Biomimetic biphasic scaffolds for osteochondral defect repair

Radial extracorporeal shock wave therapy promotes osteochondral regeneration of knee joints in rabbits

Radial extracorporeal shock wave therapy (rESWT) has been proven to be effective for nonunion fractures. It was, thus, hypothesized that it may be used as a supplement therapy to promote osteochondral regeneration when combined with a scaffold previously prepared by our research group. In the present study, to verify this hypothesis, New Zealand white adult rabbits were anaesthetized and divided into three groups, as follows: Untreated control group, in which full-thickness cylindrical osteochondral defects were created without repairing; scaffold group, in which rabbits were implanted with the scaffolds; scaffold plus rESWT group, in which rabbits were implanted with scaffolds and then treated with rESWT at 2 weeks post-surgery. At 6 and 12 weeks after surgery, the animals were sacrificed. Nitric oxide (NO) levels in the synovial cavity of the knee joints were measured by the Griess method. In addition, macroscopic observation and the gross score according to the International Cartilage Repair Society (ICRS) histological scoring system were determined. Histological evaluation was also performed by hematoxylin-eosin and Safranin O/fast green staining. The results demonstrated that both the scaffold and scaffold plus rESWT treatments significantly reduced NO levels in the synovial cavity at 6 weeks after surgery (P<0.05), whereas no significant difference was observed at 12 weeks after surgery. The ICRS scores of the scaffold and scaffold plus rESWT groups were significantly higher in comparison with those in the control group (P<0.05), and rESWT further increased these scores at 12 weeks after surgery (P<0.05). Histological results revealed that osteochondral regeneration was improved after treatment with scaffold or scaffold plus rESWT, with the latter displaying better results. These data suggested that rESWT improved the osteochondral regeneration when applied in combination with the scaffold, and that one of the underlying mechanisms may involve the reduction of NO in the synovial fluid. Therefore, rESWT may be a useful treatment for knee osteochondral regeneration.

Icariin conjugated hyaluronic acid/collagen hydrogel for osteochondral interface restoration

Over the past decades, numerous tissue-engineered constructs have been investigated for the osteochondral repair. However, it still remains a challenge to regenerate the functionalized calcified layer. In this study, the potential of icariin (Ica) conjugated hyaluronic acid/collagen (Ica-HA/Col) hydrogel to promote the osteochondral interface restoration was investigated. Compared with HA/Col hydrogel, Ica-HA/Col hydrogel simultaneously facilitated chondrogenesis and osteogenesis in vitro. The cells encapsulated in Ica-HA/Col hydrogel tended to aggregate into bigger clusters. The chondrogenic genes' expression level was remarkably up-regulated, and the matrix synthesis of sGAG and type II collagen was significantly enhanced. Similarly, the osteogenic genes, including RUNX2, ALP, and OCN were also up-regulated at early stage. Consequently, more calcium deposition was observed in the Ica-HA/Col hydrogel construct. Moreover, the gene expression and matrix synthesis of type X collagen, an important marker for the formation of calcified layer; were significantly higher in the Ica-HA/Col hydrogel. Furthermore, the in vivo study showed that Ica-HA/Col constructs facilitated the reconstruction of osteochondral interface in rabbit subchondral defects. In the Ica-HA/Col group, the neo-cartilage layer contained more type II collagen and the newly formed subchondral bone deposited more abundant type I collagen. Overall, the results indicated that Ica-HA/Col hydrogel might be a promising scaffold to reconstruct an osteochondral interface, therefore promoting restoring of osteochondral defect.

STATEMENT OF SIGNIFICANCE

The osteochondral defect restoration not only involves the repair of damaged cartilage and the subchondral bone, but also the reconstruction of osteochondral interface (the functional calcified layer). The calcified layer regeneration is essential for integrative and functional osteochondral repair. Over the past decade, numerous tissue engineered constructs have been investigated for the osteochondral repair. However, it still remains a challenge to regenerate a functionalized calcified layer. The present study demonstrates that Ica-HA/Col hydrogel facilitates deposition of matrix related to calcified layer in mixed chondrogenic/osteogenic inductive media and restoration of osteochondral defect in vivo. Since, Ica-HA/Col hydrogel as is cheaper, easier and more efficient, it might be a desired scaffold for the osteochondral defects restoration.

Healing of Osteochondral Defects Implanted with Biomimetic Scaffolds of Poly(ε-Caprolactone)/Hydroxyapatite and Glycidyl-Methacrylate-Modified Hyaluronic Acid in a Minipig

Articular cartilage is a structure lack of vascular distribution. Once the cartilage is injured or diseased, it is unable to regenerate by itself. Surgical treatments do not effectively heal defects in articular cartilage. Tissue engineering is the most potential solution to this problem. In this study, methoxy poly(ethylene glycol)-block-poly(ε-caprolactone) (mPEG-PCL) and hydroxyapatite at a weight ratio of 2:1 were mixed via fused deposition modeling (FDM) layer by layer to form a solid scaffold. The scaffolds were further infiltrated with glycidyl methacrylate hyaluronic acid loading with 10 ng/mL of Transforming Growth Factor-β1 and photo cross-linked on top of the scaffolds. An in vivo test was performed on the knees of Lanyu miniature pigs for a period of 12 months. The healing process of the osteochondral defects was followed by computer tomography (CT). The defect was fully covered with regenerated tissues in the control pig, while different tissues were grown in the defect of knee of the experimental pig. In the gross anatomy of the cross section, the scaffold remained in the subchondral location, while surface cartilage was regenerated. The cross section of the knees of both the control and experimental pigs were subjected to hematoxylin and eosin staining. The cartilage of the knee in the experimental pig was partially matured, e.g., few chondrocyte cells were enclosed in the lacunae. In the knee of the control pig, the defect was fully grown with fibrocartilage. In another in vivo experiment in a rabbit and a pig, the composite of the TGF-β1-loaded hydrogel and scaffolds was found to regenerate hyaline cartilage. However, scaffolds that remain in the subchondral lesion potentially delay the healing process. Therefore, the structural design of the scaffold should be reconsidered to match the regeneration process of both cartilage and subchondral bone.

Mimicking the 3D biology of osteochondral tissue with microfluidic-based solutions: breakthroughs towards boosting drug testing and discovery

The development of tissue-engineering (TE) solutions for osteochondral (OC) regeneration has been slowed by technical hurdles related to the recapitulation of their complex and hierarchical architecture. OC defects refer to damage of both the articular cartilage and the underlying subchondral bone. To repair an OC tissue defect, the complexity of the bone and cartilage must be considered. To help achieve this, microfluidics is converging with TE approaches to provide new treatment possibilities. Microfluidics uses precise micrometer-to-millimeter-scale fluid flows to achieve high-resolution and spatial and/or temporal control of the cell microenvironment, providing powerful tools for cell culturing. Herein, we overview the progress of microfluidics for developing 3D in vitro models of OC tissue, with a focus on cancer bone metastasis.

The unique calcium chelation property of poly(vinyl phosphonic acid-co-acrylic acid) and effects on osteogenesis in vitro

There is a clear clinical need for a bioactive bone graft substitute. Poly(vinyl phosphonic acid-co-acrylic acid) (PVPA-co-AA) has been identified as a promising candidate for bone regeneration but there is little evidence to show its direct osteogenic effect on progenitor or mature cells. In this study mature osteoblast-like cells (SaOS-2) and human bone marrow-derived mesenchymal stem cells (hBM-MSCs) were cultured with PVPA-co-AA polymers with different VPA:AA ratio and at different concentrations in vitro. We are the first to report the direct osteogenic effect of PVPA-co-AA polymer on bone cells and, more importantly, this effect was dependent on VPA:AA ratio and concentration. Under the optimized conditions, PVPA-co-AA polymer not only has an osteoconductive effect, enhancing SaOS-2 cell mineralization, but also has an osteoinductive effect to promote hBM-MSCs' osteogenic differentiation. Notably, the same PVPA-co-AA polymer at different concentrations could lead to differential osteogenic effects on both SaOS-2 and hBM-MSCs in vitro. This study furthers knowledge of the PVPA-co-AA polymer in osteogenic studies, which is critical when utilizing the PVPA-co-AA polymer for the design of novel bioactive polymeric tissue engineering scaffolds for future clinical applications. © 2017 The Authors Journal of Biomedical Materials Research Part A Published by Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 168-179, 2018.

Isolation and characterization of human mesenchymal stem cells derived from synovial fluid by magnetic-activated cell sorting (MACS)

Mesenchymal stem cells (MSCs) are the primary source of cells used for cell-based therapy in tissue engineering. MSCs are found in synovial fluid, a source that could be conveniently used for cartilage tissue engineering. However, the purification and characterization of SF-MSCs has been poorly documented in the literature. Here, we outline an easy-to-perform approach for the isolation and culture of MSCs derived from human synovial fluid (hSF-MSCs). We have successfully purified hSF-MSCs using magnetic-activated cell sorting (MACS) using the MSC surface marker, CD90. Purified SF-MSCs demonstrate significant renewal capacity following several passages in culture. Furthermore, we demonstrated that MACS-sorted CD90⁺ cells could differentiated into osteoblasts, adipocytes, and chondrocytes in vitro. In addition, we show that these cells can generate cartilage tissue in micromass culture as well. This study demonstrates that MACS is a useful tool that can be used for the purification of hSF-MSCs from synovial fluid. The proliferation properties and ability to differentiate into chondrocytes make these hSF-MSCs a promising source of stem cells for applications in cartilage repair.

Creating hierarchical porosity hydroxyapatite scaffolds with osteoinduction by three-dimensional printing and microwave sintering

Hierarchical porosity, which includes micropores and macropores in scaffolds, contributes to important multiple biological functions for tissue regeneration. This paper introduces a two-step method of combining three-dimensional printing (3DP) and microwave sintering to fabricate two-level hierarchical porous scaffolds. The results showed that 3D printing made the macroporous structure well-controlled and microwave sintering generated micropores on the macropore surface. The resulting hierarchical macro/microporous hydroxyapatite scaffold induced bone formation following intramuscular implantation. Moreover, when comparing the hierarchical macro/microporous hydroxyapatite scaffold to the non-osteoinductive hydroxyapatite scaffolds (either 3D printed or H₂O₂ foamed) subjected to muffle sintering which do not have micropores, the critical role of micropores in material-driven bone formation was shown. The findings presented herein could be useful for the further optimization of bone grafting materials for bone regeneration.

Collagen-based porous scaffolds containing PLGA microspheres for controlled kartogenin release in cartilage tissue engineering

A scaffold composed of different collagen (COL)/chitosan (CS)/hyaluronic acid sodium (HAS) salt ratios was evaluated by determining porosity, swelling, loss rate in hot water, mechanical property, and cell proliferation to obtain optimum conditions for manufacturing porous scaffolds. Results showed that the optimal ratio of COL/CS/HAS salt porous scaffold was 1:1:0.1. High swelling and loss rate of scaffolds/microspheres (MPs) could lead to high diffusion rate of MPs from the scaffolds, causing an increase in the kartogenin (KGN) release. The porous scaffolds at optimum conditions had a maximum amount of KGN release. Results of in vitro fluorescence staining and cell proliferation suggested that scaffolds/MPs had good biocompatibility and the capability to promote bone marrow stromal cell proliferation, cartilage tissue regeneration, and integration between the repaired and surrounding cartilages. Therefore, this composite could be a promising material for cartilage repair and regeneration, which could be effective in the knee osteoarthritis treatment.

Clinical and imaging outcome of osteochondral lesions of the talus treated using autologous matrix-induced chondrogenesis technique with a biomimetic scaffold

BACKGROUND

The purpose of our study was to assess the clinical and imaging outcome of autologous matrix-induced chondrogenesis (AMIC) technique consisting of microfractures followed by the filling of osteochondral lesions of the talus (OLTs) with a cell-free biphasic collagen-hydroxyapatite osteochondral scaffold (MaioRegen).

METHODS

Sixteen patients (eight males, age: 42.6 ± 18.4, range 14-74) with OLT repaired using AMIC technique, with implantation of MaioRegen, were clinically evaluated through the American Orthopedic Foot and Ankle Society Score (AOFAS) and a 10-point Visual Analogue Scale (VAS) pain score after a mean follow-up of 30 ± 16.9 months. The MRI examinations were performed 12 and 24 months after surgery. A paired t-test was applied to compare pre- and post-operative clinical findings (VAS and AOFAS) and Magnetic resonance observation of cartilage repair tissue (MOCART) score changes in the follow-up. To assess the correlation between variation of AOFAS and MOCART scores, the Pearson's correlation coefficient was calculated.

RESULTS

No complications after surgery were encountered. From pre-operative to post-operative values, there was a significant (P < 0.001) reduction of mean VAS pain score (6.3 ± 0.9,range: 4-8 and 2.9 ± 1.8,range: 0-6, respectively) and increase of AOFAS score (60.2 ± 7.8,range: 50-74 and 77.4 ± 16.2,range: 50-100, respectively). Among 16 patients, six (37%) were not satisfied at the end of follow-up, six (37%) were moderately satisfied and four (25%) were highly satisfied. The treatment was considered failed in five out of 16 patients (31%). Among them, four (25%) required re-interventions with implantation of ankle prostheses, whereas one patient was treated with a further AMIC technique combined with autologous bone graft and platelet-rich plasma. The mean MOCART score was 41.9 ± 14.6 (25-70) 12 months after surgery and 51.9 ± 11.6 (30-70) after 24 months, with a statistically significant increase (P = 0.012). However, no correlation was seen between AOFAS and MOCART changes (r = 0.215, p = 0.609).

CONCLUSION

The high rates of treatment failure encountered in our study using MaioRegen need to be confirmed by larger studies and should induce the scientific community questioning the reliability of this biomimetic scaffold for the treatment of OLTs.

Directing the osteoblastic and chondrocytic differentiations of mesenchymal stem cells: matrix vs. induction media

While both induction culture media and matrix have been reported to regulate the stem cell fate, little is known about which factor plays a more decisive role in directing the MSC differentiation lineage as well as the underlying mechanisms. To this aim, we seeded MSCs on HA-collagen and HA-synthetic hydrogel matrixes, which had demonstrated highly different potentials toward osteoblastic and chondrocytic differentiation lineages, respectively, and cultured them with osteogenic, chondrogenic and normal culture media, respectively. A systematic comparison has been carried out on the effects of induction media and matrix on MSC adhesion, cytoskeleton organization, proliferation, and in particular differentiation into the osteoblastic and chondrocytic lineages. The results demonstrated that the matrix selection had a much more profound effect on directing the differentiation lineage than the induction media did. The strong modulation effect on the transcription activities might be the critical factor contributing to the above observations in our study, where canonical Wnt-β-Catenin signal pathway was directly involved in the matrix-driven osteoblastic differentiation. Such findings not only provide a critical insight on natural cellular events leading to the osteoblastic and chondrocytic differentiations, but also have important implications in biomaterial design for tissue engineering applications.

Silk-Hydroxyapatite Nanoscale Scaffolds with Programmable Growth Factor Delivery for Bone Repair

Osteoinductive biomaterials are attractive for repairing a variety of bone defects, and biomimetic strategies are useful toward developing bone scaffolds with such capacity. Here, a multiple biomimetic design was developed to improve the osteogenesis capacity of composite scaffolds consisting of hydroxyapatite nanoparticles (HA) and silk fibroin (SF). SF nanofibers and water-dispersible HA nanoparticles were blended to prepare the nanoscaled composite scaffolds with a uniform distribution of HA with a high HA content (40%), imitating the extracellular matrix (ECM) of bone. Bone morphogenetic protein-2 (BMP-2) was loaded in the SF scaffolds and HA to tune BMP-2 release. In vitro studies showed the preservation of BMP-2 bioactivity in the composite scaffolds, and programmable sustained release was achieved through adjusting the ratio of BMP-2 loaded on SF and HA. In vitro and in vivo osteogenesis studies demonstrated that the composite scaffolds showed improved osteogenesis capacity under suitable BMP-2 release conditions, significantly better than that of BMP-2 loaded SF-HA composite scaffolds reported previously. Therefore, these biomimetic SF-HA nanoscaled scaffolds with tunable BMP-2 delivery provide preferable microenvironments for bone regeneration.

Additive manufacturing and mechanical characterization of graded porosity scaffolds designed based on triply periodic minimal surface architectures

Since the advent of additive manufacturing techniques, triply periodic minimal surfaces have emerged as a novel tool for designing porous scaffolds. Whereas scaffolds are expected to provide multifunctional performance, spatially changing pore patterns have been a promising approach to integrate mechanical characteristics of different architectures into a unique scaffold. Smooth morphological variations are also frequently seen in nature particularly in bone and cartilage structures and can be inspiring for designing of artificial tissues. In this study, we carried out experimental and numerical procedures to uncover the mechanical properties and deformation mechanisms of linearly graded porosity scaffolds for two different mathematically defined pore structures. Among TPMS-based scaffolds, P and D surfaces were subjected to gradient modeling to explore the mechanical responses for stretching and bending dominated deformations, respectively. Moreover, the results were compared to their corresponding uniform porosity structures. Mechanical properties were found to be by far greater for the stretching dominated structure (P-Surface). For bending dominated architecture (D-Surface), although there was no global fracture for uniform structures, graded structure showed a brittle fracture at 0.08 strain. A layer by layer deformation mechanism for stretching dominated structure was observed. For bending dominated scaffolds, deformation was accompanied by development of 45° shearing bands. Finite element simulations were also performed and the results showed a good agreement with the experimental observations.

Thermogel-Coated Poly(ε-Caprolactone) Composite Scaffold for Enhanced Cartilage Tissue Engineering

A three-dimensional (3D) composite scaffold was prepared for enhanced cartilage tissue engineering, which was composed of a poly(ε-caprolactone) (PCL) backbone network and a poly(lactide-co-glycolide)-block-poly(ethylene glycol)-block-poly(lactide-co-glycolide) (PLGA⁻PEG⁻PLGA) thermogel surface. The composite scaffold not only possessed adequate mechanical strength similar to native osteochondral tissue as a benefit of the PCL backbone, but also maintained cell-friendly microenvironment of the hydrogel. The PCL network with homogeneously-controlled pore size and total pore interconnectivity was fabricated by fused deposition modeling (FDM), and was impregnated into the PLGA⁻PEG⁻PLGA solution at low temperature (e.g., 4 °C). The PCL/Gel composite scaffold was obtained after gelation induced by incubation at body temperature (i.e., 37 °C). The composite scaffold showed a greater number of cell retention and proliferation in comparison to the PCL platform. In addition, the composite scaffold promoted the encapsulated mesenchymal stromal cells (MSCs) to differentiate chondrogenically with a greater amount of cartilage-specific matrix production compared to the PCL scaffold or thermogel. Therefore, the 3D PCL/Gel composite scaffold may exhibit great potential for in vivo cartilage regeneration.

Stereocomplex-Reinforced PEGylated Polylactide Micelle for Optimized Drug Delivery

The instability of PEGylated polylactide micelles is a challenge for drug delivery. Stereocomplex interaction between racemic polylactide chains with different configurations provides an effective strategy to enhance the stability of micelles as the nanocarriers of drugs. In this work, a stereocomplex micelle (SCM) self-assembled from the amphiphilic triblock copolymers comprising poly(ethylene glycol) (PEG), and dextrorotatory and levorotatory polylactides (PDLA and PLLA) was applied for efficient drug delivery. The spherical SCM showed the smallest scale and the lowest critical micelle concentration (CMC) than the micelles with single components attributed to the stereocomplex interaction between PDLA and PLLA. 10-Hydroxycamptothecin (HCPT) as a model antitumor drug was loaded into micelles. Compared with the loading micelles from individual PDLA and PLLA, the HCPT-loaded SCM exhibited the highest drug loading efficiency (DLE) and the slowest drug release in phosphate-buffered saline (PBS) at pH 7.4, indicating its enhanced stability in circulation. More fascinatingly, the laden SCM was demonstrated to have the highest cellular uptake of HCPT and suppress malignant cells most effectively in comparison to the HCPT-loaded micelles from single copolymer. In summary, the stereocomplex-enhanced PLA⁻PEG⁻PLA micelle may be promising for optimized drug delivery in the clinic.

Kartogenin-Incorporated Thermogel Supports Stem Cells for Significant Cartilage Regeneration

Recently, cartilage tissue engineering (CTE) attracts increasing attention in cartilage defect repair. In this work, kartogenin (KGN), an emerging chondroinductive nonprotein small molecule, was incorporated into a thermogel of poly(L-lactide-co-glycolide)-poly(ethylene glycol)-poly(L-lactide-co-glycolide) (PLGA-PEG-PLGA) to fabricate an appropriate microenvironment of bone marrow mesenchymal stem cells (BMSCs) for effective cartilage regeneration. More integrative and smoother repaired articular surface, more abundant characteristic glycosaminoglycans (GAGs) and collagen II (COL II), and less degeneration of normal cartilage were obtained in the KGN and BMSCs coloaded thermogel group in vivo. In conclusion, the KGN-loaded PLGA-PEG-PLGA thermogel can be utilized as an alternative support for BMSCs to regenerate damaged cartilage in vivo.