Experimental Studies of Thermophysical Properties and Microstructure of X37CrMoV5-1 Hot-Work Tool Steel and Maraging 350 Steel

Characterization of the Polyetheretherketone Weldment Fabricated via Rotary Friction Welding

Polyether ether ketone (PEEK) is frequently employed in biomedical engineering due to its biocompatibility. Traditionally, PEEK manufacturing methods involve injection molding, compression molding, additive manufacturing, or incremental sheet forming. Few studies have focused on rotational friction welding (RFW) with PEEK plastics. Based on years of RFW practical experience, the mechanical properties of the weldment are related to the burn-off length. However, few studies have focused on this issue. Therefore, the main objective of this study is to assess the effects of burn-off length on the mechanical properties of the welded parts using PEEK polymer rods. The welding pressure can be determined by the rotational speed according to the proposed prediction equation. The burn-off length of 1.6 mm seems to be an optimal burn-off length for RFW. For the rotational speed of 1000 rpm, the average bending strength of the welded parts was increased from 108 MPa to 160 Mpa, when the burn-off length was increased from 1 mm to 1.6 mm and the cycle time of RFW was reduced from 80 s to 76 s. A saving in the cycle time of RFW of about 5% can be obtained. The bending strength of the welded part using laser welding is lower than that using RFW, because only the peripheral material of the PEEK cylinder was melted by the laser.

Rotary Friction Welding of Dissimilar Polymer Rods Containing Metal Powder

Three-dimensional printing is widely used for manufacturing a variety of functional components. However, the 3D printing machine substantially limits the size of the functional components. Rotary friction welding (RFW) is a possible solution to this problem. In addition, there is a notable scarcity of research directed toward the domain knowledge of RFW involving dissimilar polymer rods containing metal powder. In this study, two welding specimens fabricated by polylactic acid (PLA)-containing copper powder and PLA-containing aluminum powder were joined using a turning machine. After RFW, a bending test and a Shore A surface hardness test were performed to investigate the weld quality. It was found that the bending strength of the welded parts fabricated by RFW of PLA and PLA-containing Al powder rods can be enhanced by about 57.5% when the welded part is placed at 45 °C. Surface hardness test results showed that the surface hardness of the weld interface is better than that of the 3D printed parts, and the average surface hardness of the weld interface from RFW of PLA and PLA is the highest. The surface hardness of the weld joint is about 3% higher than that of the base material. The surface hardness of the heat-affected zone is about 3% lower than that of the base material. The average peak temperature of the welded joint is the highest in the RFW of PLA-containing Al powder and PLA-containing Al powder rods. The average peak temperature of the weld joint can be as high as 160 °C. The average peak temperature of the welded joint is the highest in the RFW of PLA-containing Cu powder and PLA-containing Cu powder rods. The average peak temperature of the welded joint can be as high as 144 °C. A technical database was built for the selection of ambient temperatures used for the RFW of dissimilar polymer rods containing metal powder and three base materials.