Criteria for the selection of restoration materials

Comparative Evaluation of the Effect of Implant Crown Materials on Implant Components and Bone Stress Distribution: A 3D Finite Element Analysis

Background

Choosing implant crown materials for restoration remains challenging in clinical practice. This study assesses the impact of all-ceramic restoration instead of porcelain-fused-to-metal (PFM) restoration on the stress distribution within implant components and the surrounding bone.

Methods

Four 3D models of a mandibular second premolar were meticulously prepared. The study groups comprised zirconia, lithium disilicate, and zirconia lithium silicate monolithic ceramic crowns cemented onto a zirconia hybrid abutment. A PFM crown cemented onto a cementable abutment was chosen as the control group. A total vertical load of 583 N was applied to the occlusal contact areas. Stress distribution within the crown and implant components was analyzed using von Mises stress analysis. Principal stress analyses were employed to assess stress distribution in the peripheral bone.

Results

The PFM model exhibited the highest von Mises stress values for both the implant (428.7 MPa) and crown (79.7 MPa) compared to the other models. The all-ceramic models displayed the highest maximum von Mises stress within the abutment, approximately 335 MPa, compared to the PFM model. von Mises stresses of the abutment and implant in the all-ceramic models were 69% higher and 20% lower, respectively, than those in the PFM model. Screw stresses were relatively consistent across all groups. Principal stresses in spongy bone and minimum principal stress in cortical bone were consistent across all models.

Conclusions

All-ceramic restoration with a hybrid abutment, as opposed to traditional PFM restoration with a cementable abutment, does not adversely affect the implant and abutment screw and reduces crown stresses. Stresses within hybrid abutments were notably higher than those within cementable abutments. Spongy bone stresses remained unaffected by the type of crown or abutment.

Impact of Smokeless Tobacco on the Color Stability of Zirconia, Zirconia-Reinforced Lithium Silicate and Feldspathic CAD/CAM Restorative Materials: An In-Vitro Study

WHO estimates that the global number of tobacco users exceeds 1.3 billion people. Few studies have examined the effect of locally made smokeless tobacco (ST) products on the color changes of material used in dental prosthetics. Bearing the recent advances in CAD/CAM ceramic restorations material in mind, this study aimed to assess ST influence on mean color change (∆E*) values among selected CAD/CAM ceramic types: multilayer zirconia (Ceramill Zolid PS), zirconia-reinforced lithium silicate ceramic (Vita Suprinity), and feldspathic (Vita TriLuxe) restorative materials. The color changes of the ceramics were compared to VITA classical and VITA 3D-MASTER shade guides. Sixty CAD/CAM ceramic specimens (20 samples each) were fabricated from Ceramill Zolid PS, Vita TriLuxe Forte, and VITA Suprinity. Specimens were prepared and divided into two groups according to the ST type and immersed for two weeks. Basic VITA classical and VITA 3D-MASTER colors were recorded at a baseline of one week and two weeks. The highest ∆E* values were recorded in the black ST for Vita Suprinity (4.77) in the first week, followed by Vita TriLuxe (4.07) in the second week. For white ST, Vita TriLuxe (4.87), and Vita Suprinity (4.42) showed extensive color change after two weeks and one week, respectively. The color change was least in zirconia for black and white ST after one week. CAD/CAM ceramic materials showed no significant difference after 1 and 2 weeks for the tested ST types. The effects of ST on CAD/CAM ceramic material (∆E* values) were high but did not reach clinically unacceptable values. Zirconia showed the least amount of color change among all the tested materials.

Technical and Biological Complications of Screw-Retained (CAD/CAM) Monolithic and Partial Veneer Zirconia for Fixed Dental Prostheses on Posterior Implants Using a Digital Workflow: A 3-Year Cross-Sectional Retrospective Study

Objective

The introduction of CAD/CAM and the development of zirconia-based restorations have allowed clinicians to use less expensive materials and faster manufacturing procedures. The purpose of the study was to analyze the differences, in terms of mechanical and biological complication, in multiunit zirconia fixed dental prosthesis (FPDs) on posterior implants produced using a digital workflow. Method and Materials. This study was a retrospective investigation, and patients treated with screw-retained monolithic or partial veneer FPDs on dental implants were selected. Periapical radiographs were taken at baseline and at the 3-year follow-up. Complications were recorded and classified as technical and biological ones.

Results

The study population included 25 patients. The occlusal and interproximal corrections were not clinically significant. In the study sample, the survival rate and success rate of the FPDs after 3 years were 100% and 96%, respectively. One implant failed immediately after placement.

Conclusion

Monolithic zirconia FPDs and partial veneer FPDs showed a 100% survival rate, presenting an interesting alternative to metal ceramic restorations. The partial veneer FPDs had a higher technical complication rate than the monolithic FPDs; however, no statistically significant difference was found.

Effects of Khat on Surface Roughness and Color of Feldspathic and Zirconia Porcelain Materials under Simulated Oral Cavity Conditions

Background and Objectives: Khat chewing is considered as a daily habit that is practiced by more than five million people globally. The effect of khat chewing on the surface roughness and the color stability of natural teeth and the material used in the fabrication of dental prosthesis remains unknown. This study was conducted to explore and compare the effect of khat homogenate (KH) on the surface roughness (Ra) and the average color changes (ΔE*) amongst natural teeth and selected shades from different porcelain types, namely, feldspathic metal ceramic (MC) VM13, computer-aided design/computer assisted manufacture (CAD/CAM) feldspathic (Vitablocs Mark II), and multilayer zirconia (Ceramill Zolid PS) porcelains. Materials and Methods: Seventy samples were prepared from natural teeth, feldspathic MC, CAD/CAM Vitablocs Mark II, and zirconia porcelain. The Ra values were measured using a profilometer and expressed in micrometers, whereas the ΔE* values were measured using VITA Easyshade^® V spectrophotometer for all samples before and after frequent immersion and thermocycling in KH for 30 days. The surface topography was used to assess the materials surfaces (glazed or polished) after KH immersion by using a white light interferometry machine. Results: Results revealed that the Ra and the ΔE* values of the different types of tested porcelain were influenced by KH. The order of surface roughness values was glazed or polished MC > polished Zircon > polished Vitablocs Mark II > natural teeth. The lowest ΔE* values were recorded for glazed Vitablocs Mark II and MC, and the values could be arranged as polished zircon > natural teeth > glazed zircon > polished MC > polished Vitablocs Mark II. P values were significantly varied (<0.001) among all the tested groups, except the zircon group (>0.05) for both Ra and ΔE*. Conclusions: KH significantly affected both surface parameter and color of glazed or polished porcelain materials and natural teeth.