Poly(Acrylic Acid)-Sodium Alginate Superabsorbent Hydrogels Synthesized by Electron Beam Irradiation Part I: Impact of Initiator Concentration and Irradiation Dose on Structure, Network Parameters and Swelling Properties

In the present paper, hydrogels based on acrylic acid (20%), sodium alginate (0.5%) and poly(ethylene oxide) (0.1%) were obtained by electron beam irradiation at room temperature with doses between 5 and 20 kGy, using potassium persulfate in concentrations up to 0.3% as a reaction initiator. The influence of initiator concentration and irradiation dose on hydrogel network parameters, swelling and deswelling behavior, gelation and degradation points, structure and morphology were investigated. Cross-link density increased with the irradiation dose and initiator addition, except at 20 kGy. The gel fraction was over 87.0% in all cases. Swelling experiments in distilled water showed swelling degrees of 40,000% at an irradiation dose of 5 kGy when a concentration of 0.1% initiator was added. A relationship between the swelling degree and irradiation dose, cross-linking degree (that increases from 0.044 × 10² to 0.995 × 10² mol/cm³) and mesh size (that decreases from about 220 nm to 26 nm) was observed. The addition of only 0.1% of PP led to the obtaining of hydrogels with a swelling degree of 42,954% (about 430 g/g) at an irradiation dose of 5 kGy and of 7206% (about 62 g/g) at 20 kGy, which are higher percentages than those obtained in the same irradiation conditions but without PP.

NaAlg-g-AA Hydrogels: Candidates in Sustainable Agriculture Applications

Nowadays, the degradation of agricultural soil due to various factors should be a major concern for everyone. In this study, a new sodium alginate-g-acrylic acid-based hydrogel was developed simultaneously by cross-linking and grafting with accelerated electrons to be used as soil remediation. The effect of irradiation dose and NaAlg contents on the gel fraction, network and structural parameters, sol-gel analysis, swelling power, and swelling kinetics of NaAlg-g-AA hydrogels have been investigated. It was demonstrated that NaAlg hydrogels show significative swelling power that is greatly dependent on their composition and irradiation dose; they keep the structure and are not degraded in different pH conditions and different water sources. Diffusion data revealed a non-Fickian transport mechanism (0.61-0.99) also specific to cross-linked hydrogels. The prepared hydrogels were proved as excellent candidates in sustainable agriculture applications.

Degradation by Electron Beam Irradiation of Some Elastomeric Composites Sulphur Vulcanized

Composites based on natural rubber and plasticized starch obtained by the conventional method of sulfur cross-linking using four types of vulcanization accelerators (Diphenyl guanidine, 2-Mercaptobenzothiazole, N-Cyclohexyl-2-benzothiazole sulfenamide, and Tetramethylthiuram disulfide) were irradiated with an electron beam in the dose range of 150 and 450 kGy for the purpose of degradation. The vulcanization accelerators were used in different percentages and combinations, resulting in four mixtures with different potential during the cross-linking process (synergistic, activator, or additive). The resulting composites were investigated before and after irradiation in order to establish a connection between the type of accelerator mixture, irradiation dose, and composite properties (gel fraction, cross-linking degree, water absorption, mass loss in water and toluene, mechanical properties, and structural and morphological properties). The results showed that the mixtures became sensitive at the irradiation dose of 300 kGy and at the irradiation dose of 450 kGy, and the consequences of the degradation processes were discussed.

Degradation by Electron Beam Irradiation of Some Composites Based on Natural Rubber Reinforced with Mineral and Organic Fillers

Composites based on natural rubber reinforced with mineral (precipitated silica and chalk) and organic (sawdust and hemp) fillers in amount of 50 phr were obtained by peroxide cross-linking in the presence of trimethylolpropane trimethacrylate and irradiated by electron beam in the dose range of 150 and 450 kGy with the purpose of degradation. The composites mechanical characteristics, gel fraction, cross-linking degree, water uptake and weight loss in water and toluene were evaluated by specific analysis. The changes in structure and morphology were also studied by Fourier Transform Infrared Spectroscopy and Scanning Electron Microscopy. Based on the results obtained in the structural analysis, possible mechanisms specific to degradation are proposed. The increasing of irradiation dose to 450 kGy produced larger agglomerated structures, cracks and micro voids on the surface, as a result of the degradation process. This is consistent with that the increasing of irradiation dose to 450 kGy leads to a decrease in crosslinking and gel fraction but also drastic changes in mechanical properties specific to the composites’ degradation processes. The irradiation of composites reinforced with organic fillers lead to the formation of specific degradation compounds of both natural rubber and cellulose (aldehydes, ketones, carboxylic acids, compounds with small macromolecules). In the case of the composites reinforced with mineral fillers the degradation can occur by the cleavage of hydrogen bonds formed between precipitated silica or chalk particles and polymeric matrix also.

Water Absorption Kinetics in Composites Degraded by the Radiation Technique

Rubber-based wastes represent challenges facing the global community. Human health protection and preservation of environmental quality are strong reasons to find more efficient methods to induce degradation of latex/rubber products in order to replace devulcanization, incineration, or simply storage, and electron beam irradiation is a promising method that can be can be taken into account. Polymeric composites based on natural rubber and plasticized starch in amounts of 10 to 50 phr, obtained by benzoyl peroxide cross-linking, were subjected to 5.5 MeV electron beam irradiation in order to induce degradation, in the dose range of 150 to 450 kGy. A qualitative study was conducted on the kinetics of water absorption in these composites in order to appreciate their degradation degree. The percentages of equilibrium sorption and mass loss after equilibrium sorption were found to be dependent on irradiation dose and amount of plasticized starch. The mechanism of water transport in composites was studied not only through the specific absorption and diffusion parameters but also by the evaluation of the diffusion, intrinsic diffusion, permeation, and absorption coefficients.

A Method to Improve the Characteristics of EPDM Rubber Based Eco-Composites with Electron Beam

A natural fiber reinforced composite, belonging to the class of eco composites, based on ethylene-propylene-terpolymer rubber (EPDM) and wood wastes were obtained by electron beam irradiation at 75, 150, 300, and 600 kGy in atmospheric conditions and at room temperature using a linear accelerator of 5.5 MeV. The sawdust (S), in amounts of 5 and 15 phr, respectively, was used to act as a natural filler for the improvement of physical and chemical characteristics. The cross-linking effects were evaluated through sol-gel analysis, mechanical tests, and Fourier Transform Infrared FTIR spectroscopy comparatively with the classic method with dibenzoyl peroxide (P) applied on the same types of samples at high temperature. Gel fraction exhibits values over 98% but, in the case of P cross-linking, is necessary to add more sawdust (15 phr) to obtain the same results as in the case of electron beam (EB) cross-linking (5 phr/300 kGy). Even if the EB cross-linking and sawdust addition have a reinforcement effect on EPDM rubber, the medium irradiation dose of 300 kGy looks to be a limit to which or from which the properties of the composite are improved or deteriorated. The absorption behavior of the eco-composites was studied through water uptake tests.

New Type of Sodium Alginate-g-acrylamide Polyelectrolyte Obtained by Electron Beam Irradiation: Characterization and Study of Flocculation Efficacy and Heavy Metal Removal Capacity

The goals of the paper were first the obtainment and characterization of sodium alginate-g-acrylamide polyelectrolytes by electron beam irradiation in the range of 0.5 to 2 kGy, and second, the evaluation of flocculation efficacy and heavy metal removal capacity from aqueous solutions of known concentrations. Based on sodium alginate concentration, two types of grafted polymers were obtained. Physical, chemical, and structural investigations were performed. Flocculation studies under different stirring conditions on 0.5, 0.1 and 0.2% kaolin suspension were done. The removal capacity of Cu2+ and Cr6+ ions was also investigated. The acrylamide grafting ratio on sodium alginate backbone was found up to 2000% for samples containing 1% sodium alginate and up to 500% for samples containing 2% sodium alginate. Transmittances between 98 and 100% were obtained using, in the flocculation studies, polyelectrolytes containing 2% sodium alginate in concentrations of 0.5 and 1 ppm on kaolin suspension of 0.1 wt %. The polymer concentration was found critical for kaolin suspension of 0.05 and 0.1 wt %. Polymers containing 1% sodium alginate were efficient in Cr6+ ion removal, while those containing 2% in Cu2+ ion removal.

Effects of Electron Beam Irradiation on the Mechanical, Thermal, and Surface Properties of Some EPDM/Butyl Rubber Composites

The effects of electron beam irradiation on the properties of ethylene propylene diene monomer (EPDM)/butyl rubber composites in presence of a polyfunctional monomer were investigated by means of differential scanning calorimetry (DSC), thermal analysis, scanning electron microscopy (SEM), attenuated total reflection absorption infrared spectroscopy (ATR-IR), and mechanical and surface energy measurements. The samples were exposed over a wide range of irradiation doses (20⁻150 kGy). The EPDM matrix was modified with butyl rubber, chlorobutyl rubber, and bromobutyl rubber. The gel content and crosslink density were found to increase with the electron beam irradiation dose. The values of the hardness and modulus increased gradually with the irradiation dose, while the tensile strength and elongation at break decreased with increasing irradiation dose. The EPDM/butyl rubber composites presented a higher thermal stability compared to the initial EPDM sample. The incorporation of butyl rubbers into the EPDM matrix led to an increase in material hydrophobicity. A similar trend was observed when the irradiation dose increased. The greatest change in the surface free energy and the contact angles occurs at an irradiation dose of 20 kGy. The Charlesby⁻Pinner plots prove the tendency to crosslinking as the irradiation dose increases.

Degradation Studies Realized on Natural Rubber and Plasticized Potato Starch Based Eco-Composites Obtained by Peroxide Cross-Linking

The obtaining and characterization of some environmental-friendly composites that are based on natural rubber and plasticized starch, as filler, are presented. These were obtained by peroxide cross-linking in the presence of a polyfunctional monomer used here as cross-linking co-agent, trimethylolpropane trimethacrylate. The influence of plasticized starch amount on the composites physical and mechanical characteristics, gel fraction and cross-link density, water uptake, structure and morphology before and after accelerated (thermal) degradation, and natural (for one year in temperate climate) ageing, was studied. Differences of two orders of magnitude between the degradation/aging methods were registered in the case of some mechanical characteristics, by increasing the plasticized starch amount. The cross-link density, water uptake and mass loss were also significant affected by the plasticized starch amount increasing and exposing for one year to natural ageing in temperate climate. Based on the results of Fourier Transform Infrared Spectroscopy (FTIR) and cross-link density measurements, reaction mechanisms attributed to degradation induced by accelerated and natural ageing were done. SEM micrographs have confirmed in addition that by incorporating a quantity of hydrophilic starch amount over 20 phr and by exposing the composites to natural ageing, and then degradability can be enhanced by comparing with thermal degradation.

The Composition of Essential Oils Obtained from Achillea millefolium and Matricaria chamomilla L., Originary from Romania

In the present study we have investigated the chemical composition of the essential oils extracted by the procedure of hydrodistillation, from fresh flowers of Matricaria Chamomilla L. and Achillea Millefolium from Romania, two genres belonging to the same family, Asteraceae. The obtained essential oils were analyzed using the techniques of Gas Chromatography coupled with Mass Spectrometer and Fourier Transform Infrared Spectroscopy. It was found that both essential oils were dominated by the presence of terpenes. Aliphatic components were modest represented in both essential oils. The results were compared with those reported by other authors. Similarities consist in the domination of the same class of compounds and in the same modest representation of others. One of differences consists in the presence of some compounds with significant medicinal role, which were not reported by other authors. Another difference consists in the presence of some compounds in higher concentrations than those reported by other authors.

Development and Characterization of Polymer Eco-Composites Based on Natural Rubber Reinforced with Natural Fibers

Natural rubber composites filled with short natural fibers (flax and sawdust) were prepared by blending procedure and the elastomer cross-linking was carried out using benzoyl peroxide. The microbial degradation of composites was carried out by incubating with Aspergillus niger recognized for the ability to grow and degrade a broad range of substrates. The extent of biodegradation was evaluated by weight loss and cross-linking degree study of composites after 2 months incubation in pure shake culture conditions. Scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FT-IR) have proved to be precious and valuable instruments for morphological as well as structural characterization of the composites before and after incubation with Aspergillus niger.

Hydrogels Synthesized by Electron Beam Irradiation for Heavy Metal Adsorption

Poly(acrylamide co-acrylic acid) hydrogels were prepared by free-radical copolymerization of acrylamide and acrylic acid in aqueous solutions using electron beam irradiation in the dose range of 2.5 kGy to 6 kGy in atmospheric conditions and at room temperature. The influence of the absorbed dose, the amount of cross-linker (trimethylolpropane trimethacrylate) and initiator (potassium persulfate) on the swelling properties and the diffusion coefficient and network parameters of hydrogels were investigated. The structure and morphology of hydrogels were characterized by Fourier Transform Infrared Spectroscopy (FTIR) and Scanning Electron Microscopy (SEM). The use of the obtained hydrogels by the removal of Cu²⁺ and Cr⁶⁺ from aqueous solutions was investigated at room temperature. During the adsorption of metal ions on hydrogels, the residual metal ion concentration in the solution was measured by an atomic absorption spectrophotometer (AAS). It has been established that the use of a relatively small amount of trimethylolpropane trimethacrylate for hydrogel preparation has led to the increasing of swelling up to 8500%.

New Elastomeric Materials Based on Natural Rubber Obtained by Electron Beam Irradiation for Food and Pharmaceutical Use

The efficiency of polyfunctional monomers as cross-linking co-agents on the chemical properties of natural rubber vulcanized by electron beam irradiation was studied. The following polyfunctional monomers were used: trimethylolpropane-trimethacrylate, zinc-diacrylate, ethylene glycol dimethacrylate, triallylcyanurate and triallylisocyanurate. The electron beam treatment was done using irradiation doses in the range of 75 kGy-300 kGy. The gel fraction, crosslink density and effects of different aqueous solutions, by absorption tests, have been investigated as a function of polyfunctional monomers type and absorbed dose. The samples gel fraction and crosslink density were determined on the basis of equilibrium solvent-swelling measurements by applying the modified Flory-Rehner equation for tetra functional networks. The absorption tests were done in accordance with the SR ISI 1817:2015 using distilled water, acetic acid (10%), sodium hydroxide (1%), ethylic alcohol (96%), physiological serum (sodium chloride 0.9%) and glucose (glucose monohydrate 10%). The samples structure and morphology were investigated by Fourier Transform Infrared Spectroscopy and Scanning Electron Microscopy techniques.

Wood Sawdust/Natural Rubber Ecocomposites Cross-Linked by Electron Beam Irradiation

The obtaining and characterization of some polymeric eco-composites based on wood sawdust and natural rubber is presented. The natural rubber was cross-linked using the electron beam irradiation. The irradiation doses were of 75, 150, 300 and 600 kGy and the concentrations of wood sawdust were of 10 and 20 phr, respectively. As a result of wood sawdust adding, the physical and mechanical properties such as hardness, modulus at 100% elongation and tensile strength, showed significant improvements. The presence of wood sawdust fibers has a reinforcing effect on natural rubber, similar or better than of mineral fillers. An increase in the irradiation dose leads to the increasing of cross-link density, which is reflected in the improvement of hardness, modulus at 100% elongation and tensile strength of blends. The cross-linking rates, appreciated using the Flory-Rehner equation, have increased with the amount of wood sawdust in blends and with the irradiation dose. Even if the gel fraction values have varied irregularly with the amount of wood sawdust and irradiation dose it was over 90% for all blends, except for the samples without wood sawdust irradiated with 75 kGy. The water uptake increased with increasing of fiber content and decreased with the irradiation dose.

The Improvement of the Resistance to Candida albicans and Trichophyton interdigitale of Some Woven Fabrics Based on Cotton

This paper presents the improvement of the antimicrobial character of woven fabrics based on cotton. The woven fabrics were cleaned in oxygen plasma and treated by padding with silver chloride and titanium dioxide particles. The existence of silver and titanium on woven fabrics was evidenced by electronic microscope images (SEM, EDAX) and by flame atomic absorption spectrophotometry. The antimicrobial tests were performed with two fungi: Candida albicans and Trichophyton interdigitale. The obtained antimicrobial effect was considerably higher compared to the raw fabrics. Treatment of dyed fabrics with a colloidal solution based on silver chloride and titanium dioxide particles does not considerably influence colour resistance of dyes.

Combined effects of microwaves, electron beams and polyfunctional monomers on rubber vulcanization

This paper presents comparative results obtained by conventional vulcanization with benzoyl peroxide (CV-BP), separate electron beam vulcanization (EB-V) and simultaneous electron beam and microwave vulcanization (EB+MW-V) applied to two kind of rubber samples: EVA (ethylene vinyl acetate) rubber-sample (EVA-sample) and EPDM (ethylene-propylene terpolymer) rubber-sample (EPDM-sample). The EVA-samples contain 61.54% EVA Elvax 260, 30.77% carbon black, 1.85% TAC (triallylcyanurate) polyfunctional monomer and 5.84% filler (zinc oxide, stearic acid, polyethylene glycol and antioxidant). The EPDM-samples contain 61.54% EPDM Nordel 4760, 30.77% carbon black, 1.85% TMPT (trimethylopropane trimethacrylate) polyfunctional monomer and 5.84% filler (zinc oxide, stearic acid, polyethylene glycol and antioxidant). The rubber samples designed for different vulcanization methods were obtained from raw rubber mixtures, as compressed sheets of 2 mm in the polyethylene foils to minimize oxidation. For EB and EB + MW treatments the sheets were cut in rectangular shape 0.15 x 0.15 m2. The physical properties of samples obtained by CV-BP EV-Vand EB + MW-V methods were evaluated by measuring the tearing strength, residual elongation, elongation at break, tensile strength, 300% modulus, 100% modulus, elasticity and hardness. The obtained results demonstrate an improvement of rubber several properties obtained by EB and EB + MW processing as compared to classical procedure using benzoyl peroxide.

Vaccine preparation by radiation processing

A new radiation biotechnology for the acquirement of a commercial vaccine, designed for prophylaxis of ruminant infectious pododermatitis (IP), produced by gram negative bacteria Fusobacterium necrophorum (F.n.), is presented. Two different processes for preparing F.n. vaccine are used: a) the inactivation of F.n. bacteria exotoxins by microwave (MW) or/and electron beams (EB) irradiation; b) the isolation of exotoxins from F.n. cultures irradiated with MW or/and EB and the inactivation of isolated F.n. exotoxins with formalin. The EB irradiation of F.n. cultures produced simultaneously with the cells viability decrease an increasing of exotoxin quantity released in the culture supranatant as compared with classical methods. The MW irradiation is able to reduce the cells viability to zero but without an increase of exotoxin quantity in cultures supranatant. Instead of this MW irradiation, for certain conditions, is able to induce an important stimulation degree of the F.n. proliferation in cultures, from two to three log10. Two vaccine types were prepared: A1 vaccine that contains whole cell culture irradiated with MW/EB and A2 vaccine that contains cell-free culture supernatant of an MW/EB irradiated F.n. strain producing exotoxins. Also, other two vaccines are prepared: B1 and B2 that contain the same materials as A1 and A2 respectively, but without using MW/EB exposure. The vaccine efficiency is tested in ruminant farms in which IP evolves. It is expected that this new vaccine to offer a better protection, more than 60%, which is the best presently obtained result in ruminant farms.

Combined microwave and electron beam exposure facilities for medical studies and applications

The paper presents two radiation exposure facilities (REFs) which permit separate and simultaneous irradiation with microwaves (MW) of 2.45 GHz and electron beams (EB) of 6.23 MeV for malignant melanoma (MM) cell investigations, in vitro (MW+EB-REF-vitro) and in vivo (MW+EB-REF-vivo). The REFs are specifically designed for the following medical studies: 1) The effects of separate and combined (successive and simultaneous) MW and EB irradiation on the B16F10 mouse--MM cell cultures without/with drugs incubation, 2) The effects of separate and combined MW and EB irradiation on human blood components irradiated in samples of integral blood from healthy donors and from donors with MM; 3) The effects of separate and combined MW and EB whole body irradiation on the C57 BL/6 mice bearing MM without/with drugs administration. Several representative results obtained by experiments with REFs in vitro and in vivo are discussed. The most important conclusion of the experimental results is that low dose-total body MW+EB irradiation combined with drugs administration could present a valuable potential for an advanced study in malignant melanoma therapy.

Cell investigations simultaneously with exposure to 2.45 GHz microwaves

The paper presents two microwave (MW) exposure systems (MWESs) that permit observations and measurements on cell cultures during their exposure to MW of 2.45 GHz: MWES-1 and MWES-2. MWES-1 is designed for the measurement of the cell membrane fluorescence anisotropies (MFA) simultaneously with MW exposure. MWES-2 is designed for the cells culture exploration under an inverted microscope before, during and after MW exposure. MWES-1 consists mainly of a 2.45 GHz microwave generator (MWG-2.45 GHz-SAIREM) of 0-25 W, equipped with forward power and reflected power displaying, and an adjustable coaxial antenna immersed directly into the cuvette with the cells-suspension of a Spex type spectrofluorometer. The MW effect on membrane fluidity of B16F10 malignant melanoma (B16F10-MM) cells in suspension were investigated with MWES-1, by MFA measurements. We observed a MW induced transition temperature (ITT) rising strongly during the MW exposure as compared with ITT obtained by classical heating (CH). The MWES-2 consists of the MWG-2.45 GHz-SAIREM generator and a rectangular waveguide applicator with traveling wave placed between the condenser and the objective of a Zeiss Axiovert 200 microscope, equipped with a fluorescence device and image acquisition. The MW effects on shape and apoptosis of the B16F10-MM cells were investigate with MWES-2. The B16F10-MM cells exhibited visible shape changes during MW exposure up to 37 degrees C. The MW exposure induced cells apoptosis/necrosis in several seconds after that MW are applied, beginning with SAR = 1.5 W/sample, compared to CH controls exposed at the same temperature dynamics.