Polysaccharide films built by simultaneous or alternate spray: a rapid way to engineer biomaterial surfaces

We investigated polysaccharide films obtained by simultaneous and alternate spraying of a chitosan (CHI) solution as polycation and hyaluronic acid (HA), alginate (ALG), and chondroitin sulfate (CS) solutions as polyanions. For simultaneous spraying, the film thickness increases linearly with the cumulative spraying time and passes through a maximum for polyanion/CHI molar charge ratios lying between 0.6 and 1.2. The size of polyanion/CHI complexes formed in solution was compared with the simultaneously sprayed film growth rate as a function of the polyanion/CHI molar charge ratio. A good correlation was found. This suggests the importance of polyanion/polycation complexation in the simultaneous spraying process. Depending on the system, the film topography is either liquid-like or granular. Film biocompatibility was evaluated using human gingival fibroblasts. A small or no difference is observed in cell viability and adhesion between the two deposition processes. The CHI/HA system appears to be the best for cell adhesion inducing the clustering of CD44, a cell surface HA receptor, at the membrane of cells. Simultaneous or alternate spraying of CHI/HA appears thus to be a convenient and fast procedure for biomaterial surface modifications.

Biaxial nematic order and phase behavior studies in an organosiloxane tetrapode using complementary deuterium NMR experiments

The biaxial nematic phase was recently observed in different thermotropic liquid crystals, namely bent-core compounds, side-chain polymers, bent-core dimers, and organosiloxane tetrapodes. In this work, a series of experiments with a nematic organosiloxane tetrapode where nuclear magnetic resonance (NMR) spectra are collected while the sample is continuously rotating around an axis perpendicular to the magnetic field, are discussed in conjunction with the analysis of a deuterium NMR experiment on the same system reported earlier. The sample used is a mixture of a deuterated probe with the tetrapode. The mixture exhibits a nematic range between -40 degrees C and 37 degrees C. The results of the two independent, but complementary deuterium NMR experiments confirm the existence of a biaxial nematic phase for temperatures below 0 degrees C with high values of the asymmetry parameter at low temperatures. The presence of slow movements of the tetrapode mesogenic units in the low-temperature regime could also be detected through the analysis of the NMR spectra. Simulations indicate that these movements are mainly slow molecular reorientations of the mesogenic units associated with the presence of collective modes in the nematic phases of this compound. In the case of tetrapodes, recent investigations attribute the origin of biaxiality to the hindering of reorientations of the laterally attached mesogenic units which constitute the tetrapode. This study relates the molecular movements with the nematic biaxial ordering of the system.

Deuterium NMR investigation of the biaxial nematic phase in an organosiloxane tetrapode

Deuterium NMR is used to examine the molecular order exhibited by an organosiloxane tetrapode giving the first experimental evidence, using a bulk sample, for the existence of a biaxial nematic phase in this type of compounds. The temperature dependence of the averaged quadrupolar coupling constant and asymmetry parameter was determined in the compound's nematic phase. Two distinct regimes could be identified, one with a vanishing asymmetry parameter corresponding to a uniaxial nematic phase and another with a significant temperature dependent asymmetry parameter, corresponding to a biaxial nematic phase. The high values obtained for the asymmetry parameter at the lower end of the nematic range are well above experimental error and constitute a definite proof of the biaxial nature of the nematic phase exhibited by the studied compound for those temperatures.

Complexing capsules--metal extraction and modeling of ion transfer

Polyamide complexing capsules containing a poly(acrylic acid) gel are synthesized by a two steps polymerization process with various diameters (10 microm for microcaps or 200 microm for mcaps). A cationic exchange between gel carboxylic functions and metal ions is realized. Extraction and stripping measurements show that the composition of the capsule membrane doesn't hinder the mass transfer. A model, taking account only of the diffusion in the gel phase, is studied.

Extraction of metal cations by polyterephthalamide microcapsules containing a poly(acrylic acid) gel

Polyterephthalamide microcapsules containing a poly(acrylic acid) gel as a macromolecular ligand (PAA-CAPS) were prepared using an original two step polymerization process in a water-in-oil inverse emulsion system. A polyamide microcapsule containing acrylic acid, initiator and cross-linking agent, is formed by interfacial polycondensation of terephthaloyl dichloride with hexamethylenediamine. In situ radical polymerization of the microcapsule core acrylic acid is initiated to obtain encapsulated poly(acrylic acid) gel. Reference polyamide microcapsules, i.e. without ligand (CAPS), were also synthesized. The mean diameter of synthesized microcapsules was 210 microm, and the microcapsule wall thickness was evaluated by SEM and TEM observations of microcapsule cross-section cuts. The microcapsule water content was determined by thermogravimetric experiments. The extractabilities of Cu(II), Ni(II), Co(II) and Zn(II) into PAA-CAPS were examined. The stripping of the various cations can be promoted in diluted hydrochloric acid solutions.