbon (OMC) has attracted a great deal of attention as catalyst support due to their tunable morphological and textural properties. In this study, the characteristics and catalytic properties of OMC-supported Pt catalysts prepared by one-step modified soft-template self-assembly method (Pt/OMC-one-pot) were compared to the Pt impregnated on OMC, activated carbon (AC), and non-uniform meso/macroporous carbon (MC) in the selective hydrogenation of furfural to furfuryl alcohol (FA) under mild conditions (50°C, 2 MPa H₂). Larger Pt particle size (~4 nm) was obtained on the Pt/OMC-onepot comparing to all the impregnated ones, in which the Pt particle sizes were in the range 0.5 - 2 nm. Reduction step was not necessary on the Pt/OMC-one-pot and among the catalysts studied, the Pt/OMCone-pot exhibited the highest furfural conversion and FA selectivity under aqueous conditions. The use of methanol as the solvent resulted in the formation of solvent product (2-furaldehyde dimethyl acetal) instead. The amount of Pt being deposited, location of Pt particles, and metal-support interaction strongly affected recyclability of the catalysts because some larger size Pt particles with weak metal-support interaction could be leached out during the liquid-phase reaction, rendering similar catalytic performances of the various porous carbon supported catalysts after the 3^rd cycle of run.

Effects of TiO2 structure and Co addition as a second metal on Ru-based catalysts supported on TiO2 for selective hydrogenation of furfural to FA

The TiO2 supported Ru-based catalysts were prepared with 1.5 wt% Ru and 0-0.8 wt% Co on various TiO2 (anatase, rutile, P-25, and sol-gel TiO2) and studied in the liquid-phase selective hydrogenation of furfural to furfuryl alcohol (FA) under mild conditions (50 °C and 2 MPa H2). The presence of high anatase crystallographic composition on TiO2 support was favorable for enhancing hydrogenation activity, while the strong interaction between Ru and TiO2 (Ru-TiOx sites) was required for promoting the selectivity to FA. The catalytic performances of bimetallic Ru-Co catalysts were improved with increasing Co loading due to the synergistic effect of Ru-Co alloying system together with the strong interaction between Ru and Co as revealed by XPS, H2-TPR, and TEM-EDX results. The enhancement of reducibility of Co oxides in the bimetallic Ru-Co catalysts led to higher hydrogenation activity with the Ru-0.6Co/TiO2 catalyst exhibited the best performances in FA selective hydrogenation of furfural to FA under the reaction conditions used.

Preparation of improved Ag–Pd/TiO2 catalysts using the combined strong electrostatic adsorption and electroless deposition methods for the selective hydrogenation of acetylene

Ag–Pd/TiO₂ catalysts prepared by the strong electrostatic adsorption and electroless deposition with θ_Ag 0–0.92.