Mechanism and characterization of microplastic aging process: A review

Exploring the hidden environmental pollution of microplastics derived from bioplastics: A review

Bioplastics might be an ecofriendly alternative to traditional plastics. However, recent studies have emphasized that even bioplastics can end up becoming micro- and nano-plastics due to their degradation under ambient environmental conditions. Hence, there is an urgent need to assess the hidden environmental pollution caused by bioplastics. However, little is known about the evolutionary trends of bibliographic data, degradation pathways, formation, and toxicity of micro- and nano-scaled bioplastics originating from biodegradable polymers such as polylactic acid, polyhydroxyalkanoates, and starch-based plastics. Therefore, the prime objective of the current review was to investigate evolutionary trends and the latest advancements in the field of micro-bioplastic pollution. Additionally, it aims to confront the limitations of existing research on microplastic pollution derived from the degradation of bioplastic wastes, and to understand what is needed in future research. The literature survey revealed that research focusing on micro- and nano-bioplastics has begun since 2012. This review identifies novel insights into microbioplastics formation through diverse degradation pathways, including photo-oxidation, ozone-induced degradation, mechanochemical degradation, biodegradation, thermal, and catalytic degradation. Critical research gaps are identified, including defining optimal environmental conditions for complete degradation of diverse bioplastics, exploring micro- and nano-bioplastics formation in natural environments, investigating the global occurrence and distribution of these particles in diverse ecosystems, assessing toxic substances released during bioplastics degradation, and bridging the disparity between laboratory studies and real-world applications. By identifying new trends and knowledge gaps, this study lays the groundwork for future investigations and sustainable solutions in the realm of sustainable management of bioplastic wastes.

New insights into the size-independent bioactive potential of pristine and UV-B aged polyethylene microplastics

The present study investigates the morphological, physicochemical, and structural changes occurred by the UV-B aging process of low-density polyethylene microplastics (LDPE MPs), as well as the bioactive potential of both pristine and UVaged MPs towards healthy peripheral blood lymphocytes. Specifically, LDPE MPs (100-180 μm) prepared by mechanical milling of LDPE pellets, were UV-B irradiated for 120 days (wavelength 280 nm; temperature 25 °C; relative humidity 50 %) and further examined for alterations in their particle size and surface, their functional groups, thermal stability, and crystallinity (by means of SEM, FTIR spectroscopy, XRD patterns, and TGA measurements, respectively). In parallel, isolated human peripheral blood lymphocytes were treated with different concentrations (25-500 μg mL-1) of either pristine or aged MPs (UVfree and UV120d LDPE MPs) for assessing the cytogenotoxic (by means of trypan blue exclusion test and the cytokinesis-block micronucleus assay using cytochalasin-B) and oxidative effects (using the DCFH-DA staining) in both cases. According to the results, UVfree and UV120d-LDPE MPs, with a size ranging from 100 to 180 μm, can differentially promote cytogenotoxic and oxidative alterations in human lymphocytes. In fact, UVfree LDPE MPs not being able to be internalized by cells due to their size, could indirectly promote the onset of mild oxidative and cytogenotoxic damage in human peripheral lymphocytes, via a dose-dependent but size-independent manner. The latter is more profound in case of the irregular-shaped UV120d-LDPE MPs, bearing improved dispersibility and sharp edges (by means of cracks and holes), as well as oxygen-containing and carbonyl groups. To our knowledge, the present findings provide new data regarding the bioactive behavior of pristine and UV-B aged LDPE MPs, at least in the in vitro biological model tested, thus giving new evidence for their size-independent and/or indirect mode of action.

Thermal aging of polystyrene microplastics within mussels (Mytilus coruscus) under boiling and drying processing

Aged microplastics (MPs) in the environment are a growing concern due to their higher ecological toxicity compared to pristine MPs. While previous studies have explored aging behaviors of MPs under various stress conditions, little is known about their aging during food processing. In this study, we investigated the effects of different thermal food processing methods on the aging of polystyrene (PS) MPs within mussels. We subjected the mussels containing PS MPs to boiling, boiling/solar drying, boiling/hot air drying, and boiling/microwave drying treatments, all of which are common preservation methods used in industry. We analyzed the particle size, surface morphology, yellowing, crystallinity, chemical groups, and hydrophilicity of the PS MPs to understand the aging process. Results show that all processing methods led to aging of PS MPs, with boiling/microwave drying having the most significant impact, followed by boiling/hot air drying, boiling/solar drying, and boiling alone. The aged PS MPs exhibited smaller size, morphological changes, reduced crystallinity, increased yellowness index and carbonyl index, higher presence of O-containing groups, and enhanced hydrophilicity. These findings provide evidence of MPs aging during thermal food processing and emphasize the potential risks associated with this pathway.

Various additive release from microplastics and their toxicity in aquatic environments

Additives may be present in amounts higher than 50% within plastic objects. Additives in plastics can be gradually released from microplastics (MPs) into the aquatic environment during their aging and fragmentation because most of them do not chemically react with the polymers. Some are known to be hazardous substances, which can cause toxicity effects on organisms and pose ecological risks. In this paper, the application of functional additives in MPs and their leaching in the environment are first summarized followed by their release mechanisms including photooxidation, chemical oxidation, biochemical degradation, and physical abrasion. Important factors affecting the additive release from MPs are also reviewed. Generally, smaller particle size, light irradiation, high temperature, dissolved organic matter (DOM) existence and alkaline conditions can promote the release of chemicals from MPs. In addition, the release of additives is also influenced by the polymer's structure, electrolyte types, as well as salinity. These additives may transfer into the organisms after ingestion and disrupt various biological processes, leading to developmental malformations and toxicity in offspring. Nonetheless, challenges on the toxicity of chemicals in MPs remain hindering the risk assessment on human health from MPs in the environment. Future research is suggested to strengthen research on the leaching experiment in the actual environment, develop more techniques and analysis methods to identify leaching products, and evaluate the toxicity effects of additives from MPs based on more model organisms. The work gives a comprehensive overview of current process for MP additive release in natural waters, summarizes their toxicity effects on organisms, and provides recommendations for future research.

Molecular mechanisms and physiological responses of rice leaves co-exposed to submicron-plastics and cadmium: Implication for food quality and security

The effects of co-exposure to aged submicron particles (aSMPs) and Cd as model contaminants on rice leaves via the foliar route were investigated. Thirty-day-old rice seedlings grown in soil were exposed to Cd (nitrate) through foliar spraying at concentrations of 1, 10, 50, 100, and 500 μM, with or without aSMP at a rate of 30 μg d-1. It was observed that Cd translocated from leaves to roots via stems even without co-exposure to SMP. Co-exposure can reduce cadmium levels in leaves. Laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS) analysis confirmed a significant reduction (29.3 - 77.9%) in Cadmium accumulation in the leaves of rice plants during co-exposure. Exposure to Cd resulted in physiological, transcriptomic, and metabolomic changes in rice leaves, disrupting 28 metabolism pathways, and impacting crop yield and quality. Exposure to both Cd and aSMPs can interfere with the Cd distribution in plants. Rice leaves exposed solely to Cd exhibit higher toxicity and Cd accumulation, compared to those co-exposed to Cd and aSMPs. The accumulation of Cd in plant leaves is enhanced with aSMPs, which may lead to more pronounced gene expression regulation and changes in metabolic pathways, compared to Cd exposure. Our study found that the independent Cd exposure group had higher Cd accumulation and toxicity in rice leaves compared to the combined exposure of Cd and aSMPs. We hypothesize that aged negatively charged SMPs can capture Cd and reduce its exposure in the free state while jointly inhibiting Cd-induced oxidative and chloroplast damage, thereby reducing the potential risk of Cd exposure in rice plants.

Comprehensive understanding of the aging and biodegradation of polystyrene-based plastics

The extensive utilization and inadequate handling of plastics have resulted in severe environmental ramifications. In particular, plastics composed solely of a carbon-carbon (C-C) backbone exhibit limited degradation due to the absence of hydrolyzable functional groups. Plastics with enduring longevity in the natural environment are susceptible to environmental factors and their intrinsic properties, subsequently undergoing a series of aging processes that culminate in biodegradation. This article focuses on polystyrene (PS), which constitutes 20% of total plastic waste, as a case study. Initially, the application of PS in life and the impacts it poses are introduced. Following that, the key factors influencing the aging of PS are discussed, primarily encompassing its properties (e.g., surface characteristics, additives) and environmental factors (e.g., water matrices, biofilms). Lastly, an overview of microbial degradation of PS is provided, including potential microorganisms involved in PS degradation (bacteria, fungi, algae, and insects), four processes of microbial degradation (colonization, bio-fragmentation, assimilation, and mineralization), and potential mechanisms of microbial degradation. This study provides a comprehensive understanding of the multifaceted influences affecting the aging and biodegradation mechanisms of PS, thereby contributing valuable insights for the future management of plastic pollution.

Mulch-derived microplastic aging promotes phthalate esters and alters organic carbon fraction content in grassland and farmland soils

Agricultural plastic mulch is a major microplastics (MPs) source in terrestrial ecosystems. However, knowledge about the aging characteristics of mulch-derived MPs entering natural and agricultural soils and their effects on phthalate esters (PAEs) and organic carbon fractions is still limited. Black (contains black masterbatches) and white polyethylene (PE) and biodegradable (Bio, Poly propylene carbonate and Polybutylene adipate terephthalate synthetic material (PPC+PBAT)) mulch-derived MPs, at 0.3% (w/w) dose, were added to grassland and farmland soils for eight-week incubation. Microplastic (MP) aging degree was explored by quantifying the carbonyl index (CI). The soil PAEs and organic carbon fractions were also analyzed. After incubation, black and white PE-MP aged greater in farmland than in grassland. PAEs accumulated highest in PE-MP treatment (5.27-6.41 mg kg-1) followed by Bio-MP (1.88-2.38 mg kg-1). Soil organic carbon (SOC), particulate organic carbon (POC), and microbial biomass carbon (MBC) were reduced by 5.3%-8.2%, 31.8%-41.6%, and 39.7%-63.0%, dissolved organic carbon (DOC) was increased by 10.1%-27.6% in grassland containing MP compared to control. MPs' aging degree promoted PAEs content or altered nutrients, then regulated soil microbial biomass and extracellular enzyme activity directly or indirectly, ultimately affecting SOC. ENVIRONMENTAL IMPLICATION: Microplastics are persistent environmental pollutants that gradually undergo surface aging in response to extracellular enzymes secreted by microorganisms. As microplastics age, their surface roughness and functional groups change; thus, organochemical contaminants gradually leach out. Therefore, this study analyzed the aging of mulch film-derived microplastics under the action of diverse microorganisms in farmland and grassland soils and the effect on plasticizer and organic carbon fractions. The results proved that polyethylene microplastic aging degree was highest in farmland soil. Besides, biodegradable microplastic caused lower contamination of phthalate esters than polyethylene, but they affected soil carbon balance in grassland and farmland soils. STATEMENT OF ENVIRONMENTAL IMPLICATION: This study highlights that MPs affect organic carbon fractions by influencing the PAEs, available nutrients, and extracellular enzyme activity.

Phthalate acid ester release from microplastics in water environment and their comparison between single and competitive adsorption

The ability of microplastics (MPs) to adsorb environmental pollutants has been extensively studied. However, little is known about the ability of MPs to release inherent additives and the interaction between them. This paper explored the effects of environmental factors on the release of phthalic acid esters (PAEs) from three different types of microplastics (polyethylene microplastics (PE-MPs), polypropylene microplastics (PP-MPs), and polystyrene microplastics (PS-MPs)) by simulating water environments, as well as the differences in the adsorption of one or more PAEs by MPs. The results showed that the types of MPs, single environmental factors, and combined environmental factors had a great influence on the release of di(2-ethylhexyl) phthalate (DEHP). In the influence of a single environmental factor, the releasing amount of DEHP increased significantly. When the pH value increased from 5 to 9, the release of three PAEs from all MPs decreased. Moreover, under the combined influence of three environmental factors, the DEHP release from PP-MPs was most affected by environmental factors, and the order of influence of the three environmental factors was ionic strength > organic matter > pH. The DEHP release of PS-MPs was the highest (0.058 ± 0.023 μg/L), followed by PP-MPs (0.038 ± 0.010 μg/L) and PE-MPs (0.035 ± 0.008 μg/L). Adsorption kinetics and isotherm fitting showed that the adsorption process of the three MPs was suitable for the pseudo-second-order kinetic model, and the Freundlich adsorption isotherm had a higher fitting degree. Compared with single adsorption, the competitive adsorption of three PAEs increased the adsorption capacity of DEHP and decreased the adsorption capacity of dibutyl phthalate (DBP) and diisobutyl phthalate (DIBP). These findings help predict the potential of MPs to release toxic additives under different environmental conditions.

Ecotoxicity of micro- and nanoplastics on aquatic algae: Facts, challenges, and future opportunities

The production of plastic has exponentially increased in recent years, leading to the release of millions of tons of plastic waste into the environment annually. This waste can break down into smaller micro- and nanoplastics (MNPs) that are toxic and reactive to life forms, including humans. MNPs are particularly concerning for marine biologists and environmental scientists due to their toxic impacts on aquatic organisms, including algae, which are the foundation of the food chain. The review provides a comprehensive overview of the (eco)toxicity assessment of MNPs on aquatic algal communities, highlighting the novel insights gained into the ecotoxicity of various MNPs on algae and the associated health risks for aquatic ecosystems, food chains, and humans. This article also discusses current challenges and future research opportunities to address these challenges, making it a valuable contribution to the field of environmental science. Overall, this work is one of the first efforts to comprehensively assess the effects of MNPs on aquatic algae, emphasizing the significant risks that MNPs pose to essential ecosystems and human health.

Microplastics - Back to Reality: Impact of Pristine and Aged Microplastics in Soil on Earthworm Eisenia fetida under Environmentally Relevant Conditions

Recently, studies have highlighted the potential danger for soil organisms posed by film-derived microplastics (MPs). However, the majority of those does not accurately reflect the field conditions and the degree of MP contamination that can be found in actual settings. To fill the gap between laboratory and field scenarios, the polyethylene (PE) plastic film was made into PE-MPs and aged. Toxicity and molecular mechanisms of pristine PE-MPs (PMPs) and aged PE-MPs (AMPs) with the concentration at 500 mg/kg of dry weight were determined after 14 days of exposure by measuring the oxidative stress, osmoregulation pressure, gut microbiota, and metabolic responses in earthworms under environmentally relevant conditions. Our research showed that, when compared to PMPs (13.13 ± 1.99 items/g), AMPs accumulated more (16.19 ± 8.47 items/g), caused more severe tissue lesions, and caused a higher increase of cell membrane osmotic pressure in earthworms' intestines. Furthermore, the proportion of probiotic bacteria Lactobacillus johnsonii in the gut bacterial communities was 24.26%, 23.26%, and 12.96%, while the proportion of pathogenic bacteria of the phylum Verrucomicrobia was 2.28%, 4.79%, and 10.39% in the control and PMP- and AMP-exposed earthworms, indicating that the decrease in number of probiotic bacteria and the increase in number of pathogenic bacteria were more pronounced in the gut of AMP- rather than PMP-exposed earthworms. Metabolomic analysis showed that AMP exposure reduced earthworm energy metabolites. Consequently, the constant need for energy may result in protein catabolism, which raises levels of some amino acids, disturbs normal cell homeostasis, causes changes of cell membrane osmolarity, and destroys the cell structure. Our studies showed that aged MPs, with the same characteristics as those found in the environment, have greater toxicity than pristine MPs. The results of this study broaden our understanding of the toxicological effects of MPs on soil organisms under environmentally relevant conditions.

Using Data-Driven Methods and Aging Information to Quantitatively Identify Microplastic Environmental Sources and Establish a Comprehensive Discrimination Index

The global distribution of microplastics (MPs) across various environmental compartments has garnered significant attention. However, the differences in the characteristics of MPs in different environments remain unclear, and there is still a lack of quantitative analysis of their environmental sources. In addition, the inclusion of aging in source apportionment is a novel approach that has not been widely explored. In this study, we conducted a meta-analysis of the literature from the past 10 years and extracted conventional and aging characteristic data of MPs from 321 sampling points across 7 environmental compartments worldwide. We established a data-driven analysis framework using these data sets to identify different MP communities across environmental compartments, screen key MP features, and develop an environmental source analysis model for MPs. Our results indicate significant differences in the characteristics of MP communities across environments. The key features of differentiation were identified using the LEfSe method and include the carbonyl index, hydroxyl index, fouling index, proportions of polypropylene, white, black/gray, and film/sheet. These features were screened for each environmental compartment. An environmental source identification model was established based on these features with an accuracy of 75.1%. In order to accurately represent the single/multisource case in a more probabilistic manner, we proposed the MP environmental source index (MESI) to provide a probability estimation of the sample having multiple sources. Our findings contribute to a better understanding of MP migration trends and fluxes in the plastic cycle and inform effective prevention and control strategies for MP pollution.

Effect of Aging on Physicochemical Properties and Size Distribution of PET Microplastic: Influence on Adsorption of Diclofenac and Toxicity Assessment

Microplastics (MPs) are detected in the water, sediments, as well as biota, mainly as a consequence of the degradation of plastic products/waste under environmental conditions. Due to their potentially harmful effects on ecosystems and organisms, MPs are regarded as emerging pollutants. The highly problematic aspect of MPs is their interaction with organic and inorganic pollutants; MPs can act as vectors for their further transport in the environment. The objective of this study was to investigate the effects of ageing on the changes in physicochemical properties and size distribution of polyethylene terephthalate (PET), as well as to investigate the adsorption capacity of pristine and aged PET MPs, using pharmaceutical diclofenac (DCF) as a model organic pollutant. An ecotoxicity assessment of such samples was performed. Characterization of the PET samples (bottles and films) was carried out to detect the thermooxidative aging effects. The influence of the temperature and MP dosage on the extent of adsorption of DCF was elucidated by employing an empirical modeling approach using the response surface methodology (RSM). Aquatic toxicity was investigated by examining the green microalgae Pseudokirchneriella subcapitata. It was found that the thermooxidative ageing process resulted in mild surface changes in PET MPs, which were reflected in changes in hydrophobicity, the amount of amorphous phase, and the particle size distribution. The fractions of the particle size distribution in the range 100-500 μm for aged PET are higher due to the increase in amorphous phase. The proposed mechanisms of interactions between DCF and PET MPs are hydrophobic and π-π interactions as well as hydrogen bonding. RSM revealed that the adsorption favors low temperatures and low dosages of MP. The combination of MPs and DCF exhibited higher toxicity than the individual components.