Nanoconfinement effects of chemically reduced graphene oxide nanoribbons on poly(vinyl chloride)

Melt Rheology and Mechanical Characteristics of Poly(Lactic Acid)/Alkylated Graphene Oxide Nanocomposites

Poly(lactic acid) (PLA) nanocomposites were synthesized by a solution blending and coagulation method using alkylated graphene oxide (AGO) as a reinforcing agent. Turbiscan confirmed that the alkylation of GO led to enhanced compatibility between the matrix and the filler. The improved dispersity of the filler resulted in superior interfacial adhesion between the PLA chains and AGO basal plane, leading to enhanced mechanical and rheological properties compared to neat PLA. The tensile strength and elongation at break, i.e., ductility, increased by 38% and 42%, respectively, at the same filler content nanocomposite (PLA/AGO 1 wt %) compared to nonfiller PLA. Rheological analysis of the nanocomposites in the molten state of the samples was performed to understand the filler network formed inside the matrix. The storage modulus increased significantly from PLA/AGO 0.5 wt % (9.6 Pa) to PLA/AGO 1.0 wt % (908 Pa). This indicates a percolation threshold between the two filler contents. A steady shear test was performed to examine the melt flow characteristics of PLA/AGO nanocomposites at 170 °C, and the viscosity was predicted using the Carreau-Yasuda model.

Hierarchically Nanoporous 3D Assembly Composed of Functionalized Onion-Like Graphitic Carbon Nanospheres for Anode-Minimized Li Metal Batteries

Despite the recent attention for Li metal anode (LMA) with high theoretical specific capacity of ≈3860 mA h g^-1 , it suffers from not enough practical energy densities and safety concerns originating from the excessive metal load, which is essential to compensate for the loss of Li sources resulting from their poor coulombic efficiencies (CEs). Therefore, the development of high-performance LMA is needed to realize anode-minimized Li metal batteries (LMBs). In this study, high-performance LMAs are produced by introducing a hierarchically nanoporous assembly (HNA) composed of functionalized onion-like graphitic carbon building blocks, several nanometers in diameter, as a catalytic scaffold for Li-metal storage. The HNA-based electrodes lead to a high Li ion concentration in the nanoporous structure, showing a high CE of ≈99.1%, high rate capability of 12 mA cm^-2 , and a stable cycling behavior of more than 750 cycles. In addition, anode-minimized LMBs are achieved using a HNA that has limited Li content (≈0.13 mg cm^-2 ), corresponding to 6.5% of the cathode material (commercial NCM622 (≈2 mg cm^-2 )). The LMBs demonstrate a feasible electrochemical performance with high energy and power densities of ≈510 Wh kg_electrode ^-1 and ≈2760 W kg_electrode ^-1 , respectively, for more than 100 cycles.

Carbon Nanotube Reinforced Strong Carbon Matrix Composites

As an excellent candidate for lightweight structural materials and nonmetal electrical conductors, carbon nanotube reinforced carbon matrix (CNT/C) composites have potential use in technologies employed in aerospace, military, and defense endeavors, where the combinations of light weight, high strength, and excellent conductivity are required. Both polymer infiltration pyrolysis (PIP) and chemical vapor infiltration (CVI) methods have been widely studied for CNT/C composite fabrications with diverse focuses and various modifications. Progress has been reported to optimize the performance of CNT/C composites from broad aspects, including matrix densification, CNT alignment, microstructure control, and interface engineering, etc. Recent approaches, such as using resistance heating for PIP or CVI, contribute to the development of CNT/C composites. To deliver a timely and up-to-date overview of CNT/C composites, we have reviewed the most recent trends in fabrication processes, summarized the mechanical reinforcement mechanism, and discussed the electrical and thermal properties, as well as relevant case studies for high-temperature applications. Conclusions and perspectives addressing future routes for performance optimization are also presented. Hence, this review serves as a rundown of recent advances in CNT/C composites and will be a valuable resource to aid future developments in this field.

Anode-Free Sodium Metal Batteries Based on Nanohybrid Core-Shell Templates

Anode-free sodium metal batteries (AF-SMBs) can deliver high energy and enormous power, but their cycle lives are still insufficient for them to be practical as a power source in modern electronic devices and/or grid systems. In this study, a nanohybrid template based on high aspect-ratio silver nanofibers and nitrogen-rich carbon thin layers as a core-shell structure is designed to improve the Coulombic efficiency (CE) and cycling performance of AF-SMBs. The catalytic nanohybrid templates dramatically reduce the voltage overshooting caused by metal nucleation to one-fifth that of a bare Al foil electrode (≈6 mV vs ≈30 mV), and high average CE values of >99% are achieved over a wide range of current rates from 0.2 to 8 mA cm^-2 . Moreover, exceptionally long cycle lives for more than 1600 cycles and an additional 1500 cycles are achieved with a highly stable CE of >99.9%. These results show that AF-SMBs are feasible with the nanohybrid electrode system.

Adsorption-assisted transport of water vapour in super-hydrophobic membranes filled with multilayer graphene platelets

The effects of confinement of multilayer graphene platelets in hydrophobic microporous polymeric membranes are here examined. Intermolecular interactions between water vapour molecules and nanocomposite membranes are envisaged to originate assisted transport of water vapour in membrane distillation processes when a suitable filler-polymer ratio is reached. Mass transport coefficients are estimated under different working conditions, suggesting a strong dependence of the transport on molecular interactions. Remarkably, no thermal polarization is observed, although the filler exhibits ultrahigh thermal conductivity. In contrast, enhanced resistance to wetting as well as outstanding mechanical and chemical stability meets the basic requirements of water purification via membrane distillation. As a result, a significant improvement of the productivity-efficiency trade-off is achieved with respect to the pristine polymeric membrane when low amounts of platelets are confined in spherulitic-like PVDF networks.