Huang Z, Zhou H, Yuan F, Wu J, Yuan S, Cai K, Tao X, Zhang X, Tang C, Chen J. Investigation on the Osteogenic and Antibacterial Properties of Silicon Nitride-Coated Titanium Dental Implants. ACS Biomater Sci Eng 2024; 10:4059-4072. [PMID: 38748565 DOI: 10.1021/acsbiomaterials.4c00427] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 06/11/2024]
Abstract
The silicon nitride (Si3N4) coating exhibits promising potential in oral applications due to its excellent osteogenic and antibacterial properties. However, a comprehensive investigation of Si3N4 coatings in the context of dental implants is still lacking, especially regarding their corrosion resistance and in vivo performance. In this study, Si3N4 coatings were prepared on a titanium surface using the nonequilibrium magnetron sputtering method. A systematic comparison among the titanium group (Ti), Si3N4 coating group (Si3N4-Ti), and sandblasted and acid-etched-treated titanium group (SLA-Ti) has been conducted in vitro and in vivo. The results showed that the Si3N4-Ti group had the best corrosion resistance and antibacterial properties, which were mainly attributed to the dense structure and chemical activity of Si-O and Si-N bonds on the surface. Furthermore, the Si3N4-Ti group exhibited superior cellular responses in vitro and new bone regeneration and osseointegration in vivo, respectively. In this sense, silicon nitride coating shows promising prospects in the field of dental implantology.
Collapse
Affiliation(s)
- Zhiquan Huang
- Jiangsu Key Laboratory of Advanced Metallic Materials, School of Materials Science and Engineering, Southeast University, Nanjing 211189, China
| | - Heyang Zhou
- Department of Dental Implantology, The Affiliated Stomatological Hospital of Nanjing Medical University, Nanjing 210029, China
- Jiangsu Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing 210029, China
| | - Fang Yuan
- Department of Dental Implantology, The Affiliated Stomatological Hospital of Nanjing Medical University, Nanjing 210029, China
- Jiangsu Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing 210029, China
| | - Jin Wu
- Department of Dental Implantology, The Affiliated Stomatological Hospital of Nanjing Medical University, Nanjing 210029, China
- Jiangsu Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing 210029, China
| | - Shanshan Yuan
- Department of Dental Implantology, The Affiliated Stomatological Hospital of Nanjing Medical University, Nanjing 210029, China
- Jiangsu Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing 210029, China
| | - Kunzhan Cai
- Department of Dental Implantology, The Affiliated Stomatological Hospital of Nanjing Medical University, Nanjing 210029, China
- Jiangsu Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing 210029, China
| | - Xiao Tao
- Jiangsu Key Laboratory of Advanced Metallic Materials, School of Materials Science and Engineering, Southeast University, Nanjing 211189, China
| | - Xiyu Zhang
- Jiangsu Key Laboratory of Advanced Metallic Materials, School of Materials Science and Engineering, Southeast University, Nanjing 211189, China
| | - Chunbo Tang
- Department of Dental Implantology, The Affiliated Stomatological Hospital of Nanjing Medical University, Nanjing 210029, China
- Jiangsu Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing 210029, China
| | - Jian Chen
- Jiangsu Key Laboratory of Advanced Metallic Materials, School of Materials Science and Engineering, Southeast University, Nanjing 211189, China
| |
Collapse
|
2
|
Echeverri E, Skjöldebrand C, O'Callaghan P, Palmquist A, Kreuger J, Hulsart-Billström G, Persson C. Fe and C additions decrease the dissolution rate of silicon nitride coatings and are compatible with microglial viability in 3D collagen hydrogels. Biomater Sci 2023; 11:3144-3158. [PMID: 36919682 DOI: 10.1039/d2bm02074b] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 03/16/2023]
Abstract
Silicon nitride (SiN) coatings may reduce unwanted release of metal ions from metallic implants. However, as SiN slowly dissolves in aqueous solutions, additives that reduce this dissolution rate would likely increase the lifetime and functionality of implants. Adding iron (Fe) and carbon (C) permits tuning of the SiN coatings' mechanical properties, but their effect on SiN dissolution rates, and their capacity to reduce metal ion release from metallic implant substrates, have yet to be investigated. Such coatings have recently been proposed for use in spinal implants; therefore, it is relevant to assess their impact on the viability of cells expected at the implant site, such as microglia, the resident macrophages of the central nervous system (CNS). To study the effects of Fe and C on the dissolution rate of SiN coatings, compositional gradients of Si, Fe and C in combination with N were generated by physical vapor deposition onto CoCrMo discs. Differences in composition did not affect the surface roughness or the release of Si, Fe or Co ions (the latter from the CoCrMo substrate). Adding Fe and C reduced ion release compared to a SiN reference coating, which was attributed to altered reactivity due to an increase in the fraction of stabilizing Si-C or Fe-C bonds. Extracts from the SiN coatings containing Fe and C were compatible with microglial viability in 2D cultures and 3D collagen hydrogels, to a similar degree as CoCrMo and SiN coated CoCrMo reference extracts. As Fe and C reduced the dissolution rate of SiN-coatings and did not compromise microglial viability, the capacity of these additives to extend the lifetime and functionality of SiN-coated metallic implants warrants further investigation.
Collapse
Affiliation(s)
- Estefanía Echeverri
- Division of Biomedical Engineering, Department of Materials Science and Engineering, Uppsala University, Sweden.
| | - Charlotte Skjöldebrand
- Division of Biomedical Engineering, Department of Materials Science and Engineering, Uppsala University, Sweden.
| | - Paul O'Callaghan
- Department of Medical Cell Biology, Science for Life Laboratory, Uppsala University, Sweden
| | | | - Johan Kreuger
- Department of Medical Cell Biology, Science for Life Laboratory, Uppsala University, Sweden
| | - Gry Hulsart-Billström
- Translational PET Imaging, Department of Medicinal Chemistry, Uppsala University, Sweden
| | - Cecilia Persson
- Division of Biomedical Engineering, Department of Materials Science and Engineering, Uppsala University, Sweden.
| |
Collapse
|
3
|
Nikolova MP, Apostolova MD. Advances in Multifunctional Bioactive Coatings for Metallic Bone Implants. MATERIALS (BASEL, SWITZERLAND) 2022; 16:183. [PMID: 36614523 PMCID: PMC9821663 DOI: 10.3390/ma16010183] [Citation(s) in RCA: 8] [Impact Index Per Article: 4.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Subscribe] [Scholar Register] [Received: 12/09/2022] [Revised: 12/19/2022] [Accepted: 12/21/2022] [Indexed: 06/17/2023]
Abstract
To fix the bone in orthopedics, it is almost always necessary to use implants. Metals provide the needed physical and mechanical properties for load-bearing applications. Although widely used as biomedical materials for the replacement of hard tissue, metallic implants still confront challenges, among which the foremost is their low biocompatibility. Some of them also suffer from excessive wear, low corrosion resistance, infections and shielding stress. To address these issues, various coatings have been applied to enhance their in vitro and in vivo performance. When merged with the beneficial properties of various bio-ceramic or polymer coatings remarkable bioactive, osteogenic, antibacterial, or biodegradable composite implants can be created. In this review, bioactive and high-performance coatings for metallic bone implants are systematically reviewed and their biocompatibility is discussed. Updates in coating materials and formulations for metallic implants, as well as their production routes, have been provided. The ways of improving the bioactive coating performance by incorporating bioactive moieties such as growth factors, osteogenic factors, immunomodulatory factors, antibiotics, or other drugs that are locally released in a controlled manner have also been addressed.
Collapse
Affiliation(s)
- Maria P. Nikolova
- Department of Material Science and Technology, University of Ruse “A. Kanchev”, 8 Studentska Str., 7017 Ruse, Bulgaria
| | - Margarita D. Apostolova
- Medical and Biological Research Lab., “Roumen Tsanev” Institute of Molecular Biology, Bulgarian Academy of Sciences, 1113 Sofia, Bulgaria
| |
Collapse
|
4
|
Skjöldebrand C, Tipper JL, Hatto P, Bryant M, Hall RM, Persson C. Current status and future potential of wear-resistant coatings and articulating surfaces for hip and knee implants. Mater Today Bio 2022; 15:100270. [PMID: 35601891 PMCID: PMC9118168 DOI: 10.1016/j.mtbio.2022.100270] [Citation(s) in RCA: 8] [Impact Index Per Article: 4.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/07/2022] [Revised: 04/09/2022] [Accepted: 04/24/2022] [Indexed: 10/29/2022] Open
Abstract
Hip and knee joint replacements are common and largely successful procedures that utilise implants to restore mobility and relieve pain for patients suffering from e.g. osteoarthritis. However, metallic ions and particles released from both the bearing surfaces and non-articulating interfaces, as in modular components, can cause hypersensitivity and local tissue necrosis, while particles originating from a polymer component have been associated with aseptic loosening and osteolysis. Implant coatings have the potential to improve properties compared to both bulk metal and ceramic alternatives. Ceramic coatings have the potential to increase scratch resistance, enhance wettability and reduce wear of the articulating surfaces compared to the metallic substrate, whilst maintaining overall toughness of the implant ensuring a lower risk of catastrophic failure of the device compared to use of a bulk ceramic. Coatings can also act as barriers to inhibit ion release from the underlying material caused by corrosion. This review aims to provide a comprehensive overview of wear-resistant coatings for joint replacements - both those that are in current clinical use as well as those under investigation for future use. While the majority of coatings belong predominantly in the latter group, a few coated implants have been successfully marketed and are available for clinical use in specific applications. Commercially available coatings for implants include titanium nitride (TiN), titanium niobium nitride (TiNbN), oxidized zirconium (OxZr) and zirconium nitride (ZrN) based coatings, whereas current research is focused not only on these, but also on diamond-like-carbon (DLC), silicon nitride (SiN), chromium nitride (CrN) and tantalum-based coatings (TaN and TaO). The coating materials referred to above that are still at the research stage have been shown to be non-cytotoxic and to reduce wear in a laboratory setting. However, the adhesion of implant coatings remains a main area of concern, as poor adhesion can cause delamination and excessive wear. In clinical applications zirconium implant surfaces treated to achieve a zirconium oxide film and TiNbN coated implants have however been proven comparable to traditional cobalt chromium implants with regards to revision numbers. In addition, the chromium ion levels measured in the plasma of patients were lower and allergy symptoms were relieved. Therefore, coated implants could be considered an alternative to uncoated metal implants, in particular for patients with metal hypersensitivity. There have also been unsuccessful introductions to the market, such as DLC coated implants, and therefore this review also attempts to summarize the lessons learnt.
Collapse
Affiliation(s)
| | - Joanne L. Tipper
- University of Technology Sydney, School of Biomedical Engineering, Sydney, Australia
| | | | - Michael Bryant
- University of Leeds, Department of Mechanical Engineering, Leeds, United Kingdom
| | - Richard M. Hall
- University of Leeds, Department of Mechanical Engineering, Leeds, United Kingdom
| | - Cecilia Persson
- Uppsala University, Department of Materials Science and Engineering, Uppsala, Sweden
| |
Collapse
|
5
|
Skjöldebrand C, Echeverri E, Hulsart-Billström G, Persson C. Tailoring the dissolution rate and in vitro cell response of silicon nitride coatings through combinatorial sputtering with chromium and niobium. Biomater Sci 2022; 10:3757-3769. [PMID: 35622079 DOI: 10.1039/d1bm01978c] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/21/2022]
Abstract
Ceramic coatings have been widely investigated as a means to reduce wear and metallic ion release from joint implants. Silicon nitride-based coatings have been a topic of interest specifically due to their solubility in aqueous solutions. This could imply a reduced adverse immune response since the generated debris would dissolve. However, there are concerns regarding the dissolution rate and adhesion of these silicon nitride-based coatings. This study attempts to address the concern of dissolution rate as well as coating adhesion of silicon nitride coatings. We hypothesized that alloying with chromium and niobium would affect the adhesion, dissolution rate, and the resulting ion release and cell response to the coatings. A combinatorial approach was used to deposit sputtered coatings with compositional gradients both with and without a CrN interlayer. Compositional gradients were achieved for all the investigated elements: Si (38.6-46.9 at%), Nb (2.2-4.6 at%) and Cr (1.9-6.0 at%). However, while the presence of an interlayer reduced the delamination during adhesion testing, the differences in composition in the top coating did not affect the adhesion. Nor did the top coating's composition affect the surface roughness or the coatings' inherent mechanical properties (elastic modulus and hardness). All coating compositions were associated with a low Co release from the underlying metal and points with a higher Cr content (4.3-6.0 at%) gave an overall lower release of Si, Cr and Nb ions, possibly due to the formation of a stable oxide, which reduced the dissolution rate of the coating. Optimum chromium contents were furthermore found to give an enhanced in vitro fibroblast cell viability. In conclusion, the results indicate a possibility to tailor the ion release rate, which lends promise to further investigations such as tribocorrosive tests towards a future biomedical application.
Collapse
Affiliation(s)
- Charlotte Skjöldebrand
- Division of Biomedical Engineering, Department of Materials Science and Engineering, Uppsala University, Sweden.
| | - Estefanía Echeverri
- Division of Biomedical Engineering, Department of Materials Science and Engineering, Uppsala University, Sweden.
| | - Gry Hulsart-Billström
- Translational Imaging, Department of Medicinal Chemistry, Uppsala University, Sweden
| | - Cecilia Persson
- Division of Biomedical Engineering, Department of Materials Science and Engineering, Uppsala University, Sweden.
| |
Collapse
|
6
|
Haschke H, Falkenberg A, Morlock MM, Huber G. Do SiNx coatings bear the potential to reduce the risk of micromotion in modular taper junctions? Proc Inst Mech Eng H 2020; 234:897-908. [PMID: 32507037 DOI: 10.1177/0954411920930616] [Citation(s) in RCA: 3] [Impact Index Per Article: 0.8] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/17/2022]
Abstract
Fretting corrosion is one contributor to the clinical failure of modular joint arthroplasty. It is initiated by micromotion in metal junctions exposed to fluids. Omitting metal-on-metal contacts could help to reduce the corrosion risk. The coating of one metal taper partner with a ceramic-based silicon nitride (SiNx) coating might provide this separation. The aim of the study was to identify whether a SiNx coating of the male taper component influences the micromotion within a taper junction. Hip prosthesis heads made of CoCr29Mo6 (Aesculap) and Ti6Al4V (Peter Brehm) were assembled (2000 N) to SiNx-coated and uncoated stem tapers made of Ti6Al4V and CoCr29Mo6 (2×2×2 combinations, each n = 4). Consecutive sinusoidal loading representing three daily activities was applied. Contactless relative motion in six degrees of freedom was measured using six eddy-current sensors. Micromotion in the junction was determined by compensating for the elastic deformation derived from additional monoblock measurements. After pull-off, the taper surfaces were microscopically inspected. Micromotion magnitude reached up to 8.4 ± 0.8 µm during loading that represented stumbling. Ti6Al4V stems showed significantly higher micromotion than those made of CoCr29Mo6, while taper coating had no influence. Statistical differences in pull-off forces were found for none of the taper junctions. Microscopy revealed CoCr29Mo6 abrasion from the head taper surface if combined with coated stem tapers. Higher micromotion of Ti6Al4V tapers was probably caused by the lower Young's modulus. Even in the contact areas, the coating was not damaged during loading. The mechanics of coated tapers was similar to uncoated prostheses. Thus, the separation of the two metal surfaces with the objective to reduce in vivo corrosion appears to be achievable if the coating is able to withstand in vivo conditions. However, the hard ceramic-based stem coating lead to undesirable debris from the CoCr29Mo6 heads during loading.
Collapse
Affiliation(s)
- Henning Haschke
- Institute of Biomechanics, Hamburg University of Technology (TUHH), Hamburg, Germany
| | - Adrian Falkenberg
- Institute of Biomechanics, Hamburg University of Technology (TUHH), Hamburg, Germany
| | - Michael M Morlock
- Institute of Biomechanics, Hamburg University of Technology (TUHH), Hamburg, Germany
| | - Gerd Huber
- Institute of Biomechanics, Hamburg University of Technology (TUHH), Hamburg, Germany
| |
Collapse
|
7
|
Skjöldebrand C, Hulsart-Billström G, Engqvist H, Persson C. Si-Fe-C-N Coatings for Biomedical Applications: A Combinatorial Approach. MATERIALS (BASEL, SWITZERLAND) 2020; 13:E2074. [PMID: 32366008 PMCID: PMC7254256 DOI: 10.3390/ma13092074] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 03/26/2020] [Revised: 04/15/2020] [Accepted: 04/23/2020] [Indexed: 11/17/2022]
Abstract
Ceramic coatings may prolong the lifetime of joint implants. Certain ions and wear debris may however lead to negative biological effects. SiN-based materials may substantially reduce these effects, but still need optimization for the application. In this study, a combinatorial deposition method enabled an efficient evaluation of a range of Si-Fe-C-N coating compositions on the same sample. The results revealed compositional gradients of Si (26.0-33.9 at.%), Fe (9.6-20.9 at.%), C (8.2-13.9 at.%) and N (39.7-47.2 at.%), and low oxygen contaminations (0.3-0.6 at.%). The mechanical properties varied with a hardness (H) ranging between 13.7-17.3 GPa and an indentation modulus (M) between 190-212 GPa. Both H and M correlated with the Si (H and M increased as Si increased) and Fe (H and M decreased as Fe increased) content. A slightly columnar morphology was observed in cross-sections, as well as a surface roughness in the nm range. A cell study revealed adhering pre-osteogenic MC3T3 cells, with a morphology similar to that of cells seeded on a tissue culture plastic control. The investigated coatings could be considered for further investigation due to the ability to tune their mechanical properties while maintaining a smooth surface, together with their promising in vitro cell response.
Collapse
Affiliation(s)
- Charlotte Skjöldebrand
- Department of Materials Science and Engineering, Faculty of Science and Technology, Uppsala University, 752 37 Uppsala, Sweden; (C.S.); (H.E.)
| | - Gry Hulsart-Billström
- Department of Surgical Sciences, Faculty of Medicine and Pharmacy, Uppsala University, 751 83 Uppsala, Sweden;
| | - Håkan Engqvist
- Department of Materials Science and Engineering, Faculty of Science and Technology, Uppsala University, 752 37 Uppsala, Sweden; (C.S.); (H.E.)
| | - Cecilia Persson
- Department of Materials Science and Engineering, Faculty of Science and Technology, Uppsala University, 752 37 Uppsala, Sweden; (C.S.); (H.E.)
| |
Collapse
|
8
|
The Effect of N, C, Cr, and Nb Content on Silicon Nitride Coatings for Joint Applications. MATERIALS 2020; 13:ma13081896. [PMID: 32316517 PMCID: PMC7216083 DOI: 10.3390/ma13081896] [Citation(s) in RCA: 4] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 02/29/2020] [Revised: 04/12/2020] [Accepted: 04/14/2020] [Indexed: 12/23/2022]
Abstract
Ceramic coatings deposited on orthopedic implants are an alternative to achieve and maintain high wear resistance of the metallic device, and simultaneously allow for a reduction in metal ion release. Silicon nitride based (SiNx) coatings deposited by high power impulse magnetron sputtering (HiPIMS) have shown potential for use in joint replacements, as a result of an improved chemical stability in combination with a good adhesion. This study investigated the effect of N, C, Cr, and Nb content on the tribocorrosive performance of 3.7 to 8.8 µm thick SiNx coatings deposited by HiPIMS onto CoCrMo discs. The coating composition was assessed from X-ray photoelectron spectroscopy and the surface roughness by vertical scanning interferometry. Hardness and Young's modulus were measured by nanoindentation and coating adhesion was investigated by scratch tests. Multidirectional wear tests against ultrahigh molecular weight polyethylene pins were performed for 2 million cycles in bovine serum solution (25%) at 37 °C, at an estimated contact pressure of 2.1 MPa. Coatings with a relatively low hardness tended to fail earlier in the wear test, due to chemical reactions and eventually dissolution, accelerated by the tribological contact. In fact, while no definite correlation could be observed between coating composition (N: 42.6-55.5 at %, C: 0-25.7 at %, Cr: 0 or 12.8 at %, and Nb: 0-24.5 at %) and wear performance, it was apparent that high-purity and/or -density coatings (i.e., low oxygen content and high nitrogen content) were desirable to prevent coating and/or counter surface wear or failure. Coatings deposited with a higher energy fulfilled the target profile in terms of low surface roughness (Ra < 20 nm), adequate adhesion (Lc2 > 30 N), chemical stability over time in the tribocorrosive environment, as well as low polymer wear, presenting potential for a future application in joint bearings.
Collapse
|
9
|
Zaidi UZ, Mahmoodian R, Bushroa AR, Vellasamy KM. Surface modification of Ti64-Alloy with silver silicon nitride thin films. JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY 2019; 33:2476-2493. [DOI: 10.1080/01694243.2019.1646462] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Subscribe] [Scholar Register] [Received: 03/16/2019] [Revised: 07/14/2019] [Accepted: 07/15/2019] [Indexed: 09/02/2023]
Affiliation(s)
- Umi Zalilah Zaidi
- Department of Mechanical Engineering, Faculty of Engineering, University of Malaya, Kuala Lumpur, Malaysia
| | - Reza Mahmoodian
- School of Mechanical Engineering, Engineering Campus, Universiti Sains Malaysia (USM), Nibong Tebal, Malaysia
- Department of Research and Development, Azarin Kar Ind. Co., Kerman, Iran
- Center of Advanced Manufacturing and Material Processing (AMMP), Department of Engineering, University of Malaya, Kuala Lumpur, Malaysia
| | - Abd Razak Bushroa
- Department of Mechanical Engineering, Faculty of Engineering, University of Malaya, Kuala Lumpur, Malaysia
- Center of Advanced Manufacturing and Material Processing (AMMP), Department of Engineering, University of Malaya, Kuala Lumpur, Malaysia
| | - Kumutha Malar Vellasamy
- Department of Medical Microbiology, Faculty of Medicine, University of Malaya, Kuala Lumpur, Malaysia
| |
Collapse
|
10
|
Filho LC, Schmidt S, López A, Cogrel M, Leifer K, Engqvist H, Högberg H, Persson C. The Effect of Coating Density on Functional Properties of SiN x Coated Implants. MATERIALS (BASEL, SWITZERLAND) 2019; 12:E3370. [PMID: 31618981 PMCID: PMC6829552 DOI: 10.3390/ma12203370] [Citation(s) in RCA: 4] [Impact Index Per Article: 0.8] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 09/12/2019] [Revised: 10/08/2019] [Accepted: 10/12/2019] [Indexed: 11/17/2022]
Abstract
Ceramic coatings may be applied onto metallic components of joint replacements for improved wear and corrosion resistance as well as enhanced biocompatibility, especially for metal-sensitive patients. Silicon nitride (SiNx) coatings have recently been developed for this purpose. To achieve a high coating density, necessary to secure a long-term performance, is however challenging, especially for sputter deposited SiNx coatings, since these coatings are insulating. This study investigates the time-dependent performance of sputter-deposited SiNx based coatings for joint applications. SiNx coatings with a thickness in the range of 4.3-6.0 µm were deposited by reactive high power impulse magnetron sputtering onto flat discs as well as hip heads made of CoCrMo. SiNx compositional analysis by X-ray photoelectron spectroscopy showed N/Si ratios between 0.8 and 1.0. Immersion of the flat disks in fetal bovine serum solution over time as well as short-term wear tests against ultra-high molecular weight polyethylene (UHMWPE) discs showed that a high coating density is required to inhibit tribocorrosion. Coatings that performed best in terms of chemical stability were deposited using a higher target power and process heating.
Collapse
Affiliation(s)
- Luimar Correa Filho
- Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, 75121 Uppsala, Sweden.
| | - Susann Schmidt
- Thin Film Physics Division, Department of Physics, Chemistry and Biology (IFM), Linköping University, 58183 Linköping, Sweden.
| | - Alejandro López
- Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, 75121 Uppsala, Sweden.
| | - Mathilde Cogrel
- Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, 75121 Uppsala, Sweden.
| | - Klaus Leifer
- Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, 75121 Uppsala, Sweden.
| | - Håkan Engqvist
- Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, 75121 Uppsala, Sweden.
| | - Hans Högberg
- Thin Film Physics Division, Department of Physics, Chemistry and Biology (IFM), Linköping University, 58183 Linköping, Sweden.
| | - Cecilia Persson
- Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, 75121 Uppsala, Sweden.
| |
Collapse
|
11
|
Abstract
Silicon nitride (SiNx) coatings are currently under investigation as bearing surfaces for joint implants, due to their low wear rate and the good biocompatibility of both coatings and their potential wear debris. The aim of this study was to move further towards functional SiNx coatings by evaluating coatings deposited onto CoCrMo surfaces with a CrN interlayer, using different bias voltages and substrate rotations. Reactive direct current magnetron sputtering was used to coat CoCrMo discs with a CrN interlayer, followed by a SiNx top layer, which was deposited by reactive high-power impulse magnetron sputtering. The interlayer was deposited using negative bias voltages ranging between 100 and 900 V, and 1-fold or 3-fold substrate rotation. Scanning electron microscopy showed a dependence of coating morphology on substrate rotation. The N/Si ratio ranged from 1.10 to 1.25, as evaluated by X-ray photoelectron spectroscopy. Vertical scanning interferometry revealed that the coated, unpolished samples had a low average surface roughness between 16 and 33 nm. Rockwell indentations showed improved coating adhesion when a low bias voltage of 100 V was used to deposit the CrN interlayer. Wear tests performed in a reciprocating manner against Si3N4 balls showed specific wear rates lower than, or similar to that of CoCrMo. The study suggests that low negative bias voltages may contribute to a better performance of SiNx coatings in terms of adhesion. The low wear rates found in the current study support further development of silicon nitride-based coatings towards clinical application.
Collapse
|
12
|
Lal S, Caseley EA, Hall RM, Tipper JL. Biological Impact of Silicon Nitride for Orthopaedic Applications: Role of Particle Size, Surface Composition and Donor Variation. Sci Rep 2018; 8:9109. [PMID: 29904079 PMCID: PMC6002550 DOI: 10.1038/s41598-018-27494-y] [Citation(s) in RCA: 17] [Impact Index Per Article: 2.8] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/08/2018] [Accepted: 05/23/2018] [Indexed: 01/29/2023] Open
Abstract
The adverse biological impact of orthopaedic wear debris currently limits the long-term safety of human joint replacement devices. We investigated the role of particle size, surface composition and donor variation in influencing the biological impact of silicon nitride as a bioceramic for orthopaedic applications. Silicon nitride particles were compared to the other commonly used orthopaedic biomaterials (e.g. cobalt-chromium and Ti-6Al-4V alloys). A novel biological evaluation platform was developed to simultaneously evaluate cytotoxicity, inflammatory cytokine release, oxidative stress, and genotoxicity potential of particles using peripheral blood mononuclear cells (PBMNCs) from individual human donors. Irrespective of the particle size, silicon nitride did not cause any adverse responses whereas cobalt-chromium wear particles caused donor-dependent cytotoxicity, TNF-α cytokine release, oxidative stress, and DNA damage in PBMNCs after 24 h. Despite being similar in size and morphology, silicon dioxide nanoparticles caused the release of significantly higher levels of TNF-α compared to silicon nitride nanoparticles, suggesting that surface composition influences the inflammatory response in PBMNCs. Ti-6Al-4V wear particles also released significantly elevated levels of TNF-α cytokine in one of the donors. This study demonstrated that silicon nitride is an attractive orthopaedic biomaterial due to its minimal biological impact on human PBMNCs.
Collapse
Affiliation(s)
- Saurabh Lal
- School of Biomedical Sciences, University of Leeds, LS2 9JT, Leeds, UK.
- School of Mechanical Engineering, University of Leeds, LS2 9JT, Leeds, UK.
| | - Emily A Caseley
- School of Biomedical Sciences, University of Leeds, LS2 9JT, Leeds, UK
- School of Mechanical Engineering, University of Leeds, LS2 9JT, Leeds, UK
| | - Richard M Hall
- School of Mechanical Engineering, University of Leeds, LS2 9JT, Leeds, UK
| | - Joanne L Tipper
- School of Biomedical Sciences, University of Leeds, LS2 9JT, Leeds, UK
- School of Mechanical Engineering, University of Leeds, LS2 9JT, Leeds, UK
| |
Collapse
|
13
|
Grieco PW, Pascal S, Newman JM, Shah NV, Stroud SG, Sheth NP, Maheshwari AV. New alternate bearing surfaces in total hip arthroplasty: A review of the current literature. J Clin Orthop Trauma 2018; 9:7-16. [PMID: 29628677 PMCID: PMC5884051 DOI: 10.1016/j.jcot.2017.10.013] [Citation(s) in RCA: 14] [Impact Index Per Article: 2.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 08/21/2017] [Accepted: 10/26/2017] [Indexed: 01/01/2023] Open
Abstract
As indications for total hip arthroplasty (THA) have expanded, the incidence of THA has increased among younger patients, who live longer and tend to place more strain on implants via higher activity levels. This demographical shift accentuates the importance of advancing innovation to ensure implant longevity for younger and more active patients. Future innovation, as it pertains to THA components, is likely to focus on modifying implant designs and tribology in conjunction with identification and application of newer biomaterials. By reviewing the literature for development status of various materials and novel design advancements in THA component outside of the standard highly cross-linked polyethylene, this investigation provided an update on the current and future status of design initiatives as they pertain to THA. Though the highlighted alternative bearing surfaces have shown promising in vitro and limited, yet encouraging clinical data, they lack larger and longer-term clinical trial results. Further research and innovation is warranted to identify the optimal bearing surface to most effectively accommodate for the trend of younger and more active patients undergoing THA. Implant longevity is crucial if the clinical success of THA is to be maintained.
Collapse
Affiliation(s)
- Preston W. Grieco
- Department of Orthopaedic Surgery, State University of New York, Downstate Medical Center, Brooklyn, NY 11203, USA
| | - Scott Pascal
- Department of Orthopaedic Surgery, State University of New York, Downstate Medical Center, Brooklyn, NY 11203, USA
| | - Jared M. Newman
- Department of Orthopaedic Surgery, State University of New York, Downstate Medical Center, Brooklyn, NY 11203, USA
| | - Neil V. Shah
- Department of Orthopaedic Surgery, State University of New York, Downstate Medical Center, Brooklyn, NY 11203, USA
| | - Sarah G. Stroud
- Department of Orthopaedic Surgery, State University of New York, Downstate Medical Center, Brooklyn, NY 11203, USA
| | - Neil P. Sheth
- Department of Orthopaedic Surgery, Hospital of the University of Pennsylvania, 1 Cathcart 800 Spruce Street, Philadelphia, PA 19107, USA
| | - Aditya V. Maheshwari
- Department of Orthopaedic Surgery, State University of New York, Downstate Medical Center, Brooklyn, NY 11203, USA,Corresponding author at: Adult Reconstruction and Musculoskeletal Oncology Divisions SUNY Downstate Medical Center 450 Clarkson Ave., Box 3 Box 3 Box 30 Brooklyn, NY 11203, USA.
| |
Collapse
|
14
|
Skjöldebrand C, Schmidt S, Vuong V, Pettersson M, Grandfield K, Högberg H, Engqvist H, Persson C. Influence of Substrate Heating and Nitrogen Flow on the Composition, Morphological and Mechanical Properties of SiN x Coatings Aimed for Joint Replacements. MATERIALS (BASEL, SWITZERLAND) 2017; 10:E173. [PMID: 28772532 PMCID: PMC5459168 DOI: 10.3390/ma10020173] [Citation(s) in RCA: 9] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 10/04/2016] [Revised: 12/12/2016] [Accepted: 01/30/2017] [Indexed: 11/17/2022]
Abstract
Silicon nitride (SiNx) coatings are promising for joint replacement applications due to their high wear resistance and biocompatibility. For such coatings, a higher nitrogen content, obtained through an increased nitrogen gas supply, has been found to be beneficial in terms of a decreased dissolution rate of the coatings. The substrate temperature has also been found to affect the composition as well as the microstructure of similar coatings. The aim of this study was to investigate the effect of the substrate temperature and nitrogen flow on the coating composition, microstructure and mechanical properties. SiNx coatings were deposited onto CoCrMo discs using reactive high power impulse magnetron sputtering. During deposition, the substrate temperatures were set to 200 °C, 350 °C or 430 °C, with nitrogen-to-argon flow ratios of 0.06, 0.17 or 0.30. Scanning and transmission electron spectroscopy revealed that the coatings were homogenous and amorphous. The coatings displayed a nitrogen content of 23-48 at.% (X-ray photoelectron spectroscopy). The surface roughness was similar to uncoated CoCrMo (p = 0.25) (vertical scanning interferometry). The hardness and Young's modulus, as determined from nanoindentation, scaled with the nitrogen content of the coatings, with the hardness ranging from 12 ± 1 GPa to 26 ± 2 GPa and the Young's moduli ranging from 173 ± 8 GPa to 293 ± 18 GPa, when the nitrogen content increased from 23% to 48%. The low surface roughness and high nano-hardness are promising for applications exposed to wear, such as joint implants.
Collapse
Affiliation(s)
- Charlotte Skjöldebrand
- Materials in Medicine group, Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, Uppsala 752 37, Sweden.
| | - Susann Schmidt
- Thin Film Physics Division, Department of Physics, Chemistry and Biology (IFM), Linköping University, Linköping 581 83, Sweden.
| | - Vicky Vuong
- Department of Materials Science and Engineering, McMaster University, Hamilton, ON L8S 4L7, Canada.
| | - Maria Pettersson
- Materials in Medicine group, Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, Uppsala 752 37, Sweden.
| | - Kathryn Grandfield
- Department of Materials Science and Engineering, McMaster University, Hamilton, ON L8S 4L7, Canada.
| | - Hans Högberg
- Thin Film Physics Division, Department of Physics, Chemistry and Biology (IFM), Linköping University, Linköping 581 83, Sweden.
| | - Håkan Engqvist
- Materials in Medicine group, Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, Uppsala 752 37, Sweden.
| | - Cecilia Persson
- Materials in Medicine group, Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, Uppsala 752 37, Sweden.
| |
Collapse
|
15
|
Schmidt S, Hänninen T, Goyenola C, Wissting J, Jensen J, Hultman L, Goebbels N, Tobler M, Högberg H. SiNx Coatings Deposited by Reactive High Power Impulse Magnetron Sputtering: Process Parameters Influencing the Nitrogen Content. ACS APPLIED MATERIALS & INTERFACES 2016; 8:20385-20395. [PMID: 27414283 DOI: 10.1021/acsami.6b05830] [Citation(s) in RCA: 10] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 06/06/2023]
Abstract
Reactive high power impulse magnetron sputtering (rHiPIMS) was used to deposit silicon nitride (SiNx) coatings for biomedical applications. The SiNx growth and plasma characterization were conducted in an industrial coater, using Si targets and N2 as reactive gas. The effects of different N2-to-Ar flow ratios between 0 and 0.3, pulse frequencies, target power settings, and substrate temperatures on the discharge and the N content of SiNx coatings were investigated. Plasma ion mass spectrometry shows high amounts of ionized isotopes during the initial part of the pulse for discharges with low N2-to-Ar flow ratios of <0.16, while signals from ionized molecules rise with the N2-to-Ar flow ratio at the pulse end and during pulse-off times. Langmuir probe measurements show electron temperatures of 2-3 eV for nonreactive discharges and 5.0-6.6 eV for discharges in transition mode. The SiNx coatings were characterized with respect to their composition, chemical bond structure, density, and mechanical properties by X-ray photoelectron spectroscopy, X-ray reflectivity, X-ray diffraction, and nanoindentation, respectively. The SiNx deposition processes and coating properties are mainly influenced by the N2-to-Ar flow ratio and thus by the N content in the SiNx films and to a lower extent by the HiPIMS frequencies and power settings as well as substrate temperatures. Increasing N2-to-Ar flow ratios lead to decreasing growth rates, while the N content, coating densities, residual stresses, and the hardness increase. These experimental findings were corroborated by density functional theory calculations of precursor species present during rHiPIMS.
Collapse
Affiliation(s)
- Susann Schmidt
- Thin Film Physics Division, Department of Physics (IFM), Linköping University , SE-581 83 Linköping, Sweden
| | - Tuomas Hänninen
- Thin Film Physics Division, Department of Physics (IFM), Linköping University , SE-581 83 Linköping, Sweden
| | - Cecilia Goyenola
- Thin Film Physics Division, Department of Physics (IFM), Linköping University , SE-581 83 Linköping, Sweden
| | - Jonas Wissting
- Thin Film Physics Division, Department of Physics (IFM), Linköping University , SE-581 83 Linköping, Sweden
| | - Jens Jensen
- Thin Film Physics Division, Department of Physics (IFM), Linköping University , SE-581 83 Linköping, Sweden
| | - Lars Hultman
- Thin Film Physics Division, Department of Physics (IFM), Linköping University , SE-581 83 Linköping, Sweden
| | - Nico Goebbels
- IHI Ionbond AG , Industriestraße 211, CH-4600 Olten, Switzerland
| | - Markus Tobler
- IHI Ionbond AG , Industriestraße 211, CH-4600 Olten, Switzerland
| | - Hans Högberg
- Thin Film Physics Division, Department of Physics (IFM), Linköping University , SE-581 83 Linköping, Sweden
| |
Collapse
|
16
|
Pettersson M, Skjöldebrand C, Filho L, Engqvist H, Persson C. Morphology and Dissolution Rate of Wear Debris from Silicon Nitride Coatings. ACS Biomater Sci Eng 2016; 2:998-1004. [DOI: 10.1021/acsbiomaterials.6b00133] [Citation(s) in RCA: 9] [Impact Index Per Article: 1.1] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 12/13/2022]
Affiliation(s)
- Maria Pettersson
- Materials in Medicine Group,
Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, Lägerhyddsvägen 1, 752
37 Uppsala, Sweden
| | - Charlotte Skjöldebrand
- Materials in Medicine Group,
Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, Lägerhyddsvägen 1, 752
37 Uppsala, Sweden
| | - Luimar Filho
- Materials in Medicine Group,
Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, Lägerhyddsvägen 1, 752
37 Uppsala, Sweden
| | - Håkan Engqvist
- Materials in Medicine Group,
Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, Lägerhyddsvägen 1, 752
37 Uppsala, Sweden
| | - Cecilia Persson
- Materials in Medicine Group,
Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, Lägerhyddsvägen 1, 752
37 Uppsala, Sweden
| |
Collapse
|